• 한국신재생에너지학회:학술대회논문집
• /
• 2008.05a
• /
• pp.436-437
• /
• 2008

Flexible CIGS thin film solar cell was fabricated using STS430 plate as a flexible substrate in this work. A diffusion barrier layer of $SiO_2$ thin film was deposited on STS430 substrate by PECVD followed by deposition of double layered Mo back contact. After depositing CIGS absorber layer by co-evaporation, CdS buffer layer by chemical bath deposition, ZnO window layer by RF sputtering and Al electrode by thermal evaporation, the solar cell fabrication processes were completed and its performance was evaluated. Corresponding solar cell showed an conversion efficiency of 8.35 % with $V_{OC}$ of 0.52 V, $J_{SC}$ of 26.06 mA/$cm^2$ and FF of 0.61.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.29-29
• /
• 2010

건물일체형 태양전지 (BIPV; building integrated photovoltaics)나 야외 태양광 발전 차양 등의 태양광 발전에는 기존의 유리 기판 태양전지보다 가볍고 유연한 flexible 박막 태양전지가 설치하고 운영하는데 적합하다. 이러한 flexible 박막 태양전지는 자동차나 휴대기기의 전원이나 배터리의 충전기기로도 쓰이며 그 수요가 증가 추세에 있다. 특히, flexible Cu(In, Ga)$Se_2$(CIGS) 박막 태양전지는 기존의 flexible 실리콘 박막 태양전지보다 효율이 높아서 앞으로 성장 잠재력이 매우 높다. 세계적으로도 많은 기업이 상용화를 추진하고 있으며, 2007년부터 시장에 진입하고 있다. 그러나 현재의 flexible CIGS 박막 태양전지는 유리 기판 CIGS 박막 태양전지보다 효율이 낮고 패키지를 유리에서 플라스틱으로 대체하기 때문에 수명이 짧다. 또한, 아직도 완전한 양산 체제로 전환이 이루어지지 않았기 때문에 해결해야 할 문제점이 많이 있다. Flexible 기판으로는 스테인리스 스틸이나 폴리머 기판이 사용되는데, 유리 기판에 비해 저가 태양전지를 제조할 수 있을 뿐만 아니라 roll-to-roll 공정을 적용할 수 있어 가격 경쟁력을 확보할 수 있다. 특히, 금속 유연기판을 사용할 경우, 유리 기판에 비해 상대적으로 고온 공정이 가능한 장점이 있다. 그러나, 금속 기판을 사용할 경우 해결해야 할 두 가지 이슈가 있다. 첫째, CIGS 흡수층 형성에 도움을 주는 Na의 공급 문제이다. 유리 기판의 경우 기판에 포함되어 있는 Na이 확산을 통해 공급되지만, 금속 기판의 경우 별도의 Na 공급 방법을 고려해야 한다. 둘째, 불순물 확산 방지막 및 전기 절연층으로 사용되는 유전체 박막의 문제이다. 현재 다양한 금속 산화물 유전체 박막을 사용한 연구가 진행되고 있다. 본 논문에서는 flexible CIGS 박막 태양전지의 기술적 이슈 및 현재 연구 현황을 살펴보고, 스테인리스 스틸 기판을 이용한 CIGS 박막 태양전지에서 유전체 확산 방지막에 따른 특성을 비교하고자 한다. 스테인리스 스틸 기판의 불순물로부터의 확산을 방지하기 위하여 두 종류(intrinsic ZnO와 SiOx)의 유전체 박막을 각각 Na가 도핑된 Mo층과 스테인리스 스틸 기판 사이에 삽입하여 소자를 제작하였다. 확산 방지막이 없는 경우, SiOx층을 사용한 경우, 그리고 intrinsic ZnO 층을 사용한 경우에, 효율은 각각 7.47, 11.64, and 13.95%로 나타났다. 셀의 크기는 $0.47\;cm^2$이고, 반사방지막은 사용하지 않았다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.58.1-58.1
• /
• 2011

CIS(CuInSe2)계 화합물 태양전지는 높은 광흡수계수와 열적 안정성으로 고효율 태양전지 제조가 가능하여 태양전지용 광흡수층으로 매우 이상적이다. 미국 NREL에서는 이러한 CIGS 태양전지를 Co-evaporation 방법으로 제조 20%이상의 에너지 변환 효율을 달성하였다고 보고하였다. CIGS 태양전지의 경우 기존의 유리 기판 대신 유연한 철강 기판을 사용해 태양 전지를 flexible하게 제조 할 수 있다는 장점이 있다. 이러한 flexible 태양전지의 경우 기존의 rigid 태양전지의 적용분야 뿐만 아니라 BIPV, 선박, 장난감, 군용, 자동차등 더욱 더 많은 분야에 활용이 가능하다. 본 연구에서는 기존의 rigid한 기판인 soda lime glass와 flexible 기판인 stainless steel 기판으로 소자를 제조하여 효율을 비교 분석 및 stainless steel 기판의 표면 처리 방법에 따라서 표면 조도의 특성을 분석하여 stainless steel 기판별 효율 특성도 비교 분석 하였다. 후면전극으로는 약 $1{\mu}m$의 Mo를 DC Sputtering 방법을 이용하여 증착하였고, CIGS 광흡수층은 약 $2.5{\mu}m$의 두께로 미국의 NREL과 같은 3 stage 방식을 이용하여 광흡수층을 Co-Evaporation 방법으로 제조하였고, 버퍼층인CdS는 약 50nm의 두께로 CBD 방법으로 제조 하였으며, 창층인 ZnO는 약 500nm 두께로 RF Sputtering 방법으로 제조 하였고, 마지막으로 약 $1{\mu}m$ 두께의 Al 전면전극은 Thermal Evaporation 방법으로 제조 하였다. 소자의 물리적, 전기적 특성을 분석하기위해 FE-SEM, AFM, Solar Cell Simulator 분석을 실시하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.52-52
• /
• 2010

CIS(CuInSe2)계 화합물 태양전지는 높은 광흡수계수와 열적 안정성으로 고효율 태양전지 제조가 가능하여 태양전지용 광흡수층으로 매우 이상적이다. 미국 NREL에서는 이러한 CIGS 태양전지를 Co-evaporation 방법으로 제조 20%이상의 에너지 변환 효율을 달성하였다고 보고하였다. CIGS 태양전지의 경우 기존의 유리 기판 대신 유연한 철강 기판을 사용해 태양전지를 flexible하게 제조 할 수 있다는 장점이 있다. 이러한 flexible 태양전지의 경우 기존의 rigid 태양전지의 적용분야 뿐만 아니라 BIPV, 선박, 장난감, 군용, 자동차등 더욱더 많은 분야에 활용이 가능하다. 하지만 flexible 태양전지에 사용되는 철강기판의 경우 기존의 유리 기판인 SLG에 함유되어 있는 Na이 첨가되어 있지 않아 별도의 Na 첨가가 필요하다. Na은 CIGS 광흡수층의 결정을 증가 시키며 태양전지의 전기적 특성을 향상시킨다. 이러한 Na이 없는 경우 효율이 감소한다. 따라서 flexible 태양전지 개발을 위해서는 Na 첨가에 대한 연구가 필수적이다. 본 연구에서는 Na의 증착 순서를 변화시켜서 CIGS 증착 전, 동시증착, CIGS 증착 후로 나누어 CIGS 광흡수층 결정성의 변화를 알아보고자 한다. Na의 두께를 5nm에서 500nm 까지 단계 별로 나누어 실험을 실시하였다. 이때 CIGS 광흡수층은 미국의 NREL과 같은 3 stage 방식을 이용하였다. 1st stage의 시간은 15분으로 고정하였으며 기판온도는 약 $300^{\circ}C$로 고정 하였다. 2nd stage는 실시간 온도 감지 장치를 이용하여 Cu와 In+Ga의 조성비가 1:1이 되는 시간을 기준으로 Cu의 조성을 30%더 높게 조절하였으며 기판 온도는 약 $640^{\circ}C$로 고정 후 실험을 실시하였다. 3rd stage의 경우 Cu poor 조성으로 조절하기 위해 모든 조건을 10분으로 고정 후 실험을 실시하였다. 기판은 Na의 영향만을 비교하기위하여 Na이 첨가되어있지 않은 corning glass를 사용하였다. 후면 전극으로 약 $1{\mu}m$ 두께의 Mo을 DC Sputtering 방법을 이용하여 증착 하였다. 각각의 Na 두께에 따른 CIGS 광흡수층의 특성을 분석하기 위해 FE-SEM, XRD 분석을 실시하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.3
• /
• pp.163-168
• /
• 2020

We studied the change of photovoltaic properties of a flexible CuIn_xGa(_1-x)Se₂ (CIGS) solar cell fabricated on polyimide by mechanical bending with curvature radii of 75 mm (75R) and 20 mm (20R). The flexible CIGS cells were flattened on a PET film, then placed and forced against the surface of a curved block fabricated with pre-designed curvatures. Both up (compressive) and down (tensile) bending were applied to a specimen of CIGS on PET with curvatures of 75R and 20R for 10,000 times and 2,000 times, respectively. From J-V measurements, we found that the conversion efficiency (Eff.) was reduced by 3% and 4% for up-and down-bending, respectively, at curvature 75R; it was greatly reduced by 15% for curvature 20R in the up-bending. However, the open circuit voltage (V_oc) and short-circuit current density (J_sc) seemed to change little, within 3%, for the applied mechanical stresses. The degradation in Eff. resulted from the deterioration of the series (R_s) and shunt (R_sh) resistances of the solar cell.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.153-155
• /
• 2009

In this study, we fabricated the $Cu(In,Ga)Se_2$ (CIGS) thin-film solar cells by using a polyimide substrate. The CIGS thin-film was deposited on Mo coated polyimide substrate by a 3-stage co-evaporation technique. Because the polyimide shows thermal transformation at about $400^{\circ}C$, the substrate temperature of co-evaporation process was set to below $400^{\circ}C$. Corresponding solar cell showed a conversion efficiency of 7.08 % with $V_{OC}$ of 0.58 V, $J_{SC}$ of 24.99 $mA/cm^2$ and FF of 0.49.

• Journal of Applied Reliability
• /
• v.16 no.1
• /
• pp.41-47
• /
• 2016

Purpose: The purpose of this study was to evaluate electrical and structural degradation of flexible CIGS sollar cell exposed to high temperature and humid atmosphere. Method: Accelerated degradation was performed for various time under $85^{\circ}C/85%RH$ and then electrical and structural properties were analyzed by 4-point probe method, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD). Results: Sheet resistance of the top ITO layer increased with exposure time to the high temperature and humid atmosphere. Blunting of the protrusion morphology of ITO layer was observed for the degraded specimen, while no phase change was detected by XRD. Oxygen was detected at the edge area after 300 hours of exposure. Conclusion: Increase in electrical resistance of the degraded CIGS solar cell under high temperature and humid environment was attribute to the oxygen or water absorption.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.3
• /
• pp.57-61
• /
• 2016

In order to protect the solar cells from the moisture and oxygen, we evaluated the electrical and optical properties for the $Cu(In,Ga)Se_2$ (CIGS) solar cells which were prepared by the spray coating method. Generally, the EVA (ethylene-vinyl acetate) films are laminated to protect the CIGS flexible solar cells, which results in a high cost process due to complicated devices. In this study, we tried to prepare the protection layers of the flexible CIGS flexible solar cells by using spray coating method instead of conventional laminating films in order to reduce the device weight as well as the process time. The CIGS solar cells with spray coating method showed an enhanced efficiency than the before treated sample (2.77% to 2.93%) and relatively proper water vapor transmission rate of the solar cells about 62.891 gm/[$m^2-day$].

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.62.1-62.1
• /
• 2010

CIS(CuInSe2)계 화합물 태양전지는 높은 광흡수계수와 열적 안정성 및 조성 조절을 통한 밴드갭 조절이 용이해 고효율 박막 태양전지로 각광 받고 있다. 또한 CIGS 태양전지는 기존의 유리기판 대신 유연한 기판을 사용해 flexible 태양전지 제조가 가능하다. 이러한 유연기판은 보통 stainless steel과 같은 금속 기판이 많이 사용되는데 기존의 soda-lime glass 기판과는 달리 금속기판에는 Na이 첨가되어 있지 않아 별도의 Na첨가를 필요로 한다. Na은 CIGS 흡수층의 조성조절을 용이하게 하여 태양전지의 변환 효율을 향상시키는 역할을 한다. 본 연구에서 기판은 Na이 첨가되어있지 않은 corning glass를 사용 하였으며 NaF를 이용해 Mo가 증착된 기판에 NaF의 두께를 달리하며 증착해 CIGS 흡수층의 grain 사이즈를 비교 하였으며 그 후 태양전지 소자를 제조해 광전특성을 분석하였다. 후면 전극으로 약60nm 두께의 Mo를 DC Sputtering 방법을 이용해 증착 하였다. buffer층으로는 약 50nm의 CdS층을 CBD방법을 이용하여 제조 하였으며 TCO 층으로 약 50nm의 i-ZnO와 약 450nm의 Al-ZnO를 RF Sputtering방법으로 증착 하였다. 마지막으로 앞면 전극으로 약 $1{\mu}m$의 Al을 Thermal Evaporation방법으로 증착하였다. 태양전지 소자의 면적은 $0.49cm^2$로 효율을 비교 분석하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2008.05a
• /
• pp.5.2-5.2
• /
• 2008