• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.215-222
• /
• 2007

Coating of Hot-dip galvannealed steel consists of various Fe-Zn intermetallic compounds. Since the coating is hard and there for is very brittle, the surface of steel sheet is easy to be ruptured during second manufacturing processing. This is called as powdering. In addition, forming equipment might be polluted with debris by powdering. Therefore, various research have been carried out to prohibit powdering fur improving the quality of GA steel. This paper carried out finite element analysis combined with damage model which simulate the failure of local layer of hot-dip galvannealed steel surface during v-bending test. Since the mechanical property of intermetallic compound was unknown exactly, we used the properties calculated from measurements. The specimen was divided into substrate, coating layer and interface layer. Local failure at coating layer or interface layer was simulated when elemental strain reached a prescribed strain.

• Korean Journal of Metals and Materials
• /
• v.46 no.5
• /
• pp.289-295
• /
• 2008

The effect of the alloy elements(Si/Mn) ratio on the coating quality including wettabilty with molten zinc, galvannealing kinetics and crater has been investigated in interstitial-free high strength steel(IFHSS) containing Si and Mn. When the Si/Mn ratio was below 0.75, IF-HSS exhibited a good wettability leading to a good galvannealed coating quality after annealing at $800^{\circ}C$ for 40s in $15%H_2-N_2$ mixed gas with dew point $-60^{\circ}C$. In contrast, the wettability and galvannealed coating quality were deteriorated in the Si/ Mn ratio above 0.75. It is shown that they have relevance to oxides forms by selective oxidation on the steel surface. The oxide particles dispersed on the steel surface with a surface coverage of below 40% resulted in good wettability and galvannealed coating quality. The oxide particle is mainly consisted of $Mn_2SiO_4$ with low contact angle in molten zinc. On the other hand, the continuous oxide layer on the steel surface, such as network- and film-type,caused to poor wettability and galvannealed coating quality. The coverage of oxide layer was above 80%, and its chemical species was $SiO_2$ with high contact angle in molten zinc. Consequently, the Si/Mn alloy ratio played an importance role in galvannealed coating quality of IF-HSS.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.16 no.6
• /
• pp.141-147
• /
• 2008

Hot-dip galvannealed sheet (GA) with high strength of 590MPa grade in tensile strength, has developed for automotive applications. However, for a successful application, the microstructure and galvannealing behavior of galvannealed TRIP steel sheets must be strictly controlled. High silicon contents steel has problems with weld-ability, zinc coating and reduction of retained austenite volume fraction after galvannealing process. The main purpose of this study is to solve the problem as indicated above.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.05a
• /
• pp.31-32
• /
• 2003

In the Present study, the effect of galvannealing conditions on the phase distribution of the Zn-Fe intermetallic phases in the coating layer of the galvannealed steel sheets(GA) was investigated in an interstitial free steel and two kinds of high strength steels. The composition profiles of the coating layers were analyzed using AA and EDS analysis, and the distribution of the intermetallic phases was examined with the aids of X-ray diffraction. On the basis of the pole figure and OIM analyses, it was clarified that the preferred orientation of the $\zeta$ phase depended on the development of the $\gamma$-fibre texture in the substrate.

• Corrosion Science and Technology
• /
• v.10 no.1
• /
• pp.1-5
• /
• 2011

The major purpose of the present study is to evaluate the performance of various galvanized (GI) or galvannealed (GA) mild steels and AHSS in stamping applications. Finite Element Analysis (FEA) of selected stamping operations was conducted to estimate the critical pressure boundary conditions that exist in practice. Using this information, laboratory tribotests, e.g. Twist Compression (TCT), Deep Drawing (DDT) and Strip Drawing (SDT) Tests, were developed to evaluate the performance of selected lubricants and die materials/coatings in forming galvanized steels of interest. The sheet materials investigated included mild steels and AHSS (e.g. DP600 GI/GA, DP780 GI/GA, TRIP780 GA and DP980 GI/GA). Experimental results showed that galvanized material resulted in more galling, while galvannealed material showed more powdering and flaking. The surface roughness and chemical composition of galvanized sheet materials affected the severity of galling under the same testing conditions, i.e. lubricants and die materials/coatings. The results of this study helped to determine the critical interface pressure that initiates lubricant failure and galling in stamping selected galvanized sheet materials. Thus, to prevent or postpone the critical interface conditions, the results of this study can be used to select the optimum combination of galvanized sheet, die material, die coating and lubricant for forming structural automotive components.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.10a
• /
• pp.139-139
• /
• 2003

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.11a
• /
• pp.1-1
• /
• 1998

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2009.10a
• /
• pp.117-118
• /
• 2009

• Journal of the Korean institute of surface engineering
• /
• v.33 no.2
• /
• pp.135-144
• /
• 2000

Hot-dip galvannealed sheet (GA) with high strength of $45kg/mm^2$ in tensile strength, has developed for automotive applications. However, for a successful application, the powdering behaviour of GA must be minimized. The powdering of galvannealed coatings was reduced as the silicon content in the steel increased. Rapid heating and rapid cooling rate during the galvannealing process improved the powdering resistance due to the suppression of not only the ξ phase, but also the $ \Gamma _1$, phase. An analysis of the Fe-Zn alloy phases and its relation to the powdering behaviour are discussed with SEM micrographs.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.1012-1015
• /
• 2005

This paper is designed to estimate friction and powdering characteristic of coating layer on galvannealed sheet steel with different annealing temperature, which is 465, 505, 515 and $540^{\circ}C$. Estimations of powdering and friction were done using a $60^{\circ}$ bending test and one side friction test, respectively. In order to obviously understand the effect of coatings on friction cross-section of coatings before and after friction test was also observed by SEM. The results show that powdering of coatings is increased with increasing of annealing temperature and that friction characteristic greatly depends on powdering which leads to increase of real contact area between tools and coatings.