• 한국기계가공학회지
• /
• 제9권1호
• /
• pp.25-34
• /
• 2010

Fretting damage reduces fatigue life of the material due to low amplitude cyclic sliding and changes in the contact surfaces of strongly connected machine and structures such as bolt, key, fixed rivet and connected shaft, which have relative slip of repeatedly very low frequency amplitude. In this study, the fretting fatigue behavior of 7050-T7451 aluminum alloys used mainly in aircraft and automobile industry were evaluated. The plain fatigue test and fretting fatigue test under cyclic bending load carried out commercial bending fatigue tester and specially devised equipments to cause fretting damage. From these experimental work, the following results obtained: (1) The plain fatigue limit for stress ratio R=-l was about 151MPa. (2) In case of fretting fatigue, fatigue limit for stress ratio R=-l about 72MPa, the fatigue limit for R=0 about 81MPa, and the fatigue limit for R=0.3 about 93MPa. (3) The fatigue limit reduction rates by the fretting damage were about 52%(R=-1), 46%(R=0) and 38%(R=0.3) respectively. (4) The fatigue limit reduction rate decreased with stress ratio increase. In fretting bending test, as stress ratio increased, occurrence of initial oblique crack by fretting decreased or phased out, so that fracture surfaces were formed by plain fatigue crack occurrence, and such tendency was notable as stress amplitude increased. (5) Tire tracks and rubbed scars were observed in the fracture surface and contacted surface.

• 한국해양공학회지
• /
• 제7권2호
• /
• pp.103-113
• /
• 1993

X-ray diffraction analysis technique was used for the fatigue damage analysis and fatigue life prediction in Al 7075-T651 alloy. The tensile test, fatigue strength and fatigue crack propagation test with change of stress ratio were carried out. As a result, half-value breadth was increased with the plastic deformation in the specimen increasint at all test conditions. In particular, half-value breadth at the surface of the specimens fractured by fatigue was increased as stress intensity factor range and effective stress intensity factor range were increased. In addition, the good relationship between half-value breadty and diffraction pattern was shown.

• 비파괴검사학회지
• /
• 제10권2호
• /
• pp.23-31
• /
• 1990

Acoustic Emission(AE) signals obtained during fracture toughness test and fatigue test for nuclear pressure vessel material(SA 508 cl.3) and artificial AE signals from pencil break and ultrasonic pulser were classified using pattern recognition methods. Three different classifiers ; namely Minimum Distance Classifier, Linear Discriminant Classifier and Maximum Likelihood Classifier were used for pattern recognition. In this study, the performance of each classifier was compared. The discrimination of AE signals from cracking and crack surface rubbing was possible and the analysis for crack propagation was applicable by pattern recognition methods.

• 대한의용생체공학회:의공학회지
• /
• 제19권5호
• /
• pp.433-441
• /
• 1998

본 연구에서는 전부도재관용 도재의 균열전파 양상과 구강환경이 파절강도에 미치는 영향을 평가하기 위해 시행되었다. 도재의 굽힘강도 늘 In-Ceram, IPS-Empress 및 VMK68의 순으로 나타났으며, 수중에서 좌다 기름중에서 더 놀은 강도를 보였다. 비커스 압자 압입부와 압입부를 중심으로 한 파면의 관찰 결과, VMK68 도재의 경우에는 9.8N의 압인하중하에서, IPS-Empress의 경우에는 47.0N의 압입하중하에서 교면에 median crack이 형성되는 양상을 보였으며, 균열이 압자의 압입시에 형성된 벽개면을 따라서 빠르게 성장하여 파괴에 도달한 양상을 보였다. In-Ceram의 경우에는 49.0h의 압임하중하에서 Palmqvlst clack이 형성되는 양상을 보였으며, 알루미나 입자에 의한 균열의 굴곡과 creak bridging으로 인한 강화기전이 관찰되었다.

• 한국주조공학회지
• /
• 제9권1호
• /
• pp.58-66
• /
• 1989

The effect of heat treating temperature and ${\alpha}$ phase In the ${\beta}$ phase matrix were investigated for ${\beta}-CuZnAl$ shape memory alloys by tension test, fatigue test, and shape memory effect test. After heat treatment at $677^{\circ}C$, $750^{\circ}C$, $800^{\circ}C$ and $850^{\circ}C$ for 10 min. respectively, static fracture stress(${\sigma}_f$), fatigue fracture stress(${\tau}_{max}$) at $10^6$ cycle, and elongation(${\epsilon}_f$) was $24.2kg/mm^2$, $17.21kg/mm^2$ and 11.8%, respectively. As heat treating temperature decreased, fracture surfaces of the specimens were changed from the intergranular to the transgranular fracture mode. Especially, the a phase precipitated in the ${\beta}$ phase matrix had an effect on crack propagation and the fracture surface was characterized by dimple-like pattern when crack propagated in transgranular cracking mode. Precipitation of the ${\alpha}$ phase in the ${\beta}$ phase matrix lowered the transformation temperature by $10^{\circ}C$, and about 2.5 vol.% ${\alpha}$ phase did not affect the shape memory effect examined by the bending test.

• 한국철도학회논문집
• /
• 제3권2호
• /
• pp.77-83
• /
• 2000

This study proposes the integrity evaluation of the bogie frame using ultrasonic fractography analysis. Analysis objectives in this study are to investigate fracture planes of damaged zone by the A-scan method. The surface condition of fracture planes shows degree of degradation by the stress concentration. The detection of the natural defects in the bogie frame is performed using the characteristics of echodynamic pattern in ultrasonic signal. Results of ultrasonic testing agree fairly well with those of actual fracture plane. In quantitative fractography analysis, microstructures of actual fracture plane turned out to be intergranular and transgranular fracture. Proposed ultrasonic fractography analysis in this study can be used for the integrity evaluation of the bogie frame.

• 한국정밀공학회지
• /
• 제19권5호
• /
• pp.43-50
• /
• 2002

Friction welding has many merits such as energy efficiency, simple processing, etc butt difficult to obtain good weld at the welded interface and heat affected zone. To date, the continuum mechanics and fracture mechanics are utilized to analyse stresses at the interface and propagation of cracks. In this study. STS304 and SM15C are selected because they can be differentiated distinctively from metallic point of view and crack can be observed easily. It is ovserved during friction welding that STS304, rotary part is hatter than SH15C, fixed part. The last fracture occurs around the center because the surface of fatigue fracture has smooth regions, due to the separation phenomenon in plastic flows layers and striation dimple pattern.

• 한국도로학회논문집
• /
• 제19권5호
• /
• pp.107-115
• /
• 2017

PURPOSES : The piezoelectric energy road analysis technology using a three-dimensional finite element method was developed to investigate pavement behaviors when piezoelectric energy harvesters and a new polyurethane surface layer were installed in field conditions. The main purpose of this study is to predict the long-term performance of the piezoelectric energy road through the proposed analytical steps. METHODS : To predict the stresses and strains of the piezoelectric energy road, the developed energy harvesters were embedded into the polyurethane surface layer (50 mm from the top surface). The typical type of triaxial dump truck loading was applied to the top of each energy harvester. In this paper, a general purpose finite element analysis program called ABAQUS was used and it was assumed that a harvester is installed in the cross section of a typical asphalt pavement structure. RESULTS : The maximum tensile stress of the polyurethane surface layer in the initial fatigue model occurred up to 0.035 MPa in the transverse direction when the truck tire load was loaded on the top of each harvester. The maximum tensile stresses were 0.025 MPa in the intermediate fatigue model and 0.013 MPa in the final fatigue model, which were 72% and 37% lower than that of the initial stage model, respectively. CONCLUSIONS : The main critical damage locations can be estimated between the base layer and the surface layer. If the crack propagates, bottom-up cracking from the base layer is the main cracking pattern where the tensile stress is higher than in other locations. It is also considered that the possibility of cracking in the top-down direction at the edge of energy harvester is more likely to occur because the material strength of the energy harvester is much higher and plays a role in the supporting points. In terms of long-term performance, all tensile stresses in the energy harvester and polyurethane layer are less than 1% of the maximum tensile strength and the possibility of fatigue damage was very low. Since the harvester is embedded in the surface layer of the polyurethane, which has higher tensile strength and toughness, it can assure a good, long-term performance.

• 대한치과보철학회지
• /
• 제47권4호
• /
• pp.424-434
• /
• 2009

연구목적: 임플란트는 수직교합 하중에는 비교적 잘 견디나 측방하중에 대해서는 약한 역학적 성질을 갖고 있으므로 임플란트의 재료 특성과 기하학적 형태에 따른 응력 분석 연구의 필요성이 제기되고 있다. 연구재료 및 방법: 외부육각구조를 갖는 28개의 임플란트를 7개씩 4군으로 나누어 그 제품에 적합한 UCLA gold abutment를 이용해, 제3형 금합금으로 보철 물을 제작하였고, A군 (3i, FULL $OSSEOTITE^{(R)}$-Implant), B군 (Nobelbiocare, Branemark $System^{(R)}$Mk III Groovy RP), C군 (Neobiotec, $SinusQuick^{(TM)}$ EB), D군 (Osstem, US-II)으로 분류하였다. 고정체와 지대주나사, 지대주를 연결한 후 수직적으로 절단하여 연마한 후 미세경도계를 이용하여 10군데에서 경도측정을 실시하였고, 동적하중 피로시험기를 이용하여 60-600 N범위로 파절시까지 동적 하중을 가하였다. 주사전자현미경을 이용하여 지대주나사 및 고정체의 파절 양상과 파절 위치 등을 관찰하였고, 유한요소분석을 통해 고정체와 지대주 나사에 나타나는 응력 분포와 파절면을 비교 분석하였다. 결과: 1.고정체 경도는 A, B, C, D군에서 각각 245.3, 289.7, 281.3, 300.4 Hv로 D군이 가장 높았고, A군이 가장 낮았다. 지대주 나사의 경도는 A, B, C, D군에서 각각 340.00, 317.62, 306.5, 306.2 Hv로 A군이 가장 높고, D군이 가장 낮았다. 2. 모든 실험군에서 임플란트 고정체의 파절은 응력이 집중되는 고정체 3-4번째 나사산 홈 (valley) 부위 또는 내면의 사공간부와 일치하는 부위에서 발생되었고, 피로수명은 A, B, C, D군에서 각각 31585, 47311, 30141, 105371로 D군이 가장 높았으며, A, B, C군과는 유의한 차이가 있었다(P<.05). 3. 파절양상은 B군과D군에서는 고정체와 나사 모두에서 수직 (longitudinal)파절과 수평 (transverse)파절이 동시에 일어나는 복합 (complex mode) 파절이 관찰 되었고, A와 C군에서는 고정체에서 수평 (transverse mode) 파절만이 관찰되었다. 4. 유한요소분석 결과 인장응력이 가장 높은 고정체 표면부에서 피로 균열이 시발되어 압축응력이 가장 높은 반대편 부위로 피로균열이 전파되었으며, 최대 유효 응력값은 C군이 가장 높았고, B군에서 가장 낮았다. 결론: 피질골 높이와 일치하는 임플란트 고정체 부위에서 최대 인장 주응력이 발생되며, 고정체 사공간부 (dead space)가 최대 인장 주응력이 작용하는 지그 표면과 일치할 때 피로파절이 발생되었다. 따라서 악골에 식립된 임플란트의 신뢰성을 향상시키고 수명을 증대시키기 위해서는 가능한 임플란트 주위의 골소실이 일어나지 않도록 해야 할 것이나 골흡수가 일어나 사공간부 수준까지 진행된다면 임플란트의 파절 빈도가 증가될 수 있으므로 이에 대한 대처가 필요할 것으로 사료된다.