• 한국재료학회지
• /
• 제14권9호
• /
• pp.642-648
• /
• 2004

The microstructure and crack tip opening displacement (CTOD) of deposit weld metal were investigated for a 30 mm- thick plate welded with flux cored arc welding (FCAW) and submerged arc welding (SAW) processes. The CTOD test was carried out both as welded condition and as stress-relieved specimen by local compression. The crack growth rates in FCAW were faster than those in a SAW, and the acicular ferrite content by the SAW process was increased relatively more than that by the FCAW process. The fatigue crack growth rate in a welded specimen was faster than that in locally compressed specimen. The CTOD value of locally compressed specimens was lower than that of as welded specimen. Furthermore, the CTOD value tested with the SAW process was higher than that tested with the FCAW process.

• Journal of Welding and Joining
• /
• 제26권2호
• /
• pp.69-74
• /
• 2008

590MPa grade weldable steels were gas metal arc welded with flux cored wires. Welding parameters such as current, voltage, and speed were varied independently. Effects of each parameter on the strength and chemical composition of weld metal were investigated. Increase of voltage caused decrease of weld metal tensile strength due to the low recovery of alloying elements such as carbon and manganese. On the contrary, increase of current and speed resulted in increase of weld metal strength because of higher recovery of the alloying elements.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2004년도 학술대회지
• /
• pp.365-369
• /
• 2004

Recently, Inconel 625 is used widely in offshore processing piping in order to extend the maintenance tenn and improve the quality of anti-corrosion. According to the resistance to attack in various corrosive media at temperatures from $200^{\circ}C$ to aver $1090^{\circ}C$, in combination with good low- and high-temperature mechanical strength. In general, High quality weldments for this material are readily produced by commonly used processes. in recent years, the flux cored arc welding(FCAW) process is becoming more popular due to higher deposition rate and a better weld quality as compared to the shielded metal arc welding (SMAW) process, at the same time, exhibiting equally good weld metal toughness similar to the SAW process. In this study, the weldability and weldment characteristics(mechanical properties and corrosive environment) of Inconel 625 are considered in FCAW weld associated with the several weld shielding gases($80\%Ar\;+\;20\%\;CO_2,\;50\%Ar\;+\;50\%\;CO_2,\;100\%\;CO_2$) in viewpoint of welding productivity.

• Journal of Welding and Joining
• /
• 제11권4호
• /
• pp.57-69
• /
• 1993

In the present study, the microstructure and Charpy V notch toughness of multipass $CO_2$ FCA weldment in three different heat inputs(1-3KJ/mm)were investigated. The weldments using two different domestic FCAW wires(AWS E71T-1 and E71T-5 equivalent) in C-Mn steel were chemically analysed. The following conclusions can be inferred. 1. T-1 wire Showed a stable arc transfer, less spatter and harsh, a better bead spreading and easy slag removal, whereas T-5 wire suffered from the arc stability, which tended to increase spatter and produce a more convex bead. 2.The microsturctures of the top beads of the weldments in three different heat inputs consisted of coarse-grained boundary ferrite and Widmanstatten ferrite side plate with increasing heat inputs. The modest fraction of acicular ferrite in the two wire weldments was observed in the 2KJ/mm heat input. 3.The fine-grained reheated zones of both welds consisted of a duplex microstructure of polygonal ferrite and second phases. 4. The basic flux weldment of T-5wires showed a higher Charpy impact property than that of T-1 wires because of a higher fraction of acicular ferrite in the weld microstructure.

• 공업화학
• /
• 제34권4호
• /
• pp.450-454
• /
• 2023

플럭스 코어 아크 용접(flux cored arc welding, FCAW)에서 플럭스(flux)로 사용되는 합금 분말 내의 염소이온은 용접 금속의 비드 표면에 기공을 유발하여 불량을 유발하거나, 합금 분말에 잔류한 염소가 금속의 부식을 유발할 수 있다. 합금 분말의 염소이온 정량은 주로 연소-이온크로마토그래피법이 사용되나, 장비가 고가이며 고도의 전문성이 요구되는 한계가 있다. 따라서, 본 연구에서는 합금 분말의 염소이온 정량으로 주로 쓰이는 방법인 연소-이온크로마토그래피 법과 X-선 형광분석법, 그리고 전위차 적정법을 비교하여 현장에서 적용하기 쉽고 정확한 정량법을 찾고자 한다. 염소이온 정량의 대상으로는 플럭스로 가장 흔히 사용되는 마그네슘-알루미늄 합금 분말을 대상으로 한다. 본 연구의 결과를 통해, 전위차 적정법을 현장에서 합금 분말의 염소이온 정량에 적용할 수 있다.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2004년도 학술대회지
• /
• pp.234-238
• /
• 2004

Inconel 625 is useful in variety of industrial applications because of the resistance to attack in various corrosive media at temperatures from $200^{\circ}C$ to aver $1090^{\circ}C$, in combination with good law- and high temperature mechanical strength. Rencently, this material is also used widely in offshore processing piping in order to extend the maintenance term and improve the quality of anti-corrosion. In general, high quality weldments for this material are readily produced by commonly used processes. Not all processes are applicable to this material group, Ni-alloys. Metallurgical characterictics or the unavailability of matching, position or suitable welding processes. Nowadays, the flux cored wire is developed and applied for the better productivity in several welding position including the vertical position. in this study, the weldability and weldment characteristics (mechanical properties) of inconel 625 are considered in FCAW(Flux Core Arc Welding) associated with the several shielding gases($80\%Ar\;+\;20\%CO_2,\;50\%Ar+50CO_2,\;100CO_2$) in viewpoint of welding productivity.

• 한국해양공학회지
• /
• 제18권6호
• /
• pp.96-100
• /
• 2004

Inconel 625 is useful in a variety of industrial applications because of the resistance to attack in various corrosive media at temperatures from $200^{\circ}C$ to over $1090^{\circ}C$, in combination with good low and high temperature mechanical strength. Rencently this material has also been widely used in offshore processing piping in order to extend the maintenance term and improve the quality of anti-corrosion. In general, high quality weldings for this material are readily produced by commonly used processes. How, not all processes are applicable to this material group of Ni-alloys. Metallurgical or the unavailability of matching, position or suitable welding processes produce a lower quality. Nowadays, the flux cored wire is developed and applied for increased productivity in several welding positions, including the vertical position. In this study, the weldability and weldment characteristics(mechanical properties) of inconel 625 are considered in FCAW(Flux Core Arc Welding) associated with the several shielding gases$(80\%Ar+20\%CO2,\;50\%Ar+50CO2,\;100CO2)$ in view of welding productivity.

• 한국안전학회지
• /
• 제34권6호
• /
• pp.7-12
• /
• 2019

Flux Cored Arc Welding (FCAW), which has been widely used in many industries, was developed in the 1950s to supplement shortcomings of the Shielded Metal Arc Welding (SMAW). FCAW has an advantage in that it can weld regardless of postures and give good quality results in the filed with many different working conditions. In this study, SM490A (rolled steel for welding structural purpose) with different thicknesses (L:25T+R:30T) were welded using FCAW. Then the mechanical properties (tension test, bending test, hardness test, impact test and macro test) were analyzed and the following conclusions were drawn. In the tensile test, it exceeds the KS standard tensile strength range (400~510) in all welding positions, which means there is a problem in the tensile force transmission performance. In the bending test, it was found that most of the specimens did not exhibit surface rupture or other defects during bending test and they exhibit sufficient toughness even after plastic deformation. In the hardness test, all the results were lower than the standard value of 350 Hv of KS B 0893, which means they have good hardness. In the impact test, all results were larger than the KS reference value of 27J. In the macro test, they showed uniform structure state by the shape of the weld, and there was risk of lamination because no internal defects, bubbles, or impurities were found on the surface of the weld.

• Journal of Welding and Joining
• /
• 제33권1호
• /
• pp.72-79
• /
• 2015

Evaluation of fracture toughness of welded structures has a significant influence on the structural design. However the residual stresses is redistributed while the welded structures is cut for preparing specimens. This study investigated an effect of the welding residual stress redistribution on the impact absorption energy of Charpy specimen. SA516Gr70 steel plate by at the flux cored arc welding (FCAW) and gas tungsten arc welding(GTAW) was cutting. Specimens for Charpy impact testing were taken from the welded plate. Two material removal mechanisms (wire cutting and water jet) were used to make the specimens. Welding residual stress and redistribution residual stress were measured using the XRD (X-Ray Diffraction) method. The amount of redistribution of residual stress depends on the different material removal mechanism. Redistribution of residual stress of reduced the impact absorption energy by 15%.

• Journal of Welding and Joining
• /
• 제25권2호
• /
• pp.49-54
• /
• 2007

Since the wall thickness can be up to 6" or greater, welds must be made in many layers, each layer containing several passes. However, the welding time for the conventional welding processes such as SAW(Submerged Arc Welding) and FCAW(Flux Cored Arc Welding) can be required many hours. The aim of this paper is to develop a high speed welding system with multi-torch and laser vision sensor for increasing the production speed on the line and to remove the need for the operator so that the system can run automatically for the complete multi-torch multi-layer weld. It was shown that the developed laser vision sensor and analysis of arc blow for multi-torch were effective for multi-pass seam tracking and stable arc. A new automated multi-torch welding systems for thick wall applications has been proved in several production lines.