• Corrosion Science and Technology
• /
• v.23 no.4
• /
• pp.278-282
• /
• 2024

Recently, hot rolled galvanized steel is widely used in automotive parts. As the paradigm of the automotive market has changed from fossil fuel vehicle to electric vehicle, the automotive industry needs more high-strength steels to reduce weights of automobiles. However, because high-strength steel contains high solute carbon, it is expected to have a risk of stretcher-strain on the surface due to dislocation trapping by solute [C] and [N]. Generally, galvanized steel is supposed to pass through a furnace around the temperature of Zinc pot to increase material temperature. Otherwise, the inhibition layer could not be formed. However, solute carbon and nitrogen are volatile enough to move around the furnace temperature. Moreover, the ratio of ferrite phase and precipitated Fe3C can be variable, resulting in yield point elongation related to the stretcher strain. Furthermore, the quality of the galvanized surface can be affected by a high temperature of the furnace. Although a relatively hot rolled galvanizing line furnace has a lower temperature than an annealing line furnace, it can affect various quality aspects. In other words, this paper aims to determine how these phenomena appear concerning furnace temperature.

• Korean Journal of Metals and Materials
• /
• v.47 no.4
• /
• pp.228-234
• /
• 2009

It is well known that the formation of $SiO_2$, $Al_2O_3$ and/or other oxides at the steel surface during the annealing process deteriorates the surface quality of galvanized steels. It is important to minimize oxide formation during the annealing process for the superior surface quality of galvanized steels. In order to minimize the oxide formation on the steel surface, antimony was chosen as an alloying element to the commercial steels. Then, the effect of alloying element on the oxidation behavior was investigated. A small amount of antimony was added to two types of steels, one with 0.1% C, 1.0% Si, 1.5% Mn, 0.08% P, and the other with 0.002% C, 0.001% Si, 0.104% Mn, 0.01% P. Then, the oxidation behavior was investigated from $650{\sim}900^{\circ}C$ in the air. The addition of antimony to the steels retarded the outward diffusion of elements during the oxidation, resulting in reduction of the oxidation rate.

• Corrosion Science and Technology
• /
• v.7 no.1
• /
• pp.1-5
• /
• 2008

The gas atmosphere in continuous annealing and galvanizing lines alters both composition and microstructure of the surface and sub-surface of sheet steel. The formation and morphology of the oxides of alloying elements in High Strength Interstitial Free (HS-IF), Dual Phase (DP) and Transformation-Induced Plasticity (TRIP) steels are strongly influenced by the furnace dew point, and the presence of specific oxide may result in surface defects and bare areas on galvanized sheet products. The present contribution reviews the progress made recently in understanding the selective formation of surface and subsurface oxides during annealing in hot dip galvanizing and conventional continuous annealing lines. It is believed that the surface and sub-surface composition and microstructure have a pronounced influence on galvanized sheet product surface quality. In the present study, it is shown that the understanding of the relevant phenomena requires a combination of precise laboratory-scale simulations of the relevant technological processes and the use of advanced surface analytical tools.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.342-345
• /
• 2009

Electro galvanized steel is electroplated cold roller steel for improving corrosion resistance and paintability, and is widely used in automobiles and home appliances. In the electroplating line for manufacturing electro galvanized steel if plating process is carried out with impurity on conductor roll surface, the defects in manufacturing process occurs because of steel fault. For quality, polishing is always required to separate impurity on surface of conductor roll. In this study, finite element analysis of wear for polisher brush is carried out for replaced time of it.

• Journal of Surface Science and Engineering
• /
• v.31 no.2
• /
• pp.101-108
• /
• 1998

The effect of oxidation-reduction heating conditions on coating adherence of hot-dip galvanized steel containing silicon has beeninvestigated. The presence of a stbke sillicon oxide formed on the steel surface has been shown to be very detrimenal to proper wetting by liquid zinc. When the steel has more than the critical sillicon content neeled to from a stable external oxide, the use of oxidation-reduction method has been found successful in obtaining a good quality, coated product with excellence adhreence. This can be explained by the formation of an iron oxide. The iron oxrtion of the scale is reduced, leaving the stable oxides dispersed in a fresh metallic iron surface layer. This reduced iron surface is easily wetted by the liquid zinc and excellent adherence is obtained.

• Corrosion Science and Technology
• /
• v.17 no.2
• /
• pp.74-80
• /
• 2018

The electronic industries require environmentally-friendly and highly functional materials to enhance the quality of human life. Home appliances require insect repellent steels that work to protect household microwave ovens from incurring damage by insects such as fire ants and cockroaches in tropical regions. Thus, POSCO has developed new types of functional steels, coated with an array of organic-inorganic hybrid composites on the steel surface, to cover panels in microwave ovens and refrigerators. The composite solution uses a fine dispersion of hybrid solution with polymeric resin, inorganic and a pyrethroid additive in aqueous media. The hybrid composite solution coats the steel surface, by using a roll coater and is cured using an induction curing furnace on both the continuous galvanizing line and the electro-galvanizing line. The new steels were evaluated for quality performances, salt spray test for corrosion resistance and biological performance for both insect repellent and antimicrobial activity. The new steels with organic-inorganic composite coating exhibit extraordinarily biological functionalities, for both insect repellent and antimicrobial activities for short and long term tests. The composite-coating solution and experimental results are discussed and suggest that the molecular level dispersion of insecticide on the coating layer is key to biological functional performances.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.155-157
• /
• 2007

The Friction spot dissimilar welding of galvanized steel/Al6061-T6 was performed to investigate the mechanical characteristics of the joints. The presence of thin film of aluminum oxide on the surface and melting of zinc in the coating, made substandard joint characteristics for dissimilar Friction spot joining(FSJ) performed with out removing the coating. Where as, for dissimilar FSJ of galvanized steel/Al6061-T6 after removing the coating, superior agitation and welding quality has been obtained for a configuration of galvanized steel as the upper plate and Al6061-T6 as lower plate. The results from tensile tests and microscopic examination for various combinations of the welding parameters have been presented.

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.15-19
• /
• 2012

Both electrogalvanized and hot-dip galvanized steel sheets have been finally produced via organic-inorganic surface coating process on the zinc surface to enhance corrosion resistance and afford additional functional properties. Recently, POSCO has been developed a variety of chromate-free coated steels that are widely used in household, construction and automotive applications. New organic-inorganic hybrid coating solutions as chromate alternatives are comprised of surface modified silicate with silane coupling agent and inorganic corrosion inhibitors as an aqueous formulation. In this paper we have prepared new type of hybrid coatings and evaluated quality performances such as corrosion resistance, spot weldability, thermal tolerance, and paint adhesion property etc. The electrogalvanized steels with these coating solutions exhibit good anti-corrosion property compared to those of chromate coated steels. Detailed components composition of coating solutions and experimental results suggest that strong binding between organic-inorganic hybrid coating layer and zinc surface plays a key role in the advanced quality performances.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.1
• /
• pp.32-38
• /
• 2011

Galvanized steel has gone through a chemical process to keep it from corroding. The steel gets coated in layers of zinc because rust will not attack this protective metal. For countless outdoor, marine, or industrial applications, galvanized steel is an essential fabrication component. The reduction of the corrosion rate of zinc is an important topic. In the past, a very popular way to reduce the corrosion rate of zinc was to use chemical conversion layers based on $Cr^{+6}$. However, a significant problem that has arisen is that the use of chromium salts is now restricted because of environmental protection legislation. Therefore, it is very important to develop new zinc surface treatments that are environmentally friendly to improve the corrosion resistance of zinc and adhesion with a final organic protective layer. In this study, a Urethane solution (only Urethane 20 wt.%; S-700) and an organic/inorganic solution with Si (Si polysilicate 10 wt.% + Urethane 10 wt.%; LRO-317) are used. Based on the salt spray test of 72 h, S-700 and LRO-317 had a superior effect for the corrosion resistance on EGI and HDGI, respectively.

• Corrosion Science and Technology
• /
• v.14 no.5
• /
• pp.213-217
• /
• 2015

Recently, household electronic industries require environmentally-friendly and highly functional steels in order to enhance the quality of human life. Customers especially require both excellent corrosion and abrasion resistant anti-fingerprint steels for digital TV panels. Thus POSCO has developed new functional electro-galvanized steels, which have double coated layers with organic-inorganic composites on the zinc surface of the steel for usage as the bottom chassis panel of TVs. The inorganic solution for the bottom layer consists of inorganic phosphate, magnesium, and zirconium compounds with a small amount of epoxy binder, and affords both improved adhesion properties by chemical conversion reactions and corrosion resistance due to a self-healing effect. The composite solution for the top layer was prepared by fine dispersion of organic-inorganic ingredients that consist of a urethane modified polyacrylate polymer, hardener, silica sol and a titanium complex inhibitor in aqueous media. Both composite solutions were coated on the steel surface by using a roll coater and then cured through an induction furnace in the electro-galvanizing line. New anti-fingerprint steel was evaluated for quality performance through such procedures as the salt spray test for corrosion resistance, tribological test for abrasion resistance, and conductivity test for surface electric conductance regarding to both types of polymer resin and coating weight of composite solution. New composite coated anti-fingerprint steels afford both better corrosion resistance and abrasion properties compared to conventional anti-fingerprint steel that mainly consists of acrylate polymers. Detailed discussions of both composite solutions and experimental results suggest that urethane modifications of acrylate polymers of composite solutions play a key role in enhanced quality performances.