• Journal of the Korean Society for Precision Engineering
• /
• v.15 no.10
• /
• pp.113-119
• /
• 1998

Ship structures and aircraft structures are consisted of thin sheet alloy, so it is very important to understand the characteristics of fatigue crack propagation of that material and to establish the data base. The data for fatigue crack propagation behavior scatter very much even under identical experimental conditions with constant loading. The behavior of fatigue crack propagation under regular and irregular cyclic loadings is known to be highly affected by complicated factors such as plastic zone developed at the vicinity of crack tip and reduction of cross sectional area. In this paper, the controlled stress amplitude and overload fatigue crack propagation tests have been conducted to investigate the effect of varying factors such as plastic zone size near the crack tip and area reduction factor (AF) on the fatigue crack propagation behavior A better simulation of fatigue crack propagation behavior is found to be obtainable by using Wheeler and Willenborg models with AF effect.

• Journal of Advanced Marine Engineering and Technology
• /
• v.32 no.6
• /
• pp.834-840
• /
• 2008

We carried out fatigue testing with materials of aluminum alloyC7075-T6, 2024-T4) by rotary bending fatigue tester. We investigated fatigue limit, fatigue crack initiation, fatigue crack propagation behavior and possibility of fatigue life prediction to the different small circular hole defect. The summarized result are as follows; Fatigue limit of the smooth specimens were related tensile strength and yield strength. In case of more large applied stress and small circular hole crack defect, the fatigue crack was grown rapidly. The fatigue crack propagation behavior proceed at according to inclusion. Fatigue crack propagation ratio appeared instability and retardation phenomenon in the first half of fatigue life but appeared stability and replied in the latter half. On other hand, this experimental data of the materials are appeared fatigue life predictability.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.759-764
• /
• 1997

In this study, Fatigue behavior of laser weldment in heterogeneous materials was investigated. Fatigue strength test and fatigue crack propagation test were performed for specimens with laser weldment in heterogeneous materials, and hardness test was performed. From the fatigue strength test. it was observed that the difference of strength between heterogeneous materials had eflect on crack initiation position and fatigue limit. From the fatigue crack propagation test. it was observed that fatigue behavior of laser weldment in heterogeneous materials is different from that in same materials. The difference of strength between heterogeneous materials and laser weldment had effect on fatigue crack propagation rate.

• Journal of the Korean Society of Mechanical Technology
• /
• v.13 no.2
• /
• pp.31-37
• /
• 2011

Sheet aluminum alloys have been used in manufacturing of machine structures. In fatigue crack propagation behavior of thin sheet aluminum alloys, it is important that fatigue crack growth rate is affected by crack closure phenomenon. In this work, we analyzed the characteristics of fatigue crack propagation behavior in experiment of constant stress condition for thin sheet Al 2024-T3 alloys, and identified the retardation behavior of crack growth by comparing experimental results of thin and thick plate specimen. We attempt to operate the fatigue life estimating process using the fatigue related material constants from referred fatigue crack propagation analysis. And we analyzed the experimental and prediction results of fatigue life of thin sheet aluminum alloy in order to identify the relation between retardation behavior of fatigue crack growth and crack closure phenomenon.

• Journal of Mechanical Science and Technology
• /
• v.17 no.6
• /
• pp.796-804
• /
• 2003

The use of fracture mechanics has traditionally concentrated on crack growth under an opening mechanism. However, many service failures occur from cracks subjected to mixed-mode loading. Hence, it is necessary to evaluate the fatigue behavior under mixed-mode loading. Under mixed-mode loading, not only the fatigue crack propagation rate is of importance, but also the crack propagation direction. In modified range 0.3$\leq$a/W$\leq$0.5, the stress intensity factors (SIFs) of mode I and mode II for the compact tension shear (CTS) specimen were calculated by using elastic finite element analysis. The propagation behavior of the fatigue cracks of cold rolled stainless steels (STS304) under mixed-mode conditions was evaluated by using K$\_$I/ and $_{4}$ (SIFs of mode I and mode II). The maximum tangential stress (MTS) criterion and stress intensity factor were applied to predict the crack propagation direction and the propagation behavior of fatigue cracks.

• Journal of the Korean Society for Precision Engineering
• /
• v.19 no.12
• /
• pp.127-133
• /
• 2002

The objective of this study is to investigate fatigue life and fatigue crack propagation behavior The experiment of fatigue life for MMC have been carried out for the stress ratio R＝0.1 at 20Hz. Fatigue lift limit of AC4CH alloy is about 70 ㎫ and Fatigue limit of MMC has been increment to 120 ㎫, therefore, fatigue limits of MMC is about 71 % higher than that of AC4CH alloy Crack propagation tests on half-size CT specimen of thickness 12.5mm were conducted by using sinusoidal waveform. The crack length was monitored by compliance method. Test conditions were at 0.1 and 0.05 of load ratio at 10Hz of loading frequency and test load was 2.3kN. The effects of stress ratio on the fatigue crack propagation behavior for MMC was discussed within the Paris law. As the results of this study, Fatigue crack propagation increased with increasing the load ratio.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.9
• /
• pp.131-139
• /
• 2001

The use of fracture mechanics has traditionally concentrated on crack growth under an opening mechanism. However, many service failure occur from cracks subjected to mixed mode loadings. Hence, it is necessary to evaluate the fatigue behavior under mixed mode loading. Under mixed mode loading conditions, not only the fatigue crack propagation rate is of importance, but also the crack propagation direction. The mode I and II stress intensity factors of CTS specimen were calculated using elastic finite element method. The propagation behavior of the fatigue crack of the STS304 steeds under mixed mode loading condition was evacuated by using stress intensity factors $K_I$ and $K_II. The MTS criterion and effective stress intensity factor were applied to predict the crack propagation direction and the fatigue crack propagation rate.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.6
• /
• pp.82-88
• /
• 2000

The effect of the welding for the offshore structure in the TMCP steel on the fatigue crack propagation rate and crack opening-and-closure behavior was examined. The welding anisotropy of the TMCP steel and crack propagation characteristics of the excessive loading were reviewed. (1) It seemed that a heat which was generated by the welding made a compressive residual stress over the base metal, so fatigue crack propagation rate was placed lower than in case of the base metal. (20 In the base metal, an effect of the anisotropy which has an effect of fatigue crack propagation rate of the excessive load and the constant amplitude laos was not found but in the welding material case, fatigue crack propagation rate of the excessive load in the specimen of the width direction was located in the retard side as compared with a specimen rolling direction. (3) A crack opening ratio of the used TMCP stel in this study was not changed after excessive loading but a retard phenomenon of crack propagation was observed. Consequently, it was thought that all of the retard phenomenon of crack propagation did not only a cause of the crack opening-and-closure phenomenon.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2002.04a
• /
• pp.64-69
• /
• 2002

The purpose of this paper was to investigate the welding characteristics and the fatigue crack propagation behavior of titanium commonly using power station, aircraft and ship. The experimented material was TIG welded in order to look over the characteristics according to the notch position and compare with other materials. We compared and reviewed the fatigue crack propagation behavior of nontch base metal and welded specimens having different notch position to evaluate the fatigue crack propagation behavior by welding condition.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.11
• /
• pp.69-76
• /
• 1997

The rotating bending fatigue tests were performed using the specimens taken from Cr-Mo-V steel, widely sued in thermal power plant turbines, at various temperatures such as room temperature, 300 .deg. C, 425 .deg. C and 550 .deg. C. The characteristics of fatigue crack propagation were examined and analyzed by using fracture mechanics parameter. The plastic replica method was also applied in order to measure the crack length on the basis of serial observation of fatigue crack propagation behavior on the defected specimen surface. The fatigue crack propagation behavior of Cr-Mo-V steel was investigated within the frame work of elastic-plastic fracture mechanics. The propagation law of fatigue crack is obtained uniquely by using the term .sigma. $^{n}$ sub a/where .sigma. $_{a}$ is the service stress, a is the crack length and n is a constant. The values of constant n are nearly equal to 2.48, 2.60 and 8.61 at room temperature, 300 .deg. C and 425 .deg. C.