• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계학술발표회 논문집(I)
• /
• pp.82-85
• /
• 2006

In this study, the fatigue tests were performed on a series of reinforce concrete beams with type of aggregate to investigate the fatigue behavior. The four point loading system is used in the fatigue tests. In these tests, relations between the repeated loading cycles and mid-span deflections, number of repeated loading cycles when specimen was fractured were observed. On this basis, the mid-span deflections, the crack growth and failure mode of beams were studied. The result of tests, reinforce concrete beams with recycled aggregate were about similar failure mode with natural aggregate concrete beam.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1992년도 춘계학술대회 논문집
• /
• pp.268-273
• /
• 1992

Thin walled tubular specimens of 0.45% structural carbon steel were used in the bizxial tests. Biaxial fatigue tosts were conducted on strain control including fully reversed tension-compression and in phase tension torsion loadings. The predictions of the biaxial fatigue life were based upon the uniaxial low cycle fatigue test results. Fatigue lives were ranged from 10$\^$2/to 10$\^$5/cycles. Four multiaxial strain based theories have been developed to correlate biaxial fatigue experimdntal results. These theories showed good correlatins except for maximum shear strain theory. In uniaxial tests, crack behavior was observed that crack initiated in the maximum shear strain direction and propagated in the direction perpendicular to principal stross. But, in biaxial tests, both crack initiation and growth occured on the maximum shear strain direction only.

• 산업기술연구
• /
• 제21권B호
• /
• pp.331-339
• /
• 2001

Zero to tension fatigue tests and strain controlled fatigue tests were carried out to find how initial strain induced martensite, ${\alpha}^{\prime}$ affects low and high cycle fatigue behavior and fatigue crack growth mechanisms. Microscopic study and phase analysis were carried out with TEM, SEM, EDAX, Optical Microscope, Ferriscope, and X-ray diffractometry. The amount of Initial ${\alpha}^{\prime}$ was controlled from 0% to 33% by controlling the temperatures for cold working and heat treatment. Lower contents of initial ${\alpha}^{\prime}$ showed higher fatigue resistance in low cycle fatigue but lower fatigue resistance in high cycle fatigue because it is ascribed to the more transformation of ${\alpha}^{\prime}$ martensite during low cycle fatigue and higher ductility. In high cycle fatigue, fatigue life is attributed to the strength and phase transformation of austenite into ${\alpha}^{\prime}$ during fatigue was negligible. ${\gamma}$ boundary, ${\gamma}/twin$ boundary, and ${\gamma}/{\alpha}^{\prime}$ boundary were found to be the preferred site of fatigue crack initiation.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.353-358
• /
• 2002

The purpose of this paper was to estimate the cumulative damage of pavement concrete by split tension fatigue test. The split tension fatigue test of variable amplitude loading were performed in two and three stages. The results of the fatigue test by variable amplitude loading showed that the sums of damage were greater than 1 in the increasing sequence loading tests, and less than 1 in the decreasing sequence loading tests. The remaining life estimated by equivalent damage theory was almost similar to that of experimental results.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2004년도 추계학술대회 논문집
• /
• pp.710-715
• /
• 2004

To evaluate the fatigue lifetime of structures, it is necessary to identify the value of parameters through tests or literature. it is difficult for field engineers to get the necessary data through tests from the viewpoint of time and cost. In this study. we surveyed literature and proposed a procedure to identify the fatigue parameters for fatigue life evaluation by local strain approach.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 춘계학술발표대회 논문집
• /
• pp.60-64
• /
• 2001

In this paper, the tension-compression fatigue test method and the fatigue life characteristics of carbon fabric/epoxy laminate coupon are presented. To avoid the buckling during the compression, a proper design for the test coupons is essential. The critical buckling loads for the coupons are calculated by assuming the coupons as columns under two types of fixed conditions. The first is that both ends of each coupon are perfectly clamped, the second is that both ends of each coupon are simply supported. The strain-load curves are obtained by compressing the representative coupons, on each surface of which a strain gage is attached. The buckling loads obtained from the tests are all between the two calculated critical buckling loads. All the coupons are broken by the compression during the fatigue tests. It is estimated to be the reason that the fatigue load causes delamination before the eventual failure of each coupon, and sequentially the micro-buckling in the delaminated region drives each coupon into fatigue failure during the compression. The S-N curve, the fatigue life characteristics of carbon fabric/epoxy is obtained.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 추계학술발표대회 개요집
• /
• pp.73-75
• /
• 2005

The objective of this study is to estimate the feasibility of X-ray diffraction method application for fatigue life assessment of the high-temperature pipeline steel such as main steam pipe, reheater pipe and header etc. in power plant. In this study, X-ray diffraction tests using various types of specimen simulated low cycle fatigue damage were performed in order to analyze fatigue properties when fatigue damage conditions become various stages such as 1/4, 1/2 and 3/4 of fatigue life, respectively. As a result of X-ray diffraction tests for specimens simulated fatigue damages, we conformed that the variation of the full width at half maximum intensity decreased in proportion to the increase of fatigue life ratio.

• KCI Concrete Journal
• /
• 제14권2호
• /
• pp.69-75
• /
• 2002

This is the second of two part series on experimental studies of grout type transverse joints. In this paper, grout-type transverse joints between precast concrete slabs are tested to study the fatigue behavior. The tests are per-formed with loading equipment designed and constructed especially in the lab to introduce shear fatigue failures on the joints of the test specimens with repeated loads. Non-prestressed as well as prestressed specimens are selected based on static tests and these specimens are studied to identify the effect of prestress on the fatigue strength of the grout type joint. A comparison between prestressed and non-prestressed specimens indicates that longitudinal prestressing is an effective method to increase fatigue strength of the transverse joints. Based on the fatigue test, a rational estimation of the fatigue strength is proposed to aid design of the grout-type transverse joints.

• 한국재료학회지
• /
• 제25권10호
• /
• pp.516-522
• /
• 2015

Aging aircraft structures are inevitably exposed to environment for a long time facing many potential problems, including corrosion and wide spread fatigue damage, which in turn cause the degradation of flight safety. In this study, the environmental surface damages on aging aircraft structures induced during service were quantitatively analyzed. Additionally, S-N fatigue tests were performed with center hole specimens extracted from aging aircraft structures. From the results of quantitative analyses of the surface damages and fatigue tests, it is concluded that corrosion pits initiated during service reduce the fatigue life significantly. Finally, using the fracture mechanics and the EIFS (equivalent initial flaw size) concepts, the remaining fatigue life was predicted based on actual fatigue test results.

• 한국표면공학회지
• /
• 제37권5호
• /
• pp.273-278
• /
• 2004

The requirements of getting spring steel with higher fatigue strength have been increased to achieve the weight reduction of a vehicle. As the possible increment in fatigue strength by using the conventional shot peening treatment is found to be limited, it is necessary to modify the shot peening treatment. In this study, to investigate the effects of warm shot peening on increasing fatigue strength, tests are conducted on spring steel SAE9524. By the results of rotating bending fatigue tests, the fatigue strength increases up to 23.8% in warm shot peening specimens at $200^{\circ}C$ compared with conventional shot peening. The major reason why the warm shot peening is effective to the improvement of fatigue strength is the increment of the compressive residual stress, which can be effectively formed by shot peening under the condition of warm temperature than room temperature.