• Journal of The Korean Society of Agricultural Engineers
• /
• v.54 no.6
• /
• pp.151-158
• /
• 2012

This study will not only prove experimental dynamic properties which are classified to slump, compressed strength, bending strength and toughness index blast-furnace cement concrete with polypropylene (PP) fiber that refer properties and volume of it, but also establish a basic data in order to use PP fiber reinforced blast-furnace cement concrete. The slump didn't changed by PP fiber volume $5kgf/m^3$ because of flexibility of fiber in despite of loose mixing. The reason why the slump decreased steadily by PP fiber volume $3kgf/m^3$ was rising contact surface of water. The compressed strength indicated a range of 19.49~26.32 MPa. The tensile strength indicated a range of 2.10~2.44 MPa. The bending strength was stronger about 3~16 % in case of mixing with PP fiber volume than normal concrete. The flexure strength indicated a range of 4.30~4.83 MPa. The toughness indicated a range of $0{\sim}19.88N{\cdot}mm$ and was stronger about 6.7 times in case of PP fiber volume $9kg/m^3$ than PP fiber volume $1kg/m^3$. The pavement with PP fiber volume over such a fixed quantity in the roads of a respectable amount load can have a effect to prevent not only resistance against clack but also rip off failures.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.55 no.1
• /
• pp.1-8
• /
• 2013

This study will not only prove experimental dynamic properties which are classified to slump, compressive strength, tensile strength, flexure strength and toughness granite soil concrete with a fine aggregate of granite soil and blast-furnace cement and polypropylene fiber over 45 mm, but also establish a basic data in order to use environment-friendly pavement through prove useful pavement mixed with granite and polypropylene (PP) fiber which is a kind of material to prevent a dry shrinkage clack, a partial destruction and useful and light. The value of slump test was gradually increased by PP fiber volume 3 $kgf/m^3$, but compressive strength took a sudden turn for the worse from 5 $kgf/m^3$. The compressive strength indicated a range of 13.72~18.35 MPa. On the contrary to compressive strength, the tensile strength showed to decrease with rising PP fiber volume, and the tensile strength indicated a range of 1.43~1.64 MPa. The tensile strength was stronger about 2~15 % in case of mixing with PP fiber volume than normal concrete. The flexural strength indicated a range of 2.76~3.41 MPa. The flexural strength was stronger about 20 % in case of PP fiber volume 0 $kg/m^3$ than PP fiber volume 9 $kg/m^3$. The toughness indicated a range of 0~25.46 $N{\cdot}mm$ and increased proportionally with PP fiber volume. The toughness was stronger about 8.3 times in case of PP fiber volume 9 $kg/m^3$ than PP fiber volume 1 $kg/m^3$. The pavement with PP fiber volume over such a fixed quantity in the park roads and walkways can have a effect to prevent not only resistance against clack but also rip off failures.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.40 no.2
• /
• pp.161-165
• /
• 2004

The main goal of this work is to study the effect of glass fiber volume fraction on the result of tensile test with respect to glass fiber/polypropylene(GF/PP) composites. The tensile test and failure mechanisms of GF/PP composites were investigated in the fiber volume fraction range from 10% to 30%. The tensile strength and the fracture strength increased with the increasing of the fiber volume fraction in the tested range. Fiber pull-out and debonding of this composites increased with the fiber volume fraction in thc tested range. The major failure mechanisms were classified into the debonding, the fiber pull out, the delamination and the matrix deformation.

• Carbon letters
• /
• v.3 no.3
• /
• pp.127-132
• /
• 2002

Unidirectional polymer composites were prepared using high-strength carbon fibers as reinforcement and phenolic resin as matrix precursor with keeping fiber volume fraction at 30, 40, 50 and 60% respectively. These composites were carbonized at $1000^{\circ}C$ and graphitised at $2600^{\circ}C$ in the inert atmosphere. The carbonized and graphitised composites were characterized for mechanical properties as well as microstructure. Microscopic studies were carried out of the polished surface of carbonized and graphitised composites after etching by chromic acid, to understand the effect of fiber volume fraction on oxidation at fiber-matrix interface. It is found that the flexural strength in polymer composites increases with fiber volume fraction and so does for the carbonised composites. However, the trend was found to be reversed in graphitised composites. In all the carbonized composites anisotropic region has been observed at fiber-matrix interface which transforms into columnar type microstructure upon graphitisation. The extension of strong and weak columnar type microstructure is function of fiber volume fraction. SEM microscopy of the etched surface of the sample reveal that composites containing 40% fiber volume has minimum oxidation at the interface, revealing a strong interfacial bonding.

• Structural Engineering and Mechanics
• /
• v.65 no.2
• /
• pp.163-171
• /
• 2018

Plain concrete is a brittle material with a very low tensile strength compared to compressive strength and critical tensile strain. This study analyzed the dynamic characteristics of high-performance fiber-reinforced cementitious composites based on slurry-infiltrated fiber concrete (SIFCON-based HPFRCC), which maximizes the steel-fiber volume fraction and uses high-strength mortar to increase resistance to loads, such as explosion and impact, with a very short acting time. For major experimental variables, three levels of fiber aspect ratio and five levels of fiber volume fraction between 6.0% and 8.0% were considered, and the flexural strength and toughness characteristics were analyzed according to these variables. Furthermore, three levels of the aspect ratio of used steel fibers were considered. The highest flexural strength of 65.0 MPa was shown at the fiber aspect ratio of 80 and the fiber volume fraction of 7.0%, and the flexural strength and toughness increased proportionally to the fiber volume fraction. The test results according to fiber aspect ratio and fiber volume fraction revealed that after the initial crack, the load of the SIFCON-based HPFRCC continuously increased because of the high fiber volume fraction. In addition, sufficient residual strength was achieved after the maximum strength; this achievement will bring about positive effects on the brittle fracture of structures when an unexpected load, such as explosion or impact, is applied.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.1
• /
• pp.43-48
• /
• 2008

Fifteen concrete specimens were mixed and tested to explore the significance and limitation of appling the polyvinyl alcohol (PVA) fiber and steel fiber with end hook to concrete. Main parameters investigated were volume fraction and length of the fibers. The measured mechanical properties of fiber reinforced concrete are analyzed according to the equivalent fiber amount index explaining the adding amount and length of fibers. Test results showed that compressive strength of fiber reinforced concrete was higher than that of concrete with no fiber by $10{\sim}20%$. The normalized splitting tensile strength and flexural strength of PVA fiber reinforced concrete were similar to those of concrete with no fiber, whereas those of steel fiber reinforced concrete increased with the increase of the equivalent fiber amount index. In particular, much higher ductile behavior was observed in steel fiber reinforced concrete than in PVA reinforced concrete, indicating that the slope of descending branch of load-displacement relationship of steel fiber reinforced concrete decreased with the increase of the volume fraction and length of the fiber.

• Journal of the Korean Society of Safety
• /
• v.19 no.4 s.68
• /
• pp.31-35
• /
• 2004

The A17075/CFRP multi-layered hybrid laminate material consists of the alternating A17075-T6 sheets and carbon/epoxy prepregs of M40 fade. The influence of volume fraction and fiber orientation of A17075/CFRP layer on flexural properties of A17075/CFRP laminate alternating A17075-T6 and carbon/epoxy prepreg was investigated. The results obtained from the experimental analysis are as follows: 1. In the $0^{\circ}$ fiber orientation, the mont of increase of the flexural rigidity was $20.5\%$ at the $26.5\%$ volume fraction and $38.0\%\;at\;the\;35.7\%$ volume fraction compared with the flexural rigidity level(20.0GPa) of the $10\%$ volume fraction of CFRP. 2. In the $\pm45^{\circ}$ fiber orientation the amount of decrease of the flexural rigidity was $23.5\%\;at\;the\;20.0\%$ volume fraction and $31.5\%\;at\;the\;33.3\%$ volume fraction compared with the flexural rigidity level of the $10\%$ volume fraction of CFRP. 3. In the $0^{\circ}$ fiber orientation, the flexural strength was 481.5MPa at the $10\%$ volume fraction of CFRP and 583.8MPa at the $26.5\%$ volume fraction and 653.7MPa at the $35.7\%$ volume faction. 4. In the $\pm45^{\circ}$ fiber orientation, the flexural strength was 354.0MPa at the $20.0\%$ volume fraction of CFRP and 340.5MPa at the $33.3\%$ volume fraction.

• Advances in concrete construction
• /
• v.16 no.3
• /
• pp.127-139
• /
• 2023

In this study, the steel fiber and the polypropylene fiber were used to enhance the mechanical properties of fully recycled coarse aggregate concrete. Natural crushed stone was replaced with recycled coarse aggregate at 100% by volume. The steel fiber and polypropylene fiber were used as additive material by incorporating into the mixture. In this test two parameters were considered: (a) steel fiber volume ratio (i.e., 0%, 1%, 1.5%, 2%), (b) polypropylene fiber volume ratio (i.e., 0%, 0.1%, 0.15%, 0.2%). The results showed that compared with no fiber, the integrity of cubes or cylinders mixed with fibers after failure was better. When the volume ratio of steel fiber was 1~2%, the width of mid-span crack after flexural failure was 5~8 mm. In addition, when the volume ratio of polypropylene fiber was 0.15%, with the increase of steel fiber content, the static elastic modulus and toughness of axial compression first increased and then decreased, and the flexural strength increased, with a range of 6.5%~20.3%. Besides, when the volume ratio of steel fiber was 1.5%, with the increase of polypropylene fiber content, the static elastic modulus decreased, with a range of 7.0%~10.5%. The ratio of axial compression toughness first increased and then decreased, with a range of 2.2%~8.7%. The flexural strength decreased, with a range of 2.7%~12.6%. On the other hand, the calculation formula of static elastic modulus and cube compressive strength of fully recycled coarse aggregate with steel-polypropylene fiber was fitted, and the optimal fiber content within the scope of the test were put forward.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.05a
• /
• pp.59-62
• /
• 2003

Kinds, shapes and fraction ratios of fibers have influence on properties of HPFRCC(High-Performance Fiver Reinforced Cementitious Concrete ) like bending strength, strain capacity and fracture toughness. For example, hydrophilic fibers have different chemical bond strength from hydrophobic fibers, fiber shapes influence on fiber pull-out and rupture, and fiber volume fraction influence on bending strength. In this study, to estimate influences of kinds, shapes and fraction ratios of fibers, we make HFRCC with 3 kind of fiber in various volume fraction of fiber and compare cracking, bending strength and fracture toughness. As the results, bending strength of HPFRCC was increased as fiber volume fraction was Increase and fiber tensile strength was increase, and strain capacity and fracture toughness of HFRCC was higher in fiber pull-out fracture than in fiber rupture fracture. And HFRCC showing pseudo strain hardening has higher fiber reinforce efficiency than others.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.9
• /
• pp.2782-2791
• /
• 1996

The effective longitudinal shear modulus(LSM) of continuous composites is studied theoretically and numerically using 3-phase unit cell model. Circular, hexagonal and rectangular shapes of reinforced fiber are considered to predict the shear modulus as a function of elastic modulus of each phase and volume fraction of interphase and reinforced fiber. It is found that rectangular fiber shape in low fiber volume fraction($v_f$<30%) and circular fiber shape in high volume fraction($v_f$>40%) shows the higher longitudinal shear modulus. Also the obtained values of LSM for rectangular array and by numerical analysis are higher than those of hexagonal array and by theoretical analysis respectively. The reinforcing effects of interphase are more significant in cases of higher fiber volume fraction and circular fiber shape. Not only the spatial distribution and shape of reinforcing fiber but also the volume of interphase have a pronounced effects on the overall LSM. It is also found that the tangent moduous of 2-and 3-phase polymer matrix composites is insensitive to the shape and distribution of reinforcing fibers.