• Korean Journal of Materials Research
• /
• v.12 no.5
• /
• pp.407-413
• /
• 2002

Eutectic high chromium cast irons containing 17%Cr and 26%Cr were produced for this research by making each of them solidify unidirectionally. Abrasion wear test against SiC or $Al_2$O$_3$bonded paper was carried out using test pieces cut cross-sectionally at several distances from the chill face of castings. The wear resistance was evaluated in connection with the parameters such as eutectic colony size($E_w$), area fraction of boundary region of the colony($S_B$) where comparatively large massive chromium carbides are crystallized and, average diameter of chromium carbides in the boundary region($D_c$). The wear rate($R_w$), which is a gradient of straight line of wear loss versus testing time, was influenced by the type and the particle size of the abrasives. The $R_w$ value against SiC was found to be larger than that against A1$_2$O$_3$under the similar abrasive particle size. In the case of SiC, the $R_w$ value increased with an increase in the particle size. The $R_w$ value also increased as the eutectic colony size decreased, and that of the 17%Cr iron was larger than that of the 26%Cr iron at the same $E_w$ value. Both of the $S_B$ and $D_c$ values were closely related to the $R_w$ value regardless of chromium content of the specimens. The $R_w$ values of the annealed specimens were greater than those of the as-cast specimens because of softened matrix structures. As for the relationship between wear rate and macro-hardness of the specimens, the hardness resulting in the minimum wear rate was found to be at 550 HV30.

• Korean Journal of Materials Research
• /
• v.24 no.10
• /
• pp.538-542
• /
• 2014

Microstructural and mechanical characteristics of Al-6Si-2Cu alloy for lightweight automotive parts were investigated. The test specimens were prepared by gravity casting process. Solution heat treatments were applied to as-cast alloys to improve mechanical properties. The microstructure of the gravity casting specimen presents a typical dendrite structure, having a secondary dendrite arm spacing (SDAS) of $37{\mu}m$. In addition to the Al matrix, a large amount of coarsened eutectic Si, $Al_2Cu$ intermetallic phase, and Fe-rich phases were identified. After solution heat treatment, single-step solution heat treatments were found to considerably improve the spheroidization of the eutectic Si phase. Two-step solution treatments gave rise to a much improved spheroidization. The mechanical properties of the two-step solution heat treated alloy have been shown to lead to higher values of properties such as tensile strength and microhardness. Consequentially, the microstructural and mechanical characteristics of Al alloy have been successfully characterized and are available for use with other basic data for the development of lightweight automotive parts.

• Journal of Korea Foundry Society
• /
• v.22 no.1
• /
• pp.17-25
• /
• 2002

Recently, many studies have been carried out to process on the purpose of lightness in a transport parts because of the saving energy, the environmental problem. The cast-forging process can be expected to lower costs without decreasing the mechanical properties. So, the finest microstructure is needed to get for applying the cast-forging process with Al-Si alloy because the microstructure affects to the cast-forging process. For refinement treatment of eutectic Si and Al solid-solution phase, Sr and TiB were added in Al-Si alloys. The finest microstructure could be observed when 0.075 wt.%Sr and 0.1 wt.%TiB were added respectively. In this case, tensile strength and elongation much more increased than as casting. After high temperature deformation simulation test with grain refinement specimens was carried out, about 70N per unit $area(mm^2)$ of specimen was confirmed. After hot forging, tensile strength and elongation were increased. It was considered because casting defect was removed by compressive working.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2006.11a
• /
• pp.181-184
• /
• 2006

Nano Infiltration Transient Eutectic Phase - Silicon Carbide (NITE-SiC) and $SiC_f/SiC$ composite have been fabricated by a Hot Pressing (HP) process, using SiC powder with an average size of about 30nm. Alumina ($Al_2O_3$) and Yttria ($Y_2O_3$) were used for additives materials. These mixed powders were sintered at the temperature a of $1300^{\circ}C$, $1650^{\circ}C$, $1800^{\circ}C$ and $1900^{\circ}C$ under an applied pressure of 20MPa. And unidirection and two dimension woven structures of $SiC_f/SiC$ composites were prepared starting from Tyranno SA fiber. Densification of microstructure gives an effect to density. Specially, Densification Mechanism basically is important from the sintering which use the HP. In this study, the densification of NITE-SiC and $SiC_f/SiC$ composite mechanism by a press displacement appears investigated. The mechanism on the densification of each sintering temperature was investigated. The each step is shows a with each other different mechanism quality.

• Journal of Korea Foundry Society
• /
• v.33 no.6
• /
• pp.233-241
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-9wt%Si-xMg-yFe-zMn alloy has been studied. The alloy was composed of ${\alpha}$-Al phase, Al+eutectic Si phase, ${\beta}$-Al5FeSi compound and chinese script ${\alpha}$-$Al_{15}(Mn,Fe)_3Si_2$ compound. ${\beta}$-$Al_5FeSi$ and ${\alpha}$-$Al_{15}(Mn,Fe)_3Si_2$ compounds assumed to effect the fluidity and shrinkage behaviors of the alloy during solidification due to the crystallization of ${\alpha}$-$Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}$-$Al_5FeSi$ compounds above eutectic temperature. As Fe and Mn contents of Al-9wt%Si-0.3wt%Mg system alloy increased from 0.15wt% to 0.6wt% and from 0.3wt% to 0.7wt%, fluidity of the alloy decreased by 5.7% and 3.3%, respectively. And as Mg content of Al-9wt%Si-0.45wt%Fe-0.5wt%Mn system alloy increased from 0.3wt% to 0.4wt%, fluidity of the alloy decreased by 8.6%. When Fe content of the alloy increased from 0.15wt% to 0.6wt%, macro shrinkage ratio decreased from 6.1% to 4.1%, and micro shrinkage ratio increased from 0.04% to 0.24%. Similarly, Mn content of the alloy increased from 0.3wt% to 0.7wt%, macro shrinkage ratio decreased from 6.0% to 4.5% and micro shrinkage ratio increased from 0.12% to 0.18%. Judging from the castability of the alloy, Al-9wt%Si-0.3wt%Mg alloy with low content of Fe and Mn, 0.1wt% Fe and 0.3wt% Mn, is recommendable.

• Proceedings of the KWS Conference
• /
• 1993.10a
• /
• pp.75-78
• /
• 1993

• Journal of Korea Foundry Society
• /
• v.23 no.4
• /
• pp.195-203
• /
• 2003

Hyper-eutectic Al-Si alloy is used much to automatic parts and material for the electronic parts because of the low coefficient of thermal expansion, superior thermal stability and superior wear resistance. In this work, A390 alloy specimens were fabricated for control of the Si particle size by various processes, such as spray-casting, permanent mold-casting and squeeze-casting. To minimize the effect of microporosity of the specimens, hot extrusion was carried out under equal condition. Each specimens were evaluated tensile properties at room temperature and thermal expansion properties in the range from room temperature to 400$^{\circ}C$. Ultimate tensile strength and elongation of the spray-cast and extruded specimens which have fine and well distributed Si particles were improved greatly compare to the permanent mold-cast and extruded ones. Specimens which have finer Si particles showed higher ultimate tensile strength and elongation than those having large Si particle size, and coefficient of thermal expansion of the specimens increased linearly with Si particle size. In case of the repeated high temperature exposures, thermal expansion properties of the spray-cast and extruded specimens were found to be more stable than those of the others due to the effect of fine and well distributed Si particles.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.08a
• /
• pp.277-284
• /
• 2004

Low carbon steels containing Si of up to $1.2\;wt\%$ were oxidized in air at 1373 K and 1523 K, i.e. below and above the eutectic temperature of FeO and $Fe_2SiO_4$. The influence of a impurity element, S on behavior of scale formation during oxidation was investigated by using $M\"{o}chssbauer$ spectroscopy and EDS. This allowed establishment of an interface oxidation model of Si-added steel depending on temperature and an impurity element. A compound of FeO and FeS was formed in the scale/matrix interface of low carbon steels containing S of up to $0.03\;wt\%$ oxidized above 1213 K of the eutectic temperature. This was flat formed between $Fe_2SiO_4$ nodules along the scale/matrix interface without selective oxidation. It is due to low viscosity and high wettability of the compound of FeO and FeS in liquid. Conventional metallographic examinations revealed that roughness of the scale/matrix interface in Si-added steels became flat as the content of S increased. It was independent of oxidizing temperature and Si content. Effects of oxidizing temperature and an impurity element content on descaling characteristics in Si-added steels were evaluated by using a hydraulic descaling simulator. Good descaling characteristics was attributable to this flatness of the scale/matrix interface.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.4
• /
• pp.23-28
• /
• 2009

We investigated the wafer-level MEMS capping process for which cavity formation in Si wafer was not required. Ni caps were formed by electrodeposition on 4" Si wafer and Ni rims of the Ni caps were bonded to the Cu rims of bottom Si wafer by using epoxy. Then, top Si wafer was debonded from the Ni cap structures by using SnBi layer of low melting temperature. As-evaporated SnBi layer was composed of double layers of Bi and Sn due to the large difference in vapor pressures of Bi and Sn. With keeping the as-evaporated SnBi layer at $150^{\circ}C$ for more than 15 sec, SnBi alloy composed of eutectic phase and Bi-rich $\beta$ phase was formed by interdiffusion of Sn and Bi. Debonding between top Si wafer and Ni cap structures was accomplished by melting of the SnBi layer at $150^{\circ}C$.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.471-474
• /
• 2005

This study investigates the nano/microstructure, the aging response, and the mechanical/tribological properties of the eutectic regions in rheoformed A356 alloy-T5 parts using nano/micro-indentation and mechanical scratching, combined with optical microscopy and atomic force microscope (AFM). Most eutectic Si crystals in the A356 alloy showed a modified morphology as fine-fibers. The loading curve for the eutectic region was more irregular than that of the primary Al region due to the presence of various particles of varying strength. The aging responses of the eutectic regions in the rheoformed A356 alloys aged at $150^{\circ}C$ for different times (0, 2, 4, 8, 10, 16, 24, 36, and 72 h) were investigated. Both Victors hardness $(H_v)$ and indentation $(H_{IT})$ test results showed a similar trend of aging curves, and the peak was obtained at the same aging time of 10 h. A remarkable size-dependence of the tests was found.