• Journal of the Korean Magnetics Society
• /
• v.6 no.4
• /
• pp.211-217
• /
• 1996

The effects of Al addition to Fe-B-Nb-Cu alloy for improving the high-frequency magnetic properties and the magnetic properties of ultrathin $Fe_{78}Al_{4}Nb_{5}B_{12}Cu_{1}$ nanocrystalline alloy ribbons with the thickness less than $10\;\mu\textrm{m}$ were investigated. It was found that the effective permeability at frequencies over- 100 kHz was very high and the core loss was very low for the composition $Fe_{78}Al_{4}Nb_{5}B_{12}Cu_{1}$ alloy. Moreover, the reduction of the ribbon thickness below $10\;\mu\textrm{m}$ was very effective in improving their permeability and the core loss characteristics up to the MHz frequency range. The values of effective permeability at 1 MHz and core loss at 0.2 T, 1 MHz were 5,000 and 1.4 kW/kg, respectively. It was considered that these results were due to far refined $\alpha-Fe$ phase structure with grain size less than 10 nm and domain structure modification.

• Korean Journal of Materials Research
• /
• v.24 no.8
• /
• pp.393-400
• /
• 2014

NiO catalysts were successfully coated onto FeCrAl metal alloy foam as a catalyst support via a dip-coating method. To demonstrate the optimum amount of NiO catalyst on the FeCrAl metal alloy foam, the molar concentration of the Ni precursor in a coating solution was controlled, with five different amounts of 0.4 M, 0.6 M, 0.8 M, 1.0 M, and 1.2 M for a dip-coating process. The structural, morphological, and chemical bonding properties of the NiO-catalyst-coated FeCrAl metal alloy foam samples were assessed by means of field-emission scanning electron microscopy(FESEM), scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS), X-ray diffraction(XRD), and X-ray photoelectron spectroscopy(XPS). In particular, when the FeCrAl metal alloy foam samples were coated using a coating solution with a 0.8 M Ni precursor, well-dispersed NiO catalysts on the FeCrAl metal alloy foam compared to the other samples were confirmed. Also, the XPS results exhibited the chemical bonding states of the NiO phases and the FeCrAl metal alloy foam. The results showed that a dip-coating method is one of best ways to coat well-dispersed NiO catalysts onto FeCrAl metal alloy foam.

• Journal of Magnetics
• /
• v.6 no.3
• /
• pp.94-100
• /
• 2001

Fe-Co-Ni particles with an average size of 45 and 135 nm are characterized in terms of magnetic phase transformation and magnetic properties at room temperature. BCC structure of Fe-Co-Ni spherical particles can be synthesized from Fe-Co-Ni-Al-Cu precursor films by heating at 600-80$0^{\circ}C$ for the phase separation of Fe-Co rich Fe-Co-Ni particles, followed by a post heating at $600^{\circ}C$ for 5 hours. The average size of nanoparticles was directly determined by the thickness of precursor films. Exchange interactive hysteresis was observed for the nano-composite (Fe-Co-Ni)+(Fe-Ni-Al) films resulting from the short exchange interface between ferromagnetic Fe-Co-Ni particles surrounded by almost papramagnetic Ni-Al-Fe matrix. Arraying the isolated Fe-Co-Ni nano-particles in a random arrangement on $Al_2O_3$substrate the particle assembly showed a behavior of dipole interactive ferromagnetic clusters depending on their volume and inter-particle distance.

• Applied Microscopy
• /
• v.44 no.4
• /
• pp.144-149
• /
• 2014

A strategy for phase identification of precipitates in high Al-containing austenitic and ferritic steels using electron diffraction (ED) is studied. Comparative studies of the various Al-containing precipitates (k-carbide, $Ni_3Al$, $Fe_3Al$, FeAl) show the similarities of crystal structure and lattice parameter. However, the slight differences of lattice parameter and structure display characteristic ED patterns (EDPs) which can be identified. $L1_2$ k-carbide and $Ni_3Al$ can be differentiated by the length of ${\rightarrow}_g$ (the reciprocal lattice vector), even though they show perfectly identical shapes of EDPs. $DO_3$ $Fe_3Al$ and $B_2$ FeAl show the characteristic EDs in [110] and [112] beam directions due to the differences of Fe site occupancies in unit cells. k-carbide, $Ni_3Al$, and FeAl show also the similar EDs in [112], [112], and [110] beam directions, respectively. All the possible similarities of EDs among each phases and the strategy for phase identification are discussed on the bases of kinematical ED simulation.

• Korean Journal of Metals and Materials
• /
• v.50 no.6
• /
• pp.449-454
• /
• 2012

Nanopowder of FeAl and $Al_2O_3$ was synthesized from FeO and Al powders by high energy ball milling. Using the pulsed current activated sintering method, the nanocystalline $Al_2O_3$ reinforced FeAl composite was consolidated within two minutes from mechanically synthesized powders. The advantage of this process is that it allows very quick densification to near theoretical density and prohibits grain growth in nanostuctured materials. The grain size, sintering behavior and hardness of sintered $FeAl-Al_2O_3$ composite were investigated.

• Journal of the Korean Magnetics Society
• /
• v.8 no.6
• /
• pp.362-368
• /
• 1998

The magnetic properties, thermal stability and anti-corrosion properties of $Cr_86Al_14$ spin valves multilayers were studied. It was found that the magnetic properties of $Cr_86Al_14$ spin valves depend on the thickness of antiferromagnetic, ferromagnetic and non-ferromagnetic layers. Exchange coupled field ($H_{ex}$) and magnetoresistance ratio (%) showed the largest value of 20 Oe, 2 % in $glass/Cr_{86}Al_{14}(600 $\AA$)/Ni_{81}Fe_{19}(50$\AA$)/Cu(40 $\AA$)/Ni_{81}Fe_{19}(40 $\AA$)$ spin valves. The $H_{ex}$ MR ratios (%) of CrAl and FeMn spin valves were decreased with increasing annealing temperatures and were lost at 150 $^{\circ}C$, 250 $^{\circ}C$ respectively. Based on these result, it was elucidated that CrAl is more thermally stable than FeMn. It was also shown that there was no change of $H_{ex}$ MR ratios in CrAl, while FeMn was changed and lost 15 days later in corrosion resistance test under 35 $^{\circ}C$, 90 % humidity condition. FeMn was found to be pitted and peeled off 15 days later by SEM micrographic analysis.

• Journal of Korea Foundry Society
• /
• v.41 no.1
• /
• pp.3-10
• /
• 2021

In the compound casting between the aluminum alloy and the cast iron, the iron component may be dissolved from the cast iron during the process and mixed into the aluminum melt, thereby forming various iron-containing intermetallic compounds and significantly deteriorating the tensile properties of the aluminum alloy. On the other hand, unlike Fe, which is added as an impurity, Cu is added to improve the mechanical properties of the aluminum alloy. In this study, the change in microstructure and tensile properties of aluminum alloys due to the addition of Fe and Cu was investigated. A large amount of iron-containing compounds such as coarse Al₅FeSi phases were formed when the iron content was 1% or more, and the tensile properties were significantly reduced. In the case of the aluminum alloy to which Cu was added, an Al₂Cu phase was additionally formed and the tensile strength was clearly improved.

• Korean Journal of Materials Research
• /
• v.9 no.4
• /
• pp.345-348
• /
• 1999

The properties of Fe ions in the $ CdFe_2$$O_4$ and $CdFeAlO_4$ were investigated using the Mossbauer spectroscopy, in the temperature range from 300K to 900K. The calculated Debye temperature, recoil free fraction, mean square displacement and velocity are, 476.5K, 0.835, 3.39$\times$10\ulcorner$\textrm{cm}^2$, and 1.11$\times$10\ulcorner$\textrm{cm}^2$sec$^2$for Fe ions in the $CdFe_2$$O_4$ and 369.0K, 0.741, 5.65$\times$10\ulcorner$\textrm{cm}^2$ and 1.33$\times$10\ulcorner$\textrm{cm}^2$/$sec^2$in the $CeFeAlO_4$. The difference of the properties in the two samples were explained by the variation of the Fe\ulcorner-O\ulcorner bonding length with the substituted Al ions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.108-110
• /
• 2000

The aim of this paper is to investigate the effect of Al and Ti on microstructure of Fe-Cr-Al alloy systems for applying electrical resistance wires of electrical furnace. From the preliminary study, the amount of recovered addition elements increased in the case of both vacuum and Ar-atmosphere melting than that in the case of air-atmosphere melting. Also, optimum Cr content for good performance at high temperature was approximately 24wt% from the observation of microstucture. The precipitates of Fe-Cr, Al-Cr and Al phases were observed, adding Al and Ti. Especially, Sharp rectangular shapes of precipitates were observed with increasing amount of Ti.

• Journal of Powder Materials
• /
• v.10 no.5
• /
• pp.305-309
• /
• 2003

We report on the formation and chemical leaching of non-equilibrium $Al_{0.6}(Fe_{75}Co_{25})$ alloy produced by rod milling. X-ray diffractometry, transmission electron microscopy, differential scanning calorimetry, scanning electron microscopy, and vibrating sample magnetometry were used to characterize the as-milled and leached specimens. After 400 h, only the $Al_{0.4}Fe_{0.6}$ peak of the body-centered cubic type was present in the XRD pattern. The entire rod milling process could be divided into three different stages of milling: agglomeration, disintegration, and homogenization. The saturation magnetization, $M_s$ decreased with increased milling time, the $M_s$ of the powders before milling was about 113.8 emu/g, the $M_s$ after milling for 400 h was about 11.55 emu/g. Leaching of the Al in KOH of the Al at room temperature from the as-milled powders did not induce any significant change in the diffraction pattern. After the leached specimen had been annealed at $600^{\circ}C$ for 1 hour, the nanoscale crystalline phases were transformed into the bcc Fe, cubic Co, and $CoFe_2O_4$ phases. On cooling the specimen from 85$0^{\circ}C$, the degree of magnetization increased slightly, then increased sharply at approximately 364.8$^{\circ}C$, indicating that the bcc $Al_{0.4}Fe_{0.6}$ phase had been transformed to the Fe and Co phases.