• Bulletin of the Korean Chemical Society
• /
• v.23 no.12
• /
• pp.1801-1805
• /
• 2002

The graphite intercalation compounds(GIC) were prepared by a dry process that led to the intercalation from the direct reaction of gaseous $SO_3$ with flake type graphite. The basal spacing of the GIC was increased from 8.3 ${\AA}$ to 12 in the gallery height. The ejection of interlayer $SO_3$ molecules by the heating for 1 minute at $950^{\circ}C$ resulted in an exfoliated graphite (EG) with surprisingly high expansion in the direction of c-axis. The expansion ratios of the exfoliated graphites were increased greatly between 220 times and 400 times compared to the original graphite particles, and the bulk density was range of 0.0053 to 0.01 $g/cm^3$, depending on reaction time. The pore size distribution of exfoliated graphite was in the range of $10-170{\mu}m$, which exhibites both mesoporosity and macroporosities. This result indicates that the direct reaction of graphite paricles with gaseous $SO_3$ can be proposed as an another route for the exfoliated graphite having excellent physical properties.

• Carbon letters
• /
• v.2 no.1
• /
• pp.55-60
• /
• 2001

Graphite intercalation compounds (GIC) were prepared by direct reaction of $SO_3$ gas with flake graphite. The intercalated $SO_3$ molecules were ejected by rapid heating to $950^{\circ}C$ under an oxidizing atmosphere for about 1 minute, resulting in surprisingly high expansion in the direction of c-axis. The characteristics of the micro-structure and pore size distribution were examined with a SEM and mercury intrusion porosimetry. The XRD analysis and spectroscopic analysis were used for the identification of the graphite and surface chemistry state. The pore size distribution of the exfoliated graphite (EG) was a range of $1{\sim}170{\mu}m$. The higher expanding temperature the higher expanded volume, so oil sorption capacities were 58.8 g of bunker-C oil and 34.7 g of diesel oil per 1 g of the the EG. The sorption equilibrium was achieved very rapidly within several minutes. As the treatment temperature increases, bulk density decreases.

• Journal of Korean Society of Environmental Engineers
• /
• v.36 no.1
• /
• pp.1-6
• /
• 2014

The composite anodes of exfoliated graphite (EG) and multiwall carbon nanotube (MWCNT) were fabricated by using the binders with different content of epoxy in Nafion solution. The influence of the epoxy content in the anode binder on the performance of microbial fuel cell (MFC) was examined in a batch reactor. With the increase in the epoxy content in the anode binder, increase in physical binding force was observed, but at the same time an increase in the internal resistance of MFC was also observed. This was due to the increase in activation and ohmic resistance. For the anode binder without epoxy, the maximum power density was $1,892mW/m^2$, but a decrease in maximum power density was observed with the increase in the epoxy content in the anode binder. With the epoxy content of 50% in the anode binder, a decrease in the maximum power density to $1,425mW/m^2$ was observed, which about 75.3% of the anode binder without epoxy is. However, the material consisting of the same amount of epoxy and Nafion solution is a good alternative for anode binder in terms of durability and economics of MFC.