• Journal of Korea Foundry Society
• /
• v.23 no.2
• /
• pp.77-85
• /
• 2003

Some alloying elements such as Cr, B, Ti and Si were added individually or as a mixture to Fe-30 at.%Al alloys. The alloys were melted using an arc furnace and then heat-treated for homogenization at 1000$^{\circ}C$ for 7 days and followed by rolling at 1000$^{\circ}C$. The alloying elements on rolling characteristics were investigated by the microstructures and fracture mode before and after rolling. The microstructures before rolling showed that all of the alloys had equiaxed grains. On the other hand, the microstructures of rolling plane as well as its perpendicular plane became elongated after rolling. The alloys such as Fe-30Al, Fe-30Al-3Ti, Fe-30Al-0.5B, Fe-30Al-5Cr and Fe-30Al-3Ti-0.5B revealed better rolling behaviour from the point that intergranular and cleavage fractures were not fundamentally occurred. But the addition of 5Ti or 3Si to Fe-Al alloys had detrimental effects. The Ti-added alloy system such as Fe-30Al-5Ti, Fe-30Al-5Ti-5Cr, Fe-30Al-3Ti-5Cr and Fe-30Al-5Ti-0.5B were cracked through grain and showed cleavage fracture. The Si-added alloy system such as Fe-30Al-5Si, Fe-27Al-3Si and Fe-27Al-5Cr-3Si were cracked along the grain boundary and showed intergranular fracture. $DO_3{\leftrightarrow}B_2$ transition temperature of Fe-30at.%Al alloy was 520$^{\circ}C$, whereas the addition of 3Ti and 3Ti+0.5B comparably increased the temperature to 797 and 773$^{\circ}C$, respectively.

• Journal of Korea Foundry Society
• /
• v.33 no.6
• /
• pp.233-241
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-9wt%Si-xMg-yFe-zMn alloy has been studied. The alloy was composed of ${\alpha}$-Al phase, Al+eutectic Si phase, ${\beta}$-Al5FeSi compound and chinese script ${\alpha}$-$Al_{15}(Mn,Fe)_3Si_2$ compound. ${\beta}$-$Al_5FeSi$ and ${\alpha}$-$Al_{15}(Mn,Fe)_3Si_2$ compounds assumed to effect the fluidity and shrinkage behaviors of the alloy during solidification due to the crystallization of ${\alpha}$-$Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}$-$Al_5FeSi$ compounds above eutectic temperature. As Fe and Mn contents of Al-9wt%Si-0.3wt%Mg system alloy increased from 0.15wt% to 0.6wt% and from 0.3wt% to 0.7wt%, fluidity of the alloy decreased by 5.7% and 3.3%, respectively. And as Mg content of Al-9wt%Si-0.45wt%Fe-0.5wt%Mn system alloy increased from 0.3wt% to 0.4wt%, fluidity of the alloy decreased by 8.6%. When Fe content of the alloy increased from 0.15wt% to 0.6wt%, macro shrinkage ratio decreased from 6.1% to 4.1%, and micro shrinkage ratio increased from 0.04% to 0.24%. Similarly, Mn content of the alloy increased from 0.3wt% to 0.7wt%, macro shrinkage ratio decreased from 6.0% to 4.5% and micro shrinkage ratio increased from 0.12% to 0.18%. Judging from the castability of the alloy, Al-9wt%Si-0.3wt%Mg alloy with low content of Fe and Mn, 0.1wt% Fe and 0.3wt% Mn, is recommendable.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.5
• /
• pp.365-372
• /
• 2000

Pure $Fe_3$Al alloys with three different compositions of Fe-21.8%Al, Fe-24.1%Al and Fe-27.2%Al were prepared by vacuum induction melting followed by homogenization and hot forging. The long-time oxidation behavior of the prepared alloys was studied at 1073, 1273 and 1473k in air. The oxidation resistance greatly increased with an increase in Al contents. Thin and uniform oxide scales were always formed on Fe-27.2%Al, while thick and fragile oxide scales were formed on Fe-(21.8, 24.1%)Al. Internal oxidation was observed in Fe-(21.8, 24.1%)Al, when oxidized above 1273K. The major oxidation product of all the oxidized alloys was always $\alpha$-$Al_2$$O_3$.

• Journal of Korea Foundry Society
• /
• v.29 no.5
• /
• pp.225-232
• /
• 2009

For comprehensive understanding of the formation behavior of $\beta-Al_5FeSi$ phase in Al-Si-Cu alloys with the existence of Fe element, microstructure characterizations were performed using combined analysis of OM, SEM-EDS, XRD. Especially, experimental and predictive works on solidification events of $\beta-Al_5FeSi$ phase as well as other phases formed together with $\beta-Al_5FeSi$ have been carried out by using DSC analysis and Java-based Materials Properties software (J. Mat. Pro.). Primary and eutectic $\beta-Al_5FeSi$ phases were able to distinguish from each other on microstructures by their morphological features. Primary $\beta-Al_5FeSi$ phase was seen to have rough surface perpendicular to growth direction, indicating free attachment of solute atoms in liquid state. On the other hand, the eutectic $\beta-Al_5FeSi$ phase was formed with plain and straight surface during eutectic reaction together with $\alpha$-Al phase. The eutectic reaction of $\beta-Al_5FeSi$ and $\alpha$-Al phases was seen to be able to separate into each formation depending on cooling rate.

• Journal of Powder Materials
• /
• v.6 no.4
• /
• pp.286-293
• /
• 1999

This study was to analyse the relationship between process parameters of the sintered composite and plasma nitriding properties with pulsed DC plasma. Fe-40at%$SiC_p$ composites of full density were fabricated by hot pressing at 1100~$1150^{\circ}C$. Sintered Fe-40at%Al and Fe-40at%$Al/SiC_p$ alloys were nitrided under pulsed DC plasma. Excellent surface hardness in the FeAl alloys could be obtained by plasma nitriding. ($H_v$ :100gf, diffusion layer : 1100~$1450kg/mm^2$, matrix : 330~$360kg/mm^2$) The wear resistance of $FeAl/SiC_p$ composites were improved about by 4~6times than FeAl and nitrided $FeAl/SiC_p$ were improved about 2 times than $FeAl/SiC_p$ matrix.

• Journal of Korea Foundry Society
• /
• v.31 no.1
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• Journal of the Korean institute of surface engineering
• /
• v.45 no.2
• /
• pp.61-69
• /
• 2012

Alloys of Fe-(5, 10, 15)Al and Fe-(10, 20, 30, 40)Cr were corroded at 700 and $800^{\circ}C$ for 70 hr in either atmospheric air or 1 atm of Ar+$1%SO_2$ gases. In these atmospheres, Fe-5Al and Fe-10Cr alloys displayed poor corrosion resistance. In atmospheric air, Fe-5Al alloys formed oxide nodules, while Fe-10Cr alloys formed thick scales and internal oxides. In Ar+$1%SO_2$ gases, Fe-5Al and Fe-10Cr alloys formed thick, nonadherent bi-layered scales, which grew primarily by the outward diffusion of Fe ions and inward diffusion of oxygen and sulfur ions. By contrast, in atmospheric air and Ar+$1%SO_2$ gases, Fe-(10, 15)Al and Fe-(20, 30, 40)Cr alloys displayed good corrosion resistance by forming $Al_2O_3$ and $Cr_2O_3$ layers on the surface, respectively.

• Journal of the Korean Magnetics Society
• /
• v.9 no.6
• /
• pp.296-300
• /
• 1999

Cross-shape structures of spin tunneling junctions were fabricated using DC magnetron sputtering and metal masks. The film structures were $substrate/Ta/NiFe/FeMn/NiFe/CoFe/Al_2O_3/CoFe/NiFe$ and $substrate/Ta/NiFe/CoFe/ Al_2O_3/CoFe/NiFe/FeMn/NiFe$. Fabrication conditions of insulating layer ($Al_2O_3$) and thickness and sputtering power of each film layer were varied, and maximum magnetoresistance ratio of 24.3 % was obtained. Magnetic characteristic variations in the above mentioned two structures and two types of substrates (Corning glass 7059 and Si(111)) were compared. Annealing of the junctions was performed to find out magnetic characteristic variations expected from the device fabrication. Magneoresistance Ratio were observed to maintain as-deposited value up to 150 $^{\circ}C$ annealing and then to drop rapidly after 180 $^{\circ}C$ annealing.

• Journal of Powder Materials
• /
• v.12 no.1
• /
• pp.70-78
• /
• 2005

Mechanical alloying using high-energy ball mill and subsequent spark plasma sintering (SPS) process was applied to understand mechanical alloying processing of Al-Fe alloy system. The thermal stability of mechanically alloyed Al-Fe alloy was intended to be enhanced by SPS process. Various analytical techniques including particle size analysis, density measurement, micro-Vickers hardness test, SEM, TEM, and X-ray diffractometry were adopted to find optimum processing conditions for mechanical alloying and subsequent SPS and to estimate thermal stability of the prepared alloy. It was found from the treatment of mechanically alloyed Al-8wt.%Fe powder mixture that needle-shaped $Al_3Fe$ precipitates was formed in the Al-Fe matrix, and the alloy compact showed enhanced densification and reached its full density with little loss of its fine microstructure. After heat treatment at $500^{\circC}$, it was also shown that the thermal stability of Al-8wt.%Fe alloy fabricated in the present study was enhanced, which was due to its fine microstructure developed by fast densification of SPS.

• Journal of Korea Foundry Society
• /
• v.14 no.5
• /
• pp.419-428
• /
• 1994

The microvickers hardness and microstructure of Fe/Al composite fabricated by squeeze casting method were investigated. Pure Al and A356 Alloy were chosen for the matrix composition and Fe preform was fabricated with sintered Fe powder at $1000^{\circ}C$ for 30min. under hydrogen atmosphere. Experimental variables were included preheating temperature, melt temperature and applied pressure. Analysing the experimental result concerning microstructure of fabricated composites, Fe/A356 composite showed improved microstructure at $600^{\circ}C$ melt temperature and $350^{\circ}C$ preform preheating temperature in Fe distribution and Infiltrated distance. The results of EDX and XRD showed that the interfacial zones of Fe/Al composite were composed of non-equilibrium intermetallic layers[$(Al_5Fe_2)_x$, $Al_{13}Fe_4m\;Fe_3Al$, FeAl]. The microvickers hardness of Fe/Al composite showed higher value than Fe/A356 composite in interface.