• 대한기계학회논문집A
• /
• 제39권1호
• /
• pp.89-94
• /
• 2015

본 연구의 목적은 열처리 전 후의 보론강 레이저 용접성을 비교하는 것이다. 일반적으로 보론강이 핫스탬핑 공정에 사용되고 있으며, 핫스탬핑 공정은 강판을 오스테나이트 온도까지 가열한 후 성형과 동시에 냉각하는 방법이다. 열처리후 보론강은 1500 MPa 이상의 고강도를 가진다. 따라서 본 연구에서는 보론강 및 핫스탬핑강의 레이저 용접성을 조사한 후 비교하였다. CW 디스크 레이저를 이용하여 레이저 출력 및 용접속도를 변화시켜가며 맞대기 및 겹치기 용접을 실시하였다. 맞대기 용접 결과, 핫스탬핑강에서 완전 용입을 얻을 수 있는 임계냉각속도가 보론강보다 낮았으며, 겹치기 용접결과 완전 관통이 일어난 용접 조건에서는 접합부 폭은 용접속도와 관계없이 거의 유사하였다.

• Journal of Welding and Joining
• /
• 제32권5호
• /
• pp.7-12
• /
• 2014

In this study, API-X100 steel pipes were welded with various kinds of welding wires in the laser-arc hybrid welding process. 10kW fiber laser source was combined to MIG arc welding process. API X-100 steel of base metal was of 16.9mm thickness, and butt welding applied. After welding, full penetration weld was acquired by 1-pass welding. A root porosity and the lack of fusion was observed in some welding conditions. By the mixing the melted wire, acicular ferrite, polygonal ferrite, pro-eutectoid, aligned side plate, and bainite structures were observed at the weld metal. From the observation of hybrid weld, unmixed zone had more Ni and Cr. The unmixed zone was a 1/3 area of the weld metal. As the mechanical test of the hybrid welding, tensile test and impact test applied. From the tensile test, all of the welding except SM70S was fractured at the base metal. The result of the impact test at -30 degree C led 60J~320J of the absorbed energy. The result of the low-absorbed energy might be from the coarse equiaxed structures of the weld metal.

• Journal of Advanced Marine Engineering and Technology
• /
• 제37권7호
• /
• pp.711-717
• /
• 2013

Titanium (Ti) metal and its alloys are desirable materials for ship hulls and other structures because of their high strength, light weight and corrosion-resistance. And light weight and corrosion-resistant aluminum (Al) is the ideal metal for shipbuilding. The joining of Ti and Al dissimilar metals is one of the effective measures to reduce weight of the structures or to save rare metals. Ti and Al have great differences in materials properties, and intermetallic compounds such as Ti3Al, TiAl, TiAl3 are easily formed at the contacting surface between Ti and Al. Thus, welding or joining of Ti and Al is considered to be extremely difficult. However, it was clarified that ultra-high speed welding could suppress the formation of intermetallic compounds in the previous study. Results of tensile shear strength increases with an increase in the welding speed, and therefore extremely high welding speed (50m/min in this study) is good to dissimilar weldability for Ti and Al. In this study, therefore, full penetration dissimilar lap welding of Ti (upper) - Al (lower) and Al (upper) - Ti (lower) with single-mode fiber laser was tried at ultra-high welding speed, and the microstructure of the interface zones in the dissimilar Al and Ti weld beads was investigated.

• 한국가스학회지
• /
• 제17권1호
• /
• pp.19-25
• /
• 2013

용접에 의한 가스설비, 교량, 선박 등 강 구조물의 접합 방법은 대부분 십자형이나 T형의 필릿 용접으로 이루어지며 구조물의 형상과 용도에 따라 완전 용입 또는 불완전 용입 상태로 이루어진다. 본 연구에서는 십자형 필릿용접 구조물에 대하여 재료 두께별 용입 깊이에 따른 피로 균열 특성을 파악하였고, 그 결과로부터 무한수명 영역내에서의 안전 설계응력에 대하여 고찰하였다. 미 용입 길이가 길면 루트 부 파괴가 되어 무한 수명 영역은 작고 미 용입 길이가 짧으면 토우부 파괴가 되어 무한 수명 영역은 크게 나타났다. 3층 용접한 재료 두께 20mm의 경우가 2층 용접한 재료 두께 10mm, 15mm의 경우보다 미세한 페라이트 침상 조직을 더 많게 형성시켜 노치 인성을 증가시키므로 서 피로강도와 무한 수명을 더 향상시킨 것으로 나타났다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제38권2호
• /
• pp.133-139
• /
• 2014

Titanium (Ti) metal and its alloys are desirable materials for ship hulls and other ocean structures because of their high strength, corrosion-resistance and light weight properties. And light weight and corrosion-resistant aluminum (Al) is the ideal metal for shipbuilding. The joining of Ti and Al dissimilar metals is one of the effective methode to reduce weight of the structures. Ti and Al have great differences in materials properties, and intermetallic compounds such as $Ti_3Al$, TiAl, $TiAl_3$ are easily formed at the contacting surface between Ti and Al. Thus, dissimilar welding and joining of Ti and Al are considered to be very difficult. However, it was clarified that ultra-high speed welding could suppress the formation of intermetallic compounds in the previous study. Results of tensile shear strength increases with an increase in the welding speed, and therefore extremely high welding speed (50 m/min) is good to dissimilar weldability for Ti and Al. In this study, therefore, full penetration dissimilar lap welding of Ti (upper) - Al (lower) and Al (upper) - Ti (lower) with single-mode fiber laser was tried at ultra-high welding speed, and the microstructure of the interface zones in the dissimilar Al and Ti weld beads was investigated.

• Journal of Welding and Joining
• /
• 제31권5호
• /
• pp.64-70
• /
• 2013

The joining of Ti and SUS304 dissimilar metals is one of the effective measures to save rare metal. But Ti and SUS304 have differences in materials properties, and Ti and Fe intermetallic compounds such as TiFe and $TiFe_2$ are easily formed in weld fusion zone between Ti and SUS304. Nevertheless, in this study, full penetration lap dissimilar welding of Ti and SUS304 using single-mode fiber laser with ultra-high welding speed was tried, and it was found out that ultra-high welding speed could control the generation of intermetallic compound. To recognize the formation of intermetallic phase in the weld fusion zone and the compound zone of interface weld area were observed and analyzed using energy dispersive X-ray spectroscopy (EDX). And it was confirmed that the ultra-high welding speed could reduce amount of intermetallic compounds, but the intermetallic compounds were existed in the weld fusion zone under the all conditions.

• Journal of Welding and Joining
• /
• 제30권5호
• /
• pp.70-75
• /
• 2012

This study is related to the laser weldability of AZ31B magnesium alloy, an all-purpose wrought alloy with good strength and ductility. In general, AZ31B is classified into AZ31B-H24 and AZ31B-O depending on temper designation. Thus, in this study, the laser weldability of AZ31B-H24 and AZ31B-O was investigated and compared. CW Nd:YAG laser was used to produce bead and butt joints. And the effects of welding conditions on the weldability of these joints were examined in detail. As a result of this study, AZ31B-H24 was found to have thinner oxide film and smaller grain size compared with AZ31B-O. Due to such difference, in bead welding, AZ31B-H24 had more wide welding range for full penetration compared with AZ31B-O. Furthermore, it was also confirmed that AZ31B-H24 and AZ31B-O have different welding conditions to obtain stable keyhole in butt welding.

• Journal of Welding and Joining
• /
• 제29권1호
• /
• pp.107-114
• /
• 2011

CP steel was developed to reduce the weight and increase the strength of car body. When it was welded using state-of-the-art disk laser welding, the effected of boron on the microstructure and hardness were investigated. Welding power was fixed at 3.5kW and welding speeds were 4,8 and 12m/min. Full penetration occurred in welding speed of 12m/min and weld bead was almost unchanged with boron contents. But the welding speed increased, the upper and lower bead were narrowed. In a welding speed of more than 8m/min, underfill defects were formed on the bead bottom. The hardness of weld zone was somewhat fluctuation in fusion zone and HAZ showed the highest hardness values. The hardness of each region showed little change with the boron contents, and softening phenomenon occurred in the HAZ near the base metal regardless of the boron contents.

• Journal of Welding and Joining
• /
• 제17권1호
• /
• pp.133-144
• /
• 1999

To fine seam annealer capacity of through thickness seam annealing in terms of through thickness microstructure change with increased toughness and elongation leaving heat trace on it, high strength steel pipes of ERW with different thickness were tested in different seam annealing temperature measured on the outer surface of pipes. Annealing temperature and microstructure of the weld seam were changed through applied seam annealing condition. Toughness and tensile test with hardness and microstructure analysis were done on the annealed weld seam to fine its characteristics as a primary step and annealing characteristics according to different seam annealing condition. Through a study of annealed ERW weld seam characteristics and seam annealing technology, amount of electric power should apply in decreased manner to arranged inductors of annealer in the order of 1st, 2nd, 3rd, so on for proper seam annealing. For example of 15.4mm thick and 610mm outside diameter pipe, applied power for proper seam annealing is 600 -650kw at 1st inductor, 450 - 500kw at 2nd inductor, 200-250 kw at 3rd inductor of annealer during 10 - 12M/minute moving speed of pipe. Also, the penetration depth of heat trace along the thickness direction of weld during seam annealing can be estimated through the equation 17mm/kv$\times$voltage(kv) with the microstructure and hardness analysis of thick weld seam as well as study of seam annealing and comparison of cooling condition to CCT diagram of low carbon high strength steel. From this result, the difference between the technological applicability of full annealing condition based on phase diagram and full penetration of heat trace based on CCT diagram along the thickness of weld seam is discussed.

• Journal of Welding and Joining
• /
• 제30권2호
• /
• pp.54-58
• /
• 2012

Al-coated steel sheets with excellent heat and corrosion resistance are widely used in various applications. In welding of thin plate, some defects such as unmelted zone and metal-through occur easily in the beginning and ending of welding line. In the study, the welding defects in Al-coated steel sheets were investigated with respect to plasma arc current, height between Cu block and base metals, and using a roller to align the height of the base metal. Full penetration and voids free welds were obtained with a plasma arc current 52A and weld speed 2.3m/min. An unmelted zone increased and Ericshen rate decreased as the height between Cu block and base metal increased from 0 to 0.6mm. Using a roller moving ahead of the plasma arc, the length of unmelted zone decreased from 1.7mm to 0.5mm.