• Journal of the Korean Magnetics Society
• /
• v.16 no.6
• /
• pp.279-282
• /
• 2006

Magnetic tunnel junctions (MTJs), which consisted of amorphous ferromagnetic NiFeSiB free layers, were investigated. The NiFeSiB layers were used to substitute for the traditionally used CoFe and/or NiFe layers with the emphasis being given to obtaining an understanding of the effect of the amorphous free layer on the switching characteristics of the MTJs. $Ni_{16}Fe_{62}Si_{8}B_{14}$ has a lower saturation magnetization ($M_{s}:\;800\;emu/cm^{3}$) than $Co_{90}Fe_{10}$ and a higher anisotropy constant ($K_{u}:\;2700\;erg/cm^{3}$) than $Ni_{80}Fe_{20}$. The $Si/SiO_{2}/Ta$ 45/Ru 9.5/IrMn 10/CoFe $7/AlO_{x}/CoFeSiB\;(t)/Ru\;60\;(in\;nanometers)$structure was found to be beneficial for the switching characteristics of the MTJ, leading to a reduction in the coercivity ($H_{c}$) and an increase in the sensitivity resulted from its lower saturation magnetization and higher uniaxial anisotropy. Furthermore, by inserting a very thin CoFe layer at the tunnel barrier/NiFeSiB interface, the TMR ratio and switching squareness were improved more with the increase of NiFeSiB layer thickness up to 11 nm.

• Resources Recycling
• /
• v.20 no.5
• /
• pp.34-39
• /
• 2011

Metallurgical grade silicon(MG-Si) was melted with Ca at 1500$^{\circ}C$ under Ar atmosphere. The sample was cooled at 10 $^{\circ}C$/min to room temperature and leached in aqua regia. In the present study, the effect of Ca addition and conditions of acid leaching on removal of Fe and P in MG-Si were investigated. CaSi$_2$ phase was formed at the grain boundary of MG-Si melting with Ca. Also FeSi$_2$ phase was precipitated in CaSi$_2$ phase. By the formation of CaSi$_2$ phase, 97% of Fe and 66 % of P were removed from Ca added MG-Si with the particle size of 600~850${\mu}m$ by aqua regia(more than 30%) leaching.

• Applied Microscopy
• /
• v.25 no.3
• /
• pp.90-98
• /
• 1995

In the Fe-Si system, a mixture of a($Fe_{2}Si_5$) - and ${\epsilon}$(FeSi)-composition powders was sintered and heat-treated subsequently at various temperatures and time to get thermoelectric ${\beta}$-phase($FeSi_2$) compacts. The different transformational sequences depending on the heat treating temperature were found through the investigation into phase transformation and microstructural development. That is, a rapid eutectoid decomposition of ${\alpha}{\to}{\beta}+Si$ occurred together with a accompanying slow reaction between the dispersed Si formed by above decomposition and the preexisted ${\epsilon}$ phase at temperatures below $830^{\circ}C$. The unreacted Si and the micropores formed due to the density change upon the transformation coarsened as heat treating time elapsed. At temperatures above $880^{\circ}C$, however, transformation was proceeded by a peritectoid reaction of ${\alpha}+{\epsilon}{\to}{\beta}$. It took at least 200min. to achieve 90% volume fracion of transformed ${\beta}$ phase, and the growth of micro-pores was also observed in this transformational sequence with prolonged heat treating time.

• Journal of Korea Foundry Society
• /
• v.15 no.4
• /
• pp.397-407
• /
• 1995

The objectives of this study are first, to expand our understanding of relationship between magnetic properties and microstructural features such as grain size and texture, and second to reduce core loss of Fe-6.5%Si strip through optimizing heat treatment conditions. A rapid solidification technique, planar flow casting(PFC), was adopted to produce Fe-6.5%Si strips. The strips were heat treated under various conditions. The results show that heat treatment conditions can change not only grain size but also (200) texture formation on the strip surface. Variation in magnetic properties of Fe-6.5%Si strip is analyzed in terms of the change in grain size as well as (200) texture on the strip surface. The heat treatment conditions of $1100^{\circ}C$ over 2 hr or $1150^{\circ}C$ $1{\sim}2hr$ in $N_2+5%H_2$ appear to minimize core loss of Fe-6.5%Si strips.

• Journal of the Korean Magnetics Society
• /
• v.3 no.2
• /
• pp.130-134
• /
• 1993

The magnetic properties of the amorphous $Fe_{73.5-X}Co_{X}Cu_{1}Nb_{3}Si_{13.5}B_{9}(x=2,\;4)$ alloys, fabricated by a single roll rapid quenching technique and annealed at $400~650^{\circ}C$, have been investigated. The optimum annealing temperature is $550^{\circ}C$ for the amorphous $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ alloy. The properties of the nanocrystalline $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ alloy show the relative permeability of $1.1{\times}10^{4}$ and the coercive force of 0.22 Oe at 1 kHz. When annealed at $600^{\circ}C$, the nanocrystalline $Fe_{69.5}Co_{4}Cu_{1}Nb_{3}Si_{13.5)B_{9}$ alloy shows the relative permeability of $1.0{\times}10^{4}$ and the coercive force of 0.19 Oe at 1 kHz. From the X-ray measurement, it is found that the remarkably improved soft magnetic properties are the effect of the formation of $\alpha$-Fe(Si) grain. By the results of FMR exper-imeIlt, the optimum annealing condition is just below temperature which the peak-to-peak line width of FMR spectrum increase rapidly.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.40 no.7
• /
• pp.684-689
• /
• 1991

Magnetic properties of sintered Fe-Si-P alloys have been investigated as a function of sintering condition and composition. Sintering was carried in the temperature range from 1100ø C to 1400ø C in vacuum. As the sintering temperature increases, the magnetic properties of specimens were improved mainly due to the easy movement of domain wall because large pores and large grains were formed during the sintering process at high temperature. When sintered at 1400ø C, Fe-2w/o Si-0.5w/o P compact had the best mgnetic properties, but more phosphorus addition degraded magnetic properties. It appears that the degradation was caused by the formation of non-magnetic compounds such as Si P, Fe3P in the compacts with high phosphorus contents.

• Korean Journal of Metals and Materials
• /
• v.50 no.6
• /
• pp.455-462
• /
• 2012

Al-Si coated boron steel and Zn coated DP steel plates were laser-welded to manufacture a Tailor Welded Blank (TWB) for a car body frame. Hot-stamping heat treatment ($900^{\circ}C$, 5 min) was applied to the TWB weld, and the microstructural change and transformation mechanism were investigated in the Al-rich area near the bond line of the Al-Si coated steel side. There was Al-rich area with a single phase, $Fe_3(Al,Si)$, which was transformed to ${\alpha}-Fe$ (Ferrite) after the heat treatment. It could be explained that the $Fe_3(Al,Si)$ phase was transformed to ${\alpha}-Fe$ during heat treatment at $900^{\circ}C$ for 5 min and the resultant ${\alpha}-Fe$ phase was not transformed by rapid cooling. Before the heat treatment, the microstructures around the $Fe_3(Al,Si)$ phase consisted of martensite, bainite and ${\alpha}-Fe$ while they were transformed to martensite and ${\delta}-Fe$ after the heat treatment. Due to the heat treatment, Al was diffused to the $Fe_3(Al,Si)$ and this resulted in an increase of Al content to 0.7 wt% around the Al-rich area. If the weld was held at $900^{\circ}C$ for 5 min it was transformed to a mixture of austenite (${\gamma}$) and ${\delta}-Fe$, and only ${\gamma}$ was transformed to the martensite by water cooling while the ${\delta}-Fe$ was remained unchanged.

• Korean Journal of Materials Research
• /
• v.8 no.10
• /
• pp.969-974
• /
• 1998

The effect of vanadium, which is known to decrease the stacking fault energy of Fe-base alloys, on the microstructure and elevated temperature sliding wear resistance of Fe-20Cr- 1.7C- 1Si alloy was investigated. The maximum amount of vanadium maintaining the austenitic matrix seems to be about 3wt.% in Fe-20Cr- 1.7C-1Si-xV (x = 0, 1, 3, 6. lOwt.%) alloys and the austenitic alloys showed better wear resistance than ferritic alloys. It was considered to be due to the low stacking fault energy and $\gamma->\alpha$ strain-induced phase transformation at rmm temperature. It was shown from elevated temperature sliding tests up to .$225^{\circ}C$ that the addition of vanadium increases the temperature, at which the transition from oxidative wear to adhesive wear occur, and the amount of d formed at $225^{\circ}C$. Thus, it was considered that the addition of vanadium improves the elevated temperature sliding wear resistance of Fe-20Cr- 1.7C - 1Si by reducing the increasing rate of stacking fault energy with temperature and by increasing Ma temperature.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.2
• /
• pp.135-141
• /
• 2001

Arc-melted Ti-6Al-4V, Ti-4Fe and Ti-(1,2) Si alloys were oxidized at 700, 800, 900 and $1000^{\circ}C$ in air. The oxidation resistance of Ti-4Fe was comparable to that of Ti-6Al-4V, while the oxidation resistance of Ti-(1,2) Si was superior to that of Ti-6Al-4V. Ti-2Si displayed the best oxidation resistance among the four alloys, but failed after oxidation at $1000^{\circ}C$ for 17h. The oxide scale formed on Ti-6Al-4V, Ti-4Fe and Ti-(1,2)Si consisted of ($TiO_2$ and a small amount of $Al_2$$O_3$), ($TiO_2$ and a small amount of dissolved iron), and ($TiO_2$ plus a small concentration of amorphous $SiO_2$), respectively. The oxide grains of the surface scale of the four alloys were generally fine and round.

• Journal of Korea Foundry Society
• /
• v.5 no.3
• /
• pp.13-18
• /
• 1985

Decarburization phenomena were investigated at $800^{\circ}C$ by the $PH_2O/PH_2$ + Ar gas mixture in the case iron range which contains Si, Mn and Cr as an alloying elements. Dissociation of cementite in a matrix which contains graphitizer as Si begins at the carbon rich cementite dendrite arms. Several primary austenite $({\gamma})$ skeletons are surrounded by those nucleated graphite nodules, and that forms a limited area of nucleation region. Decarburization reactions at $800^{\circ}C$ in Fe-C, Fe-Mn-C and Fe-Cr-C alloy are followed by parabolic rate law under the gas mixture of $PH_2O/PH_2=0.01$ and the modified rate const. ${\kappa}$ were in the range of $1{\sim}6{\times}10^{-10}cm^2/s$.