• Journal of Power System Engineering
• /
• v.9 no.1
• /
• pp.76-81
• /
• 2005

The effect of micro-pulse plasma nitriding temperature and time on the case thickness, hardness and nitride formation in the surface of Fe-12Cr-22Mn-X alloy with 3% Co and 1% Ti alloys elements investigated. External compound layer and internal diffusion layer was constituted in plasma nitride case of Fe-12Cr-22Mn-X alloys and formed nitride phase such as ${\gamma}'-Fe4N\;and\;{\varepsilon}-Fe2-3N$. Case depth increased with increasing the plasma nitriding temperature and time. Surface hardness of nitrided Fe-12Cr-22Mn-X alloys obtained the above value of Hv 1,600 and case depth obtained the above value of $45{\mu}m$ in Fe-12Cr-22Mn-3Co alloy and $60{\mu}m$ in Fe-12Cr-22Mn-1Ti alloy. Wear-resistance increased with increasing plasma nitriding time and showing the higher value in Fe-12Cr-22Mn-1Ti alloy than Fe-12Cr-22Mn-3Co alloy.

• Applied Microscopy
• /
• v.48 no.4
• /
• pp.117-121
• /
• 2018

The multiple length scale analysis of previously designed Fe-Mn-Al-C based low-density model alloys reveals the difference in ordered ${\kappa}-carbide$, $(Fe,Mn)_3AlC_x$, between Fe-25Mn-16Al-5.2C (at%) alloy and Fe-3Mn-10Al-1.2C (at%) alloy. For the former alloy composition consisting of fully austenite grains, ${\kappa}-carbide$ showed majorly cuboidal and minorly pancake morphology and its chemical composition was not changed through aging for 24 h and 168 h at $600^{\circ}C$. Meanwhile, for the isothermally annealed ferritic alloy system for 1 hr at 500 and $600^{\circ}C$, the dramatic change in the chemical composition of needle-shape ${\kappa}-carbide$, $(Fe,Mn)_3(Fe,Al)C_x$, was found. Here we address that the compositional fluctuations in the vicinity of the carbides are significantly controlled by abutting phase, either austenite or ferrite. Namely, the cooperative ordering of carbon and Al is an important factor contributing to carbide formation in the high-Mn and high-Al alloyed austenitic steel, while the carbon and Mn for the low-Mn and high Al alloyed ferritic steel.

• Applied Microscopy
• /
• v.45 no.1
• /
• pp.9-15
• /
• 2015

In the present study, microstructural evolution in CuCrFeNi, CuCrFeNiMn, and CuCrFeNiMnAl alloys has been investigated. The as-cast CuCrFeNi alloy consists of a single fcc phase with the lattice parameter of 0.358 nm, while the as-cast CuCrFeNiMn alloy consists of (bcc+fcc1+fcc2) phases with lattice parameters of 0.287 nm, 0.366 nm, and 0.361 nm. The heat treatment of the cast CuCrFeNiMn alloy results in the different type of microstructure depending on the heat treatment temperature. At $900^{\circ}C$ a new thermodynamically stable phase appears instead of the bcc solid solution phase, while at $1,000^{\circ}C$, the heat treated microstructure is almost same as that in the as-cast state. The addition of Al in CuCrFeNiMn alloy changes the constituent phases from (fcc1+fcc2+bcc) to (bcc1+bcc2).

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.4
• /
• pp.15-23
• /
• 1991

The damping capacities of the nonthermoelastic bcc type lath martensite and of the nonthermoelastic hcp type thin plate martensite in Fe-Mn alloys were studied. Fe-17%Mn alloy showing the hcp type thin plate martensite was superior to Fe-4%Mn alloy having the bcc type lath martensite in damping capacity. The damping capacity of the Fe-17%Mn alloy became greater with increasing the hcp martensite volume fraction. The damping mechanism of the Fe-4%Mn alloy was well explained by the dislocation model. However, the damping mechanism of the Fe-17%Mn alloy was explained on the basis of austenite/martensite interface moving model. The two alloys showed almost same levels of tensile strength. However, the elongation was greater in the Fe-17%Mn alloy than in the Fe-4%Mn alloy, showing lower yield strength in the former than in the latter. This result was considered to be attributed to formation of stress-induced martensite during tension test.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.2
• /
• pp.113-119
• /
• 1995

We have reported that an Fe-17wt%Mn alloy exhibits the highest damping capacity in the Fe-Mn binary system. In the present work, the effects of copper content on the damping capacity, atmospheric corrosion and mechanical properties were studied. The damping capacities were measured at room temperature for the air cooled Fe-17wt%Mn alloy having copper content from 0.1wt% to 1.1wt%. The damping capacity of the Fe-17wt %Mn alloy was decreased with increasing copper content. However, the addition of Copper was found to improve mechanical properties and atmospheric corrosion resistance. These mechanical properties were attributed to the formation of stress-induced martensite during tensile test.

• Journal of Power System Engineering
• /
• v.9 no.1
• /
• pp.70-75
• /
• 2005

The damping property of Fe-12Cr-22Mn-X alloys has been investigated to develop high damping and high strength alloy. Particularly, the effect of the phase of austenite, alpha and epsilon martensite, which constitute the structure of the alloys Fe-12Cr-22Mn-X alloys, on the damping capacity at room temperature has been investigated. Various fraction of these phases were formed depending on the alloy element and cold work degree. The damping capacity is strongly affected by ${\varepsilon}$ martensite while the other phase, such as ${\alpha}'$ martensite, actually exhibit little effect on damping capacity. In case of Fe-12Cr-22Mn-3Co alloy, the large volume fraction of ${\varepsilon}$ martensite formed at about 30% cold rolling, and in case of Fe-12Cr-22Mn-1Ti alloy, formed at about 20% cold rolling and showed the highest damping capacity. Damping capacity showed higher value in Fe-12Cr-22Mn-1Ti alloy than one in Fe-12Cr-22Mn-3Co alloy.

• Journal of Korea Foundry Society
• /
• v.29 no.2
• /
• pp.59-63
• /
• 2009

Effects of Ti on damping capacity and mechanical properties are investigated in hot rolled Fe-17%Mn alloy. The existing damping alloy with Fe-Mn binary system was limited the use by high production cost, however in case of using scrap iron instead of pure iron although the content of carbon is higher it is possible to be applied wider field especially construction items because the production cost is lower. However, the excellent specific damping capacity is dropped due to the high content of carbon, we developed advanced type of damping alloy included Ti. TiC is formed with added Ti and it holds the specific damping capacity similar to existing damping alloy. The effect of Ti on damping capacity is found to be beneficial in carbon-containing alloy, which is attributed to the depletion of carbon solute due to the formation of TiC.

• Transactions of the Korean hydrogen and new energy society
• /
• v.10 no.3
• /
• pp.185-189
• /
• 1999

Effects of alloy modification with the $Zr_{0.6}Ti_{0.4}V_{0.4}Ni_{1.2}Mn_{0.4}$ alloy for an electrode use have been investigated. For the alloy composition, a part of Mn was substituted by Co, Cr and Fe. The experimental results showed that Co accelerated activation of alloy, and Fe and Cr improved the discharge capacity. These results agree with P-C-T curves of each alloy. But substituting Fe for Mn showed the decrease of the discharge capacity when discharged at high rate (60mA, about 1C rate). Considering both the discharge capacity and the high rate discharge property, $Zr_{0.6}Ti_{0.4}V_{0.4}Ni_{1.2}Mn_{0.3}Cr_{0.1}$ alloy was found to be the best alloy among the alloys subjected to the test.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.385-388
• /
• 2009

Dry-sliding-wear behavior of Fe-18Cr-l0Mn steel with various carbon and nitrogen contents was characterized, and the effect of carbon and nitrogen contents on the wear was investigated. Dry sliding wear tests of the steel were carried out at room temperature against an AISI 52100 bearing steel ball using a pin-on-disk wear tester. Applied wear loads were varied from 10 N to 100 N, and the sliding distance was fixed as 720 m. Worn surfaces and the wear debris of the steel were examined using an SEM to find out the wear mechanism. It was found that the Fe-18Cr-10Mn with both carbon and nitrogen exhibited superior wear resistance to the steel with only nitrogen. The wear resistance of the Fe-18Cr-10Mn-xC-yN alloy increased with the increase of the carbon content. The excellent wear resistance of the Fe-18Cr-10Mn-xC-yN alloy was explained by the increased strain-hardening capability with the interstitial atoms.

• Journal of Powder Materials
• /
• v.25 no.4
• /
• pp.302-308
• /
• 2018

A lean alloy is defined as a low alloy steel that minimizes the content of the alloying elements, while maintaining the characteristics of the sintered alloy. The purpose of this study is to determine the change in microstructure and mechanical properties due to the addition of silicon or tin in Fe-Mo-P, Fe-Mn-P, and Fe-Mo-Mn-P alloys. Silicon- or tin-added F-Mo-P, Fe-Mn-P, and Fe-Mo-Mn-P master alloys were compacted at 700 MPa and subsequently sintered under a $H_2-N_2$ atmosphere at $1120^{\circ}C$. The sintered density of three alloy systems decreases under the same compacting pressure due to dimensional expansion with increasing Si content. As the diffusion rate in the Fe-P-Mo system is higher than that in the Fe-P-Mn system, the decrease in the sintered density is the largest in the Fe-P-Mn system. The sintered density of Sn added alloys does not change with the increasing Sn content due to the effect of non-dimensional changes. However, the effect of Si addition on the transverse rupture strengthening enhancement is stronger than that of Sn addition in these lean alloys.