• Journal of the Korean institute of surface engineering
• /
• v.47 no.6
• /
• pp.341-346
• /
• 2014

Ga-doped ZnO (GZO) single layer and $SiO_2/GZO$ bi-layered films were deposited on Polycarbonate(PC) substrate by radio frequency magnetron sputtering. Influence of the structural, electrical, and optical properties of the films was considered. We have considered the influence of electron irradiation energy of 450 and 900 eV on the stuctural, electrical and optical properties of $SiO_2/GZO$ thin films. The optical transmittance in a visible wave length region increased with the electron irradiation energy. The electrical resistivity of the films were dependent on the electron's irradiation energy. The $SiO_2/GZO$ films irradiated at 900 eV were showen the lowest resistivity of $7.8{\times}10^{-3}{\Omega}cm$. The film which was irradiated by electron at 900 eV shows 84.3% optical transmittance and also shows lower than contact angle of $58^{\circ}$ in this study.

• Journal of the Korean Society for Heat Treatment
• /
• v.27 no.1
• /
• pp.23-26
• /
• 2014

Ga doped ZnO (GZO) single layer and GZO/ZnO bi-layered films were deposited on glass substrates by radio frequency magnetron sputtering and then the influence of film thickness on the structural, electrical, and optical properties of the films was considered. Thicknesses of the GZO/ZnO films was varied as GZO 100 nm, GZO 85 nm/ZnO 15 nm and GZO 70 nm/ZnO 30 nm, respectively. The observed result means that optical transmittance and electrical resistivity of the films were influenced with film thickness and GZO 85 nm/ZnO 15 nm bilayered films show the higher figure of merit than that of the films prepared other films in this study.

• Korean Journal of Materials Research
• /
• v.21 no.4
• /
• pp.202-206
• /
• 2011

We have investigated the structural and electrical properties of Ga-doped ZnO (GZO) thin films deposited by an RF magnetron sputtering at various RF powers from 50 to 90W. All the GZO thin films are grown as a hexagonal wurtzite phase with highly c-axis preferred parameters. The structural and electrical properties are strongly related to the RF power. The grain size increases as the RF power increases since the columnar growth of GZO thin film is enhanced at an elevated RF power. This result means that the crystallinity of GZO is improved as the RF power increases. The resistivity of GZO rapidly decreases as the RF power increases up to 70 W and saturates to 90W. In contrast, the electron concentration of GZO increases as the RF power increases up to 70 W and saturates to 90W. GZO thin film shows the lowest resistivity of $2.2{\times}10^{-4}{\Omega}cm$ and the highest electron concentration of $1.7{\times}10^{21}cm^{-3}$ at 90W. The mobility of GZO increases as the RF power increases since the grain boundary scattering decreases due to the reduced density of the grain boundary at a high RF power. The transmittance of GZO thin films in the visible range is above 90%. GZO is a feasible transparent electrode for application as a transparent electrode for thin film solar cells.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.12
• /
• pp.984-989
• /
• 2012

We have investigated the structural, electrical and optical properties of Ga-doped ZnO (GZO) thin films prepared by RF magnetron sputtering with laboratory-made ZnO targets containing 1, 3, 5, 7 wt% of $Ga_2O_3$ powder as a doping source. The GZO thin films show the typical crystallographic orientation with c-axis regardless of $Ga_2O_3$ content in the targets. The $3,000{\AA}$ thick GZO thin films with the lowest resistivity of $7{\times}10^{-4}{\Omega}{\cdot}cm$ are obtained by using the GZO ($Ga_2O_3$= 5 wt%) target. Optical transmittance of all films shows higher than 80% at the visible region. The optical energy band gap for GZO films increases as the carrier concentration ($n_e$) in the film increases.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.443-443
• /
• 2008

본 연구에서는 Ga-doped ZnO(GZO)-Ag-GZO 다층 투명전극을 Dual DC magnetron sputtering system을 이용 하여 유리기판 위에 상온에서 제작하여 Ag 두께에 따른 전기적, 광학적, 구조적 특성변화를 조사하였다. Hall effect measurement와 UV/Vis spectrometer로 전기적, 광학적 특성을 분석하였으며, X-ray diffraction(XRD)와FE-SEM분석을 통해 결정성과 표면 특성을 조사하였다. FE-SEM 분석결과 island 형태에서 continuous layer로 박막의 형상이 바뀌면서 다층 투명전극의 전기적, 광학적 특성에 영향을 미치는 것을 알 수 있었다. 본 실험에서 Ag 두께 12 nm에서 가장 최적화되어 유리기판위에 상온에서 증착되었음에도 불구하고 $5.5{\times}{\times}10^{-5}\Omega$-cm, $6\Omega$/sq. 의 매우 낮은 면저항과 비저항을 각각 나타내었고 550 nm 파장에서 87 % 의 높은 광 투과도를 나타내었다. 또한 두께 12 nm의 Ag가 삽입된 다층 투명전극을 polyethylene terephthalate (PET) 기판위에 성막하여 Bending test를 실시하여 0.1% 이하의 매우 낮은 저항변화를 확인함으로써 플렉시블 기반의 디스플레이나 태양전지의 투명 전극으로서의 응용 가능성을 확인하였고 마지막으로 최적화된 다층 투명전극을 유기물태양전지의 애노드에 적용하여 기존 ITO 애노드를 대체할 수 있는 투명전극으로서의 가능성을 제시하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.9
• /
• pp.739-743
• /
• 2011

Ga doped ZnO (GZO)/Cu bi-layer films were deposited with RF and DC magnetron sputtering on glass substrate and then the effect of post deposition annealing temperature on the structural, optical and electrical properties of the films was investigated. The post deposition annealing process was conducted for 30 minutes in gas pressure of $1{\times}10^{-3}$ Torr and the annealing temperatures were 150 and $300^{\circ}C$. With increasing annealing temperature, GZO/Cu films showed an increment in the prefer orientation of ZnO (002) diffraction peak in the XRD pattern and the optical transmittance in a visible wave region was also increased, while the electrical sheet resistance was decreased. The GZO/Cu films annealed at $300^{\circ}C$ showed the highest optical transmittance of 70% and also showed the lowest electrical resistance of $85\;{\Omega}/{\Box}$ in this study.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.3
• /
• pp.215-218
• /
• 2011

A novel design of gas sensor using Ga-doped ZnO (GZO) thin films which are deposited on low temperature co-fired ceramic (LTCC) substrates is presented. The LTCC substrates with thickness of 400 ${\mu}m$ are fabricated by laminating 12 green tapes which consist of alumina and glass particle in an organic binder. The GZO thin films with different thickness are deposited on LTCC substrates, by RF magnetron sputtering method. The microstructure and sensing properties of GZO gas sensing films are analyzed as a function of the film thickness. The films are well crystallized in the hexagonal (wurzite) structure with increasing thickness. The maximum sensitivity of 3.49 is obtained at 100 nm film thickness and the fastest 90% response time of 27.2 sec is obtained at 50 nm film thickness for the operating temperature of $400^{\circ}C$ to the $NO_2$ gas.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.120-120
• /
• 2010

최근 투명전도성 산화물(Transparent Conductive Oxide, TCO) 박막은 액정 표시소자(LCD), 플라즈마 디스플레이 패널(PDP), 압전소자 및 태양전지의 투명소자로 사용되어지고 있다. 현재 가장 널리 사용되어지고 있는 투명전극물질인 인듐주석산화물(indium tin oxide, ITO)은 낮은 비저항과 높은 투과율을 가지고 있지만, 높은 원자재의 가격 및 수소플라즈마 처리시 In과 Sn이 환원되어 전기적, 광학적으로 불안정한 문제점들이 지적되고 있다. 이러한 문제점들을 해결하기 위해 최근 적외선 및 가시광선 영역에서 높은 투과도 및 전기 전도성과 수소플라즈마에 대한 화학적 안정성을 갖는 ZnO를 기반으로 3족 원소를 첨가한 새로운 투명 전도막에 대한 연구가 활발하다. 본 연구에서는 RF-Magnetron Sputtering법을 이용하여 $Ga_2O_3$ 혼합비에 따라 제작된 ZnO(GZO) 박막들의 전기적, 광학적, 구조적인 특성들을 분석하였다. 측정결과, $Ga_2O_3$의 첨가량이 7 wt.%인 GZO 박막이 가시광선영역에서 80%이상의 높은 투과율과 $50.5\;\Omega/\Box$의 가장 낮은 면저항을 나타내었다. 이는 Ga원소가 다른 3족 원소와 격자결합을 비교할 때, 이온의 크기가 Zn원소와 비슷하여 최적화된 혼합율을 가지는 경우 격자결합을 최소화시켜 캐리어 밀도의 증가로 인해 높은 전도성을 가지며, 고온에서도 전기적 특성 및 내구성이 향상되기 때문이다. 또한 기판온도에 따른 열처리 특성으로서 기판의 온도를 $100^{\circ}{\sim}400^{\circ}C$까지 변화를 주어 실험하였다. X-선 회절패턴 분석결과 기판온도가 증가함에 따라 ZnO (002) 방향이 감소하는 반면 ZnO(103) 방향이 증가하였으며, 기판온도가 $300^{\circ}C$ 일 때 $17.1\;\Omega/\Box$의로 가장 낮은 면저항이 나타났다. 이는 SEM 이미지를 분석한 결과, 실온에서 제작된 박막과 비교해 300 에서 증착된 GZO 박막이 결정립의 크기가 크고 밀도도 조밀해져 전하의 이동도가 향상되었기 때문이다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.9
• /
• pp.776-779
• /
• 2007

In this study we present the effect of annealing temperatures on the structural, electrical and optical characteristics of Ga-doped ZnO (GZO) films. GZO target is deposited on coming 7059 glass substrates by DC sputtering. and then GZO films are annealed at temperatures of 400, 500, $600^{\circ}C$ in air ambient for 20 min. in this case of as-grown film, it shows the resistivity of $6{\times}10^{-1}{\Omega}{\cdot}cm$ and transmittance under 85%, whereas the electrical and optical properties of film annealed at $500^{\circ}C$ are enhanced up to $1.9{\times}10^{-3}{\Omega}{\cdot}cm$ and 90%, respectively.

• Korean Journal of Materials Research
• /
• v.21 no.3
• /
• pp.144-148
• /
• 2011

We have investigated the structural and optical properties of Ga-doped ZnO (GZO) thin films deposited by RF magnetron sputtering at various deposition temperatures from 100 to $500^{\circ}C$. All the GZO thin films are grown as a hexagonal wurtzite phase with highly c-axis preferred parameter. The structural and electrical properties are strongly related to deposition temperature. The grain size increases with the increasing deposition temperature up to $400^{\circ}C$ and then decreases at $500^{\circ}C$. The dependence of grain size on the deposition temperature results from the variation of thermal activation energy. The resistivity of GZO thin film decreases with the increasing deposition temperature up to $300^{\circ}C$ and then decreases up to $500^{\circ}C$. GZO thin film shows the lowest resistivity of $4.3{\times}10^{-4}\;{\Omega}cm$ and highest electron concentration of $1.0{\times}10^{21}\;cm^{-3}$ at $300^{\circ}C$. The mobility of GZO thin films increases with the increasing deposition temperature up to $400^{\circ}C$ and then decreases at $500^{\circ}C$. GZO thin film shows the highest resistivity of 14.1 $cm^2/Vs$. The transmittance of GZO thin films in the visible range is above 87% at all the deposition temperatures. GZO is a feasible transparent electrode for the application to the transparent electrode of thin film solar cells.