• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1163-1164
• /
• 2006

TZM alloy having elongated coarse-grain structure was developed by three-step internal nitriding treatment at 1423 to 1873 K in $N_2$ and subsequent recrystallization treatment at 2173 K in vacuum. Some specimens were subjected to re-nitriding treatment at 1873 K for 16 h. After the recrystallization treatment, aspect ratio (L/W) of grains for rolling direction was about 50 at the maximum. Yield stress obtained at 1773 K after re-nitriding treatment was about 6 times as large as that of recrystallized specimen. Re-nitriding was very effective in the improvement in strength of TZM alloy having elongated coarse-grain structure.

• Journal of the Korean Ceramic Society
• /
• v.34 no.11
• /
• pp.1129-1138
• /
• 1997

Al2O3/20 vol%YAG composite containing equiaxed grains and Al2O3/20 vol%LaAl11O18 composite containing elongated grains were fabricated using Al2O3-Y2O3 composition and Al2O3-La2O3 composition, respectively, by hot-pressing. In order to investigate the influence of microstructural control of second phase on toughening effect of toughened ceramic composites, AE (acoustic emission) measurements have been coupled with fracture toughness experiments(SENB and SEPB method). A separation of the fracture toughness and analysis of toughening mechanism was possible using the AE technique. The fracture toughness of hot-pressed materials was estimated to be 3.2 MPam0.5 for monolithic alumina, 4.7 MPam0.5 for Al2O3/20 vol%YAG composite and 6.2 MPam0.5 for Al2O3/20 vol%LaAl11O18 composite. In monolithic Al2O3, toughening does not occur as a result of either microcracking or grain bridging, whereas, composites exhibit toughening effects by both microcracking in the frontal zone and gain bridging in the wake zone, resulting in an improvement of fracture toughness as compared with monolithic Al2O3. The fracture toughness of Al2O3/20 vol%LaAl11O18 composite is higher than that of Al2O3/20 vol%YAG composite. It may be attributed to the elongated microstructure of Al2O3/20 vol%LaAl11O18 composite, resulting relatively greater bridging effect.

• Journal of Powder Materials
• /
• v.5 no.1
• /
• pp.22-27
• /
• 1998

The effect of the $\alpha$/$\beta$ phase fraction on the mechanical properties in silicon nitrides was investigated in part 1. In part II, we describe the role of microstructure on the mechanical properties and contact damage of silicon nitrides with coarse/equiaxed and coarse/elongated microstructures. Grain sizes and shapes were controlled by starting powder. Hertzian indentation using spherical indenter was also used to investigate contact damage behavior. Cone cracks from the spherical indentation were suppressed when the silicon nitride contains coarse and elongated grains. Coarse and elongated grains played an important role of cone crack suppression. The size of quasi-plastic zone does not depend on grain size or shape but depends on the fraction of $\alpha$/$\beta$ phase. A quasi-plastic zone was consisting of microcracks by shear stress during indentation.

• Journal of the Korean Ceramic Society
• /
• v.35 no.12
• /
• pp.1266-1273
• /
• 1998

Al2O3/(5~20vol%)LaAl11O18 composites in which the second phase was dispersed with a elongated grain shape were fabricated using Al2O3 and La2O3 composition by hot-pressing. In order investigate the in-fluence of LaAl11O18 on the toughening of LaAl11O18 on the toughening of Al2O3 matrix composites AE(acoustic emission) analysis was con-ducted together with an evaluation of fracture toughness using of SEPB technique. The degree of AE events occurred in composites were more than those in monolithic alumina. The occurrences of AE event increased with increasing the amount of LaAl11O18 phase in the Al2O3/LaAl11O18 composite is two times higher compared to monolithic alu-mina. The main toughening mechanism was attributed to the bridging of LaAl11O18 grains at tip of pro-pagating crack.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.263-265
• /
• 2009

In this study, ultrafine grained (UFG) oxygen free high conductivity copper (OFHC Cu) having two different grain morphologies, one the severely elongated and the other the equiaxed, was prepared by equal channel angular pressing (ECAP) with routes A and $B_c$, respectively. The results of quasi-static tensile tests at $10^{-1}\;s^{-1}$ and $1\;s^{-1}$ and dynamic compression tests at $10^3\;s^{-1}$ order revealed that the equiaxed UFG Cu exhibited higher strength and less ductility compared to the elongated one. The difference of the plastic flow characteristics between the two were rationalized by considering their dislocation mean free length based on the orientation relationship between the possible slip planes and the loading direction.

• Journal of the Korean Ceramic Society
• /
• v.42 no.8 s.279
• /
• pp.525-531
• /
• 2005

Tailoring the microstructure and the composition of silicon nitride ceramics can have profound effects on their properties. Here it is shown that the grain growth behavior, in particular its anisotropy, is a function of the specific additives, which allow one to tune the microstructure from one consisting of more equiaxed grains to one with very elongated grains. Recent studies are discussed that provide an understanding of the atomic level processes by which these additives influence grain shapes. Next the microstructural (and compositional) parameters are discussed that can be used to modify the thermal conductivity, as well as fracture toughness of silicon nitride ceramics. As a result of the open <0001> channels in $\beta-Si_3N_4$, the c-axis conductivity can be exceptionally high. Thus, the formation of elongated c-axis grains, particularly when aligned can result in conductivity values approaching those of AlN ceramics. In addition, the controlled formation of elongated grains can also be used to significantly enhance the fracture toughness. At the same time, both properties are shown to be affected by the composition of the densification additives. Utilizing such understanding, one will be able to tailor the ceramics to achieve the properties desired for specific applications.

• Transactions of Materials Processing
• /
• v.19 no.2
• /
• pp.95-100
• /
• 2010

Drawing and normalizing are efficient means for controlling strength, fatigue and machinability of free machining steel. Normally strength and machinability are conflicting properties which need to be optimized. In this study, the effects of normalizing temperature and reduction of area on strength, fatigue and machinability were investigated. Fine grains were generated at lower normalizing temperature and fatigue life was increased with decreasing grain size. Matrix was work hardened and elongated with increasing reduction of area. Inclusions also were elongated and cross-sectional area of inclusions along drawing axis was decreased. The effects of work hardening and grain size on fatigue life were significant, but only work hardening affected machinability. Shape and distribution of inclusions after drawing had little effect on fatigue life and machinability.

• Journal of Powder Materials
• /
• v.6 no.3
• /
• pp.246-250
• /
• 1999

The effects of the ${\beta}-Si_3N_4$ starting particle size and $\alpha$/$\beta$ phase transformation during sintering process on the microstructure evolution of Yttrium $\alpha$-Sialon ceramics were investigated. As-received ${\beta}-Si_3N_4$ powder (mean particle size: 0.54$\mu$m) and classified ${\beta}-Si_3N_4$ powder(mean particle size: $0.26\mu{m}$) were used as starting powders. With decreasing the starting particle size, the growth of elongated grains was enhanced, which resulted in the whisker -like microstructure with elongated grains. These results were discussed in relation to the two-dimensional nucleation and growth theory. In the specimen heat treated at $1600^{\circ}C$ for 10h before sintering at $1950^{\circ}C$for 1h under 40atm(2-step sintering), the grain size was smaller than of the 1-step sintering at 195$0^{\circ}C$ for 1h. However, bimodal microstructure evolution were not not remarkable in both sample, which is ascribed to the $\alpha$-phase contents existing in ${\beta}-Si_3N_4$ starting powder.

• Journal of the Korean Ceramic Society
• /
• v.36 no.8
• /
• pp.799-804
• /
• 1999

Composites of SiC-Si3N4 consisted of uniformly distributed elongated $\beta$-Si3N4 grains and equiaxed $\beta$-SiC grains were fabricated with $\beta$-SiC,. $\alpha$-Si3N4 Al2O3 and Y2O3 powders. By hot-pressing and subsequent annelaing elongated $\beta$-Si3N4 grains were grown via$\alpha$longrightarrow$\beta$ phase transformation and equiaxed $\beta$-Si3N4 composites increased with increasing the Si3N4 content owing to the reduced defect size and enhanced crack deflection by elongated $\beta$-Si3N4 grains and the grain boundary strengthening by nitrogen incorporation. Typical flexural strength and fracture toughness of SiC-40 wt% Si3N4 composites were 783 MPa and 4.2 MPa.m1/2 respectively.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.6
• /
• pp.306-316
• /
• 2013

Microstructure and fracture behavior of a multi-phase low-density steel were investigated. After hot-rolling and heat treatment, the microstructure of low-density steel was composed of coarse ferrite grains and elongated bands which include second phases such as austenite, martensite and ${\kappa}$-carbide depending on holding time during isothermal heat treatment. After tensile test, microcracks were observed at martensite or ${\kappa}$-carbide interface in the elongated bands. Coarse ferrite grains showed cleavage fracture behavior regardless of second phase. The cleavage fracture of ferrite could be attributed to their coarse grain size and solute atoms that increase ductile-to-brittle transition temperature of ferrite. Despite of the tendency of cleavage fracture in coarse ferrite grains, a specimen having coarse spheroidized ${\kappa}$-carbide particles in the elongated bands showed high total elongation of 30%. Thus, the easiness of plastic deformation in the elongated band seems to play an important role in retardation of cleavage crack formation in coarse ferrite grains.