• Journal of Advanced Marine Engineering and Technology
• /
• 제23권3호
• /
• pp.338-345
• /
• 1999

The objective of this study is to developed the refrigeration vehicle system installed eutectic olu-tion plates which consists of copper tubes carrying the refrigerant between two aluminum plates and the space between the plates filled with eutectic solution. The numerical analysis for the loca-tion of plates to get the uniform low temperature distribution in storage space was carried out and the result showed that the top left-side and right-side walls were the proper places to install plates. For three different concentrations of ethylene glycol solution the temperature distribution of inside space were measured during the day time of summer and the 21% solution was found to be properto sustain the temperature of $5-10^{\circ}C$ for milk transportation. The result showed that the refrigeration truck installed eutectic plates was very efficient to keep the milk fresh during vehicle transportation.

• 한국주조공학회지
• /
• 제31권3호
• /
• pp.137-144
• /
• 2011

The effects of thickness, base element and inoculants on the number of eutectic cells and chill depth of gray cast iron plate casting were investigated. Meanwhile the number of eutectic cells increased by inoculation, chill depth decreased. The former decreased and the latter increased by holding the melt at the temperature range between 1,450 and $1,500^{\circ}C$. The former was more for the thinner casting with the thickness of 5 mm than the other. The result of thermal analysis coincided well with the change of macrostructure. The former increased and the latter decreased with the increased contents of carbon, silicon and the silicon content by inoculation. The former decreased and the latter increased with increased manganese content. The performance of the Superseed Extra was the best among 5 inoculants.

• 한국주조공학회지
• /
• 제30권6호
• /
• pp.235-240
• /
• 2010

The evolution of microstructure and phases of Mg-10Al-Mn alloy by cooling plate method during homogenization treatment have been investigated with metallographic analysis, scanning electron microscopy and energy dispersive spectroscopy. The ingots used for this experiment were prepared by cooling plate and homogenization heat treatment was performed at 300 and $400^{\circ}C$ for various holding times (0, 1, 4, 8 and 12h). The casting ingots were consisted of the fine grains and eutectic phases. And, these eutectic phases were dissolved into the matrix during homogenization treatment at $400^{\circ}C$ but the lower temperature (at $300^{\circ}C$) did not be.

• 한국주조공학회지
• /
• 제29권2호
• /
• pp.64-69
• /
• 2009

In the present study the effect of cooling rate during solidification on the microstructural characteristics of Al-xAg (x = 31, 33, 35 at.%) in-situ binary eutectic composites has been investigated. To provide a wide range of cooling rate three different casting techniques, i.e. conventional casting, injection casting, and melt spinning have been used. The observed microstructure is very much dependent on the cooling rate. The fcc ${\alpha}$-Al and hcp $Ag_2Al$ phases exhibits an orientation of (111)Al//(0001)$Ag_2Al$, [1-10]Al//[11- 20]$Ag_2Al$. The microstructure of the melt-spun samples contains Widmanstatten structure resulting from solid-state transformation and nano scale two-phase structure resulting from solid-state phase separation. The microstructure of injection-cast samples contains eutectic structure and solid state phase-separated structure. On the other hand, conventional-cast samples exhibit a microstructure consisted of plate-type eutectic structure.

• 한국주조공학회지
• /
• 제29권1호
• /
• pp.45-51
• /
• 2009

Conventionally, Al-Sn bearing manufacturing involves casting the Al-Sn alloy and roll-bonding to a steel backing strip. This article will describe the microstructural control of Al-Sn metal bearing alloy following heat treatment. When the pure aluminum rod dipped in the melt of tin maintained below the melting point of aluminum, the melting of aluminum was accelerated with penetration of tin along the grain boundary of aluminum. The length of plate-shaped eutectic tin was decreased with heat treatment time. With even longer heat treatment time over 1 hour the length of eutectic tin didn't decrease any more, while resulting in coarsening of aluminum matrix. Exuded liquid of eutectic tin was formed at the surface of Al-Sn alloy after heat treatment even at below eutectic temperature.

• 한국주조공학회지
• /
• 제35권6호
• /
• pp.178-184
• /
• 2015

Due to excellent abrasion resistance the high-chrome white irons are widely used in mining and mineral industries. Minor variation of carbon content in 28% chrome white iron resulted in difference in primarily solidified microstructure. Sub-eutectic (hypoeutectic) composition led to formation of primarily solidified dendrites. Formation of primarily solidified dendrites which were supersaturated with carbon and chrome also caused precipitation of fine secondary carbides that are different from relatively large plate type $M_7C_3$ carbides in the eutectic structure. Small portion of primarily solidified dendrite expected to contribute significantly to the improvement of abrasion resistance of the white iron because the dendrites provided mechanical support to carbides. The relative fraction of primary dendrite increased with reduction of carbon content from the eutectic composition. The increased fraction of primary dendrite increased hardness value of the white irons.

• International Journal of Advanced Culture Technology
• /
• 제3권2호
• /
• pp.132-137
• /
• 2015

The purpose of this paper was to investigate the effects of solution treatment time and Sr-modification on the microstructure and property of the Al-Si piston alloy. It was found that as-cast microstructures of unmodified and Sr-modified Al-Si alloys consisted of a coarse acicular plate of eutectic Si, $Cu_3NiAl_6$ and $Mg_2Si$ phases in the ${\alpha}$-Al matrix but different in size and morphology. Both size and inter-particle spacing of Si particles were significantly changed by increasing of the solution treatment time. After a short solution treatment, the coarse acicular plate of the eutectic Si appears to be fragmented. Fully modified microstructure of Sr-modified alloy can reduce the solution treatment time to shorter compared to unmodified alloy. The maximum of a peak hardness value is found in the very short solution treatment of both Al-Si piston alloys. Compared to 10 h solution treatment, the solution treatment of 2-4 h is sufficient to achieve appropriate microstructures and hardness. The short solution treatment is very useful to increase the productivity and to reduce the manufacturing cost of the Al-Si piston alloys.

• 한국주조공학회지
• /
• 제16권2호
• /
• pp.141-148
• /
• 1996

In high chromium cast iron, the control of matrix microstructure as well as carbide structure is important to the performance as a wear resistant material. In this study, 3.0% C-24.0% Cr white cast irons with various molybdenum contents(residual, 1.0%, 3.0% and 5.0%) were solidified conventionally and unidirectionally for studying their effects on the microstructure and hardness. In the conventional casting, two sets of castings were poured from each melt. One set of the castings consisted of cylindrical bars of 10 and 20mm by 155mm long. The second set of the castings was a cylindrical bar of 30mm by 200mm long. On the other hand, a pep-set mold set on the Cu plate was employed to make the solidification unidirectionally. X-ray diffraction method was used to observe retained austenite and carbides in the high chromium cast iron. The morphology of eutectic $M_7C_3$ carbides changed from needle-like type to nodular type with the increase of Mo content. And, the presence of $M_2C$ carbides was identified in the sample where Mo was added over 3.0 %. Primary and eutectic carbides appeared as rod type and corngrain type, respectively in the unidirectionally solidified samples which were cut to parallel to the solidification direction. In the EDX analysis, Cr concentration was higher in the primary and eutectic $M_7C_3$ carbides, Mo in the $M_2C$ carbides, and Fe in the matrix.

• 한국주조공학회지
• /
• 제4권2호
• /
• pp.96-101
• /
• 1984

The morphologies of eutectic cell formed during solidification affect on the mechanical properties in high Cr cast iron. In order to investigate the influence of Si on the structure, five kinds of specimen containing 16.42% Cr with varying amount of Si (0.51%, 1.17%, 2.22%, 2.71%, 3.56%) were poured into shell mould preheated $330^{\circ}C$ at $1510^{\circ}C$. The effect of Si on matrix in hypo-eutctic Cr cast iron (2.48% C, 16.42%) were studied through its mechanical tests and observation of microstructure using of metallurgical microscope, EPMA, SEM and Image analyzer systematically. The results obtained from the above studies are as follows: 1. Because of ${\Delta}T$ decreasing with increasing Si content, the morpologies of colony change into uniform bar-type carbide from plate-type ones, moreover eutectic colony size (Ew) becomes narrow and spacing of carbide wider. 2. As Si content increases, the amount of carbides also increases and most of Cr were dissolved in carbides while Si in matrix. 3. The hardness, tensile strength and wear resistance were increasing while impact value decreased with increasing Si content. 4. In fracture section, small amount of dimple pattern was observed in less than 1.17% Si but more than 2.22% Si river pattern was presented.

• 한국주조공학회지
• /
• 제17권3호
• /
• pp.252-257
• /
• 1997

The 8 mm dia: Sn-38%Pb eutectic alloy rods were produced by use of the horizontal continuous casting process with the heated mold and chill cast process. The cast rods were rolled into 2.0${\sim}$0.5 mm thick plates and structural and mechanical properties were examined. The results revealed that the plates produced by the continuous casting process with the heated mold show much higher superplasticity at ambient temperature (1550% elongation at 0.5mm thick plate and 0.5mm/min strain rate) than the plates procuced by chill cast process (630% elongation). Such a high superplasticity of the continuous cast plates is due to the high-quality plates free from any inside and surface defects with fine and uniform distribution of eutectic phases.