• 한국주조공학회지
• /
• 제22권6호
• /
• pp.288-292
• /
• 2002

Ni-base amorphous alloys were manufactured using melt-spinning and Cu-mold die casting methods. Amorphous formability, the supercooled liquid region before crystallization and mechanical properties were examined. The reduced glass transition temperature and the supercooled liquid region of $Ni_{51} Nb_{20} Zr_9 Ti_9 Co_8 Cu_3$alloy were 0.621 and 46 K respectively. $Ni_{51} Nb_{20} Zr_9 Ti_9 Co_8 Cu_3$ alloy was produced in the rod shape 3mm diameter using the Cu-mold die casting. Hardness, compression strength, elongation and elastic modulus of the alloy were 850 DPN, 2.75 GPa, 1.8% and 150 GPa respectively. Moreover, compression strength of 2.75 GPa was the highest value in the amorphous bulk alloy produced up to now.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.1526-1531
• /
• 2007

Data transmission capacity that is required in 2010 is forecasted that increase by optical communication capacity more than present centuple, and is doing increased demand of optical communication related industry product present. Specially, Lid glass' application that is one of optical communication parts is used in optical communication parts manufacture of Fiber array, Ferrule array, Fanout Black, Silica optical waveguide chip and splitter etc. Also, it is used widely for communication network system, CATV, ATM-PON, FTTH and system. But, Lid glass need much processing times and becomes cause in rising prices of optical communication parts because production cost is expensive. The objectives, of this work is to suggest the micro concave and convex pattern manufacturing technology on borosilicate plate using high temperature and compression molding method. As a result, could developed micro pattern Mold more than 5 pattern, and reduce Lid Glass manufacture cycle time.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 추계학술대회논문집A
• /
• pp.766-771
• /
• 2000

As using of insulating material of plastic to industrial electric field, thermoset has been gradually substituted for thermoplastic. But changing the material with crystalline has some problem, which is strength or warpage, Especially getting a strength to endure inner pressure is necessary when arc is occurred. So we use the material that is composed of glass fiber to compensate strength. By the way as the reinforced glass-fiber material is used in injection molding, unstableness of dimension is appeared frequently and it is difficult to know warpage pattern. So this paper will be contributed to know warpage pattern of mold product that is upper frame of magnetic contactor caused by glass-fiber orientation with fixed gate-system, when glass-fiber reinforced material with classification of poly-amide is used in injection molding.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 추계학술대회 논문집
• /
• pp.441-444
• /
• 2009

Weldlines are generated during the injection molding process when two or more melt flows are brought into contact. At the welded contact region, a 'V'-shaped notch is formed on the surface of the molded part. This 'V'-notch deteriorates not only surface appearance but also mechanical strength of the molded part. To eliminate or reduce weldlines so as to improve the weldline strength, the mold temperature at the corresponding weld locations should be maintained higher than the glass transition temperature of the resin material. The present study implements high-frequency induction heating in order to rapidly raise mold surface temperature without a significant increase in cycle time. This induction heating enables to local mold heating so as to eliminate or reduce weldlines in an injection-molded plastic part. The effect of induction heating conditions on the weldline strength and surface appearance of an injection-molded part is investigated.

• 한국정밀공학회지
• /
• 제12권3호
• /
• pp.110-118
• /
• 1995

The filling phase analysis of the injection molding process for thermoplastics was applied to predict pressure, themperature and shear stress in the test mold, and the results were compared with the experiment using 30% glass fiber added ABS resin. The finite difference method was used in the analysis considering the effects of heat transfer between molten polymer and mold wall, and also frictional heating by shear flow. The analysis results were considered as a method to improve the quality and the productivity of injection molding process. Using the analysis results, the molding factors such as mold-ability of polymers, performance of injection molding machine, positioning of gate and dimendsioning of runner in the injection molding process can be estimated at the design stage of mold for good quality and productivity.

• 한국정밀공학회지
• /
• 제2권3호
• /
• pp.41-46
• /
• 1985

The behavior of the burn-on in sand mold has been investigated by varying the pouring metal, bonding materials, additive materials and molding sand. The results obtained from thease experiments are as follows; 1) The burn-on layer of silica sand decreased in order of carbon steel, gray cast iron and stainless steel, and thease burn layer proceeded mostly by producing FeO. 2) The burning reaction of silica sand mold in carbon steel castings declined with increasingly bentonite content, but water-glass scarcely took part in the burn-on reaction. 3) The addition of feldspar and seacoal to silica sand promoted the inhibiting burn-on. 4) The burn-on layer of sand mold decreased of silica sand, chromite sand and olivine sand.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 금형가공,미세가공,플라스틱가공 공동 심포지엄
• /
• pp.23-28
• /
• 2005

Microlens arrays were fabricated using a modified LIGA process based on the exposure of a PMMA (Polymethylmethacrylate) sheet to deep x-rays and subsequent thermal treatment. A successful modeling and analyses for microlens formation were presented according to the experimental procedure. A nickel mold insert was fabricated by the nickel electroforming process on the PMMA microlens arrays fabricated by the modified LIGA process. For the replication of microlens arrays having various diameters with different foci on the same substrate, the hot embossing and the microinjection molding processes have been successfully utilized with the fabricated mold insert. Fabricated microlenses showed good surface roughness than the mold insert. The focal lengths of the injection molded microlenses were successfully measured experimentally and also estimated theoretically.

• Restorative Dentistry and Endodontics
• /
• 제18권1호
• /
• pp.1-26
• /
• 1993

The purpose of this study was to investigate the effect of acid etching on the surface appearance and fracture toughness of five glass ionomer cements. Five kinds of commercially available glass ionomer cements including chemical curing filling type, chemical curing lining type, chemical curing metal reinforced type, light curing tilling type and light curing lining type were used for this study. The specimens for SEM study were fabricated by treating each glass ionomer cement with either visible light curing or self curing after being inserted into a rubber mold (diameter 4mm, depth 1mm). Some of the specimens were etched with 37% phosphoric acid for 0, 15, 30, 60, go seconds, at 5 minutes, 1 hour and 1 day after mixing of powder and liquid. Unetched ones comprised the control group and the others were the experimental groups. The surface texture was examined by using scanning electron microscope at 20 kV. (S-2300, Hitachi Co., Japan). The specimens for fracture toughness were fabricated by curing of each glass ionomer cement previously inserted into a metal mold for the single edge notch specimen according to the ASTME399. They were subjected to a three-point bend test after etching for 0, 30, 60, and 90 seconds at 5 minutes-, 1 hour-and 1 day-lapse after the fabrication of the specimens. The plane strain fracture toughness ($K_{IC}$) was determined by three-point bend test which was conducted with cross-head speed of 0.5 mm/min using Instron universal testing machine (Model No. 1122) following seven days storage of the etched specimens under $37^{\circ}C$, 100% humidity condition. Following conclusions were drawn. 1. In unetched control group, crack was present, but the surface was generally smooth. 2. Deterioration of the surface appearance such as serious dissolving of gel matrix and loss of glass particles occured as the etching time was increased beyond 15 s following Immediate etching of chemical curing type of glass ionomer cements. 3. Etching after 1 h, and 1 d reduced surface damage, 15 s, and 30s etch gave rough surface appearance without loss of glass particle of chemical curing type of glass ionomer cements. 4. Light curing type glass ionomer cement was etched by acid, but there was no difference in surface appearances according to various waiting periods. 5. It was found that the value of plane stram fracture toughness of glass ionomer cements was highest in the light curing filling type as $1.79\;MNm^{-1.5}$ followed by the light curing lining type, chemical curing metal reinforced type, chemical curing filling type and chemical curing lining type. 6. The value of plane stram fracture toughness of the chemical curing lining type glass ionomer cement etched after 5 minutes was lower than those of the cement etched after 1 hour or day or unetched (P < 0.05). 7. Light curing glass ionomer cement showed Irregular fractured surface and chemical curing cement showed smooth fractured surface.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2004년도 International Symposium on Powder Materials and Processing
• /
• pp.84-85
• /
• 2004

• 한국분말재료학회지
• /
• 제13권5호
• /
• pp.351-359
• /
• 2006

Ni based($Ni_{57}Zr_{20}Ti_{18}Si_2Sn_3$) bulk metallic glass(BMG) powders were produced by a gas atomization process, and ductile Cu powders were mixed using a spray drying process. The Ni-based amorphous powder and Cu mixed Ni composite powders were compacted by a spark plasma sintering (SPS) processes into cylindrical shape. The relative density varied with the used SPS mold materials such as graphite, hardened steel and WC-Co hard metal. The relative density increased from 87% to 98% when the sintering temperature increased up to $460^{\circ}C$ in the WC-Co hard metal mold.