• Composites Research
• /
• v.36 no.1
• /
• pp.16-24
• /
• 2023

This paper presents a multi-scale progressive fatigue damage model incorporating the model for interfacial debonding between fibers and matrix. The micromechanics model for the progressive interface debonding was adopted, which defined the four different interface phases: (1) perfectly bonded fibers; (2) mild imperfect interface; (3) severe imperfect interface; and (4) completely debonded fibers. As the number of cycles increases, the progressive transition from the perfectly bonded state to the completely debonded fiber state occurs. Eshelby's tensor for each imperfect state is calculated by the linear spring model for a damaged interface, and effective elastic properties are obtained using the multi-phase homogenization method. The fatigue damage evolution formulas for fiber, matrix and interface were proposed to demonstrate the fatigue behavior of CFRP laminates under cyclic loading. The material parameters for the fiber/matrix fatigue damage were characterized using the chaotic firefly algorithm. The model was implemented into the UMAT subroutine of ABAQUS, and successfully validated with flat-bar UD laminate specimens ([0]₈,[90]₈, [30]₁₆) of AS4/3501-6 graphite/epoxy composite.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.34 no.8
• /
• pp.323-330
• /
• 1985

Dielectric loss tangent and ac dielectric strength of GFRP (Glass Fiber Reinforced Plastics, G-10)was investigated as parameters of mechanical and thermal stresses, in order to study the basic dielectrical characteristics of composite insulating materials. The dielectric loss tangent was increased and the ac dielectric strength was decreased with increase in the mechanical stresses beyond the mechanical yield point on account of fiber-matrix debonding, but the dielectric constant was not varied sigificantly. the dielectric strength of G-10 was about 2 MV/cm and the dielectric constant was about 4.8.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.3
• /
• pp.251-260
• /
• 2001

Damage Profess of CFRP laminates under monotonic tensile test was characterized by the correlation between Acoustic Emission(AE) and Ultrasonic Test(UT). The amplitude distribution of AE signal from a specimens is an aid to the determination of the extent of the different fracture mechanism such as matrix crack, debonding, fiber pullout and fiber fracture as load is increased. In addtion, the characteristics of ultrasonic amplitude attenuation are useful lot analysis of the different type of fracture mechanism. Different orientation of carbon fiber reinforced plastic specimens were used to investigate the AE amplitude range and ultrasonic amplitude attenuation. Finally, loading-unloading tests were carried out to check Felicity effect. During the tests, ultrasonic amplitude attenuation was investigated at the same time and compared with AE parameters. The result showed that two parameters of both AE and UT could be effectively used for analysis of fracture mechanism in CFRP laminates.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.28 no.3
• /
• pp.295-305
• /
• 1992

The critical strain energy release rate and the failure mechanisms of glass-carbon epoxy resin hybrid composites are investigated in the temperature range of the ambient temperature to 8$0^{\circ}C$. The direction of laminates and the volume fraction are [(+45, -45, 0, 0) sub(2) ] sub(s), 50%, respectively. The major failure mechanisms of these composites are studied using the scanning electron microscope for the fracture surface. Results are summarized as follows: 1) The critical strain energy release rate shows a maximum at ambient temperature and it tends to decrease as temperature goes up. 2) The critical strain energy release rate increases as the content of glass increases, and especially shows dramatic increase for the high glass fiber content specimens. 3) Major failure mechanisms can be classfied such as localized shear yielding, fiber-matrix debonding, matrix micro-cracking, and fiber pull-out and/or delamination.

• Polymer(Korea)
• /
• v.26 no.6
• /
• pp.718-727
• /
• 2002

In this work, an Ar+ beam was irradiated on carbon fiber surfaces to improve the interfacial shear strength (IFSS) of the resulting composites using an ion assisted reaction (IAR) method h single fiber pull-out test was executed to investigate the basic characteristics of the single Carbon fiber/matrix interface. Based on Greszczuk's geometrical model, the debonding force for pull-out of the fiber from the resins was discussed with the applied ion beam energy as a result, it was known that an ion beam treatment produced the functional groups on fiber surface and etching lines along the fiber axis direction, resulting in increasing the adhesion forces between fibers and matrix, which caused the improvement of the IFSS in a composite system. And, it was also found that the maximum IFSS was shown at 0.8 keV ion beam energy in this system.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.37 no.3
• /
• pp.240-245
• /
• 2001

The tensile strength and failure mechanisms of glass fiber polypropylene (GF/PP) composites are investigated in the temperature range from ambient to 8$0^{\circ}C$. The tensile strength increases as fiber volume fraction ratio increase. The tensile strength shows a maximum at ambient temperature, and it tens to decrease as temperature goes up. Major failure mechanisms of GF/PP composites can be classified as fiber matrix debonding, fiber pull-out, delamination and matrix deformation.

• Structural Engineering and Mechanics
• /
• v.67 no.5
• /
• pp.545-553
• /
• 2018

Mode II delamination propagation is an important damage mode in laminated composites and this paper aims to investigate the behavior of this damage in laminated composite materials using acoustic emission (AE) technique. Three different lay-ups of glass/epoxy composites were subjected to mode II delamination propagation and generated AE signals were recorded. In order to investigate the propagation of delamination behavior of these specimens, AE signals were analyzed using Wavelet Packet Transforms (WPT) and Fast Fourier Transform (FFT). In addition, conventional AE analyses were used to enhance understanding of the propagation of delamination damage. The results indicate that different fracture mechanisms were the main cause of the AE signals. The dominant mechanisms in all the specimens were matrix cracking, fiber/matrix debonding and fiber breakage, with varying percentage of the damage mechanisms for each lay-up. Scanning Electron Microscopy (SEM) observations were in accordance to the AE results.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.05a
• /
• pp.53-56
• /
• 2002

External low-velocity impact loadings onto the composites cause reduction of stiffness and/or strength. The reductions indicate that internal(external) damages were developed within the composites. These damages could be matrix cracking, fiber/matrix debonding, or delamination between layers. In previous studies, damage evaluation have been done by applying secondary mechanical loading such as buckle-driven compressive, or fatigue, or flexural loadings. An evaluation method by applying indentation loadings on the composites was proposed. The load-displacement curves obtained from the indentation testing provided the extent of damages within the composites due to impact loadings.

• Journal of the Korean Society of Safety
• /
• v.13 no.4
• /
• pp.131-136
• /
• 1998

The creep behavior and failure mechanism of the 30 vol% hot-pressed $SiC_t/Si_3N_4$ ceramic composite was experimentally investigated at $1200^{\circ}C$ and at various stress levels in air. The creep threshold stress for zero creep rate after 100 hr was found to be approximately 60 MPa. The stress exponent was estimated to be n~1, which suggests that fiber-reinforcement reduced the stress sensitivity of the HPSN matrix with the stress exponent of 2. The tertiary stage leading to creep rupture was found at 250 MPa but was very short. The microstructure of the crept specimen showed random fiber fracture and no matrix cracking. Interfacial debonding was absent.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2003.10a
• /
• pp.283-288
• /
• 2003

The object of this study is to investigate a fracture characteristics of static tensile test as a function of acoustic emission according to the fiber orientation $\theta=0^{\circ}C$ in carbon/epoxy composites, CFRP. On tensile loading, it was recognized that the fracture characteristics of CFRP in a unidirectional composites. Using the results of the AE analysis(a=2mm), it was found that the amplitude distributions of AE signals corresponding the matrix cracking, fiber debonding or delamination, and fiber breaking are 55~70dB(<200sec), 100dB(200~600sec), and 80dB(>600sec).