• Journal of Welding and Joining
• /
• 제18권2호
• /
• pp.77-85
• /
• 2000

There are many weld defects such as surface crack, lack of fusion, and incomplete penetration (IP) in the butt joint weld of existing steel bridges. The crack-like defects may significantly reduce the fatigue life of the structure. This paper presents the procedure and the results of the fatigue life assessment of the butt joints with weld defects in the existing steel girder bridge. The butt joint welds with incomplete penetration were instrumented with strain gages to determine the stress histogram under normal traffic. Based on the measured stress histogram the crack propagation analysis were performed for the fatigue life assessment. By using the suggested procedure and methodology, one can decide the time of periodic inspection and the necessity of repair of the butt joint welds with serious weld defects in the existing steel bridge.

• 대한기계학회논문집A
• /
• 제38권10호
• /
• pp.1163-1169
• /
• 2014

본 연구에서는 자동차 서스펜션 구조에 일반적으로 사용되는 용접부 형상에 대하여 굽힘 하중에 의한 피로수명을 예측할 수 있는 절차를 개발하였다. 이종 재료로 이루어진 실제 제품 용접 연결부의 피로수명 예측을 위해, 복잡한 형상의 제품을 단순화한 용접 시편을 설계하고 이에 대한 굽힘 피로 시험을 진행한 후 모멘트-피로수명(M-N) 선도를 제시하였다. 응력 집중에 의한 영향을 분석하기 위해 시편의 형상을 모델링 한 후 정적 하중에 대한 유한요소해석을 수행하여 균열 발생부의 응력을 구하고 응력-피로수명(S-N) 선도를 제시하였다. 유한요소해석을 통해 구한 응력과 이론 계산을 통해 구해준 응력을 이용하여 응력집중계수를 계산하였고, 응력집중부의 피로평가 방법 개선을 위해 보편적으로 사용되는 피로노치계수 평가법과 굽힘 피로 시험 결과를 비교 검토하였다. 그 결과, 이종 재질 용접 연결부의 정확한 피로 수명평가를 위해서는 기하형상을 고려한 피로노치계수 평가 분석뿐만 아니라 두 소재의 맞대기 용접 시편에 대한 피로 시험을 수행해 주어야 할 것으로 판단된다.

• Nuclear Engineering and Technology
• /
• 제45권1호
• /
• pp.99-106
• /
• 2013

Thermal fatigue is a significant long-term degradation mechanism in nuclear power plants. In particular, as operating plants become older and life time extension activities are initiated, operators and regulators need screening criteria to exclude risks of thermal fatigue and methods to determine significant fatigue relevance. In general, the common thermal fatigue issues are well understood and controlled by plant instrumentation at fatigue susceptible locations. However, incidents indicate that certain piping system Tee connections are susceptible to turbulent temperature mixing effects that cannot be adequately monitored by common thermocouple instrumentations. Therefore, in this study thermal fatigue evaluation of piping system Tee-connections is performed using the fluid-structure interaction (FSI) analysis. From the thermal hydraulic analysis, the temperature distributions are determined and their results are applied to the structural model of the piping system to determine the thermal stress. Using the rain-flow method the fatigue analysis is performed to generate fatigue usage factors. The procedure for improved load thermal fatigue assessment using FSI analysis shown in this study will supply valuable information for establishing a methodology on thermal fatigue.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 추계학술대회 초록집
• /
• pp.189.2-189.2
• /
• 2010

The purpose of this study is fatigue damage assessment for large sized casting parts (hub and mainframe) of the 3MW offshore wind turbine by computer simulation. Hub and mainframe durability assessment is necessary because wind turbine have to guarantee for 20 years. Fatigue life evaluation must be considered all of fatigue load conditions as the components are wind load transmission path. Palmgren-Miner linear damage accumulation hypothesis is applied for fatigue life estimation with stress-life approach. S-N curve for the spheroid graphite cast iron EN-GJS-400-18-LT is derived according to durability guidelines. Reduction factors were applied for survival probability, surface roughness, material quality and partial safety factor according to Germanischer Lloyd rules. To calculate fatigue damage, stress tensors, extracted from the unity load calculation from ANSYS is multiplied with time track of fatigue loads extracted from GH bladed. Damage accumulation is performed with all of fatigue load conditions at each finite element nodes. In this study maximum nodal damage value is under 1.0. casted parts are safe. This research was financially supported by the Ministry of Knowledge Economy(MKE), Korea Institute for Advancement of Technology(KIAT) and Honam Leading Industry Office through the Leading Industry Development for Economic Region.

• International Journal of Naval Architecture and Ocean Engineering
• /
• 제3권2호
• /
• pp.116-121
• /
• 2011

The Spectral Fatigue Analysis is representative fatigue life assessment method for vessels. This Analysis is performed generally for the whole vessel and many assessment sites. The spectral fatigue analysis is performed through the process of hydrodynamic response analysis, global structural analysis, local structural analysis and calculation of fatigue damage. In these processes, fatigue damage is affected by many variables. The representative variables are S-N curve data, wave scatter data, wave spectrum, bandwidth effect and etc. In this paper, the effects of these variables to the fatigue damage are analyzed through the spectral fatigue analysis for 170k LNGC.

• Journal of Welding and Joining
• /
• 제35권1호
• /
• pp.61-67
• /
• 2017

Recent studies on the fatigue assessment of high strength steel weld based on the fracture mechanics have frequently raised the problems related to the conservatism in the fatigue crack growth rate specified in the relevant design code. The purpose of this study is to evaluate the effect of the fatigue crack growth parameter on the fatigue life for the low carbon steel weld. In order to do it, the fatigue tests with the constant stress ratio were performed to evaluate the fatigue crack growth rate in the butt weld of SM490. And the fatigue crack growth parameters of the weld were evaluated in accordance with ASTM E647. From the comparative fatigue assessment results, it was found that the fatigue crack growth rate specified in the relevant design code was too conservative to estimate the residual fatigue life of welded structure. So, in order to get the more reliable results, it was recommended that the fatigue life estimation based on the fracture mechanics be performed with the fatigue crack growth parameter specified by test.

• 기본간호학회지
• /
• 제11권2호
• /
• pp.220-225
• /
• 2004

Purpose: The purpose of this study was to test the reliability and validity of FAI and to apply it in Korea. Method: Data were collected from 180 middle-age women. The questionnaire, which was originally developed by Schwartz, Jandorf & Krupp, was analyzed using Cronbach's a and factor analysis. Results: Cronbach's a for the FAI was .9198. As a result of item analysis, 27 items were selected from the total of 29 items, Items that showed low correlation with the total scale were excluded. Six factors were fixed from the data analysis performed using principle component analysis and varimax rotation. These six factors account for 65.3% of total variance. The first factor was global fatigue severity, and the second one was fatigue consequences. The other factors were method of fatigue reduction, fatigue caused by exercise, fatigue caused by routine activity, and fatigue caused by stress and depression, sequentially. Conclusion: The reliability and validity of FAI were verified.

• Journal of Ship and Ocean Technology
• /
• 제11권1호
• /
• pp.25-35
• /
• 2007

This paper is concerned with the fatigue strength assessment of tendon porch found which is categorized as the special structural member in TLP. Large-scale tendon porch specimens have been designed and fabricated with API 2W Gr.50 steel recently produced by POSCO. Fatigue test has been carried out for three tendon porch specimens under various load level. Fatigue strength has been evaluated based on the nominal stress range and the results are compared with the fatigue design curve of DnV RP-C203. From the present experimental study, it has been found that the porch specimens satisfy the fatigue design rule although test was carried out under the positive stress ratio. It can be, therefore, said that the API 2W steel produced by POSCO possess sufficient fatigue strength.

• Journal of Welding and Joining
• /
• 제18권2호
• /
• pp.204-204
• /
• 2000

There are many weld defects such as surface crack, lack of fusion, and incomplete penetration(IP) in the butt joint weld of the existing steel bridges. The crack-like defects may significantly reduce the life of the structure. This paper presents the procedure and the results of the fatigue life assessment of the butt joints with weld defects in the existing steel girder bridge. The butt joint welds with incomplete penetration were instrumented with strain gages to determine the stress histogram under normal traffic. Based on the measured stress histogram the crack propagation analysis were performed for the fatigue life assessment. By using the suggested procedure and methodology, one can decide the time of periodic inspection and the necessity of repair of the butt joint welds with serious weld defects in the existing steel bridge. (Received October 1, 1999)

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2006년도 춘계학술대회 논문집
• /
• pp.385-386
• /
• 2006

A brake disk in railway vehicle is safety part. Requirements not only in performance but also in comfort, serviceability and working lifetime are high and rising. In this study, we carried out fatigue test and thermal stress analysis. To determine a pressure distribution, contact pressure analysis precede thermal stress analysis. Especially, characteristics of the brake disk were analyzed in considering intial velocity, and thickness of a frictional plate. Form the comparing the results of experiment and FEM analysis, fatigue characteristic and fatigue life assessment ok a brake disk of railway vehicle were performed.