• Journal of the Korean Wood Science and Technology
• /
• v.45 no.1
• /
• pp.28-35
• /
• 2017

In this study, specimens of rigid frame joint were produced by integrating joints with adhesive and other specimens were produced by inserting a wooden gusset integrated with a column member into a slit-processed beam member and joining them with pins. Then the moment resistance performances of the specimens were examined. For the wooden gusset, a GFRP-reinforced wooden gusset was used. The calculation results of perfect elasto-plasticity for the frame specimens for which a GFRP-reinforced wooden gusset was inserted into and joined with the slit-processed beam member by pins were 20-80% lower compared to the control group which consisted of steel plate-inserted frame specimens. The rigid frame specimens for which the column and beam members have been integrated with adhesive showed almost no initial residual transformations, as well as 38% greater initial rigidity and 41% greater plasticity compared to the steel plate-inserted joint.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.5
• /
• pp.136-145
• /
• 2013

Social interest in the seismic retrofit of the structure is growing massive earthquake that occurred recently. The brittle fracture of Non-seismically designed Columns lead to full collapse of the building. In the past, cross-sectional expansion method, a steel plate reinforcing method is applied mainly in recent years, fiber-reinforced method utilizing the advantages of the composite material are preferred. However, the reinforcement methods such as this, there is a drawback to induce physical damage to structures, and time consuming work space is large. IIn this study, FRP seismic reinforcement was developed using the Aluminum connector and the composite material (Glass Fiber Reinforced Polymer). Then, the optimum quantities of FRP seismic reinforcement was determined using a nonlinear finite element analysis program. Finally, the quantity decision process through the design and analysis of FRP reinforcement was suggested.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.6
• /
• pp.868-875
• /
• 2015

In order to replace existing slit type steel plate on the wooden structure joint, the FRP-reinforced laminated plates were produced. Four types of FRP-reinforced laminated plates were produced according to the type of reinforcement and adhesive, and before applying to the joint, the adhesion performance test according to KSF 3021 and KSF 2160 and the Compact Tension (CT) type fracture toughness test specified in ASTM D5045-99 were carried out. As a result of adhesion performance test, all GFRP textile, GFRP sheet, and GFRP Textile-Sheet type FRP-reinforced laminated plates satisfied the requirement of soaking delamination percentage with smaller than 5% based on KS standard. However, aramid type specimen satisfied the standard as the soaking delamination percentage of 4.8% but it did not satisfied the standard as the water proof soaking delamination percentage of 70%. As a result of fracture toughness test, the volume ratio of reinforcement to timber became 23% so that the strength of FRP-reinforced laminated plates increased by two to four times in comparison to the control specimen. It was confirmed that the GFRP Textile-Sheet type specimen was most resistant to the fracture most since the ratio of stress intensity factor compared with that of the control increased to 61% owing to the parallel arrangement of glass fiber to the load. As a result of tensile shear strength test using FRP-reinforced laminated plates and nonmetal dowels, it is about 12% lower than metal connectors.

• Journal of Korean Society of Steel Construction
• /
• v.22 no.5
• /
• pp.477-485
• /
• 2010

Various monitoring sensors are used to predict and detect structural damage. Smart sensors, such as glass-fiber sensors, PZT, and MEMS, among others, have replaced traditional sensors. They are now being used in many areas. This study aims to predict the damage by measuring the PZT voltage attached on the specimen by the applied impact load. In the experiment to detect damages in beam connection, simple $H-400{\times}200{\times}8{\times}13$ beams were spliced with bolts. The results of FFT between PZT sensor and accelrometer were compared to measure the sensitivity of the PZT sensor. The damage to the beam was presumed by loosening the bolt, and then the damage measurement was accompanied. Secondly, a steel $PL600{\times}65{\times}5.8$ plate beam was fabricated for the purpose of experimenting on damage measurement. Impact loading test on three different locations was carried out. Damage width varied between 6~42mm on both sides by cutting, using a steel saw. The ratio of frequencies before and after the damage was computed to quantify the damage level by using FFT, and the change in mode pattern with the increased damage was investigated to measure the damage.