• Korean Journal of Materials Research
• /
• v.20 no.3
• /
• pp.148-154
• /
• 2010

It is necessary to develop new methods to prevent catastrophic failure of structural material in order to avoid accidents and conserve natural and energy resources. Design of intelligent materials with a self-diagnosing function to prevent fatal fracture of structural materials was achieved by smart composites consisting of carbon fiber tows or carbon powders with a small value of ultimate elongation and glass fiber tows with a large value of ultimate elongation. The changes in electrical resistance of CF-GFRP/GFRP (carbon fiber and glass fiber-reinforced plastics/glass fiber-reinforced plastics) composites increased abruptly with increasing strain, and a tremendous change was seen at the transition point where carbon fiber tows were broken. Therefore, the composites were not to monitor damage from the early stage. On the other hand, the change in electrical resistance of CP-GFRP/GFRP (carbon powder dispersed in glass fiber-reinforced plastics/glass fiber-reinforced plastics) composites increased almost linearly in proportion to strain. CP-GFRP/GFRP composites are superior to CF-GFRP/GFRP composites in terms of their capability to monitor damage by measuring change in electrical resistance from the early stage of damage. However, the former was inferior to the latter as an application because of the difficulties of mass production and high cost. A method based on monitoring damage by measuring changes in the electrical resistance of structural materials is promising for improved reliability of the material.

• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.669-674
• /
• 2012

Yellow phosphor dispersed color conversion glasses are promising phosphor materials for white LED applications because of their good thermal durability, chemical stability, and anti-ultraviolet property. Six color conversion glasses were prepared with high Tg and low Tg specimens of glass. Luminous efficacy, luminance, CIE (Commission Internationale de l'Eclairage) chromaticity, CCT (Correlated Color Temperature), and CRI (Color Rendering Index) of the color conversion glasses were analyzed according to the PL spectrum. Color conversion glasses with high Tg glass frit, sintered at higher temperature, showed better luminous properties than did color conversion glasses with low Tg glass frit. The characteristics of the color conversion glass depended on the glass composition rather than on the sintering temperature. The XRD peaks of the YAG phosphor disappeared in the color conversion glass with major components of $B_2O_3$-ZnO-$SiO_2$-CaO and, in the XRD results, new crystalline peaks of $BaSi_2O_5$ appeared in the color conversion glass with major components of $Bi_2O_3$-ZnO-$B_2O_3$-MgO. The characteristics of CIE chromaticity, CCT, and the CRI of low Tg color conversion glasses showed worse color properties than those of high Tg color conversion glasses. However, these color characteristics of low Tg glasses were improved by thickness variation. So color conversion glasses with good characteristics of both luminous and color properties were attained.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.37 no.4
• /
• pp.445-450
• /
• 2024

The expansion of lithium-ion battery usage beyond portable electronic devices to electric vehicles and energy storage systems is driven by their high energy density and favorable cycle characteristics. Enhancing the stability and performance of these batteries involves exploring solid electrolytes as alternatives to liquid ones. While sulfide-based solid electrolytes have received significant attention for commercialization, research on amorphous-phase glass solid electrolytes in oxide-based systems remains limited. Here, we investigate the glass transition temperatures and sintering behaviors by changing the molecular ratio of Li₂O/B₂O₃ in borate glass comprising Li₂O-B₂O₃-Al₂O₃ system. The glass transition temperature is decreasing as increasing the amount of Li₂O. When we sintered at 450℃, just above the glass transition temperature, the samples did not consolidate well, while the proper sintered samples could be obtained under the higher temperature. We successfully obtained the borate glass ceramics phases by melt-quenching method, and the sintering characteristics are investigated. Future studies could explore optimizing ion conductivity through refining processing conditions, adjusting the glass former-to-modifier ratio, and incorporating additional Li salt to enhance the ionic conductivity.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2006.08a
• /
• pp.935-937
• /
• 2006

Phosphate glass system is expected to be useful as a lead-free material in many devices in plasma display panels (PDP). The present study is mainly focused on the evaluation of interface reaction between ceramic fillers and phosphate glass matrix for barrier ribs in PDP. The results suggest that properties of barrier rib depend on the crystallization behavior and interface reaction between the fillers and glass matrix.

• Restorative Dentistry and Endodontics
• /
• v.22 no.2
• /
• pp.751-760
• /
• 1997

Resin-modified glass ionomers were introduced in 1988 to overcome the problems of moisture sensitivity and low early mechanical strengths of the conventional glass ionomers, and to maintain their dinical advantages. The purpose of this study was to evaluate the bi-axial fracture strength of four resinmodified glass-ionomers(Fuji II LC, Vitremer, Dyract, VariGlass), one resin composite material(Z-100), and one conventional glass-ionomer(Fuji II). Three specimens of each material and shade combination were made according to the manufacturers' instructions. Materials were condensed into metal mold with a diameter of 10mm and a thickness of 2.0mm and pressed between two glass plates. Resin-modified glass ionomers were polymerized using a Visilux II light curing unit by irradiating for 60 seconds from both sides, and conventional glass ionomer was cured chemically. After specimens were removed from the molds, surfaces were polished sequentially on wet sandpapers up to No. 600 silicone carbide paper. The specimens were thermocycled for 2,000 cycles between $5^{\circ}C$ and $55^{\circ}C$ distilled water. After thermocycling, bi-axial fracture strengths were measured using a compressive-tensile tester(Zwick 1456 Z020, Germany) with the cross head speed of 0.5mm/minute. The results were as follows: 1. Two factors of the kind and color of materials had a main effect on bi-axial fracture strength (p<0.01), and bi-axial fracture strength was influenced significantly by the kinds of materials (p<0.01). But there was no significant interaction between two variables of the kind and color of materials (p>0.05). 2. Comparing the mechanical properties of the materials, the elastic modulus of Z100 was higher than any other material, and there was no difference in the displacement at fracture among materials. The bi-axial fracture strength of Z100 was significantly higher than any other material, and that of resin-modified glass ionomers was significantly higher than that of conventional glass ionomer (p<0.05). 3. In the same material group, the color of material had little influence on the mechanical properties.

• Korean Journal of Materials Research
• /
• v.19 no.2
• /
• pp.95-101
• /
• 2009

Glass ceramics were made from coal bottom ash by adding CaO and $Li_2O$ as glass modifiers and $TiO_2$ as a nucleating agent in a process of melting and quenching followed by a thermal treatment. The surface of the glass ceramics has 1.6 times more $Li_2O$ compared to the inner matrix. When $TiO_2$ was not added or when only 2 wt% was added, the surface parts of the glass ceramics were crystalline with a thickness close to $130{\mu}m$. In addition, the matrixes showed only the glass phase and not the crystalline phase. However, doping of $TiO_2$ from 4 wt% to 10 wt% began to create small crystalline phases in the matrix with an increase in the quantity of the crystalline. The matrix microstructure of glass ceramics containing $TiO_2$ in excess of 8 wt% was a mixture of dark-gray crystalline and white crystalline parts. These two parts had no considerable difference in terms of composition. It was thought that the crystallization mechanism affects the crystal growth, direction and shape and rather than the existence of two types of crystals.

• Advances in materials Research
• /
• v.11 no.4
• /
• pp.251-277
• /
• 2022

Disposal of industrial waste in cities where municipal authorities permitting higher floor area ratio coupled with increasing living standards, a lot of demolition waste is being generated. Its disposal is a challenge particularly in megacities where no landfills are available. The ever-increasing cost of building construction materials also necessitates consuming demolition wastes in a useful manner to save fresh natural raw materials. In the present work, the crushed waste glass is used in high-strength concrete as a partial replacement of fine aggregate. The control concrete of grade M60 was proportioned following BIS 10262-2009. The crushed waste glass has been used as a partial replacement with varying percentages of 10, 20, 30, and 40% by weight of fine aggregate. Experimental tests were carried on the fresh and hardened state of the concrete. The effect of crushed waste glass on the workability of the concrete has been investigated. Non-destructive tests, acid attack tests, compressive strength, split tensile strength, and X-ray diffraction analysis was carried out for the control concrete and concrete containing crushed waste glass after 7, 28, and 270 days of normal curing. The results show that for the same w/c ratio, the workability of concrete increases with increasing replaced crushed waste glass content. However, the decrease in compressive strength of the concrete after 28 days of normal curing and further after 28 days of acid attacks, up to 30% replacement level of fine aggregate by the crushed waste glass is insignificant.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.119.2-119.2
• /
• 2007

• Journal of the Korean Ceramic Society
• /
• v.56 no.6
• /
• pp.577-582
• /
• 2019

Recently, E-glass fiber is the one of most widely used ceramic fiber for aerospace fields. Recycling technology for waste of wind power blades is arising issue for reasons of low manageability and high cost of wastes. Though glass fiber is perfectly dissolved in hydrofluoric acid, low cost for recycling and harmless to human is important for recycling of blades. Chemically melted glass fiber will be used as different purpose like accelerator of hardening for shotcrete. In this study, dissolution process of glass fiber is tested in NaOH solution at low temperatures. In addition, difference in diameter reduction of glass fiber is observed by various alkali concentration and reaction times, treatment temperatures using FE-SEM.

• Proceedings of the Korean Ceranic Society Conference
• /
• 1986.12a
• /
• pp.259-267
• /
• 1986

The sintering behavior of silver-oxide glass composite thick-film has been studied with varing glass content. It is shown that during heat treatment glass became liquid phase to deeply affect the microstructure development of the silver particles and to control the physical properties of the thick-films. As glass content increased, the initial repacking of silver particles took place rapidly but the homogeneities of the microstructure showed different features. When the glass content was over some range, the silver particles exuded glass to decrease net energy and glass formed liquid pools separated from the solid skeletons. Finally the relations between the microstructures and electrical properties of the thick-film were discussed.