• Transactions of Materials Processing
• /
• v.8 no.5
• /
• pp.449-453
• /
• 1999

Sheet metal forming process is a non-linearity problem which is affected by various process variables, such as geometric shape of punch and die, frictional characteristic, etc.. Therefore, the knowledge of the influence of the process variables is needed in the design of sheet metal working processes. In this paper, cylindrical cup drawing tests for blank holding force, punch speed and lubrication between sheet material and tool were carried out to investigate the influence upon sheet formability. Experimental results were discussed about the defects on the deformation behaviors during the forming process.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.241-244
• /
• 2009

This paper deals with a usefulness verification of stretch forming process using flexible die. The stretch forming method is widely used in aircraft and high-speed train industries for manufacturing of skin structure, which is made of sheet metal. A great number of solid dies are originally used and developed for specific shapes with respect to different curvature radii of the skin structures. Accordingly, flexible stretch forming process is proposed in this study. It replaces the conventional solid dies with a set of height adjustable discrete punches. A usefulness of the flexible die is verified through extensive numerical simulations of the stretch forming process for simply curved sheet plate. The elastic recovery is considered and formability evaluations are conducted through a comparison of symmetry plane configurations.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.10 no.4
• /
• pp.121-126
• /
• 2011

An accumulator placed on the refrigerant cycle pipe lines is a part to relax fluctuations of pressure within the pipe lines and stabilize refrigerants flowed into pipe. The accumulator has been mainly manufactured by the process of tube spinning using CNC(Computer Numerical Control) lathe. However, this process has the defects which are low productivity per hour and high cost. For that reason, tube end-forming using roll die is actively being developed, recently. The purpose of this study is to develope the tube end-forming process using roll die in order to manufacture the accumulator for the refrigeration pipe lines. First, the process design of tube end-forming was performed based on specification of product, and then was verified with FE analysis. Also, the effects of friction coefficient and revolution speed of roll die on forming load were investigated. The analytical results were applied in the final process design of tube end-forming. Finally, tube end-forming test was carried out to verify the validity of the FE analysis and the process design.

• Transactions of Materials Processing
• /
• v.17 no.7
• /
• pp.473-480
• /
• 2008

Sheet metal forming of Mg alloy is usually performed at elevated temperature because of the low formability at room temperature. Therefore, strain rates affected with the forming temperature and speed must be considered as important factor about formability. Effects of process parameters such as various temperatures and forming speeds were investigated in circular cup deep drawing. From the experimental results, it is known that LDR (Limit Drawing Ratio) increase as the strain rate increase. On the contrary, the FLD (Forming Limit Diagram) shows lower value as faster strain rate. Therefore, anisotropy values are investigated according to the temperature and strain rates at each forming temperature. R-values also represent higher value as faster strain rate. It is known that the formability can be different with the deformation mode on warm forming of AZ31 alloy sheet.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.10 no.5
• /
• pp.72-78
• /
• 2011

Currently, for the damper case, the material produced by cast/forge welding is mechanically processed and then the final product is mass-produced. By cutting the cast/forge welded material, the issues of excessive cutting time, multiple process production, and a large amount of chips (40% loss from the original material) arise, causing increased production cost and reduced profitability. Thus, in this study, the incremental forming technology which generates no chips was applied in production. Analysis was excuted for 1st and 2nd works by change of tool diameter and working tool. For this, 3D molding and analysis were executed, which was applied to the processing the result, successful processing could be achieved through a few trials of molding processing according to tool forming and rotation counts.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.11 no.6
• /
• pp.9-15
• /
• 2012

Vibrational film has been more employed in ear-phones or small type of speakers along with a wide use of portable multi-media equipments such as MP3 and MP4. However, the current hand work production process of diaphragms is inefficient. In this study, a die-and-mold and a single production forming machine are developed, and they result in a multi-production forming machine. The multi-production forming machine consists primarily of a film feeding unit and an unwinding unit. A vacuum suction device provides the film feeding unit, while the unwinding unit is obtained using an appropriate damper. The advantage of the developed single production forming machine is shown according to a proper voice test.

• Transactions of Materials Processing
• /
• v.23 no.2
• /
• pp.116-121
• /
• 2014

Low pressure die casting and flow forming have been successfully used to produce sound road wheels from magnesium alloy AM80. In the current study, high speed compression testing was initially conducted to simulate the flow forming of a Mg wheel. Subsequently the flow forming was simulated with "Forge$^{TM}$", an FEM software package. On the basis of flow forming simulations, the flow forming of the Mg wheel was performed under different conditions. For the flow forming experiments, the preform castings were made by low pressure die casting from AM80, a commercial magnesium alloy. In flow forming of the magnesium preform wheel, the flow forming of the Mg wheel was successfully accomplished when the feed rate was less than half that for the forming of an aluminum road wheel. The reduction in feed rate was 52%. Finally, a comparison with the flow forming simulations was made.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2001.02a
• /
• pp.25-28
• /
• 2001

Bi-2212 HTS tube was fabricated by centrifugal forming process(CFP). As a variation of melt casting process(MCP) or centrifugal casting technique, the centrifugal forming process is a flexible method for manufacturing Bi-2212 bulk tubes and has been optimized to achieve smooth surface and uniform thickness. At this process, the slurry was prepared in the mixing ratio of 10:1 between Bi-2212 powder and binder and initially charged into the rotating mold under the speed of 300~450 rpm Heat-treatment was performed at the temperature ranges of 860 ~ $890^{\circ}C$ in air for partial melting. The HTS tube fabricated by centrifugal forming process at $890^{\circ}C$ under the rotating speed of 450 rpm was highly densified and the plate-like grains with more than 20$\mu$m were well oriented along the rotating axis. The measured Tc and Jc at 10K were around 85K and 3,000A/cm2 respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.7
• /
• pp.606-610
• /
• 2001

Bi-2212 HTS tube was fabricated by centrifugal forming and partial melting processes. Bi-2212 bulk tube has been optimized to achieve smooth surface and uniform thickness. The slurry was prepared in the mixing ratio of 10:1 between Bi-2212 powder and binder and initially charged into the rotating mold under the speed of 300~450 rpm. Heat-treatment was performed at the temperature ranges of 860~89$0^{\circ}C$ in air for partial melting. the HTS tube fabricated by centrifugal forming process at 89$0^{\circ}C$ under the rotating speed of 450 rpm was highly densified and the plate-like grains with more than 20${\mu}{\textrm}{m}$ were well oriented along the rotating axis. The measured Tc and J$_{c}$ at 10K on specimen heat treated at 89$0^{\circ}C$ was around 85 K and 1,200 A/$\textrm{cm}^2$ respectively.y.

• Transactions of Materials Processing
• /
• v.21 no.6
• /
• pp.384-388
• /
• 2012

Sheet metal forming processes induce residual stress in the final product due to plastic deformation. The residual stress leads to elastic recovery of the formed part called springback, which causes shape errors in the final product. This error is a serious issue, especially for high strength steels, which are widely used in auto-body structures. Therefore, the evaluation of the amount of springback becomes critical for high strength steels. This paper investigates the springback behavior of DP780 steel sheets after the U-bending process using the geometry of the standard U-shape tool from the NUMISHEET'93 benchmark problem. The amounts of springback were measured as a function of the intrusion direction, forming speed and blank holding force.