• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.10 no.4
• /
• pp.7-13
• /
• 2001

This Study is to investigate the influence of weld residual stresses on the fatigue crack growth behaviors in pressure ves-sel reinforcement. In order to perform this study, the automatically welded specimens are prepared. The material is ASTM A516 grade 60 steel used in pressure vessel mainly. For pad-on-plate of skip welding continuous welding and PWHT specimen, fatigue crack initiation is generally initiat-ed at weld starting and end toe zone, and ruptured at weld starting toe zone, Fatigue life if pad-on-plate continuous speci-men is increased more than that of pad-on-plate skip fillet welding specimene about 85% under low load, about 20% under high load, and decreased than that of two-pad continuous welding specimen about 85%. In da/dN-$\Delta$ Κ curve under low load, pad-on-plate skip fillet welding specimen showed retardation on the initial crack, and the fatigue crack growth rate at the low region of $\Delta$Κ greater specimene E(3.8{\times}10^{-6}$mm/cycle). And the fatigue life of welding specimen was smaller than that of PWHT specimen.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.11
• /
• pp.1415-1422
• /
• 2011

Sheet aluminum alloys used in manufacturing of machine structures for transportation show the difference of crack growth speed depending on thickness under the constant fatigue stress condition. The referred thickness effect is a major fatigue failure property of sheet aluminum alloys. In this work, we identified the thickness effect in fatigue test of thick plate and thin plate of Al 2024-T3 alloy under the constant fatigue stress condition, and presented the thickness effect to a correlative equation, $U_{i}^{equ}=f(R_t)$ which is determined by the shape factor, thickness ratio, $R_t$ and the loading factor, equivalent effective stress intensity ratio depending on thickness, $U_{i}^{equ}$. And we analyzed quantitatively the crack growth retardation behavior in thin plate compared to thick plate by the thickness effect using ${\Delta}K$ conversion method. We obtained such values as decrement of thickness(DoT), decrement of stress intensity factor range, ${\Delta}K$ (DoS) and identified the relation between them to present the nature of thickness effect in this work.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.9 no.3
• /
• pp.181-189
• /
• 2001

For the Tailor Welded Blank sheet used fur automobile body panel, the characteristics of fatigue crack propagation behavior were studied. The thickness of specimen was machined to be same (0.9+0.9mm) and different (0.9+2.0mm). As a base test, mechanical properties around welding zone were examined. The results indicated that there were no significant decreases in mechanical properties, but hardness around welding bead is 2.3 times greater than base material. The crack propagation rate was noticeably decreased around welding line and rapidly increased as it passed by welding line. Reviewing the shape of the crack propagation, crack width around welding line was wide around the welding zone due to retardation of crack growth, but it became narrow passing welding line due to decreased toughness. Elasto-Plastic analysis was performed by finite element analysis fur explaining the test results.

• Journal of Ocean Engineering and Technology
• /
• v.6 no.1
• /
• pp.131-139
• /
• 1992

The understanding and appllication of fatigue crack propagation mechanism in variable amplitude loading is very important for life prediction of the air travel structures. Particularly, the retardation and arrest behavior of fatigue crack propagation by single tension overloading is essential to the understanding and appllication of fatigue crack propagation mechanism in variable amplitude loading. Numerous studies of the retardation behavior have been performed, however investigations of the arrest behavior have not been enough yet. As for the arrest behavior, Willenborg had reported that the overload shut-off ratio $[R_{so}=(K_{OL})/K_{max})_{crack arrest}]$ had been the material constant, but recently several investigators have reported that the overload shut-off ratio depends upon the stress ratio. In this study, authors have investigated the effect of stress ratio on the threshold overload shut-off ratio to generate arrest of fatigue crack growth in high tensile aluminum alloy 7075-T735 which have used in material for air travel structures, It has been $-0.4\leqqR\leqq0.4$ till now, the region of stress ratio investigated. The threshold overload shut-off ratio has decreased as stress ratio has increased in overall region of -$-0.4\leqqR\leqq0.4$ and the linearity has been seen in this material. Moreover, the experimental equation between $R_{so}$ and R has been made; The relation has been $R_{so}=-R+2.6$.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.4
• /
• pp.49-60
• /
• 1997

This paper deals with the effect of coating layer on the fatigue strength of TiN coated 1Cr-1Mo-0.25V steel prepared by using the arc ion plating (AIP) process, in which it was characterized by the presence of extractor grid (ion filter). The rotary bending fatigue tests were carried out under room air conditions, and the fatigue crack initiation and growth bwhavior were observed by using plastic replica method. As experimental results, it was found that the obvious improvement of fatigue life at lower stress region was confirmed in TiN coated specimen processed with ion filter. It was also exlained that the increase of fatigue life in the case of an improved AIP process with ion filter was attributed to the retardation of crack initiation of the substrate surface due to hard coating layer, more densly formed with the reduced size and density of droplets.

• Journal of Welding and Joining
• /
• v.14 no.2
• /
• pp.79-89
• /
• 1996

일정진폭하중과 과대하중비 2.5의 단일 인장과대하중에 의한 4140강 용접부 의 피로균열성장거동을 실온과 -45.deg.C의 저온에서 피로시험과 파면관찰을 통하여 고찰하였다. 이때, 용접부 미시조직의 영향을 평가하기 위해 모재(parent metal), 열영향부(as-welded HAZ), 열처리된 열영향부(PWHT HAZ)로 나누어 응력비 0과 0.5로 CT시험편을 이용하여 피로시험을 실시하였다. 피로균열성장거동은 재료의 미시조직과 온도변화보다는 응력비에 크게 영향을 받았으며, 단일 과대하중에 의한 피로균열성장 지연효과가 모든 재료에서 상당히 크게 나타났다. 전자현미경에 의한 피로파면 관찰 결과, 실온에서는 연성의 스트라이에이숀과 -45.deg.C에서는 의벽개파면과 같은 피로 균열성장거동을 나타내고 있다.

• Metals and materials international
• /
• v.24 no.6
• /
• pp.1412-1421
• /
• 2018

Cold-expanded austenitic high nitrogen steel (HNS) was subjected to investigate the effects of grain size on the stress-controlled high cycle fatigue (HCF) as well as the strain-controlled low cycle fatigue (LCF) properties. The austenitic HNSs with two different grain sizes (160 and $292{\mu}m$) were fabricated by the different hot forging strain. The fine-grained (FG) specimen exhibited longer LCF life and higher HCF limit than those of the coarse-grained (CG) specimen. Fatigue crack growth testing showed that crack propagation rate in the FG specimen was the same as that in the CG specimen, implying that crack propagation rate did not affect the discrepancy of LCF life and HCF limit between two cold-expanded HNSs. Therefore, it was estimated that superior LCF and HCF properties in the FG specimen resulted from the retardation of the fatigue crack initiation as compared with the CG specimen. Transmission electron microscopy showed that the effective grain size including twin boundaries are much finer in the FG specimen than that in the CG specimen, which can give favorable contributions to strengthening.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.32 no.1
• /
• pp.44-49
• /
• 2004

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.4
• /
• pp.48-55
• /
• 2000

For the Tailor Welded Blank sheet used for automobile body panel, the characteristics of fatigue strength and crack propagation behavior were studied. The thickness of specimens was joined to be same (0.9mm+0.9mm) and different (0.9mm+2.0mm) .As a base test, mechanical properties around weld zone were examined . The results indicated that there were no significant decreases in mechanical properties , but hardness around weld bead was 2.3 times greater than base material . The fatigue strength was the highest when the loading direction was parallel to the welding direction, which was about 85% of tensile strength of base material. It was decreased by 8.5% when the thickness of specimens and base metal was different, and it was increased by 25% when pres-strain was applied. The crack propagation rate was noticeably decreased around weld line and rapidly increased as it passed through weld line. Reviewing the shape of the crack propagation , crack width around weld line was around the weld zone due to retardation of crack growth , but is became narrow passing weld line due to decreased toughness.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1999.10a
• /
• pp.339-344
• /
• 1999

For the Tailor Welded Blank sheet used for automobile body panel, the characteristics of fatigue strength and crack propagation behavior were studied. The thickness of specimen was machined to be same (0.9mm+0.9mm) and different (0.9mm+2.0mm). As a base test, mechanical properties around welding zone were examined. The results indicated that there were no significant decreases in mechanical properties, but hardness around welding bead is 2.3 times greater than base material. The fatigue strength was the highest when the loading direction was parallel to the welding direction, which was about 85% of tensile strength of base material. It was decreased by 8.5% when the thickness of specimen and base material was different, and it is increased by 25% when pre-strain was applied. The crack propagation rate was noticeable decreased around welding line and rapidly increased as it passed by welding line. Reviewing the shape of the crack propagation, crack width around welding line was wide around the welding zone due to retardation of crack growth, but it became narrow passing welding line due to decreased toughness.