• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2007년도 동계학술연구발표회 및 스핀트로닉스와 나노물리에관한 국제심포지움
• /
• pp.220-221
• /
• 2007

• 한국재료학회지
• /
• 제22권1호
• /
• pp.46-53
• /
• 2012

In this study, mechanical tests and microstructural analyses including TEM analyses with EDX of precipitates in modified 9Cr-1Mo steel were carried out to determine the cause of embrittlement observed after heat-treatment, which limits the usage of the alloy for power plants. Mod. 9Cr-1Mo steel specimens at austenite temperature were quenched to the molten salt baths at $760^{\circ}C$ and $700^{\circ}C$, in which the specimens were kept for 10 min ~ 10 hr with subsequent air-cooling. Impact tests showed that the impact value dropped abruptly when the specimens were kept longer than 30 min at $\sim760^{\circ}C$ reaching to minima in about 1 hr, and then increasing at further retention. The tensile strength of the specimens reached the minimum value without much change afterward, whereas the values of elongation showed the same trend as that of the impact value. The isothermally heat-treated steel at $700^{\circ}C$ also showed a minimum impact value in about 1 hr. These results suggest that the isothermal heattreatment at 760 and $700^{\circ}C$ for about 1 hr induces temporal embrittlement in Mod. 9Cr-1Mo steel. The microstructural examination of all the specimens with extraction replica of the carbides revealed that the specimens with temporal embrittlement had $Cr_2C$, indicating that the cause of the embrittlement was the precipitation of the $Cr_2C$. In addition, TEM/EDX results showed that the Fe/Cr ratio was 0.033 to 0.055 for $Cr_2C$, whereas it was 0.48 to 0.75 for $Cr_{23}C_6$, making the distinction of the $Cr_2C$ and $Cr_{23}C_6$ possible even without direct electron diffraction analyses.

• The Korean Journal of Ecology
• /
• 제20권5호
• /
• pp.385-391
• /
• 1997

충남 광천과 홍성 일대의 사문암과 변성암 지역의 암석, 토양 및 출현빈도가 높은 대나물의 중금속 함량을 측정하여 사문암 토양의 독성화 정도와 식물체의 흡수관계를 조사하였다. Ni, Cr 및 Co는 사문암에 매우 높았으며 Zn, Sc, Mo 및 Fe 는 변성암에서 더 높았다. 사문암 풍화토에서는 Ni, Cr 및 Co가 높았으며 Zn과 Fe는 비사문암 풍화토(사문암 및 변성암 풍화토와 변성암 풍화토)에서 높았고, 토양의 중금속은 암석내의 함량보다 낮았다. 사문암 풍화토에 출현하는 대나물내 중금속 함량은 혼합 풍화토의 그것보다 높게 나타났으며, 같은 사문암 지역이라도 홍성보다 광천의 중금속 함량이 높았다. 대나물의 평균 Fe:Ni의 비율은 혼합 풍화토에서는 216이고 사문암 풍화토에서는 49였다. 대나물내 Ni, Cr, Co, Fe 및 Sc 등은 지상부보다 지하부에서 높았으며, Zn과 Mo 함량은 지상부에서 높았다. 암석과 식물체의 중금속 함량 비교 결과 식물체에서보다 암석의 중금속 함량이 높았고, 대나물에 의한 Zn의 흡수는 사문암과 변성암 지역에서 높았으며 Sc와 Fe는 사문암 지역에서 뚜렷이 높았다.

• Corrosion Science and Technology
• /
• 제2권1호
• /
• pp.18-25
• /
• 2003

Effects of the precipitation of $\sigma$ phase on the metastable pitting as a precursor of stable pitting corrosion and also on the progress of stale pitting of the 25Cr-7Ni-3Mo-0.25N duplex stainless steel were investigated in chloride solution. Electrochemical potential and current noises of the alloy were measured in 10 % ferric chloride solution ($FeCl_3$) with zero resistance ammeter (ZRA), and then analyzed by power spectral density (PSD) and by corrosion admittance ($A_c$) spectrum. With aging at $850^{\circ}C$, the passive film of the alloy was found to get significantly unstable as represented by power spectral density (PSD) and a transition from metastable pitting state to stable one was observed. In the corrosion admittance spectrum, the number of negative $A_c$ corresponding to the state of localized corrosion increased with aging, suggesting that the precipitation of $\sigma$ phase considerably degraded the passive film by depleting Cr and Mo around it at $\alpha/\sigma$ or $\gamma/\sigma$ phase boundaries, thereby leading to the initiation of the pitting corrosion. However, the Cr and Mo at $\alpha/\sigma$ or $\gamma/\sigma$ phase boundaries which were once depleted due to the precipitation of the $\sigma$ phase were partly replenished by the diffusion of Cr and Mo from the surrounding matrix with aging time longer. The initiation of pitting seems to be associated with the precipitation density of the $\sigma$ phase with an effective size needed to induce the sufficient depletion of Cr and Mo around it.

• 자원환경지질
• /
• 제24권3호
• /
• pp.245-260
• /
• 1991

Surficial dispersion patterns of heavy metals and toxic elements (U, Mo, Cu, Zn, Fe, Mn, Co, Cr, V, Ni, Pb, and Cd) were investigated in the Dukpyungri, Goesan area covered with low grade uranium-bearing black shales. Maximum abundance of U in the black shale was 455ppm. Radioactivity was counted at a maximum of 7cps in black shales, and was less than 0.5cps in shales, slates, and oil shales of the control areas. Enrichment of Mo, V, Cu, Zn, Cd, and Pb in black shales is particularly characteristic compared with shales, slates, and oil shales of the control areas, whereas contents of Mn, Cr, Co, and Th in all rock samples tend to be almost similar. Residual top soils (0~15cm depth) over black shales show high contents of Mo, Cu, Zn, Ni, Cd, and V in comparison with the control areas. Contents of trace elements in subsoils (15~30cm depth) were higher about one and half times than those in topsoils. Average contents of Mo, Cu, Pb, Zn, Cd and V in garden soil and playground soil of an elementary school in Dukpyungri, Goesan area, were high about two to fifteen times compared with the control areas. Contents of trace elements in stream sediments were higher from two to eight times than those in residual soils. Sodium, AI, K, V, Cr, and Fe were more enriched in the roots of pine than in the twigs of pine. Contents of Li, AI, V, Ni, Cd, Fe, and Co were higher in the roots of azalea than in the twigs of azalea. Enrichment of P, Ca, and Mg was remarkable in the twigs of both pine and azalea. Biological absorption coefficients for essential elements (Zn, P, Mn, Ca and K)tend to be high, whereas those for the non-essential elements.(Ba, Ti, V, and Mo) and toxic elements(Cr, Co, Pb and Ni) be low. Less mobile elements (Pd, Cd, and Co) tend to show anomalies with higher contrast than more mobile elements(Mo, V, Zn, Cu and Ni) in the area covered with black shales.

• 한국주조공학회지
• /
• 제20권4호
• /
• pp.260-268
• /
• 2000

응고 및 마모거동을 연구하기 위하여 Cr, V, Mo 및 W의 조성이 다른 3종류의 백주철을 주조하였다. 고주파유도용해로에서 장입시켜 1873K까지 승온시켜 장입원료들을 모두 용해시킨 후 1823K에서 Y블럭주형에 주입하였다. 얻어진 3종류의 백주철조성은 다음과 같다: Fe-3%C-10%Cr-5%Mo-5%W(합금1), Fe-3%C-10%V-5%Mo-5%W(합금2) 및 Fe-3%C-17%Cr-3%V(합금 3)응고과정을 추적하기 위하여 각 시편으로부터 50g을 채취한 후 알루미나도가니에 넣고 실리콘카바이드로를 사용하여 1723K의 알콘분위기하에서 재용해를 시켰다. 용금을 10K/분의 속도로 냉각시키면서 열분석을 행하였으며 도중 몇 차례 소입 실험을 병행하였다.합금1의 경우 초정오스테나이트, (오스테나이트+$M_7C_3$)공정, (오스테나이트+$M_6C$)공정, 합금2의 경우 초정 MC, 초정오스테나이트, (오스테나이트+MC)공정 , (오스테나이트+$M_2C$)공정, 합금3의 경우 초정 $M7C_3$와 (오스테나이트+$M_7C_3$)공정으로 구성되어 있었다. 주방상태, 균질화열처러상태, 공냉상태, 템퍼링상태에서 내마모시험을 행하였다. 먼저 주방상태시 편을 진공분위기하에서 1223K에서 5시간동안 균질화열처리를 행한후 로냉을 시켰다. 다시 이 시편을 1323K에서 2시간 유지후 강제공냉을 시켰으며 강제공냉된 시편을 573K에서 3시간동안 템퍼링처리를 하였다. 내마모시험은 120 mesh마모지에 10N의 하중을 가하여 실시하였다. 각 사이클마다 무게감소를 측정하였으며 8번 반복실험을 하였다. 마모량은 균질화열처리시편, 주방상태시편, 템퍼링시편, 공냉시편의 순으로 감소하였다. 합금2가 마모량이 가장 적었으며 합금3이 가장 많았다. 합금2의 마모량이 가장 적은 이유는 조직이 초정 MC, 공정 MC 및 공정 M2C로 구성되어 있기 때문으로 사료된다.주방상태에서 기지조직은 퍼얼라이트이었으나 열처리를 통하여 마르텐사이트, 템퍼드마르텐사이트, 잔류오스테나이트로 변태하였다. 이상의 결과를 종합해 보면 MC가 내마모성에 가장 기여하는 조직으로 판단되어진다.

• 분석과학
• /
• 제17권5호
• /
• pp.416-422
• /
• 2004

시간분해 레이저 유도 파열 분광분석 (TRELIBS) 시스템을 구성하여 원자력발전소 계통재질의 성분을 정성 분석하는 데 응용하였다. 본 연구에서는 탄소강 (A106 Gr. B, A336 P11, A335 P22), 스텐인레스강 (type 304, type 316) 및 인코넬 계열 합금(인코넬 600, 인코넬 690, 인코넬 800) 시료를 사용하였다. 탄소강의 종류는 485~575 nm 파장영역에서 나타난 Cr/Fe과 Mo/Fe의 TRELIBS 피크 비에 의해서 서로 구분 가능하였다. type 304와 type 316 스텐인레스강은 485~575 nm 파장영역에서 나타나는 Mo의 TRELIBS 피크 존재 여부에 의해서 쉽게 구분 가능하였다: type 304는 어떤 Mo의 피크도 나타내지 않지만, type 316은 Mo의 피크를 보여준다. 인코넬 계열 합금강 종류는 420~510 nm 파장영역에서 나타난 Cr/Fe과 Ni/Fe의 TRELIBS 피크비에 의해서 서로 구분 가능하였다. TRELIBS는 시료의 전처리 없이 빠르고 쉽게 합금을 분석할 수 있는 효과적인 분석 기술임이 입증되었다.

• 공업화학
• /
• 제9권7호
• /
• pp.1023-1029
• /
• 1998

5Cr-1Mo steel을 이용하여 나트륨 분위기에서 미량 물 누출 실험을 수행하였다. 시편에서 미량 물 누출로 인한 누출경로의 완전 re-open time은 129분으로 나타났고, 그 크기는 직경 2mm를 나타냈다. 누출경로는 re-open되기 전에 누출부위를 중심으로 halos현상을 형성하였으며, halos의 크기와 실제 re-open크기와는 다르게 나타났다. 나트륨-물 반응으로 인한 재질의 부식은 나트륨부위로부터 시작되었으며, steam 부위에서는 부식이 발생하지 않았다. 시편 누출부위를 AES로 분석한 결과 Cr의 segregation이 가장 많이 나타났으며, SEM과 EPMA 관찰로부터 나트륨화합물들이 누출부위 주변에 대량 침적되어 있는 것이 관찰되어 나트륨 철 크롬혼합물 형태로 부식생성물들이 혼재되어 있는 것으로 예측되었다.

• 대한치과기공학회지
• /
• 제37권1호
• /
• pp.23-29
• /
• 2015

Purpose: The selective laser melting (SLM) process for dentistry, which is one of the additive manufacturing technologies (AM) allows for rapid production of a three-dimensional model with complex shape by directly melting metal powder. This process generates detailed items of a three-dimensional model shape through consolidation of a thin powder layer by utilizing both selective melting and laser beam simultaneously. In regard to SLM process, Fe-base powder, Ti-6AI-4V powder, AI-base powder, etc. have been researched. It is believed that the aforementioned technologies will be widely utilized in manufacturing metal parts using metal powder of raw material. This study chose Ni-Cr-Mo metal powder in order to manufacture metal powder materials that would be used in the selective laser melting for dentistry. Methods: This study manufactured metal powder using mechanical alloying technique (MA) among those metal powder manufacturing techniques. Moreover, this study aimed to utilize the metal powder manufactured after observing the characteristics of powder as preliminary data of Ni-Cr-Mo metal powder. This study could obtain the following conclusions within the experimental limitations. Results: As a result of mechanically alloying Ni-Cr-Mo powder over time, its mean particle size was $66.93{\mu}m$ $54.4{\mu}m$ and $45.39{\mu}m$ at 10h, 20h and 30h, respectively. The gtain form of metal powder by mechanical alloying technique was a sponge-like shape of irregular plate; however, the gtain form manufactured by high-pressure water aromization process had the following three types: globular type, chain type and oval type. Conclusion: This study found $37.65{\mu}m$ as the mean particle size of Ni-Cr-Mo metal powder, which was manufactured using water atomization technique under the following conditions: water atomization flux of 300 liter/min, hydraulic pressure of $400kgf/cm^2$ and injection angle of $45^{\circ}$. This study confirmed that the grain form of powder (solid particle form) would vary depending on the manufacturing process.

• 한국재료학회지
• /
• 제8권10호
• /
• pp.969-974
• /
• 1998

Fe 계 합금의 적층결함에너지를 감소시키는 거승로 알려진 vanadium이 Fe-20Cr-1.7C-1Si합금의 미세조직과 고온 마모저항성에 미치는 영향에 대하여 조사하였다. Fe-20Cr-1.7C-1Si-xV (x=0, 1, 3, 6, 10wt.%)조성에서 오스테나이트 기지상을 유지하면서 첨기될 수 있는 V의 최대 첨가량은 약 3wt.%이었으며 오스테나이트 기지상을 갖는 합금은 상온에서 낮은 적층결함에너지와 $\gamma->\alpha$ 변형유기 상변태에 의해 페라이트 합금보다 높은 마모저항성을 보인 것으로 생각된다.$225^{\circ}C$에서 $\alpha$ 생성량도 많은 것으로 보다 V은 Fe-20Cr-1.7C-1Si 합금의 온도에 따른 적층결함에너지 증가율를 억제하고 Md온도도 증가시킴으로써 고온 마모저항성을 증가시키는 것으로 생각된다.