• Korean Journal of Materials Research
• /
• v.13 no.9
• /
• pp.613-618
• /
• 2003

The magnetic heating effect of $SiO_2$coated $ \Upsilon-Fe_2$$O_3$nanocomposite particle due to magnetic relaxational loss of superparamagnetic regime was investigated by measuring the generated heat from nanocomposite particles in alternative applied magnetic fields. The commercial $ \Upsilon-Fe_2$$O_3$nanoparticles were coated by SiO$_2$in water solution with TEOS and the synthesized nanocomposite powders and its magnetic properties were characterized and compared with the raw$ \Upsilon-Fe_2$$O_3$nanoparticles. The 10∼30 nm sized $ \Upsilon-Fe_2$$O_3$. nanoparticles were coated by 5 nm thickness of amorphous $SiO_2$film. The nanocomposite particle has very low Mr and Hc value showing superparamagnetic behavior The magnetic heating effect of nanocomposite particle on surface coating phase of $SiO_2$was discussed in terms of superparamagnetic behaviors of each particles, and their potential for hyperthermia application was evaluated.

• Korean Journal of Materials Research
• /
• v.6 no.11
• /
• pp.1061-1066
• /
• 1996

RF magnetron reactive sputtering법으로 Fe75.5Zr8.3N16.2/SiO2(250$\AA$) 다층 박막을 FeZrN의 두께를 변화시키면서 제조하고, 제조된 박막을 진공 열처리하여 열처리 온도에 따른 포화자화, 보자력, 고주파에서의 투자율 그리고 열적 안정성을 조사하였다. Fe75.5Zr8.3N16.2/SiO2(250$\AA$) 다층박막은 FeZrN의 두께가 800$\AA$이상일 때 좋은 연자성을 나타내었다. Fe75.5Zr8.3N16.2/SiO2(250$\AA$)다층 박막을 45$0^{\circ}C$로 열처리 했을 때 포화자속밀도(1.08 T), 보자력 0.41 Oe, 1 MHz에서의 실효 투자율은 3000이상의 연자성을 나타내었다. 그 이유는 X-선 회절 분석 결과 열처리에 의해서 ZrN 미결정이 석출하여 $\alpha$-Fe 결정 성장이 억제되어 우수한 연자기적 성질이 나타난다고 판단된다. 이때 $\alpha$-Fe 입자 크기는 40-50$\AA$, ZrN의 입자 크기는 10-15$\AA$이다. 그리고 실효 투자율의 주파수 의존성에서 단층막에서는 5 MHz 이상에서 실효 투자율이 급격히 감소하는 경향을 보였으나, 다층막에서는 40MHz까지 실효 투자율이 1600이 되어 고주파에서의 연자성이 개선되었다.

• Korean Chemical Engineering Research
• /
• v.50 no.3
• /
• pp.398-402
• /
• 2012

The catalytic performance of some metal oxides in the vapor phase selective oxidation of $H_2S$ in the stream containing ammonia and water was investigated. Among the catalysts tested $Fe_2O_3/SiO_2$ was the most promising catalyst for practical application. It showed higher than 90% $H_2S$ conversion and very small amount of $SO_2$ emission over a temperature range of $240{\sim}280^{\circ}C$. The effects of reaction temperature, $O_2/H_2S$ ratio, amount of ammonia and water vapor on the catalytic activity of $Fe_2O_3/SiO_2$ were discussed to better understand the reaction mechanism. The $H_2S$ conversion showed a maximum at $260^{\circ}C$ and it decreased with increasing temperature over $280^{\circ}C$. With an increase of $O_2/H_2S$ ratio from 0.5 to 4, the conversion was slightly increased, but the selectivity to elemental sulfur was remarkably decreased. The increase of ammonia amount favored the conversion and the selectivity to elemental sulfur with a decrease in $SO_2$ production. The presence of water vapor decreased both the activity and the selectivity to sulfur, but increased the ATS selectivity.

• Korean Journal of Materials Research
• /
• v.1 no.4
• /
• pp.198-205
• /
• 1991

Sintered thermistor body was fabricated by solid reaction method using $Fe_2O_3, \;Al_2O_3, \;TiO_2$ and Si powder. Surface matrix of sintered body was investigated by SEM and $\beta$-constant was obtained from measurement of resistance variation in liquid bath. The values of thermistor constant $\beta$ of samples in the temperature range $-50~+50^{\circ}C$ were distributed from 927 to 4005k. This thermistor body can be used as temperature sensor for radiosonde.

• Journal of Surface Science and Engineering
• /
• v.34 no.2
• /
• pp.135-141
• /
• 2001

Arc-melted Ti-6Al-4V, Ti-4Fe and Ti-(1,2) Si alloys were oxidized at 700, 800, 900 and $1000^{\circ}C$ in air. The oxidation resistance of Ti-4Fe was comparable to that of Ti-6Al-4V, while the oxidation resistance of Ti-(1,2) Si was superior to that of Ti-6Al-4V. Ti-2Si displayed the best oxidation resistance among the four alloys, but failed after oxidation at $1000^{\circ}C$ for 17h. The oxide scale formed on Ti-6Al-4V, Ti-4Fe and Ti-(1,2)Si consisted of ($TiO_2$ and a small amount of $Al_2$$O_3$), ($TiO_2$ and a small amount of dissolved iron), and ($TiO_2$ plus a small concentration of amorphous $SiO_2$), respectively. The oxide grains of the surface scale of the four alloys were generally fine and round.

• Advances in nano research
• /
• v.10 no.3
• /
• pp.295-312
• /
• 2021

A new ionic liquid functionalized magnetic silica nanoparticle was synthesized and characterized and tested as an adsorbent. The adsorbent was used for magnetic solid phase extraction on ICP-MS method. Simultaneous determination of precious metal Au has been addressed. The method is simple and fast and has been applied to standard water and surface water analysis. A new method for separation/analysis of trace precious metal Au by Magnetron Solid Phase Extraction (MSPE) combined with ICP-MS. The element to be tested is rapidly adsorbed on CoFe2O4@SiO2@[BMIM]PF6 composite nano-adsorbent and eluted with thiourea. The method has a preconcentration factor of 9.5-fold. This method has been successfully applied to the determination of gold in actual water samples. Hydrophobic Ionic Liquids (ILs) 1-butyl-3-methylimidazole hexafluorophosphate ([BMIM]PF6) coated CoFe2O4@SiO2 nanoparticles with core-shell structure to prepare magnetic solid phase extraction agent (CoFe2O4@SiO2@ILs) and establish a new method of MSPE coupled with inductively coupled plasma mass spectrometry for separation/analysis of trace gold. The results showed that trace gold was adsorbed rapidly by CoFe2O4@SiO2@[BMIM]PF6 and eluanted by thiourea. Under the optimal conditions, preconcentration factor of the proposed method was 9.5-fold. The linear range, detection limit, correlation coefficient (R) and relative standard deviation (RSD) were found to be 0.01~1000.00 ng·mL-1, 0.001 ng·mL-1, 0.9990 and 3.4% (n = 11, c = 4.5 ng·mL-1). The CoFe2O4@SiO2 nanoparticles could be used repeatedly for 8 times. This proposed method has been successfully applied to the determination of trace gold in water samples.

• Journal of the Korean Magnetics Society
• /
• v.4 no.1
• /
• pp.12-19
• /
• 1994

The crystallization behavior of the amorphous $Fe_{73.5}Cu_{1}Nb_{3}Si_{16.5}B_{6}$ alloy with isothermal annealing at $552^{\circ}C$ was studied by $M\"{o}ssbauer$ spectroscopy. The amorphous phase was revealed to coexist together with $Do_{3}-FeSi$ nanocrystalline and Cu-duster in annealed alloys by $M\"{o}ssbauer$ spectrum analysis. At the early stage of crystallization, Si content of FeSi is high due to the creation of Cu-cluster, and decreases with annealing until 60 minutes, which results in the increase in the mean hyperfine field of FeSi, and thereafter keeps constant. After 60 minutes, the decrease in the mean hyperfine field of the residual armrphous, in spite of a slight change in the volume fraction of the FeSi and the residual armrphous, is caused by the increase in the content of Nb and B in residual amorphous phase. Both directions of the hyperfine field, those of the FeSi and the residual amorphous, become randomly oriented in about 60 minutes. For FeSi and Cu-duster, the Avrami exponents are 0.51 and O.65, the activation energies are 2.35 eV and 2.44 eV, and the incubation times are 2.4 minutes and 0.8 minutes respectively. Earlier formation of Cu-duster than that of FeSi is coincidence with the fact that Cu atom promotes the nucleation of the FeSi.

• Journal of the Korean Magnetics Society
• /
• v.25 no.2
• /
• pp.43-46
• /
• 2015

$Si(100){\backslash}200nm$ $SiO_2{\backslash}5nm$ $Ta{\backslash}5nm$ $MgO{\backslash}35nm$ $Fe_3O_4$ multi-layers were prepared by using RF-sputtering and ultra-high vacuum molecular beam epitaxy (UHV-MBE) techniques. After post-annealing the multi-layers at $500^{\circ}C$ for 1 hour under the high vacuum of ${\sim}1{\times}10^{-6}Torr$, we observed ferromagnetic properties at room temperature as well as the Verwey transition which is the typical features of magnetite crystals formed. We have carried out a comparative study of the effect of Ta buffered layer on the crystallinity and magnetic properties of $Fe_3O_4$ thin films prepared under different growth and annealing conditions.

• Economic and Environmental Geology
• /
• v.46 no.2
• /
• pp.199-206
• /
• 2013

The Daehyun gold-silver deposit consists of two hydrothermal quartz veins that fill NE-trending fractures in the Cambro-Ordovician calcitic marble. I have sampled wallrock, hydrothermaly-altered rock and gold-silver ore vein to study the element dispersion and element gain/loss during wallrock alteration. The hydrothermal alteration doesn't remarkably recognized at this deposit and consists of mainly calcite, dolomite, quartz and minor epidote. The ore minerals composed of arsenopyrite, pyrrhotite, pyrite, sphalerite, stannite, chalcopyrite, galena, electrum, native bismuth and silver-bearing mineral. Based on analyzed data, the chemical composition of wallrock consists of mainly $SiO_2$, CaO, $CO_2$ with amounts of $Al_2O_3$, $Fe_2O_3(T)$ and MgO. The contents of $SiO_2$, $Fe_2O_3(T)$, MgO, CaO and $CO_2$ vary significantly with distance from ore vein. The element dispersion doesn't remarkably recognized during wallrock alteration and only occurs near the ore vein margin because of physical and chemical properties of wallrock. Remarkable gain elements during wallrock alteration are $Fe_2O_3(T)$, total S, Ag, As, Bi, Cd, Cu, Ni, Pb, Sb, Sn, W and Zn. Remarkable loss elements are $SiO_2$, MnO, MgO, CaO. $CO_2$ and Sr. Therefore, Our result may be used when geochemical exploration carry out at deposits hosted calcitic marble in the Hwanggangri metallogenic district.

• Journal of the Korean Vacuum Society
• /
• v.7 no.1
• /
• pp.17-23
• /
• 1998

$Pb(Fe_{0.5}Nb_{0.5}O_3(PFN)$ thin films were prepared by rf magnetron co-sputtering method on $SiO_2/Si$, ITO/glass, and $Pt/Ti/SiO_2/Si$ substrates and post-annealed at the $N_2$ atmosphere by RTA(rapid thermal annerling). The degree of crystallinity of PFN films was identified on various substrates. Electrical properties of PFN films was characterized for $Pt/PFN/Pt/Ti/SiO_2/Si$ structure. The composition of PFN films was estimated by EPMA (electron probe micro analysis). PFN films would be crystallized better to perovskite phase on ITO/glass substrate than $SiO_2/Si$ substrate. This may be induced by the deformation of Pb deficient pyrochlore phase due to Pb diffusion into $SiO_2/Si$ substrate. PFN films on $Pt/Ti/SiO_2/Si$ substrate. PFN films with 5-10% Pb excess were crystallized to perovskite phase from $500^{\circ}C$ temperature. In summary, we show that Pb composition and annealing temperature were critically influenced on crystallinity to perovskite phase. When PFN film with 17% Pb excess was annealed at $600^{\circ}C$ at the $N_2$ atmosphere for 300kV/cm and 88. Its remnant polarization coercive field $2.0 MC/cm^2$ and 144kV/cm, respectively.