• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.302-307
• /
• 2004

This paper reviewed characteristics of fatigue crack behavior observed by changing various shapes of initial crack and magnitudes of loading in compact tension shear(CTS) specimen subjected to shear loading. In the high-loading condition, fatigue crack under shear loading propagated branching from the pre-crack tip. Meanwhile, the secondary fatigue crack in the low-loading condition which was created in the notch root due to friction on the pre-crack face grew to a main crack. Influenced by the mode II loading condition, fatigue crack propagation retardation appeared in the initial propagation region due to the reduction of crack driving force and friction on crack face. In both cases, however, fatigue cracks grew in tensile mode type. Propagation path of fatigue crack under the shear loading was 70 degree angle from the initial crack regardless of its shape and load magnitude.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.487-490
• /
• 2004

In this paper, we investigated the characteristics of initiation and propagation behavior for fatigue crack observed by changing various shapes of initial crack and magnitudes of loading in modified compact tension shear(CTS) specimen subjected to shear loading. In the low-loading condition, the secondary fatigue crack was created in the notch root due to friction on the pre-crack face grew to a main crack. In the high-loading condition, fatigue crack under shear loading propagated branching from the pre-crack tip. Influenced by the shear loading condition, fatigue crack propagation retardation appeared in the initial propagation region due to the reduction of crack driving force and friction on crack face. In both cases, however, fatigue cracks grew in tensile mode type. The propagation path of fatigue crack under the Mode II loading was 70 degree angle from the initial crack regardless of its shape and load magnitude.

• Journal of Advanced Marine Engineering and Technology
• /
• v.28 no.5
• /
• pp.762-772
• /
• 2004

Fatigue life of a Piston for large liquid Petroleum liquid injection(LPLi) bus engines is analyzed considering effects of cooling condition parameters : temperature of cooling water, and heat transfer coefficients at oil gallery and bottom surface of piston head. Temperature of the piston is analyzed with varying cooling conditions Stresses of the piston from two load cases of pressure loading. and pressure and thermal loading are analyzed Fatigue life under repeated peak pressure and thermal cycle is analyzed by the strain-life theory. For the two load cases, required loading cycles for engine life are defined, and loading cycles to failure and partial damages are calculated. Based on the resulting accumulated fatigue usage factors, endurance of the piston is evaluated and effects of varying cooling condition Parameters are discussed.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.214-219
• /
• 2004

Crack tip behavior of single mode loading condition(mode I)depend on tensile loading component but one of mixed mode loading condition(mode I+II) have influenced on shear loading component like the practical structure. Because crack closure is caused by shear loading component under mixed-mode loading a research on the behavior in the stage of crack initiation and propagation require to be evaluate about crack closure effect by fatigue crack surface friction. For that reasion we examined the behavior at the crack tip by direct measuring method. Measured behavior at the crack tip was analyzed through vector crack tip displacement. As a result, crack propafation equation was corrected by considering with crack closure effect. In addition we compared fatigue fracture crack surface and crack closure level.

• Proceedings of the KSR Conference
• /
• 2009.05a
• /
• pp.1125-1131
• /
• 2009

This paper presents the evaluation of fatigue life for a journal box attached to rolling stock bogie under random dynamic loading condition. Because a journal box was under random dynamic loading conditions, the fatigue life assessment due to these loads requires the analysis considering the multiaxial effect of random dynamic loading. To do this work, the finite element analysis has been conducted to calculate random dynamic response using multiaxial acceleration data. Then, the fatigue life assessment of component has been conducted using vibration fatigue analysis applying the power spectral densities of the responses obtained through the FEA The results of fatigue life assessment were compared to the damage from the strain measurement. This study shows that can be evaluated the fatigue life assessment considering real service condition about a component attached to rolling stock bogie.

• Nuclear Engineering and Technology
• /
• v.33 no.5
• /
• pp.526-538
• /
• 2001

Fatigue tests in air and in room temperature water were performed to obtain comparable data and stable crack measuring conditions. In air environment, fatigue crack growth rate was increased with increasing temperature due to an increase in crack tip oxidation rate. In room temperature water, the fatigue crack growth rate was faster than in air and crack path varied on loading conditions. In simulated light water reactor (LWR) conditions, there was little environmental effect on the fatigue crack growth rate (FCGR) at low dissolved oxygen or at high loading frequency conditions. While the FCGR was enhanced at high oxygen condition, and the enhancement of crack growth rate increased as loading frequency decreased to a critical value. In fractography, environmentally assisted cracks, such as semi-cleavage and secondary intergranular crack, were found near sulfide inclusions only at high dissolved oxygen and low loading frequency condition. The high crack growth rate was related to environmentally assisted crack. These results indicated that environmentally assisted crack could be formed by the Electrochemical effect in specific loading condition.

• Journal of the Korean Society of Safety
• /
• v.28 no.3
• /
• pp.1-5
• /
• 2013

In order to evaluate fatigue endurance for an MTB(mountain bike) frame, FEM(finite element method) analysis was performed. For evaluating the fatigue endurance of the MTB frame, the S-N data for Al-6061 fillet weldment were compared with the stress analysis results through FEM analysis of the frame. Three loading condition, pedalling, horizontal and vertical loading conditions were considered for fatigue endurance evaluation. Horizontal loading(+1200 N) condition was found to be the most severe to the frame. The maximum von Mises stress of the frame under horizontal loading(+1200 N) condition was determined 294 MPa through FEM analysis of the frame. Conclusively, on the basis of fatigue strength of 200 MPa at the number of cycles of 50,000, the MTB frame has an improper safety factor of approximately 0.25, suggesting that this frame needs reinforcement.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.20 no.1
• /
• pp.141-146
• /
• 2012

Aluminum alloys have been used with various thicknesses suitable for light weight of structure. It is known that the thickness effect of material is an important factor affecting fatigue crack propagation under constant fatigue stress condition. In this work, we presented the behavior of fatigue crack propagation in thin plate compared to thick plate Al 2024-T3 alloy with referred thickness effect in a correlative equation determined by the shape factor and the loading factor. We chose two factors that are used in the correlative equation with considering that the experiments were carried out under a constant fatigue stress condition. The thickness ratio of thin plate compared to thick plate and the equivalent effective stress intensity factor ratio depending on thickness were chosen as shape and loading factors. A correlative equation is utilized to determine the equivalent effective stress intensity factor range of thin plate and identify the degree of increasing phenomenon of fatigue life in thin plate compared to thick plate.

• Journal of the Korean Society for Precision Engineering
• /
• v.24 no.2 s.191
• /
• pp.103-109
• /
• 2007

In fatigue life prediction, it is important that fatigue life is affected by crack closure phenomenon in thin sheet Al alloy. In this research, we attempt to (1)analyze the characteristics of fatigue crack propagation in constant loading condition for thin sheet Al 2024-T3 alloy which is generally used in transportation structures, (2)identify the crack closure phenomenon in thin sheet comparing experimental results of thin and thick sheet specimen under same fatigue loading condition. In using the fatigue related material constants from these fatigue crack propagation analysis, we attempt to (3)operate the fatigue life estimating process with considering crack closure phenomenon and (4)analyze the experimental and prediction results of fatigue life in thin sheet Al alloy.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.7
• /
• pp.22-28
• /
• 2019

In this study, as part of the subway braking system, the structural analysis was performed with the fatigue analysis by comparing subway brake disc and wheel-type brake. When structural analysis was performed, it was possible to verify that the wheel-type brake were higher than the brake discs in case of total deformation. As the same loading conditions were given to the subway brake disc and wheel-type brake, wheel-type brakes was shown to have more deformation than brake disk but lower damage than the subway brake disc. Comparing with each fatigue loading condition, the maximum fatigue life for 'Sample history' is found to be about 60 times longer than for 'SAE bracket history'.