Abstract
It has been well recognized that a long term service at elevated temperature of $350^{\circ}C{\sim}550^{\circ}C$ induces embrittlement damage due to carbide precipitation and/or P, Sb and Sn segregation at grain boundaries and thereby deteriorates the grain boundary strength of heat resisting components in the energy-related plants. Therefore, it is very important to assess quantitatively the extent of embrittlement damage of heat resisting components to secure the reliable and efficient service condition and to prevent brittle failure in service. However, because fracture tests are limited in size and number of specimen obtained from the structural components, nondestructive test method is required. In this study, the optimum electrochemical parameters are investigated and discussed to evaluate nondestructive embrittlement damage for aged 2.25Cr-1Mo steels by means of electrochemical polarization test method (ECPTM) in proper corrosive environment. In addition, the electrochemical test results are compared with embrittlement degree evaluated by semi-nondestructive SP test.
에너지 변환설비와 관련된 기계구조물의 내열재료는 $350^{\circ}C{\sim}550^{\circ}C$의 온도범위에서 장시간 사용되는데 이때 조직의 결정입계에는 불순물 원소(P, Sn, Sb등)의 편석과 탄화물의 석출 등으로 인하여 재료의 취화 현상이 발생되고, 그로 인해 입계강도의 저하가 초래된다. 따라서 노후화된 고온설비의 안전성 및 효율적인 운전조건을 확보하고, 취성파괴 방지를 위해서는 취화손상의 정량적 평가는 매우 중요하다. 그러나 가동중인 고온설비에서 파괴시험을 위한 대량의 시험편채취가 거의 불가능한 경우가 대부분이므로 비파괴적인 시험방법이 요구된다. 본 연구에서는 인공시효열처리된 2.25Cr-1Mo강의 비파괴적인 취화손상도 평가를 위해 적정 부식환경하에서 전기화학적 분극시험 방법에 의한 최적의 평가인자를 조사하였다. 또한 전기화학 시험결과들은 준비파괴시험인 SP시험에 의한 취화도 평가결과와 비교되었다.