• Composites Research
• /
• v.17 no.5
• /
• pp.1-6
• /
• 2004

Composite pressure vessels with HDPE (high density polyethlyne) liner with metal boss at each end were developed by Filament Winding Process. The vessel is composed of a dome-shaped part at each end and a cylinder-shaped part at the middle of the vessel. The environmental tests carried out for possible vessel materials such as High Density Polyethlyn (HDPE), resins and reinforcing fibers up to a year showed no significant damages. The boss was designed to minimize the gas leak which was verified by FEM analysis. Most ideal fiber tension was obtained by experimental method and the fiber volume fraction, $\textrm{V}_{f}$, obtained by image analyzer were 55.4 % in cylinder and 55.6 % in dome parts, respectively. Winding pattern is programmed to control the composite thickness in the dome areas such that the failure of the vessel may occur in the cylinder. During the cure, the vessel was rotated and a constant internal pressure of 0.62 bar was applied. From this, the vessel's burst pressure is improved by 28 %. The burst and fatigue tests for under-wound and fully wound vessel showed satisfactory results.

• Journal of the Society of Naval Architects of Korea
• /
• v.60 no.1
• /
• pp.38-47
• /
• 2023

According to the government policy of environmental regulations, interest of ship, which made with High-Density Polyethylene (HDPE) as a low-carbon and eco-friendly material, is growing as a substitute for the existing fishery boat hull materials such as FRP, aluminum, steel etc. However, regulations related to the production of HDPE ship are still quite incomplete. Even there are no regulations related to structural analysis. Therefore, in this study, structural analysis is carried out by applying different design loads for each international classification for 38ft class HDPE power boats, and the results are compared and analyzed. According to this study, although there is a correlation between the based pressure value and the analysis result value of each class regulation, it is not necessarily proportional. Also, This analysis result shows a difference not only depending on the size of design load, but also application range of the load, the pressure adjustment factor and section shape. However, the occurrence point and trend of the maximum stress values were quite consistent. It is hoped that the results of this study will be used when establishing HDPE ship structure analysis procedures and standards in the future.

• Journal of Aerospace System Engineering
• /
• v.17 no.6
• /
• pp.127-132
• /
• 2023

In this study, designing of a Type 4 pressure vessel using the filament winding method was conducted. In order to prevent leakage in consideration of the design of the hydrogen storage tank, a liner was designed by applying high-density polyethylene (HDPE), and the composite structure was designed by stacking carbon/epoxy in the hoop and helical directions. As a theoretical approach, the angle of the helical fiber and fiber thickness of each hoop and helix were designed. The safety of the design was verified using the commercial software ANSYS.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.4
• /
• pp.405-413
• /
• 2015

In the US, the number of cases of subterranean water contamination from tritium leaking through a damaged buried nuclear power plant pipe continues to increase, and the degradation of the buried metal piping is emerging as a major issue. A pipe blocked from corrosion and/or degradation can lead to loss of cooling capacity in safety-related piping resulting in critical issues related to the safety and integrity of nuclear power plant operation. The ASME Boiler and Pressure Vessel Codes Committee (BPVC) has recently approved Code Case N-755 that describes the requirements for the use of polyethylene (PE) pipe for the construction of Section III, Division 1 Class 3 buried piping systems for service water applications in nuclear power plants. This paper contains tensile and slow crack growth (SCG) test results for high-density polyethylene (HDPE) pipe welds under the environmental conditions of a nuclear power plant. Based on these tests, the fracture surface of the PENT specimen was analyzed, and the fracture mechanisms of each fracture area were determined. Finally, by using 3D finite element analysis, limit loads of HDPE related to premature failure were verified.