• 한국응용과학기술학회지
• /
• 제20권1호
• /
• pp.8-19
• /
• 2003

Environmental friendly acrylics/urea high-solid paints (BEHCU) were prepared through the curing reaction of acrylics resin(BEHC) containing 70wt% of solids content and butylated urea curing agent. BEHC was synthesized by addition copolymerization of caprolactone acrylate(CLA), 2-hydroxypropyl methacrylate(2-HPMA), ethyl methacrylate, and n-butyl acrylate. The addition polymerization of these monomers, especially including flexible CLA monomer and 2-HPMA monomer with OH funtional group, under appropriate reaction conditions resulted in polymers with controlled glass transition temperature($T_g$) and crosslinking density. The molecular weight($M_w$) of these polymers(BEHCs) was 2940${\sim}$3240 and polydispersity ($M_w/M_n$) was in the range of 1.61${\sim}$1.72. The viscosity and the molecular weight of these acrylic resins increased with increasing $T_g$. The coated films were prepared using curing reaction between BEHC resin and butylated urea curing agent at 100$^{\circ}C$ for 30 minutes. Our experimental resulted showed that enhancement of the coating properties such as adhesion, flexibility, impact resistance, water resistance, and abrasion resistance could be expected through introducing CLA component in acrylic resin for the high-solid content acrylics/urea coatings.

• 한국자동차공학회논문집
• /
• 제18권2호
• /
• pp.83-90
• /
• 2010

The windshield wiper consists of 4 parts: a blade, an arm, a linkage and a motor. The wiper blade makes contact with the windshield and is designed to be operated normally at an angle of 30~50 degrees to the front glass. If the contact pressure between the wiper blade and windshield surface is too high, noise and wear of the rubber will result. On the other hand, if the contact pressure is too low, the performance will do badly, since foreign substances such as dust and stains will not be removed well. The pressure and friction of the wiper blade has a great influence on its effectiveness in cleaning the front window. This is due to the contact of the rubber with the window. This paper presents the dynamic analysis method to estimate the performance of the flat type blade of the wiper system. The blade has a nonlinear characteristic since the rubber is an incompressible hyper-elastic and visco-elastic material. Thus, Structural dynamic analysis using a complex contact model for the blade is performed to find the characteristics of the blade. The flexible multi-body dynamic model is verified by the comparison between test and analysis result. Also, the optimization using the central composite design table is performed.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2010년도 제39회 하계학술대회 초록집
• /
• pp.168-168
• /
• 2010

Transparent conduction oxides (TCOs) films is extensively reported for optoelectronic devices application such as touch panels, solar cells, liquid crystal displays (LCDs), and organic light emitting diodes(OLEDs). Among the many TCO film, indium tin oxide(ITO) is in great demand due to the growth of flat panel display industry. However, indium is not only high cost but also its deposits dwindling. Therefore, many studies are being done on the transparent conductive oxides(TCOs). We fabricated a target of IZTO(In2O3:ZnO:SnO2=70:15:15 wt.%) reduced indium. Then, IZTO thin films were deposited on glass substrates by pulsed DC magnetron sputtering with various oxygen flow ratio. The substrate temperature was fixed at the room temperature. We investigated the electrical, optical, structural properties of IZTO thin films. The electrical properties of IZTO thin films were dependent on the oxygen partial pressure. As a result, the most excellent properties of IZTO thin films were obtained at the 3% of oxygen flow rate with the low resistivity of $7.236{\times}10^{-4}{\Omega}cm$. And also the optical properties of IZTO thin films were shown the good transmittance over 80%. These IZTO thin films were used to fabricated organic light emitting diodes(OLEDs) as anode and the device performances studied. The OLED with an IZTO anode deposited at optimized deposition condition showed good brightness properties. Therefore, IZTO has utility value of TCO electrode although it reduced indium and we expect it is possible for the IZTO to apply to flexible display due to the low processing temperature.

• Biomolecules & Therapeutics
• /
• 제16권4호
• /
• pp.425-430
• /
• 2008

The objectives of this study were to prepare PLGA film onto the surface of the capsular tension ring (CTR) for controlled drug release and investigate the influence of plasticizers, the test drug and measurement conditions on flexibility of the film. Film solutions were prepared by dissolving PLGA, plasticizer (triethyl citrate, TEC or polyethylene glycol, PEG), test drug (dexamethasone) in ethyl acetate then films were prepared by spray coating and evaporation method. Then, the flexibility of PLGA film was determined by elongation test. The addition of plasticizer, PEG or TEC to PLGA copolymer caused a depression of glass transition temperature ($T_g$) and the elasticity of PLGA films increased. The addition of dexamethasone to the PLGA/TEC matrix decreased the flexibility of film. Dimensional factors of the PLGA films such as width and thickness were significantly influenced on flexibility of films and film length and elongation speed had no considerable influence on elongation of films. In this study, sufficiently flexible and stable PLGA films capable of being coated onto CTR could be prepared. This PLGA films can be used as a platform for local drug delivery.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제41회 하계 정기 학술대회 초록집
• /
• pp.286-286
• /
• 2011

최근 폴리머를 기판으로 하는 Flexible TFT (thin film transistor)나 3D-ULSI (three dimensional ultra large-scale integrated circuit)에서 높은 에너지 소비효율과, 빠른 반응 속도를 실현 시키기 위해 낮은 비저항(resistivity)을 가지며, 높은 홀 속도(carrier hall mobility)를 가지는 다결정 반도체 박막(poly-crystalline thin film)을 만들고자 하고 있다. 이를 실현 시키기 위해서는 높은 온도에서 장시간의 열처리가 필요하며, 이는 폴리머 기판의 문제점을 야기시킬 뿐 아니라 공정시간이 길다는 단점이 있었다. 이에 반도체 박막의 재결정화 온도를 낮춰주는 metal (Al, Ni, Co, Cu, Ag, Pd etc.,)을 이용하여 결정화 시키는 방법이 많이 연구 되어지고 있지만, 이 또한 재결정화가 이루어진 반도체 박막 안에 잔여 금속(residual metal)이 존재하게 되어 비저항을 높이고, 홀 속도를 감소시키는 단점이 있다. 이에 본 실험은 HiPIMS (High power impulse magnetron sputtering)와 PIII and D (plasma immersion ion implantation and deposition) 공정을 복합시킨 프로세스로 적은양의 금속이온주입을 통하여 재결정화 온도를 낮췄을 뿐 아니라, 잔여 하는 금속의 양도 매우 적은 다결정 반도체 박막을 만들 수 있었다. 분석 장비로는 박막의 결정화도를 측정하기 위해 GAXRD (glancing angle X-ray diffractometer)를 사용하였고, 잔여 하는 금속의 양과 화학적 결합 상태를 알아보기 위해 XPS를 통해 분석을 하였다. 마지막으로 홀 속도와 비저항을 측정하기 위해 Hall measurement와 Four-point prove를 사용하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.335-335
• /
• 2011

Instability of a thin film attached to a compliant substrate often leads to emergence of exquisite wrinkle patterns with length scales that depend on the system geometry and applied stresses. However, the patterns that are created using the current techniques in polymer surface engineering, generally have low aspect ratio of undulation amplitude to wavelength, thus, limiting their application. Here, we present a novel and effective method that enables us to create wrinkles with a desired wavelength and high aspect ratio of amplitude over wavelength as large as to 2.5:1. First, we create buckle patterns with high aspect ratio of amplitude to wavelength by deposition of an amorphous carbon film on a surface of a soft polymer poly(dimethylsiloxane) (PDMS). Amorphous carbon films are used as a protective layer in structural systems and biomedical components, due to their low friction coefficient, strong wear resistance against, and high elastic modulus and hardness. The deposited carbon layer is generally under high residual compressive stresses (~1 GPa), making it susceptible to buckle delamination on a hard substrate (e.g. silicon or glass) and to wrinkle on a flexible or soft substrate. Then, we employ glancing angle deposition (GLAD) for deposition of a high aspect ratio patterns with amorphous carbon coating on a PDMS surface. Using this method, pattern amplitudes of several nm to submicron size can be achieved by varying the carbon deposition time, allowing us to harness patterned polymers substrates for variety of application. Specifically, we demonstrate a potential application of the high aspect wrinkles for changing the surface structures with low surface energy materials of amorphous carbon coatings, increasing the water wettability.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.87-87
• /
• 2011

Oxide semiconductors are attractive materials for thin-film electronics and optoelectronics due to compatibility with synthesis on large-area, glass and flexible substrate. However, development of thin-film electronics has been hampered by the limited number of semiconducting oxides that are p-type. We report on the effect of the oxygen partial pressure ratio in the gas mixture on the electrical and optical properties of spinel Mg:$ZnCo_2O_4$ thin films deposited at room temperature using RF sputtering, that exhibit p-type conduction. The thin-films are deposited at room temperature in a background of oxygen using a polycrystalline Mg:$ZnCo_2O_4$ ablation target. The p-type conduction is confirmed by positive Seebeck coefficient and positive Hall coefficient. The electrical resistivity and carrier concentration in on dependent Mg:$ZnCo_2O_4$ thin films were found to be dependent on the oxygen partial pressure ratio. As a result, it is revealed that the Mg:$ZnCo_2O_4$ thin-films were greatly influenced on the electrical and optical properties by the oxygen partial pressure condition. The visible region of the spectrum of 36~85%, and hole mobility of 1.1~3.7 $cm^2$/Vs, were obtained.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.144-144
• /
• 2012

최근 폴리머를 기판으로 하는 고속 Flexible TFT (Thin film transistor)나 고효율의 박막 태양전지(Thin film solar cell)를 실현시키기 위해 낮은 비저항(resistivity)을 가지며, 높은 홀 속도(carrier hall mobility)와 긴 이동거리를 가지는 다결정 반도체 박막(poly-crystalline semiconductor thin film)을 만들고자 하고 있다. 지금까지 다결정 박막 반도체를 만들기 위해서는 비교적 높은 온도에서 장시간의 열처리가 필요했으며, 이는 폴리머 기판의 문제점을 야기시킬 뿐 아니라 공정시간이 길다는 단점이 있었다. 이에 반도체 박막의 재결정화 온도를 낮추어 주는 metal (Al, Ni, Co, Cu, Ag, Pd, etc.)을 이용하여 결정화시키는 방법(MIC)이 많이 연구되어지고 있지만, 이 또한 재결정화가 이루어진 반도체 박막 안에 잔류 금속(residual metal)이 존재하게 되어 비저항을 높이고, 홀 속도와 이동거리를 감소시키는 단점이 있다. 이에 본 실험은, 종래의 MIC 결정화 방법에서 이용되어진 금속 증착막을 이용하는 대신, HIPIMS (High power impulse magnetron sputtering)와 PIII&D (Plasma immersion ion implantation and deposition) 공정을 복합시킨 방법으로 적은 양의 알루미늄을 이온주입함으로써 재결정화 온도를 낮추었을 뿐 아니라, 잔류하는 금속의 양도 매우 적은 다결정 반도체 박막을 만들 수 있었다. 분석 장비로는 박막의 결정화도를 측정하기 위해 GIXRD (Glazing incident x-ray diffraction analysis)와 Raman 분광분석법을 사용하였고, 잔류하는 금속의 양과 화학적 결합 상태를 알아보기 위해 XPS (X-ray photoelectron spectroscopy)를 통한 분석을 하였다. 또한, 표면 상태와 막의 성장 상태를 확인하기 위하여 HRTEM(High resolution transmission electron microscopy)를 통하여 관찰하였다.

• 한국표면공학회지
• /
• 제42권3호
• /
• pp.128-132
• /
• 2009

Transparent conducting thin films of indium tin oxide(ITO) co-sputtered with aluminum-doped zinc oxide(AZO) were deposited on glass substrate by dual magnetron sputtering. It was found that the electrical properties and structural characteristics of the films are significantly changed according to the sputtering power of the AZO target. The IAZTO film prepared with D.C power of ITO at 100 W and R.F power of AZO at 50 W shows an electrical resistivity of $4.6{\times}10^{-4}{\Omega}{\cdot}cm$ and a sheet resistance of $30{\Omega}/{\square}$ (for 150 nm thick). Besides of the improvement of the electrical properties, compared to the ITO films deposited at the same process conditions, the IAZTO films have very smooth surface, which is due to the amorphous nature of the films. However, the electrical conductivity of the IAZTO films was found to be deteriorated along with the crystallization in case of the high temperature deposition (above $310^{\circ}C$). In this work, high quality amorphous transparent conductive oxide layers could be obtained by mixing AZO with ITO, indicating possible use of IAZTO films as the transparent electrodes in OLED and flexible display devices.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제41회 하계 정기 학술대회 초록집
• /
• pp.341-341
• /
• 2011

최근 AMOLED 구동이 가능한 소자에 대한 연구가 활발히 진행중이다. AMOLED구동 가능소자는 LTPS TFT, a-Si TFT, OTFT, Oxide TFT가 있으며 그 중에서 현재 대부분 LTPS TFT를 사용하고 있다. LTPS TFT는 높은 전자 이동도와 안정성을 가지고 있기 때문에 현재 각광 받는 AMOLED에 잘 맞는다. 하지만 LTPS TFT는 고비용, 250$^{\circ}C$ 이상의 공정온도, Substrate가 Glass, Metal로 제한 된다는 문제점이 있으며, 균일성이 낮고 현재 대면적 기술이 부족한 상태이다. 해결방안으로 AMOLED를 타겟으로 하는 Oxide TFT 기술이 떠오르고 있다. Oxide TFT는 이동도가 높고 저온공정이 가능하며 Substrate로 Plastic 기판을 사용할 수가 있어 차후에 Flexible 소자로서의 적용이 가능하다. 또한 기존의 진공장비 사용대신 용액공정이 가능하여 장비사용시간 및 절차를 단축시킬 수 있어 비용적인 유리함을 가지고 있다. Oxide TFT는 단결정 산화물과 다결정 복합 산화물 두 가지 범주를 가지고 있다. Oxide TFT의 재료물질은 ZnO, ZTO, IZO, SnO2, Ga2O3, IGO, In2O3, ITO, InGaO3(ZnO)5, a-IGZO이 있다. 본 연구에서는 산화물질 중 하나인 ZTO를 이용하여 TFT 소자를 제작하였다. 산화물 특성상 열처리 온도에 따라 형성되는 결정의 정도가 다르기 때문에 온도 및 시간 변수에 따른 ZTO의 특성변화에 초점을 맞추어 연구함으로서 최적화된 조건을 찾고자 실험을 진행하였다. 실험을 위한 기판으로 n-type wafer을 사용하였다. PE-CVD 장비를 이용하여 SiNx를 120 nm 증착하고, ZTO 용액을 spin-coating을 이용하여 channel layer을 형성하였다. 균일하게 형성된 ZTO의 결정을 위하여 200$^{\circ}C$, 300$^{\circ}C$, 400$^{\circ}C$, 500$^{\circ}C$에서 1시간, 3시간, 6시간, 10시간의 온도 및 시간 변수를 두어 공기 중에서 열처리 하였다. ZTO는 약 30 nm 두께로 형성되었다. Thermal evaporator를 이용하여 Source, Drain의 알루미늄 전극을 형성하고, wafer 뒷면에는 Silver paste를 이용하여 Gate전극을 만들었다. 제작된 소자를 dark room temperature에서 측정하였다.