• Resources Recycling
• /
• v.25 no.5
• /
• pp.75-83
• /
• 2016

AlN powder was prepared by carbon reduction and subsequent nitridation method through the scale-up experiments of 0.7 ~ 1.5 kg per batch. AlN powder was synthesized using the mixture of $Al_2O_3$ powder and carbon black at $1,550{\sim}1,750^{\circ}C$ for 0.5 ~ 4 hours under nitrogen atmosphere (flow rate of nitrogen gas: $10{\sim}40{\ell}/min$) at $2.0{\times}10^{-1}Torr$. Experimental results showed that $1,700{\sim}1,750^{\circ}C$ for the reaction temperature, 3 hr for reaction time, and $40{\ell}/min$ for the flow rate of nitrogen gas were the optimal conditions. Also, in order to remove carbon in the synthesized AlN, the remained carbon was removed at $650{\sim}750^{\circ}C$ for 1 ~ 2 hr using horizontal tube furnace. The results showed that 1 : 3.2 mol ratio of $Al_2O_3$ to carbon black, reaction temperature of $750^{\circ}C$, reaction time of 2 hours, rotating speed of 1.5 rpm under atmosphere condition were the optimal conditions. Under these conditions, high-purity AlN powder over 99% could be prepared: carbon and oxygen contents of the AlN powder were 835 ppm and 0.77%, respectively.

• Journal of Life Science
• /
• v.19 no.9
• /
• pp.1271-1276
• /
• 2009

Unlike the traditional preparation method for Chungkukjang, we prepared Dua-Chungkukjang with soybean fermented at $40^{\circ}C$ after the soaking, germination and steaming process, and we studied the physico-chemical characteristics of Dua-Chungkukjang. Reducing sugar content in both traditional Chungkukjang and Dua-Chungkukjang increased sharply after 10 hr of fermentation, but it decreased slightly after that. Total nitrogen content in both traditional Chungkukjang and Dua-Chungkukjang increased slowly as fermentation took place. Total nitrogen content reached 3,500 mg% and 3,700 mg%, and soluble nitrogen compound reached 750 mg% and 1,800 mg% after 40 hr of fermentation, respectively. $\beta$-Glucosidase activity increased continuously as fermentation took place, and it reached 193, 223, 235 and 248 units in Dua-Chungkukjang while it reached 125, 178, 205 and 214 units in traditional Chungkukjang after 10 hr, 20 hr, 30 hr and 40 hr of fermentation. This means that $\beta$-Glucosidase activity in Dua-Chungkukjang was $1.2{\sim}1.5$ times higher than that in the control treatment, traditional Chungkukjang. Total isoflavone content was $101.44{\mu}g$/g and $365.92{\mu}g$/g for 10 hr of fermentation, and $225.98{\mu}g$/g and $441.37{\mu}g$/g for 40 hr in traditional Chungkukjang and Dua-Chungkukjang, respectively. Isoflavone content of Dua-Chungkukjang was 2-3.5 times higher than that of traditional Chungkukjang. Anthocyanin content also increased continuously as fermentation took place, and it reached 5.0 mg/g and 6.9 mg/g in traditional Chungkukjang and Dua-Chungkukjang after 40 hr of fermentation, respectively.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.16 no.3
• /
• pp.29-37
• /
• 2008

The objective of this research is to evaluate the optimum treatment methods for disposal sludge cake at different temperatures and periods of time. The disposal dehydrated sewage cake used in this study was obtained from N wastewater treatment plant in the P City. This system consists of continuous conveyer thermal dryer and pyrolysis. The continual conveyer thermal dryer was operated to evaluate the optimum conditions with temperature settings, ranges from 130 to $180^{\circ}C$, loading rates of 650~750 kg/hr and operating times of 110~120 minutes. The continual pyrolysis was also operated to evaluate the optimum conditions with temperature settings, ranges from 650 to $750^{\circ}C$, loading rates of 100~158 kg/hr and operating times of 20~40 minutes. The sewage sludge cake has a moisture content of 78~80% (wt) which decreased up to 1~3%(wt) resulted in breaking of cell wall after operating the continuous conveyer thermal dryer and pyrolysis. Important parameters which were operating times, moisture contents, loading rates, conveyer velocities and rotary velocities effects on the thermal kinetics and dynamics were investigated to evaluate the optimum conditions for the continual thermal dryer and pyrolysis.

• Mycobiology
• /
• v.35 no.3
• /
• pp.157-158
• /
• 2007

The alkaloid fuyuziphine was isolated from the whole plant of Fumaria indica. It had inhibitive effect against spore germination of some plant pathogenic fungi (Collectotrichum sp., C. gloeosporioides, C. falcatum, Curvularia maculans, C. lunata, Erysiphe cichoracearum, Helminthosporium pennisetti, Oidium erysiphoides, Ustilago cynodontis, Alternaria chieranthi, A. mel-ongenae, A. brassicicola and A. solam). Curvularia lunata, Oidium erysiphoides, Alternaria brassicicola and A. solani did not germinate at 750 and 1000 ppm and Colletotrichum gloeosporioides, C. falcatum, Curvularia maculans were inhibited at 1000 ppm for 24 hr incubation. Germination of most fungi was significantly inhibited at $100{\sim}750ppm$.

• Journal of Korean Society of Water and Wastewater
• /
• v.25 no.5
• /
• pp.741-750
• /
• 2011

A pilot-scale biofilter was constructed to discover degradation characteristics of the complex odor discharged from Ansan wastewater treatment plant. Candida tropicalis for volatile organic compounds, sulfur oxidizing bacteria(SOB) for hydrogen sulfide, and bacteria extracted from feces soil were immobilized on a polymer gel media. According to this study, the EBCT was varied from 36 sec to 18 sec. Toluene was removed as 80% along the variations, but it was recovered as 100% within 1 week. All benzene and xylene were removed during the operation while the efficiency of hydrogen sulfur was temporary decreased at 18 sec of EBCT, thereafter it was recovered to 100% within a week. The maximum elimination capacities of the benzene, toluene, xylene, and hydrogen sulfur were 6.6 g/$m^{3}$/hr, 31.7 g/$m^{3}$/hr, 7.8 g/$m^{3}$/hr, and 133.6 g/$m^{3}$/hr, respectively. There were merits on removal both organic and inorganic complex odor using the pilot-scale biofilter embedded with microorganisms immobilized on polymer gel media.

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 2002.09a
• /
• pp.355-358
• /
• 2002

A sediments are Integral called as gravel, sand, clay, mineral materials which are settling in bottom layer of reservoir, stream, and oceans from land. In practical problems relations of sediments are flood by decreed of flow capacity and down of water quality. Dredged sediments are composed with constructed material and variety of pollutant compounds. Therefore, it is very much of cost effects in nationally, if development for use of constructed material separated only constructed material within sediments. And it will be continue to the dredge operation of stream sediment for retrofit of water environment and sustainable's after the years. The following results could be obtained : In case of high concentration sediments, sample for design of CDF was shown property of flocculent settling. Assuming that average inflow rate is 1, 000㎥/hr, mean residence time( $T_{d}$), average ponding depth( $H_{pd}$ ), and design surface area for flocculent settling( $A_{df}$ ) were 5 hr, 0.6m, and 15, 750 $m^2$ respectivelyrespectivelyy

• Journal of the Korean Society of Tobacco Science
• /
• v.19 no.1
• /
• pp.70-75
• /
• 1997

The expansive properties of leaf tobacco by nitrogen gas was investigated with cut tobacco AB3O-1, CD3L-1(NC82). Major factors for the best expansion of the tobacco by the gas were an impregnated pressure and expansion temperature. The expansion rate for AB3O-1 and CD3L-1 at 250℃, 750kg/cm2 was 96.6%, 99.4% respectively. The shred size and fineness index at 96.6% of expansion rate for AB3O-1 was almost the same as at 58.3% for CD3L-1. The time reaching at equilibrium moisture under of RH 57% was 36hr in non-treated leaf tobacco, but it was 20hr in expanded tobacco. We confirmed that total sugar contents of leaf tobacco by the expansion was decreased with 9.3∼10.9%. Total alkaloid was decreased with 17.5∼21.1% and ether extracts was declined with 4.9∼9.3%. These results suggest that the expansion method of leaf tobacco by nitrogen gas is a useful method without any serious environmental troubles. Key words : expansion, nitrogen gas, heat treatment, tobacco.

• Journal of the Korean Ceramic Society
• /
• v.28 no.9
• /
• pp.675-682
• /
• 1991

Among many problems that need to be solved in the process of preparing multilayer chip LC filters, we studied the control of shrinkage in order to prevent the crack, warpage, and/or delamination which occurs at the interface between the inductance (L part) and the capacitance (C part). Shrinkage was controlled by compositions, powder size, calcining temperature and amount of organic binder. Capacitance sheet was prepared by mixing 65 wt% binder with the composition of 96 wt% TiO2 having an average particle size of 0.5 $\mu\textrm{m}$, 3 wt% CuO. After small amount of MnO2 and SiO2 added, it was calcined at 750$^{\circ}C$ for 2 hr. Inductance sheet was prepared by mixing 60 wt% binder with the composition of 49.5% mol% Fe2O3, 20.5 mol% ZnO, 20 mol% NiO and 10 mol% CuO which was calcined at 775$^{\circ}C$ for 2 hr. These sheets was laminated at 250 kg/$\textrm{cm}^2$, and cofired at 900$^{\circ}C$ for 2 hr to give rise to a multilayer chip LC filter without any warpage.

• Korean Journal of Materials Research
• /
• v.11 no.9
• /
• pp.745-750
• /
• 2001

Ni-33.3at%Si elemental powder mixtures were mechanically alloyed by a high-energy ball mill, followed by CIP (cold isostatic pressing) and HIP (hot isostatic pressing) for different processing conditions. Only elemental phases (Ni and Si) were observed for the 15 min mechanically alloyed (MA 15 min) powder. but $Ni_2$Si and elemental phases were observed to coexist for the 30 min mechanically alloyed (MA 30 min) powder. Elemental Ni and $Ni_2$Si phases were observed for the HIPed compact of MA 15 min powder at 100 and 150 MPa for 2 hr at $800^{\circ}C$. Only the $Ni_2$Si phase was, however, observed for the HIPed compacts of MA 30 min powder. For the HIPed compacts, the highest sintered density was obtained to be 99.5% of theoretical density by a HIP step at $1100^{\circ}C$ at 150MPa for 2hr. The hardness values of the HIPed $Ni_2$Si compacts at $1100^{\circ}C$ at 100/150 MPa for 2 hr were higher than HRC 66. The densification and mechanical property of HIPed $Ni_2$Si compacts were found to depend on more HIP temperature than HIP pressure.

• Journal of Welding and Joining
• /
• v.7 no.4
• /
• pp.30-37
• /
• 1989

Effect of heat treatment on mechanical properties of an overlay weldment was investigated. Over welding was carried out on the structural C-Mn mild steel substrate to take required test specimens. Shielded metal arc welding process with 13Cr-0.2Ni stick electrode was applied. The heat treatment temperatures and holding times were $450{\circ}C., 550{\circ}C., 650{\circ}C., 750{\circ}C., 850{\circ}C.$ and 0.5hr, 2hr, 10hr, respectively. Mechanical tests and microscopic inspection were also carried out to investigate welds soundness. Test results indicated that carbon migration was dominant near bonded zone. At temperature of around 650.deg. C, carburized layer and decarburized layer were formed remarkably along overlay welds region and C-Mn mild steel region, respectively. The wideth of these layers became wider with increasing heat treatment temperature and/or holding time at the elevated temperature, and this relationship agreed with Larson-Miller parameter. Side bending test results demonstrated that the crack free region of overlay welds could be deduced from the relationship between temperature and holding time.