• Progress in Superconductivity
• /
• v.1 no.1
• /
• pp.56-60
• /
• 1999

Ultra fine MgO particles added BSCCO tapes were fabricated by tape casting using Doctor Blade Method and enclosed by silver foil for different starting compositions (that is, 2223 major, 2212 major). In order to obtain optimum microstructure, thermomechanical treatment was done. Microstructure and phase were analyzed by XRD, SEM and DTA. The critical current density was measured under magnetic field at 77K. The tapes fabricated from the precursor powder with BSCCO-2223 phase (>90%) result in a microstructure with a larger grain size and higher transport critical current density value under magnetic field at given thermomechanical treatment conditions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.63-66
• /
• 1996

The method for calculation of $Y_2$BaCuO$_{5}$ contents was set up. It was estimated that the optimum value of 211 contents in the textured YBCO superconductor as flux pinning center was about 20wt.%. Ag contents have no influence on the critical temperature, but have large influence on the critical current density of the textured YBCO. When Ag contents over 15wt.%, which was the solubility of condensed YBCO, the critical current densities tend to a stable value.e.

• 한국초전도학회:학술대회논문집
• /
• v.15
• /
• pp.89-89
• /
• 2005

• Progress in Superconductivity and Cryogenics
• /
• v.24 no.4
• /
• pp.55-58
• /
• 2022

Carbon-based doping to MgB₂ superconductor is the simplest approach to enhance the critical current densities under magnetic fields. Carbon quantum dots is synthesized in this work as a carbon provider to MgB₂ superconductors. Polyvinyl Pyrrolidone is pyrolyzed and dispersed in dimethylfomamide solvent as a dopant to the mixture of Mg and B powders. Doped MgB₂ bulk samples clearly show the decrease of a-axis lattice constant, grain refinements, and broadening of FWHM of diffraction peaks compared to un-doped MgB₂ possibly due to the carbon substitution and/or boron vacancy at the boron site in MgB₂ lattice. Also, high-field J_c for the doped MgB₂ is enhanced significantly with the crossover about 3 T at 5 & 20 K when increasing the doping of carbon quantum dots.

• Progress in Superconductivity
• /
• v.3 no.1
• /
• pp.23-27
• /
• 2001

We have investigated the mixed-state magnetoresistance of high quality c-axis-oriented MgB2 thin film for magnetic field from 0.5 T to 5.0 T, applied normal to ab-plane. The temperature dependence of magnetoresistance was well described by vortex glass and fluctuation theories for different temperature regimes. We observed glassy exponent of v(z-1)~3 and upper critical field of $H_{c2}$(0)~35 T, which is consistent with previous data obtained from direct $H_{c2}$(0) measurements. Interestingly, the thermally activated flux flow region was observed to be very narrow, suggesting that the pinning strength of this compound is very strong. This finding is closely related to the recent reports that the bulk pinning is dominant in $MgB_2$and the critical current density of $MgB_2$ thin film is very high, comparable to that of cuprate superconductor. The present results further suggest that $MgB_2$is beneficial to technical applications.ons.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.61 no.2
• /
• pp.339-341
• /
• 2012

The high Tc superconductor of YBCO system with the nominal composition of precursor was prepared from mixed powders of $Y_2O_3$, $BaCO_3$, CuO and $TiO_2$ by the thermal pyrolysis method. The effect of $TiO_2$ doping to Y based ceramics superconductors fabricated by the thermal pyrolysis reaction, to investigate the effect of the dopant on the superconductivity. The voltage appearing across the field-cooled HTS sample increased with external magnetic field. The improvement of critical current property as well as the mechanical property is important for the application. The improvement of the critical current can be achieved by forming the nano size defect working as a flux pining center inside the superconductor. We simply added $TiO_2$ to starting materials to dope $TiO_2$ and observed an increase in the trapped field and the critical current density up to at least 5 wt % $TiO_2$. The $TiO_2$ was converted to fine $BaTiO_3$ particles which were trapped in YBCO matrix during the sintering process. We observed a peak effect of Jc that can be attributed to $TiO_2$ doping and results suggest that introducing a proper amount of pinning centers can significantly enhance current density.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.343-345
• /
• 2002

The influence of starting precursor powders on the phase formation and transport properties of Bi-2223/Ag tapes has been studied. The experimental results show that the average particle size of precursors as fine as 1.64 ${\mu}{\textrm}{m}$ and 1.51 ${\mu}{\textrm}{m}$ can still increase the transport properties. The J$_{c}$-B behavior is also enhanced in tapes fabricated with powders in finer particle sizes. However, at higher magnetic fields, J$_{c}$ of tape started from the powder with the finest particles drops rapidly at the direction of H//c, which is possibly attributed to the small grain sizes and weak flux pinning ability that due to the short induction period at the initial stage of phase formation as the result of fine particles in precursor powder.der.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.362-362
• /
• 2009

$MgB_2$ bulk samples were sintered at different ambient. In this work, high purity Ar gas was added with oxygen and hydrogen gas, which can be regarded as impurity in a sense, as a possible dopant in the $MgB_2$. It was found that oxygen in the sintering ambient leads to a decrease in the critical current density $J_c$ at self field and lower fields. However, we can obtained higher $J_c$ at higher fields. It was also noted that $MgB_2$ samples sintered with 5% hydrogen in Ar revealed the increased $J_c$ at all fields compared to those processed in pure Ar ambient. From the XRD and FESEM analysis, the impurity gas in Ar can refine the $MgB_2$ grain size and result in increased grain. boundary, which can act as a strong flux pinning sites in $MgB_2$ samples. Also discussed are the effects of sintering ambient on irreversibility field, $H_{irr}$ and the upper critical field, $H_{C2}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.363-364
• /
• 2009

For the application of superconductor technology, we need critical properties of superconductors such as a critical current ($I_c$). $I_c$ is varied as processing method by action of flux pinning center. Our research activities are reported on the establishment of standard measurement method for critical current in coated conductor. And then, we researched pre-studies for standardization of critical current evaluation method using IEC/TC 90 standard.

• Transactions of Materials Processing
• /
• v.29 no.1
• /
• pp.37-43
• /
• 2020

Increasing the critical current density of superconducting wire is one of the difficult challenges in the field of superconductivity. It is well known that the higher volume fraction of uniformly dispersed α-Ti is able to enhance the critical current density of superconducting material NbTi because α-Ti serves as a flux pinning center. The volume fraction of α-Ti highly depends on the grain size of NbTi because α-Ti precipitates at the grain boundaries or triple points. For this purpose, we investigated the effect of initial microstructures of NbTi obtained from hot rolling in various temperature conditions on the critical current density. In addition, subsequent heat treatment was assigned to precipitate α-Ti and groove rolling/cold drawing was adopted to produce a wire with a diameter of about 1.0 mm. It was observed that the band structure was formed after hot rolling at 500~600℃. It was also found that the volume fraction of α-Ti after hot rolling at 500~600℃ was higher and it led to the highest critical current density.