• 한국정밀공학회지
• /
• 제18권1호
• /
• pp.129-138
• /
• 2001

This study examined the effects of the annealing heat treatments on the mechanical properties of the Invar(Fe-36%Ni Alloy) materials. Invar materials were annealed at various temperatures range 900~120$0^{\circ}C$ in vacuum(10-4Torr) and hydrogen atmospheres. And annealing conditions were changed by cooling rate and holding time at 110$0^{\circ}C$. The grain size of rolled Invar materials was very fine but those of annealed Invar materials at 900~120$0^{\circ}C$ in vacuum and hydrogen atmosphere increased with increasing annealing temperature. The micro-vickers hardness values of annealed Invar materials were decreased about 15% that of the rolled Invar materials, regardless of the various of annealing temperatures, atmosphere(vacuum, hydrogen) and annealing conditions. The tensile strength and yield strength of annealed Invar materials at 900~120$0^{\circ}C$ in vacuum and hydrogen atmosphere were decreased 10.0~14.4% and 34.6~39.1% those of the rolled Invar materials, respectively. The strength ratio(tensile strength/ yield strength) of annealed Invar materials was improved to 1.7~1.8 from the value of 1.2~1.3 of rolled Invar materials. The degree of spring back of annealed Invar materials was about 50% of the rolled Invar materials, regardless of the various of annealing temperatures, atmosphere(vacuum, hydrogen) and annealing conditions.

• 한국재료학회지
• /
• 제8권8호
• /
• pp.766-774
• /
• 1998

32$0^{\circ}C$, 40%NaOH 용액의 autoclave에서 약 300wppm의 탄소를 함유하고 있는 15Cr-9Fe-balanced Ni 합금 판상시편에 대해 응력부식 저항성을 조사하였다. 부식시편은 $700^{\circ}C$, 100시간 동안의 열처리로 합금내부에 석출될 수 있는 가능한 한 많은 양의 크롬계 탄화물을 석출시킨 후, 다시 재용해에 의해 크롬계 탄화물의 형태를 조절하는 $800^{\circ}C$-$950^{\circ}C$범위의 최종열처리를 시행하고 급냉시킨 다음 U-자형으로 응력을 가하여 준비되었다. 최종열처리 온도가 올라감에 따라 시편들의 입계응력부식균열(IGSCC ) 전파속도는 $900^{\circ}C$까지는 거의 직선적으로 증가하다가 $950^{\circ}C$에서는 $700^{\circ}C$에서 얻은 값보다도 더 낮게 감소하였다. 즉, 크롬계 탄화물이 재용해되어 그 밀도가 감소함에 따라 IGSCC저항성이 감소하다가 완전히 재용해된 $950^{\circ}C$ 열처리 조건에서 오히겨 가장 큰 IGSCC 저항성을 나타내었다. 이와같은 최조열처리 온도에 따른 니켈계 합금 600의 부식거동은 입계에 존재하는 크롬계탄화물의 형태변화 때문이 아니라 입계에서 탄소-크롬계 탄화물-크롬간의 상평형에 의해 이루어지는 탄소의 입계편석량이 크롬계탄화물이 존재할 때에는 열처리 온도에 따라 증가하다가 그것이 완전히 재용해 되었을 때 가장 낮아지기 때문인 것으로 생각된다.

• Corrosion Science and Technology
• /
• 제22권5호
• /
• pp.359-367
• /
• 2023

The localized corrosion resistance of the Ni-based Inconel 718 alloy after solution heat treatment was evaluated using electrochemical techniques in a solution of 25 wt% NaCl and 0.5 wt% acetic acid. Solution heat treatment at 1050 ℃ for 2.5 hours resulted in an increased average grain diameter. Both Ti carbides (10 ㎛ diameter) and Nb-Mo carbides (1 - 9 ㎛ diameter) were distributed throughout the material. Despite heat treatment, the shape and composition of these carbides remained consistent. An increase in solution temperature led to a decrease in pitting potential value. However, the pitting potential value of solution heat-treated Inconel 718 was consistently higher than that of as-received Inconel 718 at all tested temperatures. Localized corrosion initiation occurred at 0.4 V_SSE in a temperature environment of 80 ℃ for both as-received and solution heat-treated Inconel 718 alloys. X-ray photoelectron spectroscopic analysis indicated that the composition of the passive film formed on specimen surfaces remained largely unchanged after solution heat treatment, with O1s, Cr2p_3/2, Fe2p_3/2, and Ni2p_3/2 present. The difference in localized corrosion resistance between as-received and solution heat-treated Inconel 718 alloys was attributable to microstructural changes induced by the heat treatment process.

• 공업화학
• /
• 제27권1호
• /
• pp.21-25
• /
• 2016

리드프레임에 구리합금소재를 사용할 경우 구리이외의 고농도의 철, 니켈, 아연 등이 포함되며 여기서 발생되는 에칭폐액은 지정폐기물로 지정되어 있다. 따라서 본 연구에서는 전기도금용 산화구리(II)를 제조하기 위해 고농도 중금속을 함유한 리드프레임 에칭폐액의 맞춤형 정제과정을 설계하였다. 리드프레임 에칭폐액의 경우 중금속 함유량이 높아 이온교환수지법 단독으로는 중금속을 제거하는데 한계가 있었다. 따라서 본 연구에서는 물에 대한 용해도차를 이용한 환원-산화법을 연계하여 염화구리(I)을 제조한 후 산화제인 과황산나트륨을 이용하여 염화구리(II)로 재회수하는 방법을 사용하였다. 최적 환원제로는 하이드라진을 선택하였고, 최적 첨가량은 구리 1.0 mol당 1.4 mol이다. 환원-산화법과 이온교환수지법을 연결하여 중금속을 제거할 경우 3회 반복 시 $Fe^{3+}$ (4.3 ppm), $Ni^{2+}$ (2.4 ppm), $Zn^{2+}$ (0.78 ppm)로 전기도금용 산화구리(II) 제조용 원료로 사용이 가능할 것으로 사료된다.

• 한국산학기술학회논문지
• /
• 제17권9호
• /
• pp.718-723
• /
• 2016

중형 차량용 에어컨에 사용되는 스크롤 압축기는 토크변동이 적고 에너지 효율이 높으며, 소음이 적어 적용이 확대되어 가고 있다. 또한 경량화에 따라 압축기를 구성하는 주요부품이 스틸에서 알루미늄으로 변경하는 등 소재에 대한 연구가 활발히 이루어지고 있다. 또한 스크롤 압축기는 고정 스크롤과 선회 스크롤의 인벌루트 랩의 가공 정밀도가 $10{\mu}m$ 이하로 정밀도가 높은 전용장비와 전용 툴은 물론 숙련된 가공기술이 요구되므로 가공 품질을 확인하기 위하여 표면조도와 윤곽도를 측정하였으며, 알루미늄을 모재로하여 양극 산화 처리하여 사용되고 있는 선회스크롤의 경도를 향상시키기 위한 방법의 일환으로 봉공처리를 수행에 따른 특성들을 살펴보았다. 알루미늄 소재는 Al-Mg-Cu계 합금으로 미량의 Ni, Fe, Zn 이 부가된 것으로 나타났으며, 표면조도는 $3{\mu}m$이하로 가공 정밀도 기준 $10{\mu}m$를 만족하였다. 또한 양극산화 후 나노다이아몬드, CNT로 봉공처리 한 경우 경도는 450 이상으로 수봉공처리의 경우 보다 50% 이상 경도가 향상됨을 알 수 있었으며, 봉공재로 사용하기 위한 소재로서 탄소나노튜브나 나노다이아몬드는 큰 차이를 보이지 않았다.

• 한국분말재료학회지
• /
• 제9권6호
• /
• pp.394-408
• /
• 2002

Nanostructured high strength metastable Al-, Mg- and Ti-based alloys containing different amorphous, quasicrystalline and nanocrystalline phases are synthesized by non-equilibrium processing techniques. Such alloys can be prepared by quenching from the melt or by powder metallurgy techniques. This paper focuses on one hand on mechanically alloyed and ball milled powders containing different volume fractions of amorphous or nano-(quasi)crystalline phases, consolidated bulk specimens and, on the other hand. on cast specimens containing different constituent phases with different length-scale. As one example. $Mg_{55}Y_{15}Cu_{30}$- based metallic glass matrix composites are produced by mechanical alloying of elemental powder mixtures containing up to 30 vol.% $Y_2O_3$ particles. The comparison with the particle-free metallic glass reveals that the nanosized second phase oxide particles do not significantly affect the glass-forming ability upon mechanical alloying despite some limited particle dissolution. A supercooled liquid region with an extension of about 50 K can be maintained in the presence of the oxides. The distinct viscosity decrease in the supercooled liquid regime allows to consolidate the powders into bulk samples by uniaxial hot pressing. The $Y_2O_3$ additions increase the mechanical strength of the composites compared to the $Mg_{55}Y_{15}Cu_{30}$ metallic glass. The second example deals with Al-Mn-Ce and Al-Cu-Fe composites with quasicrystalline particles as reinforcements, which are prepared by quenching from the melt and by powder metallurgy. $Al_{98-x}Mn_xCe_2$ (x =5,6,7) melt-spun ribbons containing a major quasicrystalline phase coexisting with an Al-matrix on a nanometer scale are pulverized by ball milling. The powders are consolidated by hot extrusion. Grain growth during consolidation causes the formation of a micrometer-scale microstructure. Mechanical alloying of $Al_{63}Cu_{25}Fe_{12}$ leads to single-phase quasicrystalline powders. which are blended with different volume fractions of pure Al-powder and hot extruded forming $Al_{100-x}$$(Al_{0.63}Cu_{0.25}Fe_{0.12})_x$ (x = 40,50,60,80) micrometer-scale composites. Compression test data reveal a high yield strength of ${\sigma}_y{\geq}$700 MPa and a ductility of ${\varepsilon}_{pl}{\geq}$5% for than the Al-Mn-Ce bulk samples. The strength level of the Al-Cu-Fe alloys is ${\sigma}_y{\leq}$550 MPa significantly lower. By the addition of different amounts of aluminum, the mechanical properties can be tuned to a wide range. Finally, a bulk metallic glass-forming Ti-Cu-Ni-Sn alloy with in situ formed composite microstructure prepared by both centrifugal and injection casting presents more than 6% plastic strain under compressive stress at room temperature. The in situ formed composite contains dendritic hcp Ti solid solution precipitates and a few $Ti_3Sn,\;{\beta}$-(Cu, Sn) grains dispersed in a glassy matrix. The composite micro- structure can avoid the development of the highly localized shear bands typical for the room temperature defor-mation of monolithic glasses. Instead, widely developed shear bands with evident protuberance are observed. resulting in significant yielding and homogeneous plastic deformation over the entire sample.

• 한국수소및신에너지학회논문집
• /
• 제5권2호
• /
• pp.81-90
• /
• 1994

The hydrogen fuel tanks having hydrogen storing capacity of about 300g and 1200g are manufactured using $MmNi_{4.7}Al_{0.25}V_{0.05}Fe_{0.001}$ alloy. They are composed of several unit reactor made of Cu-tube(outer diameter = 50.1mm, thickness = 2mm). In order to increase the heat and mass transfer property of the hydride bed, Al-plates are inserted perpendicular to axial direction at intervals of 5mm and three arteries of diameter 8mm are installed symmetrically in each unit reactor. Hydrogen absorption is proceeded about 80% within 30 minute and is completed within 60 minute at the conditions of charging hydrogen pressure of 25atm and temperature of $22^{\circ}C$. On desorbing hydrogen at a constant rate of 30 slm at $20^{\circ}C$, discharging hydrogen pressure is sustained at 3~5atm for 120 minutes. The discharging pressure is increased upto 5~8atm as the increase of the reactor temperature to $30^{\circ}C$. From the experimental results and the brief discussions about the hydrogen absorption and disorption behaviors of the hydrogen storage tank, it is suggested that the behaviors of hydrogen charging and discharging could be controlled by adjusting the operating parameters and the reactor design parameters.

• 마이크로전자및패키징학회지
• /
• 제17권4호
• /
• pp.83-88
• /
• 2010

복합전기도금은 도금 중 반응성이 없는 물질을 첨가하여 도금층 내부에 함께 존재하도록 함으로써 이루어진다. 퍼멀로이는 철과 니켈의 합금을 말하는 것으로써 높은 투자율를 나타내기 때문에 산업 여러 분야에 응용된다. 복합도금을 통해 제품의 미세경도를 향상시킬 수 있으며 이는 제품의 수명과 연관된다. 하지만 실리카 나노분말 표면의 수산화기는 표면을 수분에 취약하게 만들고 이는 나노분말의 응집을 발생시켜 균일한 도금층의 형성을 어렵게 하는 요인이 된다. 본 연구에서는 실리카 나노분말의 응집을 줄이기 위하여 첨가제의 변화, 초음파 처리 시간의 변화를 살펴보았다. 초음파 처리시간의 증가시 입자의 분산효과가 좋았고 조성의 변화가 발생하였다. 첨가제에 따라 표면 형상과 공석되는 실리카 나노입자의 함량 차이가 나타났다. 염기성 도금용액에서 sodium lauryl sulfate를 사용하였을 경우 표면이 매끄럽고 공석되는 실리카 나노분말의 양도 높았다.

• 방사성폐기물학회지
• /
• 제3권1호
• /
• pp.31-40
• /
• 2005

발전소 내 방사화 부식생성물의 대부분을 차지하고 있는 니켈 페라이트계 부식생성물을 모사 발생시키기 위한 고온 고압용 장치를 제작하여 연구를 수행하였다. 배관형 포집기를 이용한 부식생성물 발생장치로부터 방사화 부식생성물과 가장 유사한 부식생성물을 얻을 수 있었다. 발전소에서 입자성 부식생성물이 발생되는 원리인 온도에 따른 용해도 차이를 구현하기 위하여 270$\^{circ}$C에서 부식반응이 일어나 상대적으로 높은 온도를 가진 포집용 장치에 부식생성물이 포집되도록 장치를 제작하였으며 , 발생된 부식생성물은 주사전자현미경 관찰과 EDAX를 통한 조성분석으로 그 특성을 관찰하였다. 부식생성물은 포집 된 위치 에 따라서 침상 형태의 산화물과 결정 형태의 산화물로 나뉘었으며, 조성 분석 결과 결정 형태의 부식생성물이 니켈 페라이트로서 발전소에서 발생되는 입자성 부식생성물과 유사한 것을 알 수 있었다.

• 한국분말재료학회지
• /
• 제22권3호
• /
• pp.197-202
• /
• 2015

In this study, porous stainless steel (STS316L) sintered body was fabricated by powder metallurgy method and its properties such as porosity, compressive yield strength, hardness, and permeability were evaluated. 67.5Fe-17Cr- 13Ni-2.5Mo (wt%) powder was produced by a water atomization. The atomized powder was classified into size with under $45{\mu}m$ and over $180{\mu}m$, and then they were compacted with various pressures and sintered at $1210^{\circ}C$ for 1 h in a vacuum atmosphere. The porosities of sintered bodies could be obtained in range of 20~53% by controlling the compaction pressure. Compressive yield strength and hardness were achieved up to 268 MPa and 94 Shore D, respectively. Air permeability was obtained up to $79l/min{\cdot}cm^2$. As a result, mechanical properties and air permeability of the optimized porous body having a porosity of 25~40% were very superior to that of Al alloy.