• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.29 no.12
• /
• pp.28-32
• /
• 2015

In this work, we reported fabrication of sealing the glass substrate using laser treatment at low temperature for electrochemical luminescence (ECL) cell. The laser treatment at temperature is using laser diode. The glass substrate sealing by laser treatment tested at 3-10W, 2-5 mm/s for build and tested. The sealing laser treatment method will allow associate coordination between the two glass substrate was enclosed. The effect of laser treatment to sealing the glass substrate was found to have cracks and air gap at best thickness of about 550-600 im for condition 3 W, 3 mm/s. The surface of sealing was roughness which was not influent to electrodes It can reduce the cracks, crevices and air gaps as well, improves the performance viscosity in butter bus bar electrodes. Therefore, it is more effective viscosity between two FTO glasses substrate.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1538-1541
• /
• 2005

For reliability evaluation of AC-PDP, one of the most important factor is sealing property. In this paper, the reliability evaluation test method of the commercialized sealing glass frit in AC-PDP was studied. 6 inch AC-PDP panels were tested for evaluation of sealing glass frit by vibration shock test, thermal shock test, non -destructive X-ray inspection, residual stress inspection and residual gas detection. These test methods are proposed as a standard for testing the reliability of sealing glass frit. The main failure mode of sealing glass frit in AC-PDP seems to be the crack propagation from thermal cycling rather than mechanical factor.

• Korean Journal of Materials Research
• /
• v.19 no.11
• /
• pp.613-618
• /
• 2009

We designed new compositions for lead free and low temperature sealing glass frit of $ZnO-V_2O_5-P_2O_5$ system, which can be used for PDP (Plasma Display Panel) or other electronic devices. The $ZnO-V_2O_5-P_2O_5$ system can be used as a sealing material at temperatures even lower than 430$^{\circ}C$. This system, however, showed lower bonding strength with glass substrate compared to commercialized Pb based sealing materials. So, we added $TiO_2$ as a promoter for bonding strength. We examined the effect of $TiO_2$ addition on sealing behaviors of $ZnO-V_2O_5-P_2O_5$ glasses with the data for flow button, wetting angle, temporary & permanent residual stress of glass substrate, EPMA analysis of interface between sealing materials and glass substrate, and bonding strength. As a result, sealing characteristics of $ZnO-V_2O_5-P_2O_5$ system glasses were improved with $TiO_2$ addition, but showed a maximum value at 5 mol% $TiO_2$ addition. The reason for improved bonding characteristics was considered to be the chemical interaction between glass substrate and sealing glass, and structural densification of sealing glass itself.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.1
• /
• pp.40-45
• /
• 2012

The glass edge sealing is one of the vacuum glazing core manufacturing process and it needs the high reliability for the vacuum keeping. Conventionally, the glass edge sealing had been being researched by the method that pasted the flit on the glass edge part and bonded two sheets of glass. But this way has the defect that can't make tempered glass. In order to remedy it's faults, in this paper, the glass edge was sealed by using the hydrogen mixture gas torch within the furnace. The parameter having an effect on the glass edge sealing through the basic test was set. And the correlation of the thickness of the glass edge and parameter were analyzed through the design of experiment. By using the Taguchi method, the optimal process condition for the glass edge sealing was drawn and the validity was verified.

• Journal of the Korean Ceramic Society
• /
• v.18 no.2
• /
• pp.99-104
• /
• 1981

Glass-ceramics possessed a number of characteristics which suggested their suggested their use for sealing to metals. The choice of particular glass-ceramics compositions for this application is governed by various factors, including workability of the glasses, thermal expansion characteristics and the matching of these to appropriate metals. Other properties, such as mechanical strength, determined the performance of glass-ceramics to metal seals. The purpose of the present study was to investigate direct sealing behaviour of copper to $Li_2O-ZnO-SiO_2$ system glass-ceramics. The design of the seal was a concentric seal which might contribute to the strong bond formation by providing compressive stress during thermal excursions. Tensile strengths of sealing layers were measured by Instron test machine. The layers were examined by electron probe microanalyzer. Crsystallization rate was increased with the amount of ZnO or $Li_2O$, and ZnO increased the sealing strength, but $Li_2O$ lowered it. Sealing mechanism was due to the formation of metal oxides, which acted as binder between copper and glass-ceramics. The nickle-plated copper seal with 10% $Li_2O$ and 30% ZnO was the most strong seal, and its sealing strength was more than 56kg/$\textrm{cm}^2$.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2010.11a
• /
• pp.791-792
• /
• 2010

• Proceedings of the KIEE Conference
• /
• 2015.07a
• /
• pp.1134-1135
• /
• 2015

In this paper, we reported fabrication of sealing the glass substrate using laser treatment at low temperature for electrochemical luminescence (ECL) cell. The laser treatment at temperature is using laser diode. The glass substrate sealing by laser treatment tested at 1-5 W, 1-5 mm/s for builted and tested. The sealing laser treatment method will allow associate coordination between the two glass substrate was enclosed. The effect of laser treatment to sealing the glass substrate was found to have cracks and air gap at best thickness of about $845-780{\mu}m$ for condition 5 W, 1-5 mm/s. The surface of sealing was roughness which was not influent to electrodes So, it is more effective viscosity between two glasses substrate.

• Journal of the Korean Ceramic Society
• /
• v.52 no.2
• /
• pp.103-107
• /
• 2015

The effective glass frit composition used to absorb laser energy and to seal commercial dye-sensitized solar cell panel substrates has been previously developed using $V_2O_5-TeO_2$-based glass with 10 wt% ${\beta}$-eucryptite as a CTE controlling filler. The optimum sealing conditions are provided using a 3 mm beam, a laser power of 40 watt, a scan speed of 300 mm/s, and 200 irradiation cycles. In this study, the feasibility of the developed glass frit is investigated in terms of the sealing strength and chemical durability against the commercial iodide/triiodide electrolyte solution and fluorine-doped tin oxide (FTO) electrode in order to increase the solar cell lifetime. The sealing strength of the laser-sealed $V_2O_5-TeO_2$-based glass frit is $20.5{\pm}1.7MPa$, which is higher than those of thermally sealed glass frit and other reported glass frit. Furthermore, the developed glass frit is chemically stable against electrolyte solutions. The glass frit constituents are not leached out from the glass after soaking in the electrolyte solution for up to three months. During the laser sealing, the glass frit does not react with the FTO electrode; thus, the resistivity of the FTO electrode beneath the laser-sealed area remains the same.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.6
• /
• pp.981-986
• /
• 2003

In order to investigate the possibility of processing of brittle material by ball impact, the effects of boundary conditions about impact damage of soda-lime glass by small spheres were evaluated experimentally. It was investigated that crack appearance developed in soda-lime glass with boundary conditions of without sealing, single-sealing and double-sealing by impact velocity. The double-sealing was most effective in the development of perfect cone than other boundary condition. In case of double-sealing condition, PVC and Polyurethane sealing were more effective in producing a perfect cone formation than other sealing materials. The impact velocity range over which perfect cones were formed was influenced by both the contact area and diameter of impact particle.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.4
• /
• pp.57-61
• /
• 2016

Thick film sealing glass paste is required for cell packaging of NaS based battery for energy storage system, to join the beta-alumina electrolyte tube and the alpha-alumina battery cell cap components. This paper presents the effect of the particle sizes of seal glass powder and the sealing temperatures on the microstructure of the glass sealants was investigated. It was found that the larger in the particle size of seal glass powder, the smaller the pore volume and the number of pores in a unit area. Also, the number of pores decreased with increasing the sealing temperatures while the pore size was increased. This result enables the control of porosity, pore distribution and number of pores in a microstructure of glass sealing component by proper selection of glass powders particle size and sealing temperature.