• Journal of Welding and Joining
• /
• 제34권6호
• /
• pp.1-10
• /
• 2016

Flux Cored Wire is the most widely used welding material for Flux Cored Arc Welding these days. This paper introduces the technical aspects of manufacturing FCW and the development trend of FCW for each type of steel and metal. The studies are ongoing to lower the production cost of seamless-type FCW since it has not been generally used in welding shops so far because of it high cost even though the seamless-type FCW has various advantages than folded-type FCW in terms of manufacturing technology. Meanwhile, a technical research has been carried out to develop a rutile type of FCW products which satisfies high toughness after post heat treatment. In addition, for high-speed fillet welding, there has been a development of welding materials which can be welded in Single Auto-Carriage 100 cpm or more and up to Twin Tandem 200 cpm without occurring any welding defect in order to improve the welding productivity. As Zn coated steel is being used recently to improve the corrosion resistance of the automotive parts, a research and development for Metal Cored Wire has been conducted to reduce the Si island produced in welding operation than those produced when using the former solid wires. A development of welding material that guarantees CTOD performance beyond $-40^{\circ}C$ CTOD to $-60^{\circ}C$ is underway by different steel grades, and FCW for super austenitic stainless steel is being developed as the corrosion resistant steel has been upgraded.

• Journal of Welding and Joining
• /
• 제17권1호
• /
• pp.116-123
• /
• 1999

The $CO_2$ welding with 100% $CO_2$ shielding gas is commonly used because of its cost and efficiency. Arc phenomena of the $CO_2$ welding is influenced by various factors such as chemical compositions of welding wire, shielding gas, welding condition and welding power source etc. In this study, arc phenomena is investigated by using two type of FCW(titania type, semi-metal type). Then, the welding quality and optimum welding condition can be selected. From this study, the following results were obtained; 1) In low current range(140A), FCW up to welding voltage(22V) resulted in a typical short circuit transfer. 2) In high current range(320A), the arc stability in titania FCW of a typical globular transfer is better than that of semi-metal FCW.

• Journal of Welding and Joining
• /
• 제32권2호
• /
• pp.18-21
• /
• 2014

Cold cracking of weldment is one of the most serious welding problems. A sufficient quantity of diffusible hydrogen, a residual stress, and a sensitive microstructure are the causes of cold cracking. Removal of any one of these factors can be used to prevent cold cracking. Application of flux cored arc welding process is increasing due to high productivity and easiness of welding. In addition, to prevent cold cracking in the HAZ or weldment, preheat temperature and interpass temperature have to be controlled. In this study, the effect of preheat temperature on the levels of diffusible hydrogen in the weld metal deposited using flux cored wire was examined. The levels of preheat temperature of base metal specimen were ambient temperature, 50, 100 and $150^{\circ}C$ respectively. The result showed that the increase of preheat temperature was a linear relationship with reduction of diffusible hydrogen content in weldment.

• Journal of Welding and Joining
• /
• 제16권5호
• /
• pp.93-99
• /
• 1998

Effects of gas formers of MgCO$_3$, CaCO$_3$ and Li$_2$CO$_3$ on the spattering phenomena were investigated for non-shielded flux cored arc welding. Spattering phenomena were pictured using high speed camera as a speed of 3000 frames per sec. As experimental results, spattering modes were classified into 4 types. The modes were spattering by arc force, gas explosion, short circuit and pore escape. The amount of spatters by arc force was 30%, gas blowing force was 40%, short circuit 10%, pore escape was 10% and others were 10%. When Li$_2$CO$_3$ was added, the amount of spatters was largest, and it decreased in the order of CaCO$_3$ and MgCO$_3$.

• 대한조선학회논문집
• /
• 제35권4호
• /
• pp.65-75
• /
• 1998

GMA 용접 중 100% $CO_2$ 가스를 사용하는 $CO_2$ 용접은 경제적이고 고능률적이라는 점 때문에 많이 사용되고 있다. $CO_2$ 용접의 아크현상과 스패터 발생량은 용접용 와이어의 화학성분, 실드가스, 용접조건 등에 영향을 받는다. 특히 용접조건은 용적이행 모드를 결정하기 때문에 스패터 발생량에 커다란 영향을 미친다. 본 연구는 $CO_2$ 용접 재료 중 두 type의 FCW(titania계, semi-metal계)를 이용하여 용접조건을 변화시켜 아크현상과 스패터 발생량을 파악하여 용접부의 품질 평가와 용접조건 설정에 기여코져 한다. 본 연구를 통해, 다음과 같은 결론을 얻을 수 있다. 1) 저전류 영역(140A)의 FCW 모두 22V까지는 전형적이 단락이행이 나타났고, 스패터 발생량의 증가와 저전류 스패터 입도를 대립화하였다. 2) 대전류 영역(320A)의 전형적인 globular이행에서 titania계 FCW가 semi-metal계 FCW보다 아크 안정성이 양호하였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 1998년도 추계학술발표회 초록집
• /
• pp.19-20
• /
• 1998

오버레이용접에 의한 표면개질기술(Weld Surfacing or Hardfacing Technology)은 내식성, 내 마모성, 또는 내열성을 갖는 합금의 용접재료를 모재 표면에 균일하게 용착(오버레이:Ovedayer)시킴으로써 목적하는 재료의 표면성질을 향상시키는 표면처리의 한 방법이으로써 1922년 Stoody가 Steel Tube에 Cr합금 분말을 충진한 용접봉을 제조하여 석유시추용 회전드릴의 선단 표면을 오버 레이 용접시켜 내마모성을 획기적으로 개선시킴으로써 이루어 졌다. 초기 오버레이 용접기술은 발전설비I 제철설비I 시벤트설비, 그리고 제지설비 등 주로 설비 부품들의 표면부 내마모성을 개선시키는 방향으로 주로 연구 개발이 이루어졌으나, 기술개발의 진전으로 탈황설비 둥의 표면부 내식성 향상, 연속주조롤 표면부의 내산화성, 내열피로성, 내마모 성 향상 둥을 위해 점차 산업전반에 널리 이용되고 있으며, 설비의 고도화 및 장수명화가 요구되 면서 본 기술의 중요성 또한 점차 부각되고 있다. 그림 1은 연강의 모재 위에 셀프쉴드플럭스코어드와이어(Self-Shield Flux Cored Wire:SS-FCW, 이하 55-FCW라 기술함)를 사용하여 오버레이 용접올 하는 장면을 도식적으로 나 타낸 것이다. 모재와 전극재인 용접봉(S5-FCW) 사이에서 아크가 발생되고, 아크열에 의해서 용접 봉 및 모재 일부가 용융되면서 모재 표면에 새로운 오버레이 표면층이 형성된다. 통상 오버레이 층의 1층 두께는 2-6mm 내외이며, 단층 혹은 다충 오버레이를 자유롭게 실시한다. 오버레이층의 물성은 아크열에 의한 모재로의 용입정도에 따라 1층부에서는 모재의 영향을 크게 받지만 오버레 이충 수가 증가된 3층부에서 부터는 전적으로 용접봉의 성분에 좌우된다. 사진 1은 연강(55-41)의 모재위에 크롬탄화물이 다량 함유된 고크롬 탄화물형 내마모재가 오버 레이된 내마모 복합강판 (wear plate)의 단면 미세조직 사진으로써 모재부와 오버레이충을 함께 보여주고 있다. 모재와 오버레이 충간의 경계면은 모재 일부가 용융된 후 웅고하면서 형성됨으로 인해서 도금이나 용사층과는 달리 매우 견고하게 결합되어 있다. 따라서 계면부의 탈락이라는 문 제점은 거의 없어 심한 응력을 받는 기계구조물 및 부품에도 본 기술은 널리 적용되고 있다. 그리고 사진 1에서 알 수 있는 바와 같이 모재와는 전혀 상이한 재료를 자유로이 선택하여 표면 유효층 일부만 오버레이시키며I 주조 및 단조가 불가능한 재료까지도 표면부에 오버레이 시킴으로 서 부품 및 설비의 제조에 있어 재료비의 절감과 제품의 수명이 획기적으로 개선될 수 있다. 그리고 최근에는 도금 빛 용사 둥과 같은 표면처리를 할 경우임의 소재 표면에 도금 및 용 사에 용이한 재료를 오버레이용접시킨 후 표면처리를 함으로써 보다 고품질의 표면층을 얻기위한 시도가 이루어지고 있다. 따라서 국내, 외의 오버레이 용접기술의 적용현황 및 대표적인 적용사례, 오버레이 용접기술 및 용접재료의 개발현황 둥을 중심으로 살펴봄으로서 아직 국내에서는 널리 알려지지 않은 본 기 술의 활용을 넓이고자 한다.