• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2019년도 추계 학술논문 발표대회
• /
• pp.31-32
• /
• 2019

In this study, oxidized graphene nanoplatelet(GO) was prepared by oxidizing graphene nanoplatelet(GNP) with nitric acid in order to solve the problem of dispersion of GNP, one of nano materials. GNP/Epoxy and GO/Epoxy paint were prepared by mixing GNP, GO with 0.1, 0.3, 0.5 and 1.0 wt.% in epoxy paint and the mechanical properties were evaluated. As a result, GNP/Epoxy and GO/Epoxy paints showed better mechanical properties than Neat Epoxy which did not incorporate GNP, GO. Especially, when 0.3 wt.% of GO was incorporated into epoxy resin, it showed higher tensile strength than Neat Epoxy. It was confirmed that acid treatment of GNP was effective in improving the mechanical properties of epoxy paint. However, graphene material was found that it was not effective in improving the bond performance of the epoxy paint.

• 한국건축시공학회지
• /
• 제17권5호
• /
• pp.465-471
• /
• 2017

본 연구에서는 그래핀 나노플레이트릿(Graphene nanoplatelet ; GNP)의 분산에 대한 문제를 해결하고자 질산으로 이를 산화시켜 GO를 제조하였다. 이렇게 제조한 GO를 에폭시 도료에 혼입하기 전, 푸리에변환적외선분광법(Fourier transform infrared spectroscopy; FT-IR)을 이용한 화학조성 분석과 용매에서의 분산안정성을 확인하였다. 그 후, GNP, GO를 에폭시 도료에 0.1, 0.3, 0.5, 1.0wt.% 혼입하여 GNP/Epoxy, GO/Epoxy 도료를 제조하고 역학적 특성을 평가하였다. 실험 결과, FT-IR 분석을 통해 GO에서 하이드록시기, 에폭시기, 카르복시기 기능기가 생성된 것을 확인할 수 있었다. 또한, GO는 GNP보다 증류수와 에탄올에서 분산안정성이 향상되는 것을 확인하였다. 한편, GO/Epoxy 도료는 Neat Epoxy, GNP/Epoxy에 비해 역학적 특성이 향상되었으며, 특히 0.3wt.% 혼입률에서 높은 역학적 특성을 나타내었다. 따라서 GO를 에폭시 수지에 강화제로써 혼입할 경우 에폭시 도료의 역학적 특성을 향상시키는데 효과적인 것으로 판단된다.

• Corrosion Science and Technology
• /
• 제14권2호
• /
• pp.59-63
• /
• 2015

Airless spray which is widely used for painting to ship blocks and hull sides is the coating method for attaching atomized paint material to the substrate using spray tip nozzle with compressed air. When the paint material which has high solid contents such as epoxy primer paint is atomized by passing through spray tip nozzle with high pressure, the nozzle composed of tungsten carbide(WC) undergoes the erosive wear, leading to widening of nozzle hole. The deformation of nozzle hole induces improper spray pattern and coating failures such as finger pattern and sagging because the conditions of spray pump pressure and paint flow rate for developing full spray pattern are changed. In this study, an appropriate replacement cycle of spray tip was predicted by measuring the erosive wear tendency as increasing the spraying time of epoxy primer paint.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 봄 학술논문 발표대회
• /
• pp.181-182
• /
• 2020

In this study, oxidized graphene nanoplatelet(GO) was prepared by oxidizing graphene nanoplatelet(GNP) with nitric acid in order to solve the problem of dispersion of GNP, one of nano materials. GNP/Epoxy and GO/Epoxy were prepared by mixing GNP, GO with 0.1, 0.3, 0.5 and 1.0 wt.% in epoxy and the mechanical properties, bond performance were evaluated. As a result, GNP/Epoxy and GO/Epoxy showed higher tensile strength than Neat Epoxy at the 0.1, 0.3 wt.%. Especially, when 0.1 wt.% of GO was incorporated into epoxy resin, it showed highest tensile strength. It was confirmed that acid treatment of GNP was effective in improving the mechanical properties of epoxy paint. However, graphene material was found that it was not effective in improving the bond strength of the epoxy paint.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2005년도 전기학술대회논문집
• /
• pp.423-428
• /
• 2005

We prepared paint-type and sheet-type EM wave absorbers with Mn-Zn Ferrite, Ni-Zn Ferrite, Ba Ferrite, Sr Ferrite, and Sendust against ghosts of a mater in ships. To prepare the absorbers, enamel paint and epoxy paint were used as binders. The prepared EM wave absorber's absorption properties were investigated. The prepared EM wave absorbers have 6 dB over in 2 GHz ${\sim}$ 4 GHz. We compared properties of wave absorption between paint-type and spray-type

• 한국농공학회지
• /
• 제25권2호
• /
• pp.67-75
• /
• 1983

The objectives of this paper were to measure the bond strengths of reinforced concrete in which the steel rods were coated with five different kinds of anticorrosion paints, and to compare their prevention effects in salt water. The paints used in the study were epoxy resin I . II . III, Z.R. P., and silicone resin, which were applied at rates recommended by the manufacturers. The bond strengths were measured on the 7-, 14-, and 28-th days after molding. Corrosion conditions of coated steel plate under fresh water, seawater, 10 % salt water, and 20% salt water, were inspected every month during four months test peoriods, respectively. The results obtained from tests are summarized as follows: 1. Paint-coating may reduce the bond strengths of reinforced concrete. Silicone resin paint showed some 20% reduction in the strength compared to those without the paint. However, the other paints seemed not to significantly affect the strength. 2. Picture analyses showed that epoxy resin I and II significantly prevented corrosion steel plates in seawater. Epoxy resin I and silicone resin coating did not do a good job in corrosion prevention. Z.R. P. paint was found to be moderate as preventive coating paint. 3. Varying soluble salt contents had little effects on the corrosion prevention of tested paints. 4. Epoxy resin I and II were found to be appropriate as a coating material to prevent the corrosion of steel rods in seawater. Z.R.P. may also be used for the purpose.

• 한국분무공학회지
• /
• 제12권3호
• /
• pp.138-145
• /
• 2007

In the present work, the breakup mechanism of highly viscous epoxy paints discharged from a fan spray nozzle was examined experimentally. The paints tested were non-Newtonian fluids, composed of epoxy resin, solid particles and other additives. The paint spray discharged from the nozzle was visualized and recorded using a digital camera with back illumination. Due to presence of the solid particles, perforation of liquid sheet was observed in most cases, even at low-Reynolds number conditions (Re < 15,000) where the aerodynamic-wave breakup mode is used to be dominant for pure liquids. However, with the increase of the particle concentration, the sheet became longer and the thickness at breakup became thinner to some extent. This is because, with higher concentration of solid particles, the stabilizing effect by the viscosity increase predominates over the destabilizing effect by perforation.

• Corrosion Science and Technology
• /
• 제15권6호
• /
• pp.290-296
• /
• 2016

This study was conducted in order to examine the effect of burn damage and the resultant anti-corrosion performance. The breakdown and defect of the paint film caused by burn damage are considered to affect not only the macroscopic appearance but also the adhesive force and the anti-corrosion performance of the paint film. The material of the paint film was epoxy paint that is used most widely for heavy-duty coating, and in order to induce burn damage, heat treatment with a torch was applied to the other side of the paint film. Surface and chemical structure changes according to aging were analyzed using FE-SEM and infrared absorption spectroscopy, and variation in the anti-corrosion performance was analyzed through the AC impedance test.

• 청정기술
• /
• 제12권1호
• /
• pp.27-35
• /
• 2006

본 실험은 에폭시계 분체도료의 물성에 영향을 미치는 에폭시 수지, 경화제, 충전제 및 안료 의 최적 조성 결정에 대한 연구이다. 본 연구에서 사용된 에폭시계 수지의 경화 시스템은 Diglycidyl ether of bisphenol-A (DGEBA)와 경화제로 dicyan diamide (DICY)를 사용하였다. 코팅 재료의 경화거동과 유변물성은 DSC와 레오메터를 사용하여 조사되었다. 또한 코팅재료의 스틸에 대한 접착력은 lap shear 실험을 이용하여 조사되었다. 연구 결과에 따르면 에폭시계 분체도료의 최적 조성은 에폭시계 수지 기준으로 DICY 6 phr, $CaCO_3$ 20 phr 및 $TiO_2$ 10 phr 이었다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제29권5호
• /
• pp.519-525
• /
• 2005

An electrochemical evaluation on the corrosion resistance for heavy anticorrosive paint(DFT:25um) was carried out for 5 kinds of heavy anticorrosive paints such as high solid epoxy(HE), solvent free epoxy(SE). tar epoxy(TE), phenol epoxy(PE). and ceramic epoxy(CE). Corrosion current densities obtained by Tafel extrapolation method from anodic and cathodic polarization curves didn't correspond with the values obtained by AC impedance measurement, however, the values of polarization resistance obtained from the cyclic voltammogram showed a good tendency corresponding well with the values of AC impedance measurement. Futhermore there was a good correlation against the corrosion resistance evaluation between passivity current density of the anodic polarization curve and diffusion limiting current density of the cathodic polarization curve. And corrosion resistance increased with corrosion potential shifting to noble direction. From the results discussed above. HE and CE had a relatively good corrosion resistance than other heavy anticorrosive paints.