• Journal of the Korean Magnetics Society
• /
• v.10 no.6
• /
• pp.269-273
• /
• 2000

Fe-l7Cr-2M(M=Si, Nb, Mo) alloy powder was prepared by plasma electrode rotating atomizer and than the alloy powder was formed and sintered. The particle shape of the Fe-l7Cr-2M(M=Si, Nb, Mo) alloy power is spherical. The saturation magnetization of the sintered Fe-17Cr-2Mo and Fe-l7Cr-2Nb alloy are 155 emu/g. The saturation magnetization of the sintered Fe-l7Cr-2Si alloy is less than that of the sintered Fe-l7Cr-2Mo and Fe-l7Cr-2Nb alloy. The amplitude relative permeability of the sintered Fe-l7Cr-2M(M=Si, Nb, Mo) alloy has the maximum value in the range of 3∼5 Oe applied field at forming pressure 12 ton/cm$^2$, sintering temperature 1200$^{\circ}C$, and frequency 1 kHz. Power loss of the sintered Fe-l7Cr-2Nb alloy is 40 mW/cc at applied field, H$\sub$a/=5 Oe, and frequency, f=1 kHz. The power loss of the sintered Fe-l7Cr-2Nb alloy is a half of that of the sintered Fe-l7Cr-2Si and Fe-l7Cr-2Mo alloy.

• Journal of Powder Materials
• /
• v.12 no.1
• /
• pp.43-50
• /
• 2005

Mechanical alloying using high-energy ball mill and subsequent spark plasma sintering (SPS) process was applied to Al-Fe-Cr and Al-Fe-Mo powder mixture to investigate effects of Cr and Mo addition on thermal stability of Al-Fe, and thereby to enhance its thermal stability up to $500^{\circC}$. Various analytical techniques including micro-Vickers hardness test, SEM, TEM, X-ray diffractometry and corrosion test were carried out. It was found that addition of Cr and Mo to Al-Fe system played a role of grain growth inhibitor of matrix Al and some precipitates such as $Al_3Fe$ during SPS and subsequent heat treatment. The inhibition of grain growth resulted in increased Vickers hardness and thermal stability up to $500^{\circC}$ comparing to those of Al-Fe alloy system.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.6
• /
• pp.354-359
• /
• 2018

NaCl-induced hot corrosion behavior of ASTM T22 (Fe-2.25Cr-1Mo), T91 (Fe-9Cr-1Mo), T92 (Fe-9Cr-1.8W-0.5Mo), 347HFG (Fe-18-Cr-11Ni), and 310H (Fe-25Cr-19Ni) steels was studied after spraying NaCl on the surface. During corrosion at $600-800^{\circ}C$ for 50-100 h, thick, non-adherent, fragile, somewhat porous oxide scales formed. All the alloys corroded fast with large weight gains owing to fast scaling and destruction of protective oxide scales. Corrosion rates increased progressively as the corrosion temperature and time increased. Corrosion resistance increased in the order of T22, T91, T92, 347HFG, and 310H, suggesting that the alloying elements of Cr, Ni, and W beneficially improved the corrosion resistance of steels. Basically, Fe oxidized to $Fe_2O_3$, and Cr oxidized to $Cr_2O_3$, some of which further reacted with FeO to form $FeCr_2O_4$ or with NiO to form $NiCr_2O_4$.

• Korean Journal of Materials Research
• /
• v.12 no.11
• /
• pp.845-849
• /
• 2002

Alloys of $Fe_3$Al, $Fe_3$Al-6Cr, $Fe_3$Al-4Cr-1Mo, $Ni_3$Al, and $Ni_3$Al-2.8Cr were oxidized at $1000^{\circ}C$ in air, and the oxide scales formed were studied using XRD. SEM, EPMA, and TEM. The oxide scales that formed on $Fe_3$Al-based alloys consisted primarily of $\alpha$-$Al_2$$O_3$ containing a small amount of dissolved Fe and Cr ions, whereas those that formed on $Ni_3$Al-based alloys consisted primarily of $\alpha$-$Al_2$$O_3$, together with a small amount of $NiAl_2$$O_4$, NiO and dissolved Cr ions. For the entire alloys tested, nonadherent oxide scales formed, and voids were inevitably existed at the scale-matrix interface.

• Korean Journal of Materials Research
• /
• v.10 no.2
• /
• pp.144-147
• /
• 2000

10%C-5%Mo-5%W-10%Cr 및 10%C-5%Mo-5%W-10%V 백주철의 응고거동을 열분석을 통하여 연구하였다. 15Kg 용량의 고주파 유도옹해로에 선철, 고철, Fe-Mo, Fe-W, Fe-Cr, Fe-V 등을 장입시켜 용해시킨 후 슬래그를 제거시키고 $1550^{\circ}C$에서 Y블럭의 펩 주형에 주입하였다. 응고거동을 조사하기 위하여 50g을 Y블럭에서 채취한 뒤 알루미나 도가니에 넣어 재용해시킨 후 1$0^{\circ}C$/min의 냉각속도로 냉각시키면서 여섯 종류의 다른 온도에서 도중에 급냉시켜 응고조직을 광학현미경으로 관찰하였다. 10%C-5%Mo-5%W-10%Cr 백주철의 경우 초정 오스테나이트, 오스테나이트와 M(sub)7C(sob)3의 공정, 오스테나이트와 M(sub)6C의 공정으로, 10%C-5%Mo-5%W-10%V 백주철의 경우 초정 MC, 오스테나이트와 MC의 공정, 오스테나이트와 M(sub)2C의 공정으로 각각 순차적으로 정출하였다. 정출하였다.

• Corrosion Science and Technology
• /
• v.2 no.1
• /
• pp.12-17
• /
• 2003

The effects of Cr content and film formation potential on electronic behaviors of the passive film on Fe-Cr alloys were investigated in borate buffer solution. Influence of pH on passive films of both Fe-Cr and Fe-Cr-Mo alloys was also investigated. Mott-Schottky and cyclic voltammetry techniques were used to elucidate electronic behaviors of passive films and their electrochemical characteristics. AES analysis of passive films was carried out. Results showed that doping density decreased as Cr content and film formation potentials increased. The addition of Mo to Fe-Cr alloy had little influence on donor densities in pH 9.2 solution but some effects on the decrease in donor densities in pH 1.6 acidic solution.

• Korean Journal of Materials Research
• /
• v.14 no.1
• /
• pp.52-58
• /
• 2004

The surface property and formation behavior of a boride layer formed on Ni-Cr-Mo steel in a plasma paste boronizing treatment were investigated. The plasma paste boronizing treatment was carried out at 973～1273 K for 1-7 hrs under the gas ratio of Ar:H$_2$ (2:1). The thickness of the boride layer increased with increasing temperature and time in the boronizing treatment. The cross-section of the boride layer was a tooth structure and the hardness was Hv 2000～2500. XRD analysis revealed that the compound was identified as FeB, $Fe_2$B, and mixed phase of FeB/$Fe_2$B in the boride layer formed at 973～1073 K, 1173K, and 1273K, respectively. The Ni-Cr-Mo alloy boronized at 1173-1273 K showed the best excellent wear resistance against the sand. As a results of corrosion test in 1 M $H_2$$SO_4$ solution, $Fe_2$B formed on the matrix alloy exhibited higher corrosion resistance than FeB.

• Journal of the Korean Magnetics Society
• /
• v.1 no.2
• /
• pp.37-41
• /
• 1991

Amorphous $Fe_{68.5}Co_5M_3Cu_1Si_{13.5}B_9(M=Nb, Mo, Mn, Cr)$ alloys were prepared by using rapidly quenching techinque and were annealed above their crystallization temperatures. Coercive force, initial permeability and AC power loss of the annealed $Fe_{68.5}Co_5M_3Cu_1Si_{13.5}B_9(M=Nb, Mo, Mn, Cr)$ alloys have been studied systematically. Nanocrystallines are formed in the annealed alloys which include Mo and Nb. Remarkably improved soft magnetic properties are obtained in the alloys whose average grain size is around 10 nm. However, soft magnetic properties of the alloys are degraded when grain size is less than IOnm or larger than 15nm. It is considered that the degradation of soft magnetic properties in the alloys whose average grain size is less than 10 nm is due to the Fe-rich amorphous phase retained at grain boundary during the initial crystallization process.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.77-77
• /
• 2002

• Journal of Powder Materials
• /
• v.20 no.1
• /
• pp.7-12
• /
• 2013

The effect of particle size distribution on green and sintered properties of Fe-Cr-Mo prealloy powder was investigated in this study. For the study, prealloyed Fe-Cr-Mo powders with different particle sizes were mixed as various ratios and cold compacted at various pressure and sintered at $1250^{\circ}C$ for 30 min, $90%N_2+10%H_2$ atmosphere in the continuous sintering furnace. The results shows that the powders with large particle size distribution have high compressibility and low ejection force. However the green strength are much less than those with small particle size distribution. Tensile prperties of the sintered specimes with large particles size also have high strength and elongation.