• Restorative Dentistry and Endodontics
• /
• v.5 no.1
• /
• pp.19-23
• /
• 1979

This experimental study was made to investigate the tensile strength of composite resins to etched enamel surface with a 50% phosphoric acid. Recently extraced 40 maxillary incisors were chosen. These were divied into 4 groups: Group I: Restodent adaptation to the etched enamel surface with 50% phosphoric acid. Group II: Restodent adaptation to only the ground enamel surface. Group III: Hi-pol adaptation to the etched enamel surface with 50% phosphoric acid. Group IV: Hi-pol adaptation to only the ground enamel surface. The results were as follows: 1. The tensile strength of Hi-pol showed much better results than that of Restodent. 2. Hi-pol and Restodent on the ground enamel surfaces showed little difference. 3. Adhesion to enamel increased on the average over 200% after a 50% phosphoric acid etch.

• Restorative Dentistry and Endodontics
• /
• v.12 no.2
• /
• pp.91-98
• /
• 1987

This study was designed to investigate the changing depositional pattern of inorganic enamel substances during enamel formation and maturation. For this purpose, white rat incisors which continuously grow and develop during the life, were chosen as specimens. And after treated with 20% KOH solution, outer surface of forming inorganic enamel were observed with the scanning electron microscope, dividing into 6 types according to the forming pattern from apical to cuspal direction. The observations lead to the following conclusions: 1. During the initial enamel forming stage, inorganic enamel substances were deposited with very irregular pyramidal shape on the root dentin surface. 2. During the enamel forming stage, inorganic enamel substances were deposited with relatively regular hexagonal, honey-comb appearance. 3. During the later enamel forming stage, inorganic enamel substances were deposited with very irregular and roughly amorphous appearance. 4. During the later enamel maturating stage, very small and round inorganic enamel substances were deposited densely, and made a flat enamel surface.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.25 no.1
• /
• pp.209-224
• /
• 1998

The purpose of this study was to compare the amount of calcium fluoride deposited on the enamel and dentin surface and to obtain information on the morphological change and crystallographic details of mineral deposition after 12,000ppm APF application in vitro. The bovine enamel and dentin blocks were randomly assigned to eight groups according to artificial caries lesion formation and difference of fluoride application time. The fluoride concentration and morphological characteristics on the treated enamel and dentin surface were investigated by using fluoride quantitative analysis and SEM. The powdered enamel and dentin of the intact bovine incisors were prepared for the X-ray diffraction analysis. The following results were obtained. 1. The amounts of KOH-soluble fluoride on the carious enamel and dentin surface after 24h APF application were higher than after only 5min APF application(p<0.05), but in the case of the sound enamel and dentin surface were similar after 5min and 24h application (P>0.05). The fluoride content was highly increased in the carious dentin as compared with sound dentin after APF application(P<0.05). 2. The carious enamel surface after APF application, the demineralized enamel surface were recovered a more dense enamel surface and precipitation of crystal was observed a distintive surface layer of spherical globules of about 1 m diameter. In the case of the fluorided carious dentin surface, precipitation of calcium fluoride-like material was deposited both inside the dentinal tubules as well as in the intertubular regions. 3. The crystallographic structure of powdered enamel and dentin after 24h APF application had large crystallities of apatite and CaF2 diffraction peaks in the enamel as compared with dentin. The diffraction data collected from the 27.50-29.50(2) angular range of the powdered enamel, the (105) apatite, (225) apatite and (111) CaF2 peaks of the enamel crystallities were detected after 24h APF application.

• Journal of Korean society of Dental Hygiene
• /
• v.10 no.4
• /
• pp.757-764
• /
• 2010

Objectives : The fluoride coating for caries prevention and strengthen enamel use NaF(sodium fluoride, Junsei Chemical Co., Ltd, Japan) 2% gel, SnF2(stannous fluoride, SIGMA-ALDRICH Gmbh, USA)8% gel and APF(acidulated phosphate fluoride, Sultan health care, USA) 1.23% gel. Methods : After put the enamel piece in these fluoride compound gel, we observed density level. And after measuring the vickers hardness, Got the following conclusions. Results : 1. After settling in the APF 1.23% during 6 days, we observed high density level of enamel surface using 250 magnification scanning microscope. The vacuum of surface packed (in) like sardines. 2. After settling in the APF 1.23% during 6 days, we observed reducing the space between the cluster of enamel surface using 50,000 magnification scanning microscope. 3. The vickers hardness change was very much on the all kinds of fluoride compound gel[2% NaF(sodium fluoride)gel, 8% SnF2(stannous fluoride) gel, 1.23% APF(acidulated phosphate fluoride)gel]. It's all because of reducing the space between the cluster of enamel surface(p<0.001). Conclusions : The vickers hardness change was very much on the all kinds of fluoride compound. It's all because of reducing the space between the cluster of enamel surface.

• Journal of Oral Medicine and Pain
• /
• v.21 no.2
• /
• pp.207-224
• /
• 1996

This study was designed to determine the most effective concentration of fluoride and energy density of laser irradiation for the anticarious effect. For this study surface hardness in enamel was measured before and after irradiation with pulsed Nd;YAG laser and the topical application of fluoride. Of the permanent mandibular anterior hovine teeth, healthy, carious free ones were used. Three hundred specimens were made. Specimens within 25~45 Vickers hardness numbers were assigned to 20 control and experimental stoops ; each containing 15 specimens. After forming artificial carious lesions, 10 J/$\textrm{cm}^2$, 20 J/$\textrm{cm}^2$, and 30 J/$\textrm{cm}^2$ energies were irradiated on the enamel surface of each experimental group. Also NaF, NH4F, Elmex gel(amine fluoride) and APF gel fluoride compounds were applied topically. Next, all the specimens were placed into the pH circulatory procedures for eight days. Vickers hardness numbers were measured using a microhardness tester. Surface changes of the enamel were observed using an scanning electron microscope. The comparative ana1ysis yielded the following results : 1. The reduction of surface hardness of the enamel surface was less in all groups with fluoride application than in the group without fluoride application. 2. The APF gel croup with 10 J/$\textrm{cm}^2$ irradiation showed the lowest reduction of surface hardness. 3. The reduction of surface hardness of the enamel surface in the group of laser irradiation without fluoride application not showed any significant difference according to the energy density of the laser. 4. Under the scanning electron microscope, in enamel irradiated with 10J/$\textrm{cm}^2$ showed appearance similar to acid etching surface. In enamel irradiated with 20 J/$\textrm{cm}^2$, line enamel crack was detected. In enamel irradiated with 30j/$\textrm{cm}^2$, severe enamel crack and fusion of enamel were detected. These results suggest that one could obtain the best anticariogenic effects without damage to teeth in the group of application of APF gel after laser irradiation with 10 J/$\textrm{cm}^2$.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.8 no.1
• /
• pp.47-53
• /
• 1981

Author have studied with electron microscope on the effect of biscuit solution dissolved in natural saliva on the enamel surface of the primary teeth. Four of the teeth were natural primary teeth and the other four teeth were treated in acidulated phosphate fluoride during four minute. The obtained results were as follows; 1. The pH value of the solution was decreased according to the time passed, and gradually became 3.75 at the end of 48 hours. 2. Natural teeth appeared normal enamel surface appearance during first 12 hours, and at 24 hours, it appeared some degree of decalcified appearance near the enamel rods and surfaces. 3. The decalcified appearances of the enamel surfaces of the fluoride treated teeth were not significant compared with the fluoride untreated teeth. 4. Streptococci of the enamel surface were increased according to the time passed.

• Restorative Dentistry and Endodontics
• /
• v.5 no.1
• /
• pp.7-12
• /
• 1979

After applying three types of composite resins - Hi-Pol composite with Enamel bond, Hi-Pol composite without Enamel bond, Restodent - to the intact and the ground surface of tooth that had been acid etched for one or two minutes, the author observed the penetration of these resins into the acid etched enamel surface with scanning electron microscope. The results were as follows. 1. All the experimented materials showed the penetration into the acid etched enamel surface, and the average depth of penetration was 7 microns. 2. There was no significant difference in the penetration of these three resins despite different etching, time. 3. The grinding of the Enamel surface before acid - etching was not effective in altering the depth of penetration of these materials.

• The Journal of the Korean dental association
• /
• v.9 no.4
• /
• pp.151-157
• /
• 1971

Freshly extracted permant teeth were examined by electron microscope according to the Filmy replica method. Preparatory method with hydrochloric acid or proteolytic enzyme treatment was used in order to injure the structural composition of enamel surface to compare between the natural carious defects and the etched samples used in this study. The natural carious defects were chalky white or brown discolored portions at the smooth enamel surface without having visible loss of enamel substances. The findings were as follows: 1. The first caries attact initiated from the mineralized portion of rod sheath which is located at the top of enamel rod. 2. The caries developed downward along the rod sheath interprismatic substances and enamel rods subsequently. However, the caries involvement of interprismatic substances and enamel rods occured almost at the same time. 3. The rod sheath attached to the remineralized smooth emael surface was located at the top of enamel rod.

• Restorative Dentistry and Endodontics
• /
• v.20 no.1
• /
• pp.1-16
• /
• 1995

The purpose of this study was to investigate the effect of dentin bonding agents on the bond strength of composite resin restorations in case of applying the dentin bonding agents to acid etched enamel surfaces. Freshly extracted 364 bovine anterior teeth were selected as a adherents. 320 enamel specimens were divided into two groups(unetched group (1) and etched group (2) for testing the shear bond strength, 40 specimens were used for the hardness testing, and 4 specimens of rest were to observe the resin-tag formation into etched enamel surfaces. All surfaces of enamel specimens were polished with 320~1500 SiC paper under continuous running water. In Group (1), 100 enamel specimens were polished and unetched. 220 polished enamel specimens in Group (2) were etched with 37 % phosphoric acid solution for 60 seconds, washed with water for 20 seconds, and dried with a light air pressure for 60 seconds. Three kinds of dentin bonding agents(Gluma, Prisma, Scotchbond 2) were evaluated the effect on the bond strength to conditioned enamel surfaces. Shear bond strengths were measured on the three cases such as a coating of primer only, a coating of sealer only, and a sequential coating of primer and sealer to acid etched enamel surfaces were compared with the bond strengths measured by the coating of enamel bonding agent followed by the bonding of composite resin (Photo clearfil bright, Kuraray, Japan) to unetched and acid etched enamel surfaces. In addition, the hardness tested on the adhesive fractured surface between composite resin enamel as a mean of evaluation of a factor whether the mechanical bond strengths were affected and the penetration of dentin bonding agents into etched enamel surfaces was also observed. Bond strengths were measured using the method of shear bond strength by a universal testing machine (Instron-4467, USA), statistical test were applied to the results using a one way analysis variance(ANOVA), and hardness was measured by the Vicker's Hardness Tester(MHT-i, Matsuzawa, Japan) and the penetration of the resins were observed by the SEM (Hitachi, S-2300, Japan). The following conclusions were drawn; 1. Enamel bonding agent showed to affect the improvement of bond strength of composite resin to enamel surface both unetched and etched. 2. Dentin bonding agents could be resulted in increase of bond strength to unetched enamel surface, but there were no statistical significances. 3. Bond strengths to etched enamel surface were significantly decreased with a coating of dentin primer only. 4. Coating of sealer only and coating of primer and sealer noticed the similar bond strengths of composite resin to etched enamel using the enamel bonding agents. 5. The applying method proved to be more effective than the kinds of dentin bonding agents on the bond strength of composite resin to etched enamel than the kind of dentin. 6. Vicker's hardness numbers of dentin bonding agents were lower than that of composite resin, but the degree of penetration of dentin bonding agents into etched enamel surfaces was excellent.

• Restorative Dentistry and Endodontics
• /
• v.19 no.1
• /
• pp.159-168
• /
• 1994

The purpose of this study was to evaluate the shear bond strength of the porcelain laminate specimens according to the surface roughness of the cut enamel of human anterior teeth. Flat enamel surfaces were prepared in 30 extracted human anterior teeth with diamond disc which were divided into two groups. Group 1 Coarse enamel surface group prepared with LVS-3 bur. Group 2 Fine enamel surface group prepared with superfine diamond bur. 30 teeth specimens of two group were stored in normal saline during 24 hours. 30 disk - type porcelain laminate specimens with diameter 4mm and thickness 1mm were made and sand - blasted on internal surface which were to cemented on enamel surface. Porcelain laminate specimens were cemented on enamel surface with Choice Veneer System (Bisco Dental, U.S.A) according to manufacture's instructions. All teeth specimens of two groups were manipulated with same method and stored In normal saline before testing. An Universal Testing machine (Model No.UTM-4206,Instron, U.S.A) was used to apply shear loads in the vertical directed, and the force required for separation was recorded with a cross head speed of 3mm/min and 500kg in full scale. The results were as follow ; 1. The mean shear bond strength of coarse surface group was 36.30kg and that of fine surface group was 44.39 kg, but there was no significant difference in breaking strength of two groups(p>0.05).