• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.2
• /
• pp.232-242
• /
• 2003

Statement of problem : Fiber-reinforced posts have lower modulus of elasticity than titanium post or cast post-core. With this similar elasticity to that of dentin, fiber-reinforced posts have been known to have a tendency to reduce the risk of root fracture. However, there were few studies on the teeth restored with fiber-reinforced posts under the condition of reduced periodontal support. Purpose : The purpose of this study was to evaluate the fracture strength and failure mode of endodontically treated teeth restored with fiber-reinforced posts and titanium posts under the condition of reduced periodontal support. Material and method : Extracted human maxillary incisor roots were divided into 3 groups (group 1 carbon fiber post, group 2 : glass fiber post, and group 3 : titanium alloy post). After coronectomy and endodontic treatment, teeth were restored with each post systems and resin core according to the manufacturer's recommendation. Then, teeth with simulated periodontal ligament were embedded in the acrylic resin blocks at the level of 4 mm below the cemento-enamel junction. Each specimen was exposed to $10^5$ load cycles with average 30 N force in $36.5^{\circ}C$ water using a computer-controlled chewing simulator. Loads were applied at $45^{\circ}$ angle to the long axis of the teeth. After cyclic loading, teeth were subjected a compressive load until failure at a crosshead speed of 0.5 mm/min. Fracture strength (N) and failure mode were examined. The fracture strength was analyzed with one-way ANOVA and the Scheffe adjustment at the 95% significance level. Results and conclusion : The results were as follows. 1. There was no statistically significant difference in the mean fracture strength among the groups (P<.05). 2. Carbon fiber post and glass fiber post group showed less root fracture tendency than control group. 3. All specimens with root fractures showed fracture lines above the level of acrylic resin block, except for only one specimen in group 3.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.1
• /
• pp.60-65
• /
• 2014

Teeth that have short clinical crown, which are not alone enough to support the definitive restoration can be best treated using the post and core system. The advantages of fiber post over conventional metallic post materials have led to its wide acceptance. In addition to that the combination of aesthetic and mechanical benefits of fiber post has provided it with a rise in the field of dentistry. Also the results obtained from some clinical trials have encouraged the clinicians to use the fiber posts confidently. Fiber posts are manufactured from pre-stretched fibers impregnated within a resin matrix. The fibers could that be of carbon, glass/silica, and quartz, whereas Epoxy and bis-GMA are the most widely used resin bases. But recently studies are also found to be going on for polyimide as possible material for the fiber post resin base as a substitute for the conventional materials.

• The Journal of Advanced Prosthodontics
• /
• v.4 no.1
• /
• pp.37-42
• /
• 2012

PURPOSE. The influence of the modified process in the fiber-reinforced post and resin core foundation treatment on the fracture resistance and failure pattern of premolar was tested in this study. MATERIALS AND METHODS. Thirty-six human mandibular premolars were divided into 4 groups (n = 9). In group DCT, the quartz fibre post (D.T. Light-post) was cemented with resin cement (DUO-LINK) and a core foundation was formed with composite resin (LIGHT-CORE). In group DMO and DMT, resin cement (DUO-LINK) was used for post (D.T. Lightpost) cementation and core foundation; in group DMO, these procedures were performed simultaneously in one step, while DMT group was accomplished in separated two steps. In group LCT, the glass fiber post (LuxaPost) cementation and core foundation was accomplished with composite resin (LuxaCore-Dual) in separated procedures. Tooth were prepared with 2 mm ferrule and restored with nickel-chromium crowns. A static loading test was carried out and loads were applied to the buccal surface of the buccal cusp at a 45 degree inclination to the long axis of the tooth until failure occurred. The data were analyzed with MANOVA (${\alpha}$= .05). The failure pattern was observed and classified as either favorable (allowing repair) or unfavorable (not allowing repair). RESULTS. The mean fracture strength was highest in group DCT followed in descending order by groups DMO, DMT, and LCT. However, there were no significant differences in fracture strength between the groups. A higher prevalence of favorable fractures was detected in group DMT but there were no significant differences between the groups. CONCLUSION. The change of post or core foundation method does not appear to influence the fracture strength and failure patterns.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.2
• /
• pp.126-132
• /
• 2013

PURPOSE. Post surface conditioning is necessary to expose the glass fibers to enable bonding between fiber post and resin cement. The purpose of the present study was to evaluate the effect of different surface conditioning on tensile bond strength (TBS) of a glass fiber reinforced post to resin cement. MATERIALS AND METHODS. In this in vitro study, 40 extracted single canal central incisors were endodontically treated and post spaces were prepared. The teeth were divided into four groups according to the methods of post surface treatment (n=10): 1) Silanization after etching with 20% $H_2O_2$, 2) Silanization after airborne-particle abrasion, 3) Silanization, and 4) No conditioning (Control). Adhesive resin cement (Panavia F 2.0) was used for cementation of the fiber posts to the root canal dentin. Three slices of 3 mm thick were obtained from each root. A universal testing machine was used with a cross-head speed of 1 mm/minute for performing the push-out tests. Two-way ANOVA and Tukey post hoc tests were used for analyzing data (${\alpha}$=0.05). RESULTS. It is revealed that different surface treatments and root dentin regions had significant effects on TBS, but the interaction between surface treatments and root canal regions had no significant effect on TBS. There was significant difference among $H_2O_2$ + Silane Group and other three groups. CONCLUSION. There were significant differences among the mean TBS values of different surface treatments. Application of hydrogen peroxide before silanization increased the bond strength between resin cements and fiber posts. The mean TBS mean values was significantly greater in the coronal region of root canal than the middle and apical thirds.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.5
• /
• pp.582-595
• /
• 2003

Statement of problem : Most posts are metallic, but in response to the need for a post that possesses optical properties compatible with an all-ceramic crown. an esthetic post has been developed. Although there have been many studies about the esthetic post materials, 3-dimensional finite element studies about the stress distribution of them are in rare. Purpose : The purpose of this study is to investigate comparatively the distribution of stresses of the restored, endodontically treated maxillary incisors with the esthetic post materials and the displacement on the cement layer on simulated occlusal loading by using a 3-dimensional finite element analysis model. Material and method : Four 3-dimensional finite element models were constructed in a view of a maxillary central incisor, a post, a core, and the supporting tissues to investigate the stresses in various esthetic posts and cores and the displacement on the cement layer (Model 1 ; Cast gold post and core, Model 2 ; Glass fiber post with composite core, Model 3 ; Zirconia post with composite core. Model 4 ; Zirconia post with ceramic core). Force of 300N was applied to the incisal edge and the cingulum (centric stop point) with the angle of 135-degree to the long axis of the tooth. Results : 1. The stresses and displacement on the incisal edge were higher than on the cingulum 2. The stresses in dentin were the highest in Model 2 (Glass fiber post with composite core), and the second was Model 3, the third Model 1, and the lowest Model 4. 3. The stresses in post and core were the highest in Model 4 (Zirconia post with ceramic core), and the second was Model 1, the third Model 3, and the lowest Model 2. 4. The displacement on the cement layer was the highest in Model 2 (Glass fiber post with composite core), and the second was Model 3, the third Model 1, and the lowest Model 4. Conclusion : When a functional maximum bite force was applied, the distribution of stresses or the esthetic post and core materials and the displacement on the cement layer were a little different. It seems that restoring extensively damaged incisors with esthetic post and core materials would be decided according to the remaining tooth structure.

• The Journal of Advanced Prosthodontics
• /
• v.3 no.2
• /
• pp.90-95
• /
• 2011

PURPOSE. To compare the fracture resistance and the mode of failure of endodontically treated teeth restored with different post-core systems. MATERIALS AND METHODS. Root canal treatment was performed on 40 maxillary incisors and the samples were divided into four groups of 10 each. For three experimental groups post space preparation was done and teeth were restored with cast post-core (Group B), stainless steel post with composite core (Group C) and glass fiber post with composite core using adhesive resin cement (Group D). Control group (A) samples were selected with intact coronal structure. All the samples were prepared for ideal abutment preparation. All the samples were subjected to a load of 0.5 mm/min at $130^{circ}$.until fracture occurred using the universal testing machine. The fracture resistance was measured and the data were analyzed statistically. The fracture above the embedded resin was considered to be favorable and the fracture below the level was considered as unfavorable. The statistical analysis of fracture resistance between different groups was carried out with t-test. For the mode of failure the statistical analysis was carried out by Kruskal-Wallis test and Chi-Square test. RESULTS. For experimental group Vs control group the fracture resistance values showed significant differences (P<.05). For the mode of failure the chi-square value is 16.1610, which means highly significant (P=.0009) statistically. CONCLUSION. Endodontically treated teeth without post core system showed the least fracture resistance demonstrating the need to reinforce the tooth. Stainless steel post with composite core showed the highest fracture resistance among all the experimental groups. Teeth restored with the Glass fiber post showed the most favorable fractures making them more amenable to the re-treatment.

• Journal of the Korean Society for Precision Engineering
• /
• v.28 no.4
• /
• pp.474-481
• /
• 2011

The purpose of this study was to investigate the effect of rigidity of post core systems on stress distribution by the finite element stress analysis method. Three-dimensional finite element models simulating an endodontically treated maxillary central incisor restored with a zirconia crown were prepared. Each model contained cortical bone, trabecular bone, periodontal ligament, 4mm apical root canal filling, and post-and-core. A 50N static occlusal load was applied to the palatal surface of the crown with a $60^{\circ}$ angle to the long axis of the tooth. And three parallel type post (zirconia, glass fiber and stainless steel) and two core (Paracore and Tetric ceram) materials were evaluated, respectively. The differences in stress transfer characteristics of the models were analyzed. von Mises stresses were chosen for presentation of results and maximum displacement and hydrostatic pressure were also calculated. For the Result of the research, the model applied glass fiber to post material has lowest von Mises stress and it is suitable for material of post core systems.

• 대한치과보철학회:학술대회논문집
• /
• 2002.11a
• /
• pp.73-73
• /
• 2002

• Structural Engineering and Mechanics
• /
• v.53 no.6
• /
• pp.1253-1269
• /
• 2015

The present paper investigates the post heating behavior of concrete beams reinforced with fiber reinforced polymer (FRP) bars, namely carbon fiber reinforced polymer (CFRP) bars and glass fiber reinforced polymer (GFRP) bars. Thirty rectangular concrete beams were prepared and cured for 28 days. Then, beams were either subjected (in duplicates) to elevated temperatures in the range (100 to $500^{\circ}C$) or left at room temperature before tested under four point loading for flexural response. Experimental results showed that beams, reinforced with CFRP and GFRP bars and subjected to temperatures below $300^{\circ}C$, showed better mechanical performance than that of corresponding ones with conventional reinforcing steel bars. The results also revealed that ultimate load capacity and stiffness pertaining to beams with FRP reinforcement decreased, yet their ultimate deflection and toughness increased with higher temperatures. All beams reinforced with FRP materials, except those post-heated to $500^{\circ}C$, failed by concrete crushing followed by tension failure of FRP bars.

• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.737-742
• /
• 1994

The fracture energy of glass fiber/carbon fiber/epoxy resin hybrid composite system was investigated in the aspect of fracture mechanism. Epoxy resin matrix was DGEBA-MDA-SN-HQ system. On the interface of glass fiber and matrix, post debone friction energy provided a major contribution to the fracture energy, and debonding energy and pull-out energy were of the similar value. In the case of fracture on the interface of carbon fiber and matrix, pull-out energy was the major contributor.