• Bulletin of the Korean Chemical Society
• /
• 제31권10호
• /
• pp.2913-2917
• /
• 2010

When rubber dissolved in toluene was used as a binding material of graphite powder, the mechanical robustness of the carbon paste was guaranteed by the fast volatility of the solvent immediately after electrode construction. This characteristic of the rubber solution met qualifications for practical use of carbon paste electrodes and enabled the design of a new enzyme electrode bound with EPDM. In order to confirm whether the electrode shows quantitative electrochemical behaviors or not, its kinetic parameters, e. g. the symmetry factor (0.2), the exchange current density ($3.66\;{\mu}A/cm^2$), the capacity of the double layer ($2.0{\times}10^{-5}\;F$), the Michaelis constant ($4.39{\times}10^{-3}\;M$), the diffusion coefficient of substrate ($2.58{\times}10^{-12}\;cm^2/sec$), the time constant (0.018 sec) and other factors were investigated.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.144-147
• /
• 2000

The effect of accelerated aging test on ethylene-propylene-diene monomer(EPDM) rubber used for outdoor insulation was studied by X-ray photoelectron spectroscopy(XPS), scanning electron microscope(SEM), FFT spectrum alalysis, and electrical pulse counts using PC by oscilloscope(300 MHz). In electrical alalysis, FFT spectrum analysis indicated arcing caused a significant increase in the third harmonic content of the leakage current of polluted insulator. Also, pulse counts increased as aging time. The surface oxygen and aluminum content were found to increase and that of carbon and nitrogen were found to decrease with time. The detailed XPS analysis indicated that the concentration of carbon in C-C decreased and concentration of highly oxidized carbons increased with time, which was due to the oxidation of EPDM rubber polymer SEM analysis indicated that crack and erosion of EPDM rubber occurred with time.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.132-135
• /
• 2000

This paper present the results of measured Thermally Stimulated Current of EPR(Ethylene Propylene Rubber) sheet material with variation of bias temperature range of -35~80[$^{\circ}C$], the quality of the material of electrode, condition. The origins of these peaks are that, low temperature peak seems to result from dipole, and high temperature peak from the orientation electronic trap.

• Elastomers and Composites
• /
• 제45권3호
• /
• pp.212-216
• /
• 2010

리튬 이온 전지의 가스켓 재료로 사용되기 위해서는 내전해액성, 전기절연성, 낮은 압축 영구 줄음률, 비오염성, 내열성이 요구된다. Perfluoroalkoxy (PFA)보다 압축 영구 줄음률이 우수한 고무의 적합성을 평가하기 위하여 Ethylene Propylene Diene Monomer (EPDM), Nitrile Butadiene(NBR), Fluoro Elastomers(FKM), Methyl-Vinyl Silicone Rubber (VMQ), Fluorosilicone(FVMQ)을 이용하여 최적상태의 compound를 제작하고 특성을 살펴보았다. 시험편을 $80^{\circ}C$의 propylene carbonate액에 침적하여 경도 및 체적변화를 1,000시간까지 시간별로 측정하였다. EPDM과 VMQ가 내전해액성이 우수하였으며, 전기절연성에서도 체적저항 기준 $10^{10}{\Omega}cm$이상의 결과를 얻을 수 있었다. 따라서, EPDM과 VMQ가 적절한 것으로 판단되었다.

• Elastomers and Composites
• /
• 제35권4호
• /
• pp.288-295
• /
• 2000

가황 EPDM(ethylene-propylene-diene terpolymer) 고무를 화학적 탈황처리 방법을 통하여 가교 밀도를 감소시키고자 시도하였다. 화학적 탈황처리를 위하여 상이동 촉매(phase transfer catalyst), 알카리 금속인 sodium, triphenylphosphine 등을 탈황 조제로 사용하였으며 또한 2-butanol을 탈황반응의 반응용매로 사용한 경우에 대한 탈황처리 효과도 아울러 조사하였다. 4급 암모니움염 형태의 상이동 촉매를 탈황반응에 이용할 경우 촉매의 분자량에 따른 변화 그리고 bromide(Br) 음이온 대비 chloride(Cl)음이온 사용에 따른 변화 등을 비교하였다. Sodium(Na)을 탈황반응에 투여할 경우 Na의 사용량, 반응온도, 반응시간 그리고 반응 분위기로 이용된 수소가스의 압력 등 반응변수에 따른 탈황효과를 살펴보았다. 가교밀도를 정량적으로 나타내는 수치인 $M_c$값(가교점 사이의 수평균 분자량)을 평형팽윤법을 이용하여 실험적으로 결정하였고 가황 EPDM 고무시료의 탈황효과 분석은 탈황 전과 탈황 후 시료에 대한 $M_c$ 값을 비교함으로써 수행되었다.

• 대한기계학회논문집A
• /
• 제31권9호
• /
• pp.915-923
• /
• 2007

Rubber hoses for automobile radiators are apt to be degraded and thus failed due to the influence of contacting stresses of air and coolant liquid under thermal and mechanical loadings. The aging behaviors of the skin part of the hoses due to thermo-oxidative and electro-chemical stresses were experimentally analyzed. Through the thermo-oxidative aging test, it was shown that the surface hardness IRHD(International Rubber Hardness Degrees) of the rubber increased with a considerable reduction of failure strain as the aging time and temperature increased. On account of the penetration of coolant liquid into the skin part influenced by the electro-chemical degradation(ECD) test the weight of the rubber hose increased, whereas their failure strain and IRHD hardness decreased. The hardness of the hose in the side of the negative pole was the most deteriorated at the test site of the hose skin just below the coolant surface.

• 폴리머
• /
• 제29권2호
• /
• pp.166-171
• /
• 2005

EPDM(ethylene propylene diene monomer)1실리콘 고무 블렌드를 제조하고, 상용화제와 열노화 시간에 따른 물성 변화를 살펴보았다. EPDM과 실리콘 고무(SR)의 조성비는 90/10에서 $10/90\;wt\%$ 사이로 조절하였으며, Brabender사의 Plasticoder를 사용하여 용융 혼합하고, 열프레스로 가교하였다. 가교된 EPDM/SR 블렌드의 모폴로지를 주사전자현미경으로 관찰하였다. 또한, 블렌드를 $100^{\circ}C$에서 24, 48, 96시간 동안 열노화시켜 경도, 인장 강도, 신장률 및 접촉각을 측정하였다. 모폴로지를 조사한 결과 상용화제를 첨가한 블렌드의 분산상의 크기가 감소하였다. 열노화 시간이 증가함에 따라, 블렌드의 경도와 인장 강도는 감소하였으며, 신장률과 접촉각은 증가하였다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제26권6호
• /
• pp.167-174
• /
• 2022

이 연구의 목적은 감쇠능력이 우수한 재료로 구성된 DUS(damping-up system)의 동적특성을 평가하고 일반 행어볼트와의 성능을 비교하는데에 있다. 주요변수는 고무의 종류 및 경도(𝜂_H) 그리고 프리스트레스력(고무의 응력-변형률 관계에서 압축변형률(𝜂_R)로부터 환산된 값)이다. 동적특성은 고유진동수(𝜔_n), 최대 응답가속도(A_m), 증폭계수(𝛼_p), 최대 상대변위(𝚫_m) 및 감쇠비(𝜉_D)로부터 평가되었다. 실험결과 DUS의 A_m, 𝛼_p 및 𝚫_m 는 일반 행어볼트 보다 각각 46.3%, 46.6% 및 62.9% 낮았으며, 𝜉_D는 3.89배 높았다. 특히 DUS의 𝛼_p 는 평균 1.3으로서 KDS 41 17 00의 강성요소에서 제시하는 값과 비슷한 반면, 일반 행어볼트의 𝛼_p 는 2.45로 연성요소에서 제시하는 값과 비슷하였다. 결과적으로 DUS의 최적상세는 𝜂_H가 50인 NR(natural rubber)과 45인 EPDM(ethylene propylene diene monomer)을 권장하며, 이들의 𝜂_R는 5%로 추천한다.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제50권10호
• /
• pp.479-488
• /
• 2001

The effects of accelerated Ultraviolet (UV) radiation on High temperature vulcanized (HTV), Room temperature vulcanized (RTV) silicone rubber and two types of ethylene propylene diene terpolymer (EPDM) used for composite insulator were inverstigated by hydrophobicity class (HC), surface voltage decay after corona charging, SEM-EDS, FTIR and XPS. The contact angle in two kinds of silicone rubber was scarcely change, but EPDM occurred to the loss of hydrophobicity followed by surface cracking and chalking. The surface voltage decay on UV-treated silicone rubber and EPDM showed a different decay trend with UV treatment. EDS and XPS analysis indicated that the oxygen content increased with UV treatment time in all samples. For silicone rubber, the oxidized groups of inorganic silica-like structure increased with UV treatment time. The oxidized carbon of C=0, O=C-O in EPDM increased. These oxidized surface for each material had different electrostatic characteristics, so deposited charges were expected to have different impacts on their surface hydrophobicity. The degradation mechanism based on our results was discussed.

• Elastomers and Composites
• /
• 제47권3호
• /
• pp.201-209
• /
• 2012

그로멧은 자동차의 고무부품들 중의 하나로 에틸렌 프로필렌 고무로 구성되어 있으며, 고무의 비선형 초탄성 성질은 고무제품의 거동을 예측하는데 중요하다. 본 논문에서는, 일축인장시험과 이축인장시험을 통하여 안정된 응력-변형률 관계를 구하고 그로멧에 대한 유한요소해석을 수행하였고, 수명예측을 위한 노화시험을 소개하였다.