• Journal of Welding and Joining
• /
• v.22 no.5
• /
• pp.65-72
• /
• 2004

The tendency and degree of hot cracking of high strength 5083, 6N01 and 7N01 Al alloy welds by using DCSP-GTAW through modified Varestraint test and autogenous butt welding were investigated. In hot cracking test, 6N01 alloy showed the highest susceptibility to hot cracking in the weld metal and HAZ. Cracking susceptibilities generally increased with increase of solidification temperature range of the base metal and bead penetration-to-width ratio of the weld metal. The cracks in welds of the alloys vertically formed to solid-liquid interface and propagated along with columnar grain boundaries. The fracture facets of cracks showed the typical morphology of solidification crack observed as dendritic structures. Especially, in 6N01 alloy, liquation cracks which were due to elements of Si, Fe and Mg also observed in HAZ near fusion boundary. In butt welding of different Al alloys, the bead crack was mainly occurred in the welds of 6N01, 7N01 and other Al alloys together with 6N01 or 7N01. In the butt welds of 7N01, it was found that the component of Cu had an effect on the higher susceptibility to the hot cracking.

• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.561-567
• /
• 1991

Submicron ${\alpha}-SiC$ powder with $Al_2O_3$ addition was hot-pressed under the controlled heating and pressurizing schedule. $SiO_2$ layer on ${\alpha}-SiC$ powder was effective for the sintering of ${\alpha}-SiC$ powder when $Al_2O_3$ was used as an additive. Applying of pressure under the controlled schedule accelerated the rearrangment of SiC grains, yielding 98% of theoretical density of SiC even at $1900^{\circ}C$. Flexural strength of the specimen containing 2 wt% $Al_2O_3$ was increased as increasing the hot-pressing temperature up to $2050^{\circ}C$ and maximum value was 800 MPa, while the flexural strength of the specimen containing 10 wt% $Al_2O_3$ was decreased as increasing the hot-pressing temperature above $2000^{\circ}C$ due to the formation of continuous grain boundary phase. Fracture toughness of the specimens was in the range of $3.5~4.5\;MNm^{-3/2}$ regardless of the amount of $Al_2O_3$ addition.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.5
• /
• pp.151-156
• /
• 2007

In this paper, the creep characteristics of lead and lead-free solder joint were investigated using the QFP(Quad Flat Package) creep test. Two kind of solder pastes(Sn-3Ag-0.5Cu, Sn-0.2Sb-0.4Ag-37.4Pb) were applied to the QFP solder joints and each specimen was checked the external and internal failures(i.e., wetting failure, void, pin hole, poor-heel fillet) by digital microscope and X-ray inspection. The creep test was conducted at the temperatures of $100^{\circ}C$ and $130^{\circ}C$ under the load of 15$\sim$20% of average pull strength in solder joints. The creep characteristics of each solder joints were compared using the creep strain-time curve and creep strain rate-stress curves. Through the comparison, the Sn-3Ag-0.5Cu solder joints have higher creep resistance than that of Sn-0.3Sb-0.4Ag-37.4Pb. Also, the grain boundary sliding in the fracture surface and the necking of solder joint were observed by FE-SEM.

• Laser Solutions
• /
• v.7 no.3
• /
• pp.25-36
• /
• 2004

This study was performed to clarification of the formation of weld discontinuities in the dissimilar laser fusion zone. Welding parameters were beam power of 1300, 1430, 1560, and 1700 W and travel speed of 1, 1.3, and 1.7 m/min. Most cavities in the fusion zone were observed near the tip. Cavities in the fusion zone observed to be formed and grown from pores in the tip. More cavities were formed as the beam position moves to the tip side. Small cavities were decreased but large cavities were increased when the energy input increased. W content in the fusion zone was increased with heat input and as the beam position close to the tip. In the fusion zone, W content in the dendrite boundary was increased with heat input. Considering the propagation path and fracture morphology, cracks were solidification cracking, and were initiated and propagated along the dendrite boundaries. The formation of cracks might be related with the W rich ${\mu}$ phase which was formed in the grain boundaries and dendrite boundaries.

• Journal of Ocean Engineering and Technology
• /
• v.27 no.2
• /
• pp.8-12
• /
• 2013

Four kinds of silicon nitride composites with tri-laminate structure were prepared by stacking tapes with aligned ${\beta}-Si_3N_4$ whisker seeds. The composites were fabricated using a modified tape casting method for enhanced alignment of the whisker seeds. The relative densities of all four samples reached 99% at room temperature. The three-point flexural strengths of the samples according to the stacking sequences were measured at both room temperature and 1723 K. The high temperature strength of sample WWW was $457{\pm}14$ MPa. The fracture of sample WWW occurred mainly along the grain boundary. The room temperature strengths of samples OOO, OWO, WOW, and WWW were $430{\pm}32$ MPa, $470{\pm}19$ MPa, $700{\pm}14$MPa, and $940{\pm}14$ MPa, respectively.

• International Journal of Safety
• /
• v.6 no.2
• /
• pp.1-7
• /
• 2007

In this study mechanical strength of A53B carbon steel was analyzed using several types of test specimens directly machined from oil recycling pipe experienced a failure due to hydrogen attack in chemical plants. High temperature hydrogen attack (HTHA) is the damage process of grain boundary facets due to a chemical reaction of carbides with hydrogen, thus forming cavities with high pressure methane gas. Driven by the methane gas pressure, the cavities grow on grain boundaries forming intergranular micro cracks. Microscopic optical examination, tensile test, Charpy impact test, hardness measurement, and small punch (SP) test were performed. Carbon content of the hydrogen attacked specimens was dramatically reduced compared with that of standard specification of A53B. Traces of decarburization and micro-cracks were observed by optical and scanning electron microscopy. Charpy impact energy in hydrogen attacked part of the pipe exhibited very low values due to the decarburization and micro fissure formation by HTHA, on the other hand, data tested from the sound part of the pipe showed high and scattered impact energy. Maximum reaction forces and ductility in SP test were decreased at hydrogen attacked part of the pipe compared with sound part of the pipe. Finite element analyses for SP test were performed to estimate tensile properties for untested part of the pipe in tensile test. And fracture toughness was calculated using an equivalent strain concept with SP test and finite element analysis results.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.19 no.6
• /
• pp.411-419
• /
• 1999

It has been well recognized that a long term service at elevated temperature of $350^{\circ}C{\sim}550^{\circ}C$ induces embrittlement damage due to carbide precipitation and/or P, Sb and Sn segregation at grain boundaries and thereby deteriorates the grain boundary strength of heat resisting components in the energy-related plants. Therefore, it is very important to assess quantitatively the extent of embrittlement damage of heat resisting components to secure the reliable and efficient service condition and to prevent brittle failure in service. However, because fracture tests are limited in size and number of specimen obtained from the structural components, nondestructive test method is required. In this study, the optimum electrochemical parameters are investigated and discussed to evaluate nondestructive embrittlement damage for aged 2.25Cr-1Mo steels by means of electrochemical polarization test method (ECPTM) in proper corrosive environment. In addition, the electrochemical test results are compared with embrittlement degree evaluated by semi-nondestructive SP test.

• Journal of Welding and Joining
• /
• v.32 no.1
• /
• pp.6-14
• /
• 2014

This paper has an aim to evaluate microstructure and fracture toughness of TMCP steel weldment applied for off-shore wind tower with the focus on the effect of heat input on the weldment with various welding processes; FCAW(13kJ/cm and 30kJ/cm), SAW(62kJ/cm), and EGW(177kJ/cm). Based on experimental results developed from this study, it was found that the impact toughness of top side for TMCP steel weldments with heat input up to 62 kJ/cm satisfied the required minimum value except the EGW(177kJ/cm). The heat input and microstructure are the main factors of impact toughness. The heat input of 13kJ/cm on back side with low heat input increased the amount of grain boundary ferrite which has low impact toughness, and heat input of 177kJ/cm on top side is significant enough to produce the austenite grain growth. The compositions and sizes of inclusions which are the dominant factors for the formation of acicular ferrite were analyzed by OM and EDS. As the heat input increased, the inclusions also grew and a nucleation site decreased. The size of nonmetallic inclusions and the crack width was nearly similar, therefore the inclusions were related with the crack propagation.

• The Journal of Engineering Geology
• /
• v.6 no.2
• /
• pp.59-64
• /
• 1996

Acoustic Emission(AE) signals are emitted by a sudden release of strain energy associated with material damage. A multi-channels of LeCroy system and piezoelectric pressure transducers are employed for AE measurement to investigate the roles of AE in the propagation of macro cracks as well as the characteris-tics of AE wave in occurrence, amplitude and dominant frequency with changes in macro loading modes. Deduced crack opening volume of micro cracks varied widely and implies that AE events could be caused by crystal dislocations on a small scale and grain boundary movements on a large scale. Amplitude of first arrival AE wave emitted during mode I test was approximately 3 times higher than those from mixed mode test, while the number of AE count in mode I test was only 25% of mixed mode. It may imply that the total energy required for generation of a given fracture surface is similar regardless in change of macroloading modes.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.2
• /
• pp.236-242
• /
• 1989

In order to investigate the effects of hot corrosion on the creep rupture properties and creep life of 304 stainless steel being used as tube materials of heavy oil fired boiler, the creep rupture tests were carried out at temperature 630.deg.C, 690.deg.C and 750.deg.C in static air for the specimens with or without coating of double layer corrosives according to the new hot corrosion test method simulating the situation commonly observed on superheater tubes of the actual boiler. The double layer corrosives are 85% V$_{2}$O$_{5}$ + 10% Na$_{2}$So$_{4}$ + 5% Fe$_{2}$O$_{3}$ as the inner layer corrosive being once melted at 900.deg. C and crushed to powder, and 10% V$_{2}$O$_{5}$ + 85% Na$_{2}$SO$_{4}$ +5% Fe$_{2}$O$_{3}$ as the outer layer corrosive. As results, in the specimen coated with the double layer corrosives, the rupture strength was extremely lowered and showed a large difference each other. The rupture ductility also lowered remarkably as a result of the brittle fracture mode due to hot corrosion. These results indicate that hot corrosion could essentially alter the creep fracture mechanism. From the metallographic observation, it was clarified that the rupture life of 304 stainless steel subjected to hot corrosion was chiefly determined by the behavior of the aggressive intergranular penetration of sulfides.des.