• 한국세라믹학회지
• /
• 제31권12호
• /
• pp.1577-1587
• /
• 1994

TiO2 thin films with the substitution of oxygen with nitrogen were deposited on silicon substrate by metalorganic chemical vapor deposition (MOCVD) using Ti(OCH(CH3)2)4 (titanium tetraisopropoxide, TTIP) and N2O as source materials. X-ray diffraction (XRD) results indicated that the crystal structure of the deposited thin films was anatase TiO2 with only (101) plane observed at the deposition temperatures of 36$0^{\circ}C$ and 38$0^{\circ}C$, and with (101) and (200) plane at above 40$0^{\circ}C$. Raman spectroscopic results indicated that the crystal structure was anatase TiO2 in accordance with the XRD results without any rutile, fcc TiN, or hcp TiN structure. No fundamental difference was observed with temperature increase, but the peak intensity at 194.5 cm-1 increased with strong intensity at 143.0 cm-1 for all samples. The crystalline size of the films varied from 49.2 nm to 63.9 nm with increasing temperature as determined by slow-scan XRD experiments. The refractive index of the films increased from 2.40 to 2.55 as temperature increased. X-ray photoelectron spectroscopy (XPS) study showed only Ti 2s, Ti 2p, C 1s, O 1s and O 2s peaks at the surface of the film. The composition of the surface was estimated to be TiO1.98 from the quatitative analysis. In the bulk of the film Ti 2s, Ti 2p, O 1s, O 2s, N 1s and N 2s were detected, and Ti-N bonding was observed due to the substitution of oxygen with nitrogen. A satellite structure was observed in the Ti 2p due to the Ti-N bonding, and the composition of titanium nitride was determined to be about TiN1.0 from the position of the binding energy of Ti-N 2p3/2 and the quatitative analysis. The spectrum of Ti 2p energy level could be the sum of a 4, 5, or 6 Gaussian curve reconstruction, and the case of the sum of the 6 Gaussian curve reconstruction was physically most meaningful. From the results of Auger electron spectroscopy (AES), it was known that the composition was not varied significantly throughout the whole thickness of the film, and silicon oxide was not observed at the interface between the film and the substrate. The composition of the film was possible (TiO2)1-x.(TiN)x or TiO2-2xNx and in this experimental condition x was found to be about 0.21-0.16.

• 한국수소및신에너지학회논문집
• /
• 제8권3호
• /
• pp.121-129
• /
• 1997

아크 용해법으로 제작한 $ZrV_{0.1}Mn_{0.7}Ni_{1.2}$ 합금(bulk 합금) 잉고트는 $ZrV_{0.2}Mn_{0.98}Ni_{1.04}$의 조성식을 가지는 fcc 구조의 C15형 Laves상이 주류를 이루는 matrix와 $ZrV_{0.01}Mn_{0.13}Ni_{1.2}$의 조성으로 $Z_9Ni_{11}$의 금속간 화합물 구조를 가지는 2nd phase가 균일하게 분포된 2개의 상으로 구성되어 있었다. $ZrV_{0.1}Mn_{0.7}Ni_{1.2}$ 합금의 방전 특성에 이 두 가지 상들이 미치는 영향을 알아보기 위해서 matrix와 2'nd phase합금을 분리 제작하였고, 이들 전극에 대한 전기 화학적인 충방천 특성들을 조사하였다. 그 결과 방전용량은 2nd phase가 가장 낮은 $160mAh/g$, 그 다음으로 matrix가 200mAh/g으로 bulk의 250mAh/g보다 낮았다. Matrix조성의 합금은 bulk합금과 거의 유사한 활성화, 고율 방전율, 자기방전 특성을 가졌고, 또한 활성화 후에 충방전에 따른 용량감소의 경향이 현저히 관찰되었다. 그러나 2nd phase 조성의 합금은 이들과는 확연한 차이를 보였다. 즉 활성화되기 어렵지만 활성화된 후에 용량감소의 경향은 거의 없었고 또한 자기방전 특성도 우수하였다.

• 한국안광학회지
• /
• 제20권3호
• /
• pp.333-339
• /
• 2015

목적: 양안크로스실린더법으로 결정된 자각적 조절래그와 개방형 자동굴절계를 이용하여 결정된 타각적 조절래그를 미보정한 값과 보정한 값을 대상으로 임상적으로 그 특성을 평가하고자 하였다. 방법: 건강한 33명(남 26명, 여자 7명, 22~27세의 평균 나이 $23.73{\pm}1.35$세)을 대상으로 하였다. 조절래그는 4가지 방법 (1) +2.00 D 운무와 양안크로스실린더를 이용한 자각적 방법, (2) 자동굴절계로 측정한 미보정 타각적 방법, (3) 타각적 방법에서 Gwiazda 등이 제시한 식으로 보정한 방법(유효 조절래그)과 (4) 타각적 방법에서 Mutti 등이 제시한 식으로 보정한 방법으로 결정하였다. 결과: 평균 조절래그는 자각적 방법이 0.72 D, 미보정 타각적 방법이 0.82 D, Gwiazda식으로 보정한 타각적 방법이 0.88 D, Mutti 식으로 보정한 타각적 방법이 0.78 D였다. 타각적 조절래그 간에는 유의한 차이를 보였으나 자각적 조절래그와 타각적 조절래그 간에는 유의한 차이를 보이지 않았다. 유효 조절래그는 사위도와 굴절 이상 간에 유의한 상관관계를 나타내었고, Muttii 등이 제시한 식으로 보정한 타각적 조절래그는 보정하지 않은 타각적 조절래그와 높은 상관성을 보였다(r=0.99, p<0.001). 결론: 타각적 조절래그는 사위와 굴정이상과 상관관계가 있으며, 특히 증상과 관련하여 임상적 활용과 정량적 평가에 Muttii 등이 제시한 타각적 유효 조절래그를 고려하여야 할 것이다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1999년도 제17회 학술발표회 논문개요집
• /
• pp.232-232
• /
• 1999

교류형 플라즈마 방전 표시기(AC Plasma Display Panel, AC PDP)에 사용되는 플라즈마는 그 부피가 너무 작아서 플라즈마에 변화를 일으키지 않고 그 물성을 관측하기란 쉬운일이 아니다. 그래서 주로 PDP 내의 물성을 관측하는 데 시뮬레이션에 의존하게 된다. 그 물성중에 PDP내의 전계 분포에 대한 정보는 방전의 형성 및 소멸에 대한 많은 단서를 제공하고 있다. 특히 AC PDP의 경우, 유전체에 형성되는 벽적하(wall charge)가 방전의 형성 및 PDP 구동에 중요한 역할을 하는데, 이는 PDP 내의 전계 분포를 살펴봄으로써 대략 예측할 수 있다. 본 연구에서는 시뮬레이션에 의존하지 않고, 직접 레이저 유도 형광법을 이용하여 AC PDP 내의 전계를 측정하였다. 방전 가스인 헬륨(He)의 에너지 준위는 전계의 크기에 따라 에너지 준위가 변화하여, Rydberg(n$\geq$8) 준위가 여러 개의 준위로 나누어지는 현상이 일어나는데, 이를 Stack 효과라고 한다. 따라서 전계의 세기가 커짐에 따라서 각 준위와 준위 사이 값(splitting)이 커지는데, 이를 이용하면 전계를 측정할 수 있다. 즉, 헬륨 원자를 여기시키는 레이저 파장을 변화시키면서 관측되는 레이저 유도 형광 신호를 관측하면, 준위의 splitting을 관측할 수 있다. 본 연구에서는 PDP 내의 전계의 시간적 변화를 관측하였다. 50%, 40kHz의 구형파를 PDP의 두 전극에 가하였을 때, 플라즈마가 켜진 상태뿐만 아니라 플라즈마가 꺼진 후에도 전계에 의한 Splitting 신호가 관측이 되었는데, 전계로 환산하였을 때, 그 값은 대략 수 kV/cm의 값을 갖았는데, 이는 wall charge에 의한 값으로 사료된다.결과로 생각되어진다.플라즈마의 강도값을 입력하여 플라즈마의 radiation을 검출하고, 스퍼터링 공정중 실질적인 in-situ 정보로 이용하였다. PEM을 통하여 In/Sn의 플라즈마 강도변화를 조사하였다. 초기 In/Sn의 플라즈마 강도(intensity)는 강도를 100하여, 산소를 주입한 결과, plasma intensity가 35 줄어들었고, 이때 우수한 ITO 박막을 얻을 수 있었다. Pulsed DC power를 사용하여 아크 현상을 방지하였다. PET 상에 coating 된 ITO 박막의 표면저항과 광투과도는 4-point prove와 spectrophotometer를 이용하여 분석하였고, AES로 박막의 두께에 따른 성분비를 확인하였다. ITO 박막의 광투과도는 산소의 유량과 sputter 된 In/Sn ion의 plasma emission peak에 따라 72%-92%까지 변화하였으며, 저항은 37$\Omega$/$\square$ 이상을 나타내었다. 박막의 Sn/In atomic ratio는 0.12, O/In의 비율은 In2O3의 화학양론적 비율인 1.5보다 작은 1.3을 나타내었다.로 보인다.하면 수평축과 수직축의 분산 장벽의 비에 따라 cluster의 두께비가 달라지는 성장을 볼 수 있었고, 한 축 방향으로의 팔 넓이는 fcc(100) 표면의 경우 동일한 Ed+Ep값에 대응하는 팔 넓이와 거의 동일한 결과가 나타나는 것을 볼 수 있다. 따라서 이러한 비대칭적인 모양을 가지는 성장의 경우도 cluster 밀도, cluster 모양, cluster의 양 축 방향 길이 비, 양 축 방향의 평균 팔 넓이로부터 각 축 방향의 분산 장벽을 얻어낼 수 있을 것으로 보인다. 기대할 수 있는 여러

• 한국콘텐츠학회논문지
• /
• 제20권2호
• /
• pp.248-264
• /
• 2020

본 연구는 국내 인터넷 개인방송의 사회적/법적 현황을 분석하고, 해외 규제 법률과 인터넷 방송의 매체적 특성을 근거로 개인방송 규제의 방향을 제안하는 데 목적을 둔다. 인터넷 개인방송의 영향력이 더욱 커지고 있으며, 음란물, 가짜뉴스 등 사회적/법적 문제점 또한 증가하고 있다. 인터넷 개인방송에 관한 법적 규제가 부재한 상황에서, 학계 역시 개괄적인 분석 수준에서 관련 법제 및 정책을 논의하고 있다. 또한, 급변하는 미디어 환경에 대응하고 새롭게 등장하고 있는 인터넷 방송콘텐츠와 플랫폼에 대응하기 위해 새로운 법제 연구의 필요성이 대두되고 있다. 연구결과 표현의 자유를 중요한 가치로 삼고, 미성년자 대상 음란물은 철저히 규제하되, 관련 기관/사업자 간의 협의회 구성을 통한 자율규제 가이드라인으로 최소한의 범위에서 인터넷 개인방송 규제를 주장한다. 본 연구는 인터넷 개인방송 콘텐츠의 질적 향상과 공정하고 다양한 콘텐츠 개발을 위한 새로운 방송정책 구축, 개인방송 콘텐츠의 효율적/공정한 규제를 위해 실질적이고 구체적인 법률을 제안했다는 점에 큰 의의가 있다.

• 한국재료학회지
• /
• 제23권1호
• /
• pp.59-66
• /
• 2013

Opal glass samples having different chemical compositions were synthesized and transparent glass was obtained after melting. The effects of $TiO_2$, $BaF_2$, and $CeO_2$ content on the color of the opal glass were studied by observing images of the opal samples and analyzing the results via ultraviolet visible spectroscopy and color spectrometry. The aesthetic properties of the opal glass were determined by studying the transmittance of visible light in the 400 nm to 700 nm range. The basic chemical composition of opal glass was $SiO_2$ 52.9 wt%, $Al_2O_3$ 12.35 wt%, $Na_2CO_3$ 15.08 wt%, $K_2CO_3$ 10.35 wt%, $Ca_3(PO)_4$ 4.41 wt%, $MgCO_3$ 1.844 wt%, $LiCO_3$ 2.184 wt%, and $TiO_2$ 0.882 wt%. The glass samples were prepared by varying the weight percentage of $TiO_2$, $BaF_2$, and $CeO_2$. The transmittance of visible light was decreased from 95 % to 75 % in the glass samples in which $TiO_2$ content was increased from 0 to 3.882 wt%. In the blue spectrum region, as the content of $TiO_2$ increased, the reflectance value was observed to become higher. This implies that $TiO_2$ content induces more crystal formation and has an important effect on the optical properties of the glass. The opalescence of opal samples that contained $CeO_2$ or $BaF_2$ is stronger than that in the samples containing $TiO_2$. Opal glass samples comprising $TiO_2$ had tetragonal lattice structures; samples including $CeO_2$ as an additive had cubic lattice structures (FCC, $CeO_2$).

• 한국재료학회지
• /
• 제8권12호
• /
• pp.1115-1120
• /
• 1998

Ni계 경면합금인 Deloro 50의 마모거동을 15ksi와 30ksi 접촉응력하의 여러 마모조건에서 조사하였다. 상온대기중에서 Deloro 50는 15ksi 응력에서도 극심한 응착마모가 발생하는 매우 낮은 마모저항성을 보였는데 이는 fcc 결정구조를 갖는 Deloro 50 기지상의 경도와 가공경화율이 strain-induced 상변태를 이웅한 hcp 결정구조의 Stellite 6보다 낮기 때문으로 생각된다. 상온 수중에서 Deloro 50는 15ksi 응력에서 Stellite 6와 비슷한 마모저항성을 보였는데 이는 물이 미세요철간의 금속간 접촉을 억제하였기 때문으로 생각된다. 그러나, 30ksi의 높은 접촉응력에서는 상온 대기중길 같은 응착마모가 발생하는 것으로 보아, 30ksi의 높은 응력에서는 물의 응착마모 억제 효과가 없었기 때문으로 생각된다. $300^{\circ}C$ 대기중에서 Deloro 50는 30ksi의 높은 접촉응력에서도 Stellite 6보다 우수한 마모저항성을 보였는데 이는 고온에서 마모시 생성되는 복합산화물층이 효과적으로 금속간 접촉을 방해하여 응착마모를 억제하였기 때문으로 생각된다.

• 한국시뮬레이션학회:학술대회논문집
• /
• 한국시뮬레이션학회 1999년도 추계학술대회 논문집
• /
• pp.70-74
• /
• 1999

발전소 시뮬레이션 시스템 기술은 종합적인 지식을 바탕으로 자료수집 및 분석, 소프트웨어 개발 환경, 수학적 모델, 전산기 구성, 각종 계기류 설계 및 구매 장착 등의 노하우를 알아야만 제작할 수 있는 종합적인 기술이다. 또 지시기반의 기술이며 부가가치가 높은 기술이기 때문에 선진 각국에서는 계측제어 시스템의 기술개발 및 시장 확대를 위하여 힘을 쓰는 동시에 타국으로의 기술정보 유출을 경계하는데 신경을 곤두세우고 있다. 현재 복잡화되어 가고 있는 산업 사회의 전력 수요에 대한 대폭적인 증가 추세에 따라 발전소에서는 보다 효율적이며 합리적이고 경제적인 전력 공급을 위해서 전력 생산에 대한 신뢰성 향상 및 안정성 확보는 물론, 효율성 높은 운전이 절실히 요구되고 있다. 한편, 국내의 시뮬레이션 시스템 분야 기술은 아직도 완벽한 수준에는 미치지 못하며, 이 분야의 기술력 확보 및 신기술 개발은 향후 미래의 모든 시스템산업의 성쇄를 판가름하는 아주 중요한 척도가 될 것이다. 이 중에서 접지 분야는 고전압 혼촉에 의한 저압측 선로의 전압상승 방지, 모선(Bus)이나 전력 기기의 절연보호 및 회로전압의 안정등으로 시스템 성능을 한층 증가 시켜줄 뿐아니라 기기의 오동작이나 낙뇌등으로 인명피해 발생을 없애주는 아주 중요한 분야임에도 불구하고 이 분야의 국내 관련법규등이 미비한 사항이다. 그래서 발전소 분산제어 시스템분야의 장기간 신뢰성 및 안정성을 가지고 있고, 국내에서 많이 사용하는 미국 Bailey의 infi-90 및 독일 ABB의 Procontrol-P를 비교 분석하여 발전소 시뮬레이션 시스템의 접지에 응용 하고져 한다.상호 발생기를 이용한 다양한 시스템 검증 및 분석에 이용할 수 있을 것이다. 본 논문은 가상호 발생기의 구조와 최대 용량 시험 방법을 소개하고, 더 나아가 호 Traffic에 대한 최대 용량 시험뿐 아니라 QoS를 향상시키기 위한 교환 시스템의 제반 성능 시험 및 분석에 이를 이용하기 위해 개선이 필요함을 서술하고자 한다.textrm{m}$~3.4$\mu\textrm{m}$ 범위에서의 투과 및 흡수 스펙트럼을 측정하였다. 결정 성장 결과 B3+, Er3+, Cr3+ 이온은 Ti4+ 이온과 이온의 크기 차이가 심하여 결정의 정상적인 성장을 방해하는 물성을 나타냈고, V5+, Cr3+ 이온은 흑색의 결정, Fe3+ 이온은 적갈색의 결정으로 성장되었다. Al3+, Zr4+, Al3+의 순서로 투과도가 높아지는 것이 관찰되었다. 불순이온의 농도에 따른 영향으로서 Al3+ 이온의 경우 주입농도가 높아질수록 low angle boundary와 oxygen deficiency가 감소하였고, 투과율은 조금 감소하거나 큰 차이가 없는 것으로 나타났다. 반면에 Cr3+ 이온을 주입한 경우 0.003 atomic%에서 최적의 물성을 보였으며, 주입농도가 높아질수록 결정성장이 어려워지고 광의 투과도가 급격히 저하되었다.은 1.3을 나타내었다.로 보인다.하면 수평축과 수직축의 분산 장벽의 비에 따라 cluster의 두께비가 달라지는 성장을 볼 수 있었고, 한 축 방향으로의 팔 넓이는 fcc(100) 표면의 경우 동일한 Ed+Ep값에 대응하는 팔 넓이와 거의 동일한 결과가 나타나는 것을 볼 수 있다. 따라서 이러한 비대칭적인

• 한국자기학회지
• /
• 제8권3호
• /
• pp.156-160
• /
• 1998

고주파 마그네트론 스퍼링법에 의하여 두께 약 2000$\AA$으로 제조한 (Mn0.5-ZSb0.5+Z)100-yPty(0$0^{\circ}C$의 진공중에서 열처리한 후, X-선회질장치, 토크자려계, kerr 효과 즉정장치를 이용하여 결정구조 및 자기광학적 특성을 조사하였다. 열처리 후, MnSbPt 합금막은 FDD의 Clb-형구조를 갖으나, MnSbAg 합금막은 HCP의 NiAs-형구조를 갖고 c-축이 막면에 수직하여 배향하는 이방성조직이 형성되나 열처리시간이 길어지면 등방성조직으로 바뀐다. 30$0^{\circ}C$에서 3시간 동안 dufcjflgksMnSbAg 합금막에서 우수한 수직자기이방성이 관측되었으며 Mn47.4Sb47.5Ag5.1 합금막으로부터 K1=6.6$\times$105 erg/cm3, K2=1.9$\times$105 erg/cm3의 수직자기이방성값을 얻었다. 입사파장 700~100nm 범위에서 MnSbpt 합금막의 Kerr 회전각은 입사파장이 감소할수록 증가하나 MnSgAg 합금막은 반대경향을 보인다. 입사파장 λ=700nm에서 Mn41.1Sb44.9Pt14.0 및 Mn47.4Sb47.5Pt5.1 합금막의 Kerr 회전각 $\theta$k는 각각 1.7$^{\circ}$와 0.2$^{\circ}$이고 λ=1000nm에서는 각각 0.6$^{\circ}$와 0.97$^{\circ}$이다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1999년도 제17회 학술발표회 논문개요집
• /
• pp.229-229
• /
• 1999

교류형 플라즈마 방전 표시기(AC Plasma Display Panel, AC PDP)의 구동에서의 방전 현상은 기입방전, 유지방전, 소거 방전이 있다. 이중 유지 방전은 표시장치로서의 휘도와 계조의 표현을 위한 방전으로 표시기로서의 효율을 결정하게 된다. 본 연구에서는 유지 방전 전압의 상승 시간의 변화에 따른 방전현상과 휘도, 효율의 변화를 살펴 보았다. 방전 현상에서의 가장 큰 변화는 교류형 플라즈마 방전 표시기의 방전 개시 전압과 방전 유지 전압의 변화이다. 유지 전압의 상승시간이 증가할수록 방전 개시 전압과 방전 유지 전압의 변화이다. 유지 전압의 상승 시간이 증가할수록 방전 개시 전압과 방전 유지 전압의 차(sustain margin)는 감소하여 상승 시간이 1$\mu$s/100V 이상의 영역에서는 방전 개시 전압과 방전 유지 전압이 차이가 없어지게 된다. 이는 방전 유지 전극 위의 유전체에 쌓이게 되는 벽전하(wall charge) 양의 감소에 의한 방전 약화의 영향을 보여질 수 있다. 그러나 방전 유지 전압의 형태와 전류의 시간적인 변화를 살펴보면 이러한 약한 방전은 벽전하의 감소에 의한 방전 시의 전계 감소보다는 방전 전류의 발생 시간이 방전 전압이 증가하여 최고점에 이르지 못한 시간에 위치하여 방전이 형성될 때의 전계가 강하지 못하기 때문인 것을 알 수 있다. 방전 전류를 측정한 결과에 의하면 방전 전류의 시작은 변위 전류가 흐르고 난 후부터 시작되며 그 결과 방전 전류가 최고점에 도달하는 시간은 방전 전압 상승 시간이 길어질수록 낮은 전압에서 형성되게 된다. 또한 방전 유지 전압의 상승 시간이 길어질수록 플라즈마 방전표시기의 휘도와 효율은 낮아지고 이 결과 또한 약한 전계에서의 방전에 의한 결과로 생각되어진다.플라즈마의 강도값을 입력하여 플라즈마의 radiation을 검출하고, 스퍼터링 공정중 실질적인 in-situ 정보로 이용하였다. PEM을 통하여 In/Sn의 플라즈마 강도변화를 조사하였다. 초기 In/Sn의 플라즈마 강도(intensity)는 강도를 100하여, 산소를 주입한 결과, plasma intensity가 35 줄어들었고, 이때 우수한 ITO 박막을 얻을 수 있었다. Pulsed DC power를 사용하여 아크 현상을 방지하였다. PET 상에 coating 된 ITO 박막의 표면저항과 광투과도는 4-point prove와 spectrophotometer를 이용하여 분석하였고, AES로 박막의 두께에 따른 성분비를 확인하였다. ITO 박막의 광투과도는 산소의 유량과 sputter 된 In/Sn ion의 plasma emission peak에 따라 72%-92%까지 변화하였으며, 저항은 37$\Omega$/$\square$ 이상을 나타내었다. 박막의 Sn/In atomic ratio는 0.12, O/In의 비율은 In2O3의 화학양론적 비율인 1.5보다 작은 1.3을 나타내었다.로 보인다.하면 수평축과 수직축의 분산 장벽의 비에 따라 cluster의 두께비가 달라지는 성장을 볼 수 있었고, 한 축 방향으로의 팔 넓이는 fcc(100) 표면의 경우 동일한 Ed+Ep값에 대응하는 팔 넓이와 거의 동일한 결과가 나타나는 것을 볼 수 있다. 따라서 이러한 비대칭적인 모양을 가지는 성장의 경우도 cluster 밀도, cluster 모양, cluster의 양 축 방향 길이 비, 양 축 방향의 평균 팔 넓이로부터 각 축 방향의 분산 장벽을 얻어낼 수 있을 것으로 보인다. 기대할 수 있는 여러 장점들을 보고하고자 한다.성이 우수한 시