• Journal of the Korean Society of Safety
• /
• v.17 no.1
• /
• pp.33-38
• /
• 2002

SS41 material is welded automatically and is investigated some effects of the welding residual stress on the growth and propagation of fatigue crack, so as to study the fatigue behaviour in the welding residual stress field. The summarized results are as follows; 1) In case of the load amplitude is constant, as the stress ration is changing to 0.1, 0.33 and 0.5 the propagation life is constant but the initiation life decreases. And than, when maximum load or minimum load is constant, s the stress ration increases the initiation life and propagation life. 2) It was shown that the fatigue crack propagation ratio da/dn was almost constant regardless of the stress ratio change at constant load amplitude and that the larger stress ratio, the slower was the fatigue crack propagation ratio. 3) The opening ratio U is influenced by $K_{max}$ but it isn't only the function of $K_{max}$ because data range is very large. 4) The fatigue life of the specimens on tensile compressive residual stress field was decreased and increased respectably more than that of the base metal.

• Journal of Ocean Engineering and Technology
• /
• v.2 no.2
• /
• pp.61-70
• /
• 1988

In order to consider the concept of the fitness for purpose'in fatigue design of offshore structure, fracture mechanics is applied to evaluate initial or weld defects. Generally, linear elastic fracture mechanics has been applied to tstimate initial fatigue crack propagation rate as well as long fatigue crack propagation rate. But, initial fatigue crack propagation rate in elasto-plastic notch field may not be characterized by application of stress intensity factor range .DELTA. K, because plastic effect due to stress concentration of notch may contribute to initial crack propagation. Therefore, to introduce the plastic effect into fatigue crack driving force, in this studty, the evaluating method of J-integral range .DELTA. J, was developed by willson was modified for application to notch field. In calculation of .DELTA. J obtained from the modified J-integral, stress gradient and crack closure behavior in the notch field were considered. The initial crack propagation rates in the notch fields of mild steels and high tensile strength steels were correlated to .DELTA. J. As the result, it was cleared that the present .DELTA. J is applicable to charachterize the fatigue crack propagation rates in both the elastic and elasto-plastic notch fields.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.9
• /
• pp.1691-1699
• /
• 1992

The experimental results of fatigue crack propagation under constant amplitude loading show that intra-and inter-specimen variability exist. In this paper, a stochastic model for the estimation of mean and variance of crack propagation life is presented To take into account the intra-specimen variability, the material resistance against crack propagation is treated as an 1-dimensional spatial stochastic process, i. e. random field, varying along the propagation path. For the inter-specimen variability, C in paris equation is assumed to be a random variable. Compared with experimental results reported, the present method well estimate the variation in fatigue crack propagation life. And it is confirmed that the thicker the specimen thickness is, the less the variation of propagation life is.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.3
• /
• pp.20-28
• /
• 1997

The fatigue crack propagation properties and fatigue life of two kinds of Al body panel for automobile were examined experimentally by using the plate specimen and the single spot welding specimen. The fatigue limit of spot welding specimens was lower than that of a plate specimen. The fatigue limit was similar in two kinds of spot welding specimen. The shape and size of crack propagation were observed and measured on beach mark of fracture surface. The crack propagation of surface crack specimen showed almost same tendency to that of a thick plate as almost semi-elliptical. In spot welding specimen, the fatigue crack occurred in inside surface of nugget area was almost semi-elliptical. The crack growth rate can be explained using equation of stress intensity factors.

• Transactions of Materials Processing
• /
• v.10 no.3
• /
• pp.179-184
• /
• 2001

The influence of the fatigue crack propagation by shot peening was studied in this paper. Fatigue tests were carried out on the unpeened and shot peened CT specimens. The changes of mechanical properties, residual stress, fatigue fracture surface etc. by shot peening were investigated. The mechanical properties, residual stress, fatigue surface etc. by shot peening were investigated. The mechanical peened specimen improved in fatigue life up to 14% by shot peening. The reason of increase in the fatigue life was closely related with the compressive residual stress, which was 519.7MPa on surface. Another reason was the constraint on crack opening on surface region, it is due to the decrease in slope of crack propagation direction.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.6
• /
• pp.867-876
• /
• 1987

Corrosion fatigue fracture with change in the grain size of M.E.F. dual phase steel is investigated in 3.5% NaCI aqueous solution at pH 2, 4, 6, 9, and 11. Generally speaking, decrease in corrosion fatigue life is strongly dependent on decrease in pH and slightly on the grain size. For the B material with the big grain size, the fatigue life is small due to its large reduction ratio of corrosion fatigue life. The influence of grain size on the reduction ratio of corrosion fatigue life is large at pH 11-6. Whi9le at pH 4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. The larger grain size and the lass pH result in the greater influence on corrosion fatigue crack propagation rate. As pH decreases, the plateau portion in the crack propagation rate curves of the B material are distinct. Crack propagation rate curves become slow down at high .DELTA.K range because crack closure effect by minute corrosion products inside crack causes the oxidation corrosion action less effective for a certain period of time. In A material with small grain size, fatigue life is increased in proportion with increase of martensite intergranular which brings forth restraining the crack propagation decreases crack propagation rate. Corrosion pit which is created in the surface of specimen is found at pH 6,4 and 2 which is noticeable and the unevenness of the surface of the specimen becomes severe as pH decreases. The unevenness of corrosion fatigue fracture surface is severe as the effect of pH increases i.e. as pH decreases. In proportion with increase in the grain size and decrease in pH, the aspect of brittle fracture becomes evident.

• Journal of Mechanical Science and Technology
• /
• v.17 no.6
• /
• pp.796-804
• /
• 2003

The use of fracture mechanics has traditionally concentrated on crack growth under an opening mechanism. However, many service failures occur from cracks subjected to mixed-mode loading. Hence, it is necessary to evaluate the fatigue behavior under mixed-mode loading. Under mixed-mode loading, not only the fatigue crack propagation rate is of importance, but also the crack propagation direction. In modified range 0.3$\leq$a/W$\leq$0.5, the stress intensity factors (SIFs) of mode I and mode II for the compact tension shear (CTS) specimen were calculated by using elastic finite element analysis. The propagation behavior of the fatigue cracks of cold rolled stainless steels (STS304) under mixed-mode conditions was evaluated by using K$\_$I/ and $_{4}$ (SIFs of mode I and mode II). The maximum tangential stress (MTS) criterion and stress intensity factor were applied to predict the crack propagation direction and the propagation behavior of fatigue cracks.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1508-1512
• /
• 2003

In this study, retardation behavior of fatigue crack under single overloading of the mixed mode state was experimentally investigated. To produce single overload in the mixed mode I+II state, the compact tension shear (CTS) specimen and loading device were used. The propagation tests for fatigue crack were performed under mode I and mixed-mode loading overloading afterwards. We examined the observed deformation aspects, the variation of fatigue life and crack propagation rate, and the aspects of retardation behavior from tests. The retardation effect of mixed-mode single overload on fatigue crack propagation behavior was smaller than that of mode I single overload. Also the loading modes of variable and constant amplitude loads have influence on the retardation behavior of fatigue cracks.

• Journal of the Korean Society for Precision Engineering
• /
• v.13 no.8
• /
• pp.80-87
• /
• 1996

The present paper will give some results of the fatigue behavior of typical axi-symmetric forward extrusion die. The extrusion process is analyzed by rigid-plastic FEM and the deformation analysis of extrusion die is conducted by elasto-plastic FEM. To approach the crack problem LEFM (Linear Elastic Fracture Mechanics) is introduced. Using special element in order to conside the sigularity of stress/ strain in the vicinity of the crack tip, stress intensity factor and the effective stress intensity factor is calculated. Applying proper fatigue crack propagation criterion such as Paris/Erdogan fatigue law and maximum principal criterion to these data, then, the angle and the direction of fatigue crack propagation is simulated. In result, it is proved that the simulated fatigue crack propagates in the zigzag path along the radial direction and fatigue life of the extrusion die is evaluated by using the computed crack growth rate.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.25 no.2
• /
• pp.87-104
• /
• 1989

Recently, with the tendency of more lightening, high-strength and high-speed in the marine industries such as marine structures, ships and chemical plants, the use of the aluminium Alloy is rapidly enlarge and there occurs much interest in the study of corrosion fatigue crack characteristics. In this paper, the initiation of surface crack and the propagation characteristics on the base metal and weld zone of 5086-H116 Aluminium Alloy Plate which is one of the Al-Mg serious alloy(A5000serious) used most when building the special vessels, were investigated by the plane bending corrosion fatigue under the environments of marine, air and applying cathodic protection. The effects of various specific resistances on the initiation, propagation behavior of corrosion fatigue crack and corrosion fatigue life in the base metal and heat affected zone were examined and its corrosion sensitivity was quantitatively obtained. The effects of corrosion on the crack depth in relation to the uniform surface crack length were also investigated. Also, the structural, mechanical and electro-chemical characteristics of the metal at the weld zone were inspected to verify the reasons of crack propagation behavior in the corrosion fatigue fracture. In addition, the effect of cathodic protection in the fracture surface of weld zone was examined fractographically by Scanning Electron Microscope(S.E.M.). The main results obtained are as follows; (1) The initial corrosion fatigue crack sensitibity under specific resistance of 25Ω.cm% show 2.22 in the base metal and 19.6 in the HEZ, and the sensitivity decreases as specific resistance increases (2) By removing reinforcement of weldment, the initiation and propagation of corrosion crack in the HAZ are delayed, and corrosion fatigue life increases. (3) As specific resistance decreases, the sensitivity difference of corrosion fatigue life in the base metal and HAZ is more susceptible than that of intial corrosion fatigue crack. (4) Experimental constant, m(Paris' rule) in the marine environment is in the range of about 3.69 to 4.26, and as specific resistance increases, thje magnitude of experimental constant, also increases and the effect by corrosion decreases. (5) Comparing surface crack length with crack depth, the crack depth toward the thickness of specimen in air is more deeply propagated than that in corrosion environment. (6) The propagation particulars of corrosion fatigue crack for HAZ under initial stress intensity factor range of $\Delta$k sub(li) =27.2kgf.mm super(-3/2) and stress ratio of R=0 shows the retardative phenomenon of crack propagation by the plastic deformation at crack tip. (7) Number of stress cycles to corrosion fatigue crack initiation of the base metal and the welding heat affected zone are delayed by the cathodic protection under the natural sea water. The cathodic protection effect for corrosion fatigue crack initiation is eminent when the protection potential is -1100 mV(SCE). (8) When the protection potential E=-1100 mV(SCE), the corrosion fatigue crack propagation of welding heat affected zone is more rapid than that of the case without protection, because of the microfissure caused by welding heat cycle.