• 한국세라믹학회지
• /
• 제34권11호
• /
• pp.1151-1158
• /
• 1997

Fracture of uni-directional carbon fiber reinforced carbon matrix composite is strongly dependent on the orientation of basal plane in graphite matrix when it is limited within matrix. The orientation of basal planes are vertically stacked to carbon fiber which results in the weakness for applied tensile or shear force in thermosetting resin derived-carbon matrix composite. Microtextural control of the matrix was tried through chemical interaction between metal carbides and furan resin derived-carbon matrix. SiC and TiO2 addition made the orientation disordered. However, porosity increased due to decomposition of SiC. Interfacial bonding could be controlled by TiO2 addition, but carbon fiber was considerably reacted with TiC during thermal treatment higher than 2$600^{\circ}C$. Therefore, it is desirable to control the thermal treatment temperature at which decomposition of SiC was not serious and TiC/C was not formed eutectoid.

• 한국세라믹학회지
• /
• 제33권7호
• /
• pp.816-822
• /
• 1996

서로 다른 흑연화도를 갖는 furan 수지로 부터 얻어진 무기화합물(SiC, TiO2) 첨가 탄소재료의 산화반응의 흑연구조 의존성에 대하여 살펴보았다. 탄소재료의 산화는 시료의 표면적에 크게 의존하여, 흑연화가 상당히 진행된시료라 할지라도 표면적이 클 때는 살화속도도 빠른 것으로 밝혀졌으며, 단위 중량이 아닌 단위면적당의 산화속도로 바꿔 생각했을 때 흑연화가 진행될 수록 산화반응도 늦어지는 것을 알 수 있었다. 그리고 겉보기 활성화 에너지값으로 부터 생각할 때 흑연(TiO2 첨가시료)과 난층흑연(SiC 첨가시료)이 동일한 반응기구에 의해 산화가 진행되는 것으로 판단되었다. 또한 두종류 이상의 결정구조가 혼재하여 있는 시료의 경우 이들 성분들의 산화속도는 달라 반응의 초기에 흑연으로 결정화된 않은 비정질 탄소 성분이 흑연 성분보다 먼저 선택적으로 산화되는 것을 알 수 있었다.