• Korean Journal of Materials Research
• /
• v.16 no.4
• /
• pp.235-240
• /
• 2006

We investigated the effect of ZnO filler on the microstructure of $BaO-B_2O_3-ZnO-P_2O_5$ glass system to find an etching mechanism of barrier ribs. The sintering behavior of composites heated in the temperature range $560-600^{\circ}C$ was studied by volumetric shrinkage rate and microstructure. The etching test was carried out in $HNO_3$ solution at $50^{\circ}C$ for 10 min. The volumetric shrinkage of sintered sample decreased with the increased firing temperature because of the formation of two crystals. Glass and ZnO filler react forming the $BaZn_2(PO_4)_2$ crystal phases during the sintering process. Etching phenomenon of sintered samples by $HNO_3$ showed that the $BaZn_2(PO_4)_2$ crystal phase was strongly leached compared to glass matrix, crystal phases and fillers. Therefore, the control of interface by condition of sintering is so important to achieve etching effect in barrier ribs.

• Journal of the Society of Naval Architects of Korea
• /
• v.49 no.6
• /
• pp.521-527
• /
• 2012

It is well known that flexible composite material propeller has superior radiation noise characteristics with outstanding damping effects. In this paper, three flexible composite material propellers were produced using compression molding process, and their hydrodynamic performances and radiation noise characteristics were measured. One propeller, C1, was made up from carbon/epoxy composite laminates, and the other two ones, G1 and G2, from glass/epoxy ones. Their fiber arrays were selected by the progressive damage structural analysis of propellers using composite material model MAT_162 (Composite_DMG_MSC) linked with LS-DYNA code. Carbon/epoxy and glass/epoxy composite specimen tests were performed, their damage mechanisms were figured out, and their parameters were calibrated by their progressive damage structural analysis according to their damage criteria.

• Journal of the Korean Society for Railway
• /
• v.12 no.4
• /
• pp.590-596
• /
• 2009

In this study, the failure modes and energy absorption characteristics of four different kinds of circular tubes made of carbon, glass, Kevlar and carbon-Kevlar hybrid fibres composites with epoxy resin have been evaluated. To achieve these goals, compressive tests were conducted for the tubes under 10mm/min loading speed. Based on the test results, the carbon/epoxy tube showed the best energy absorption capability, while carbon-Kevlar/epoxy tubes were worst. In the failure mode during crushing, both of the carbon/epoxy tubes and the glass/epoxy tubes were crushed by brittle fracturing mode. The Kevlar/epoxy tubes were collapsed by local buckling mode like steel, while the carbon-Kevlar hybrid tubes were collapsed by mixed mode of local buckling and lamina bending.

• Journal of Welding and Joining
• /
• v.34 no.2
• /
• pp.22-29
• /
• 2016

Recently, Application of composite materials are increased in transport area for weight reduction. Also, Related technical developments have been implemented actively at domestic and abroad. In particular, The carbon fiber has high strength and ultra light property higher than stainless steel, aluminum, GFRP as Eco-friendly material. Carbon fiber contribute to improving the environmental effect such as fuel saving, expansion of loadage, reducing the exhaustion of carbon dioxide through the weight reduction of transport area. In addition, The carbon fiber is applied to the ship in the area of race yacht, luxury cruise boat as weight reduction and high added-value materials, but there is limited application for general boat because price of carbon fiber is very expensive. For the weight reduction of general boat hull, being used as structure materials, glass fiber and carbon fiber are applied to hull with form of hybrid composite materials, but application of domestic and research for development are incomlete. In this study, An evaluations of mechanical strength property and fatigue strength are performed on composite materials by hybrid weaving of glass fiber and carbon fiber and composite materials forming method by hybrid forming.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.4
• /
• pp.330-336
• /
• 2000

Effects of microstructure and indentation stress on fracture behavior of glass-infiltrated alumina composite for dental restorative application were investigated by the Hertzian and Vickers indentation method. Indentation stress-strain curve of glass-infiltrated alumina has showed the quasi-plastic behavior - deviation from linearity at high stress and the classical Hertzian cone crack, which could be confirmed the subsurface damage micrographs using bonded-interface specimen technique. The indentation stress-strain curves for the starting preforms are strongly dependent on porosity and microstructure of the preforms. On the other hand, the curves for the infiltrated composites are relatively insensitive to these factors. The failure of composite is originated at quasi-plastic deformation region. Damage and fracture behavior due to Hertzian stress field is theoretically examined, so that the indentation stress field plays a great role in material degradation. After Hertzian indentation annealing processing changes fracture behavior of alumina composite, so that stress field in material is healed through annealing.

• Textile Coloration and Finishing
• /
• v.33 no.3
• /
• pp.153-160
• /
• 2021

In this study, composite materials were prepared by varying the content of glass fiber and bamboo fiber in PP/glass fiber/bamboo fiber. Experiments were conducted to confirm the mechanical properties(tensile, impact and burst strength) and volatile organic compound content of the bamboo fiber composite prepared under these conditions. An improvement in the main properties was observed at a fiber content of 30wt%. When the fiber fraction was increased above 30wt%, the mechanical properties tended to decrease due to the agglomeration of fibers at higher load fractions. In addition, the content of volatile organic compounds increased as the content of bamboo fibers increased, which is thought to be due to the volatile organic compounds generated during the manufacturing process of the composite material being present in the composite material without escaping from the pores of the bamboo fibers and volatilizing at a certain temperature. As a result of confirming the physical properties of the composite, it is considered that the optimal mixing condition is 30wt% of bamboo fiber for the composite produced by varying the amount of bamboo fiber composite. In the future, it is thought that follow-up experiments to confirm and improve the pre-treatment conditions for reducing the content of volatile organic compounds in the manufactured composite material are possible.

• Composites Research
• /
• v.22 no.4
• /
• pp.13-19
• /
• 2009

Adhesive joints are widely used for structural joining applications in various fields and environmental conditions. Polyurethane adhesive is using for LNG carrier with cryogenic temperature condition. Even if similar polyurethane adhesive is used for different substrate, it shows different adhesion properties. Specially, variation of adhesion properties depending on the resin system or fiber is very important factor for selection of adhesive on industrial application. In present study, we got different peel strength according to the different test temperature when different polyurethane adhesive was used for same fiber reinforced composite. The main cause was investigated using by SEM and it was proven that the different adhesion property between glass fiber on composite surface and polyurethane adhesives at cryogenic temperature.

• Composites Research
• /
• v.22 no.5
• /
• pp.8-14
• /
• 2009

Interfacial evaluation of glass fiber reinforced carbon nanotube (CNT)-epoxy nanocomposite was investigated by micromechanical technique in combination with wettability test. The contact resistance of the CNT-epoxy nanocomposite was measured using a gradient specimen, containing electrical contacts with gradually-increasing spacing. The contact resistance of CNT-epoxy nanocomposites was evaluated by using the two-point method rather than the four-point method. Due to the presence of hydrophobic domains on the heterogeneous surface, the static contact angle of CNT-epoxy nanocomposite was about $120^{\circ}$, which was rather lower than that for super-hydrophobicity. For surface treated-glass fibers, the tensile strength decreased dramatically, whereas the tensile modulus exhibited little change despite the presence of flaws on the etched fiber surface. The interfacial shear strength (IFSS) between the etched glass fiber and the CNT-epoxy nanocomposites increased due to the enhanced surface energy and roughness. As the thermodynamic work of adhesion, $W_a$ increased, both the mechanical IFSS and the apparent modulus increased, which indicated the consistency with each other.

• Composites Research
• /
• v.37 no.4
• /
• pp.316-324
• /
• 2024

This paper presents a study on estimating the number of bridging fibers in multidirectional glass/epoxy composite laminates using acoustic emission signals. DCB test was conducted for analyzing the fracture behavior of multidirectional composite laminates, and acoustic emission sensor was utilized to measure the elastic wave generated upon specimen fracture. For unidirectional composite laminates, the initial number of bridging fibers was estimated through reference paper and fiber volume fraction. To estimate the initial number of bridging fibers for multidirectional composite laminates, the relative ratio of acoustic emission signals was utilized. The estimated number of bridging fibers was applied to FEM, and the results of FEM showed good agreement with experimental results.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.2
• /
• pp.15-22
• /
• 1999

Polymeric meterials that are used for noise and vibration damper in wood/polymer/wood sandwich composites, must have a high loss factor(tan ${\delta}$), and at the same time the storage modulus(E) of $5{\times}10^7$ to $10^9$ dyne/$cm^2$ must withstand over a wide temperature and frequency ranges. In this study, the series of epoxy resinlpolyacrylate interpenetrating polymer networks(IPNs) were synthesized by simultaneous polymerization. Their dynamic tensile properties were measured at 110Hz using Rheovibron instrument. Composite damping factor(tan ${\delta}_c$) and dynamic bending modulus($E_c,\;E_^{\prime\prime}c$) of wood/polymer/wood sandwich composites were measured at 110Hz using a Rheovibron in bending mode of vibration. These dynamic tensile studies indicated that cured epoxy resin/polyacrylates IPNs were semicompatible in the sense that both the shifting of T($E^{\prime\prime}_{max}$) or T(tan ${\delta}_{max}$) and the broadening of glass transition temperature range were observed. Especially, the cured Epikote871/P(n-BMA) IPNs of composition 70/30 to 50/50 showed a relatively high tan a and appropriate E' value over a wide temperature range; consequently the tan a e curves of wood/IPNs/wood sandwich composites was broadened over a wide temperature range.