• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2011년도 추계학술대회 초록집
• /
• pp.47.1-47.1
• /
• 2011

We report on a direct measurement of two-dimensional chemical and electrical distribution on the surface of photovoltaic Cu(In,Ga)$Se_2$ thin-films using a nano-scale spectroscopic and electrical characterization, respectively. The Raman measurement reveals non-uniformed surface phonon vibration which comes from different compositional distribution and defects in the nature of polycrystalline thin-films. On the other hand, potential analysis by scanning Kelvin probe force microscopy shows a higher surface potential or a small work function on grain boundaries of the thin-films than on the grain surfaces. This demonstrates the grain boundary is positively charged and local built-in potential exist on grain boundary, which improve electron-hole separation on grain boundary. Local electrical transport measurements with scanning probe microscopy on the thin-films indicates that as external bias is increases, local current is started to flow from grain boundary and saturated over 0.3 V external bias. This accounts for carrier behavior in the vicinity of grain boundary with regard to defect states. We suggest that electron-hole separation at the grain boundary as well as chemical and electrical distribution of polycrystalline Cu(In,Ga)$Se_2$ thin-films.

• Current Photovoltaic Research
• /
• 제3권1호
• /
• pp.21-26
• /
• 2015

High efficiency $Cu(In,Ga)Se_2$ solar cells are generally prepared above $500^{\circ}C$. Lowering the process temperature can allow wider selection of substrate material and process window. In this paper, the three-stage co-evaporation process widely used to grow CIGS thin film at high temperature was modified to reduce the maximum substrate temperature. Below $400^{\circ}C$ the CIGS films show poor crystal growth and lower solar cell performance, in spite of external Na doping by NaF. As a new approach, Cu source instead of Cu with Se in the second stage was applied on the $(In,Ga)_2Se_3$ precursor at $400^{\circ}C$ and achieved a better crystal growth. The distribution of Ga in the films produce by new method were investigated and solar cells were fabricated using these films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.330-333
• /
• 2002

The substrate temperature is an important parameter in thin film deposition process. In this paper the effects of the substrate temperature on the properties of CuIn0.75Ga0.25Se2(CIGS) thin films are reported. Structure, surface morphology and optical properties of CIGS thin films deposited at various substrate temperatures have been investigated using a number of analysis techniques. X-ray diffraction (XRD) analysis shows that CIGS films exhibit a strong <112> preferred orientation. As expected, at higher substrate temperatures the films displayed a higher degree of crystallinity. The <112> peak was also enhanced and other CIGS peaks appeared simultaneously These results were supported by experimental work using Raman spectroscopy. The Raman spectra of the as-grown CIGS thin films show only the Al mode peak. The intensity of this peak was enhanced at higher deposition temperatures. Scanning electron microscopy (SEM) results revealed very small grains in films fabricated at 48$0^{\circ}C$ substrate temperature. When the substrate temperature was increased the average grain size also increased together with a reduction in the number and size of the voids. The deposition temperature also had a significant influence on the transmission spectra.

• Current Photovoltaic Research
• /
• 제8권3호
• /
• pp.102-106
• /
• 2020

In this paper, the effect of MoSe₂ on the contact resistance (R_C) of the transparent conducting oxide (TCO) and Mo junction in the scribed P2 region of the Cu(In,Ga)Se₂ (CIGS) solar module was analyzed. The CIGS/Mo junction becomes ohmic-contact by MoSe₂, so the formation of the MoSe₂ layer is essential. However, the CIGS solar module has a TCO/MoSe₂/Mo junction in the P2 region due to structural differences from the cell. The contact resistance (R_C) of the P2 region was calculated using the transmission line method, and MoSe₂ was confirmed to increase R_C of the TCO/Mo junction. B doped ZnO (BZO) was used as TCO, and when BZO/MoSe₂ junction was formed, conduction band offset (CBO) of 0.6 eV was generated due to the difference in their electron affinities. It is expected that this CBO acts as a carrier transport barrier that disturbs the flow of current, resulting in increased R_C. In order to reduce the R_C caused by CBO, MoSe₂ must be made thin in a CIGS solar module.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 유기절연재료 전자세라믹 방전플라즈마 일렉트렛트 및 응용기술
• /
• pp.63-66
• /
• 2002

Bi-layer Mo films were deposited on sodalime glass substrates using DC magnetron sputtering. As the gas pressure and power density, the resistivity varied from $1.5{\times}10^{-5}$ to $4.97{\times}10^{-4}{\Omega}{\cdot}cm$. Furthermore, stress direction yielded compressive-to-tensile transition stress curves. The microstructure of the compressive stress films which had poor adhesion consists of tightly packed columns, but of the tensile-stressed films had less dense structure. Under all gas pressure conditions, Mo films exhibited distinctly increasing optical reflection with decreasing gas pressure. The expansion of (110) peak width with the gas pressure meant the worse crystalline growth. Also, The highest efficiency was 15.2% on 0.2 $cm^2$. The fill factor, open circuit voltage and short circuit current were 63 %, 570 m V and 42.6 $mA/cm^2$ respectively.

• 한국진공학회지
• /
• 제21권1호
• /
• pp.17-21
• /
• 2012

투명전도산화막인 Ga-도핑된 ZnO (GZO) 박막을 RF 마그네트론 스퍼터링 증착법을 이용하여 증착하고 전기적, 광학적 특성을 연구하였다. 증착변수로 공정압력에 변수를 주었으며 공정 압력 변화에 따라 전기적 특성과 광학적 특성이 달라짐을 확인할 수 있었다. 모든 박막은 공정압력에 상관없이 c-축(002) 방향성을 나타냈다. 증착된 GZO 박막의 전기저항성은 $8.68{\times}10^{-3}{\Omega}{\cdot}cm\sim2.18{\times}10^{-3}{\Omega}{\cdot}cm$이었고, 모든 가시광 영역에서 90% 이상의 평균 투과율을 보였다. 공정압력에 따라 상온에서 증착된 GZO 박막은 우수한 낮은 저항성과 높은 투과율을 나타내었고, 평판디스플레이와 태양전지의 투명전극으로 응용되기에 적합한 특성을 지닌 것을 확인 할 수 있었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.1
• /
• pp.331-334
• /
• 2003

Photovoltaics is considered as one of the most promising new energy technology, because its energy source is omni present, pollution-free and inexhaustive. It is agreed that these solar cells must be thin film type because thin film process is cost-efficive in the fact that it uses much less raw materials and can be continuous. The defect chalcopyrite material $CuIn_3Se_5$ has been identified as playing an essential role in efficient photovoltaic action in $CuInSe_2$-based devicesm It has been reported to be of n-type conductivity, forming a p-n junction with its p-type counterpart $CuInSe_2$. Because the most efficient cells consist of the $Cu(In,Ga)Se_2$ quarternary, knowledge of some physical properties of the Ga-containing defect chalcopyrite $Cu(In,Ga)_3Se_5$ may help us better understand the junction phenomena in such devices.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.237-242
• /
• 2001

The stochiometric mix of evaporating materials for the CuGaSe$_2$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, CuGaSe$_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were 610$^{\circ}C$ and 450$^{\circ}C$, respectively The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the CuGaSe$_2$ single crystal thin film, we have found that the values of spin orbit splitting Δ So and the crystal field splitting ΔCr were 91 meV and 249.8 meV at 20 K, respectively. From the Photoluminescence measurement on CuGaSe$_2$ single crystal thin film, we observed free excition (Ex) existing only high quality crystal and neutral bound exiciton (D$^{\circ}$,X) having very strong peak intensity. Then, the full-width-at-half-maximum(FWHM) and binding energy 7f neutral acceptor bound excision were 8 meV and 35.2 meV, respectivity. By Haynes rule, an activation energy of impurity was 355.2 meV

• 문화기술의 융합
• /
• 제9권5호
• /
• pp.523-528
• /
• 2023

금속염 수용액과 고분자 매개체를 출발물질로 사용한 액상합성법으로 적색 파장을 방출하는 형광체를 합성하여, 태양전지 성능향상을 위한 소재로서의 적용 가능성을 검토하였다. Ca, Zn, Al, Eu 등 금속의 질산염을 사용하여 수용액을 제조하고 이것을 식물성 고분자인 전분에 함침시킨 전구체를 소결하여 CaZnAlO:Eu 형광체 분말을 합성하였다. 합성한 CaZnAlO:Eu 형광체 분말의 표면구조 및 성분분석을 주사전자현미경(SEM)과 에너지분산형 X-선분광법(EDS)으로 분석하였다. PL측정 결과 650-780nm의 근적외선영역의 발광파장을 가지는 적색형광체가 성공적으로 합성되었다. XRD 분석결과 단일상을 가진 순수한 CZA:Eu³⁺ 형광체가 합성된 것을 확인하였다. SEM, EDS 분석 결과 합성한 Ca₁₄Zn₆Al_9.93O₃₅:Eu³⁺_0.07 형광체 분말의 입도가 균일하며, 부활제로 사용한 Eu 이온이 존재하고 있는 것을 알 수 있다. 합성된 CZA:Eu³⁺ 형광체는 자외선이나 가시광선을 근적외선영역의 파장으로 하향변환하여 태양전지의 광 흡수효율을 높일 수 있는 소재로 활용될 수 있다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2011년도 춘계학술대회 초록집
• /
• pp.106.1-106.1
• /
• 2011

The Cu(In,Ga)Se2 (CIGS) thin film solar cells have been achieved until almost 20% efficiency by NREL. These solar cells include chemically deposited CdS as buffer layer between CIGS absorber layer and ZnO window layer. Although CIGS solar cells with CdS buffer layer show excellent performance, the short wavelength response of CIGS solar cell is limited by narrow CdS band gap of about 2.42 eV. Taking into consideration the environmental aspect, the toxic Cd element should be replaced by a different material. Among Cd-free candidate materials, the CIGS thin film solar cells with ZnS buffer layer seem to be promising with 17.2%(module by showa shell K.K.), 18.6%(small area by NREL). However, ZnS/CIGS solar cells still show lower performance than CdS/CIGS solar cells. There are several reported reasons to reduce the efficiency of ZnS/CIGS solar cells. Nakada reported ZnS thin film had many defects such as stacking faults, pin-holes, so that crytallinity of ZnS thin film is poor, compared to CdS thin film. Additionally, it was known that the hetero-interface between ZnS and CIGS layer made unfavorable band alignment. The unfavorable band alignment hinders electron transport at the heteo-interface. In this study, we focused on growing defect-free ZnS thin film and for favorable band alignment of ZnS/CIGS, bandgap of ZnS and CIGS, valece band structure of ZnS/CIGS were modified. Finally, we verified the photovoltaic properties of ZnS/CIGS solar cells.