• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.05a
• /
• pp.58-58
• /
• 1994

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.1
• /
• pp.51-57
• /
• 2013

We have applied mechanical alloying (MA) to produce Heusler $Fe_2VAl$ thermoelectric alloy using a mixture of elemental $Fe_{50}V_{25}Al_{25}$ powders. An optimal milling and heat treatment conditions to obtain the single phase of Fe2VAl compound with fine microstructure were investigated by X-ray diffraction and differential scanning calorimetry (DSC) measurement. The $Fe_{50}V_{25}Al_{25}$ MA sample ball-milled for 60 hours exhibits a bcc ${\alpha}$-(Fe,V,Al) solid solution. Single phase of Heusler $Fe_2VAl$ compound can be obtained by MA of $Fe_{50}V_{25}Al_{25}$ mixture for 60 hours and subsequently heated up to $700^{\circ}C$. Sintering of the MA powders was performed in a spark plasma sintering (SPS) machine using graphite dies at $900{\sim}1000^{\circ}C$ under 60 MPa. The Vickers hardness of bulk sample sintered at $1000^{\circ}C$ was high value of Hv 870. All compact bodies have a high relative density above 90 % with metallic glare on the surface.

• Korean Journal of Materials Research
• /
• v.7 no.7
• /
• pp.592-596
• /
• 1997

LI$_{2}$형 결정구조를 갖는 Ni-20at.%AI-10at%Fe 금속간화합물에 boron, zirconium 과 hafnium을 최고 0.5at.% 까지 첨가하여 항복강도, 연성, 파괴 등 기계적 성질의 변화를 인장시험과 X선분석 및 XPS분석 등을 통하여 관찰하였다. Ni-20at.% AI-10at.% Fe금속간화합물에 boron을 첨가하였을 때는 연신율의 현저한 증가가 나타났으나 zirconium이나 hafnium첨가의 경우에는 별다른 효과가 나타나지 않았다. Ni-20at.%AI-10at%Fe 금속간화합물의 경우, boron의 양이 증가할수록 인장연신율이 증가하였으며 0.1at.%의 boron을 첨가한 경우 최고 48.5%의 상온인장연신율을 나타내었다. 첨가물을 넣지 않은 경우와 zirconium과 hafnium을 첨가한 경우, 파괴모드는 입계파괴의 형태를 나타내었으나 boron을 첨가한 경우에는 파괴모드가 입계파괴에서 입내파괴로 변화되었다. XPS분석을 통하여 boron이 입계에 편석된 것을 관찰할 수 있었으며 이는 이미 제시된 여러가지 해석들과 일치하는 결과이다. 이로부터 boron의 첨가에 따른 인장연신율의 증가는 boron의 입계편석거동과 관련이 있음을 알 수 있다.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.144-148
• /
• 1999

The relationship between oxidation and sliding wear behavior of Fe-28 at%. Al alloys with B2 ordered structure has been investigated. Sliding wear tests of the alloys have been carried out under various environmental conditions using a pin-on-disk wear tester. The wear rate of the ordered alloys in an oxygen atmoshpere was found to be much lower than in an oxygen atmosphere showed that Fe2O oxides formed on the wearing surface. The oxide layer prevented direct contact of the two mating materials and therefore improved wear resistance of the Fe-Al intermetallic alloy. It was found that the surface Al2O3 oxide layer which provides good oxidation resistance and improved mechanical properties broke down easily and didnot function properly as an oxidation barrier.

• Korean Journal of Materials Research
• /
• v.11 no.1
• /
• pp.34-38
• /
• 2001

Intermetallics of Fe-28%Al($Fe_3Al$) and Fe-28%Al-4%Cr($Fe_3Al-4Cr$) were oxidized at 1073, 1273 and 1473k in air for up to 17 days. The oxidation resistance of$Fe_3Al-4Cr$ was basically similar to or better than that of $Fe_3Al$. The oxide scales formed on $Fe_3Al$ consisted essentially of pure ${\alpha}-AL_2O_3$, while those formed on $Fe_3Al-4Cr$ consisted of ${\alpha}-AL_2O_3$ having dissolved iron and chromium ions. The preferential outward diffusion of substrate elements to form the outer oxide layer led to the formation of Kirkendall voids at the oxide-matrix interface. The scales formed on $Fe_3Al(-4Cr)$ were thin and dense up to 1273K, but they spalled easily at 1473K, accompanied by more weight gains.

• Journal of Korea Foundry Society
• /
• v.14 no.5
• /
• pp.419-428
• /
• 1994

The microvickers hardness and microstructure of Fe/Al composite fabricated by squeeze casting method were investigated. Pure Al and A356 Alloy were chosen for the matrix composition and Fe preform was fabricated with sintered Fe powder at $1000^{\circ}C$ for 30min. under hydrogen atmosphere. Experimental variables were included preheating temperature, melt temperature and applied pressure. Analysing the experimental result concerning microstructure of fabricated composites, Fe/A356 composite showed improved microstructure at $600^{\circ}C$ melt temperature and $350^{\circ}C$ preform preheating temperature in Fe distribution and Infiltrated distance. The results of EDX and XRD showed that the interfacial zones of Fe/Al composite were composed of non-equilibrium intermetallic layers[$(Al_5Fe_2)_x$, $Al_{13}Fe_4m\;Fe_3Al$, FeAl]. The microvickers hardness of Fe/Al composite showed higher value than Fe/A356 composite in interface.

• Journal of Welding and Joining
• /
• v.25 no.3
• /
• pp.51-56
• /
• 2007

A $CO_2$ laser overlay was conducted by using a Fe-based powder on the AC2B aluminum substrate. Cracks and intermetallic compounds (IMC) were observed inconsistently along the interface between the overlay and post-molten layer. A scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) detected some Fe-rich IMC ($Fe_3Al$, FeAl) as well as the brittle Al-rich IMC ($Fe_2Al_5,\;FeAl_3$). Micro vickers hardness proved the formation of Al-rich IMC ($FeAl_3$) along the interface by showing HV0.1 $800{\sim}900$. Furthermore, nano indentation was successfully applied to investigate the behavior of IMC more precisely than the micro vickers hardness.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1997.10a
• /
• pp.19-19
• /
• 1997

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.240-241
• /
• 2003

The iron aluminides have been among the most widely studied intermetallics because of their low cost, low density, good wear resistance, ease of fabrication and resistance to oxidation and corrosion. In this study, weld overlay was performed with JIS-YGW11 and A14043 wire on the base metal.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.155-155
• /
• 2000