• Journal of Ocean Engineering and Technology
• /
• v.15 no.2
• /
• pp.94-98
• /
• 2001

fatigue life and nondestructive evaluation were examined experimentally using surface crack specimen and compact tension specimen of 5083 aluminium alloy. Acoustic emission signals emanated during failure of aluminum alloys has been the subject of numerous investigations. Possible sources of AE during deformation have been suggested as the dislocations, fracture of brittle particles and debonding of these particles from the alloy matrix. Fatigue life and penetration behavior of long surface crack can be evaluated quantitatively using K values proposed by authors. The influence of stress ratio on the frequency characteristics of AE signals were investigated.

• Structural Engineering and Mechanics
• /
• v.19 no.3
• /
• pp.261-279
• /
• 2005

The hot spot stress approach is usually adopted in the fatigue design and analysis of tubular welded joints. To apply the hot spot stress approach for fatigue evaluation of long span suspension bridges, the FEM is used to determine the hot spot stress of critical fatigue location. Using the local finite element models of the Tsing Ma Bridge, typical joints are developed and the stress concentration factors are determined. As a case for study, the calculated stress concentration factor is combined with the nominal representative stress block cycle to obtain the representative hot spot stress range cycle block under traffic loading from online health monitoring system. A comparison is made between the nominal stress approach and the hot spot stress approach for fatigue life evaluation of the Tsing Ma Bridge. The comparison result shows that the nominal stress approach cannot consider the most critical stress of the fatigue damage location and the hot spot stress approach is more appropriate for fatigue evaluation.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1127-1132
• /
• 2003

Suspension system of vehicle have enough endurance during its life time to protect passenger. Spring is one of major part of vehicle. Thus, a fatigue strength evaluation for leaf spring based on road load response was carried out. At first, strain of leaf spring is measured on the city condition and proving ground condition. And next, the damage analysis of road load response data was carried out. And fatigue test of leaf spring were also carried out. Based on -N life relation, fatigue life of leaf spring was evaluated at belgian mode, city mode and drawing test specification. After that, it is compared the design life of leaf spring and evaluated fatigue life by belgian mode, city mode and drawing test specification. From the above, the maximum load-fatigue life relation of leaf spring was defined by test. and new test target of belgian mode and city mode was proposed to accept design specification of leaf spring. It is expect that proposed test target can verify leaf spring fatigue endurance at specific road condition.

• Proceedings of the KSR Conference
• /
• 2004.10a
• /
• pp.710-715
• /
• 2004

To evaluate the fatigue lifetime of structures, it is necessary to identify the value of parameters through tests or literature. it is difficult for field engineers to get the necessary data through tests from the viewpoint of time and cost. In this study. we surveyed literature and proposed a procedure to identify the fatigue parameters for fatigue life evaluation by local strain approach.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.9
• /
• pp.1498-1506
• /
• 1997

Procedures are presented for influence of shot peening on fatigue strength, fatigue life and effects of shot peening are discussed from experiments were taken between shot peened and unpeened SPS5, SM45C specimens. After the residual stress on shot peened specimens was measured by X-ray diffractometer, rotating bending fatigue tests were carried out. In addition, the compressive residual stress profile was obtained by the superposition method of three stresses which is based on Al-Obaid's equation. Predicted fatigue life considering residual stress profile which was obtained by the Al-Obaid's equation and another predicted fatigue life considering residual stress profile which was measured in test were compared. For the purpose of predicting fatigue life, Morrow's equation considering the residual stress and mean stress was used.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.9
• /
• pp.1391-1398
• /
• 2004

Railway wheels and axles belong to the most critical components in railway vehicles. The service conditions of railway vehicles became more severe in recent years due to the increase of speed. Therefore, a more precise evaluation of wheelset life and safety has been requested. Wheel/rail contact fatigue and thermal cracks due to braking heat are two main mechanisms of the railway wheel failure. In this paper, an evaluation procedure for the contact fatigue life of railway wheel is proposed. One of the main sources of the contact zone failure is the residual stress. The residual stress on wheel is formed during the manufacturing process which includes a heat treatment, and then is changed by contact stress developed by wheel/rail contact and thermal stress induced by braking. Also, the cyclic stress history for fatigue analysis is determined by applying finite elements analysis for the moving contact load. The objective of this paper is to estimate fatigue life by considering residual stress due to heat treatment, braking and repeated contact load, respectively.

• 한국기계연구소 소보
• /
• s.15
• /
• pp.75-87
• /
• 1985

A review was performed on fatigue life prediction and strength evaluation of shot peened parts. Fatigue strength of machine parts can be improved by shot peening due to compressive residual stresses on such parts. Compressive residual stress cannot be uniquely define by peening intensity. Several measuring methods of residual stress and the principle of hole drilling method are presented. Exploratory measurement of residual stress was performed on the shot peened SM35C plate with the hole drilling method. Fatigue life and failure location of shot peened parts under bending load can be predicted by a damage parameter which is incorporated with material properties, residual stress, and applied stress conditions. Some method are presented to predict the fatigue strength of shot peened parts at any given life. Shot peening gives its full benefit to the notched machine parts of high strength steels.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.13 no.6
• /
• pp.56-62
• /
• 2005

The fatigue analysis and lifetime evaluation are very important in design procedure to assure the safety and reliability of the rubber components. Fatigue lifetime prediction methodology of the rubber component was proposed by incorporating the finite element analysis and fatigue damage parameter from fatigue test. Finite element analysis of 3D dumbbell specimen and rubber component were performed based on a hyper-elastic material model determined from material test. The Green-Lagrange strain at the critical location determined from the FEM was used for evaluating the fatigue damaged parameter of the natural rubber. Fatigue life of the rubber component are predicted by using the fatigue damage parameter at the critical location. Predicted fatigue lifes of the rubber component agreed fairly well the experimental fatigue lives.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1270-1274
• /
• 2003

The objective of this paper is to introduce the standard of evaluation methods and fatigue test for linear motion rolling bearing. In particular, attention well be given to the list of evaluation and fatigue results in this paper. The life of a linear motion rolling bearing is given by the length of distance covered between the connection parts before the first evidence of fatigue develops in the material of one of the raceways of rolling elements. The main factors that contribute to fatigue failures include: Number of load cycles experienced; Range of stress experienced in each load cycle; Mean stress experienced in each toad cycle; Presence of local stress concentrations.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1995.04b
• /
• pp.39-44
• /
• 1995

The gas nitro-carburizing treatment with the merits of carburizing and nitriding treatment is recently applied to transmission gears. the shafls of an engine oil pump and steering shafls. For all that, the researches of the gas nitro-carburizing treatment are short of the fatigue behavior and the evaluation of fatigue life. In this paer, it is examined for the effect of inclusions and hole defects with fatigue limit and the evaluation of the fatigue strengthaccording tothe hardness and resifualstress with the specimen of a notro-carburizing treatment.