A Study on the Characteristics of Heat Treated ERW Weld Seam and the Technology of Seam Annealing

고장력 강재의 전기저항 용접부 열처리 특성 및 기술에 대한 연구

To fine seam annealer capacity of through thickness seam annealing in terms of through thickness microstructure change with increased toughness and elongation leaving heat trace on it, high strength steel pipes of ERW with different thickness were tested in different seam annealing temperature measured on the outer surface of pipes. Annealing temperature and microstructure of the weld seam were changed through applied seam annealing condition. Toughness and tensile test with hardness and microstructure analysis were done on the annealed weld seam to fine its characteristics as a primary step and annealing characteristics according to different seam annealing condition. Through a study of annealed ERW weld seam characteristics and seam annealing technology, amount of electric power should apply in decreased manner to arranged inductors of annealer in the order of 1st, 2nd, 3rd, so on for proper seam annealing. For example of 15.4mm thick and 610mm outside diameter pipe, applied power for proper seam annealing is 600 -650kw at 1st inductor, 450 - 500kw at 2nd inductor, 200-250 kw at 3rd inductor of annealer during 10 - 12M/minute moving speed of pipe. Also, the penetration depth of heat trace along the thickness direction of weld during seam annealing can be estimated through the equation 17mm/kv$\times$voltage(kv) with the microstructure and hardness analysis of thick weld seam as well as study of seam annealing and comparison of cooling condition to CCT diagram of low carbon high strength steel. From this result, the difference between the technological applicability of full annealing condition based on phase diagram and full penetration of heat trace based on CCT diagram along the thickness of weld seam is discussed.